CN110499639A - A kind of antibacterial-high imbibition method for sorting of the sustained release of degreasing cotton gauze - Google Patents
A kind of antibacterial-high imbibition method for sorting of the sustained release of degreasing cotton gauze Download PDFInfo
- Publication number
- CN110499639A CN110499639A CN201910733131.3A CN201910733131A CN110499639A CN 110499639 A CN110499639 A CN 110499639A CN 201910733131 A CN201910733131 A CN 201910733131A CN 110499639 A CN110499639 A CN 110499639A
- Authority
- CN
- China
- Prior art keywords
- cotton gauze
- degreasing cotton
- parts
- antibacterial
- sustained release
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of antibacterial-high imbibition method for sorting of the sustained release of degreasing cotton gauze, by SODIUM PERCARBONATE solution heating water bath, degreasing cotton gauze is put into wherein, is neutralized to neutrality with hydrochloric acid solution after oxidation processes, sufficiently wash, dry oxidation processes degreasing cotton gauze;Dissolving the chitosan in acetum, magnetic agitation mixes, wherein by the degreasing cotton gauze dipping of oxidation processes, the oxidation degreasing cotton gauze of dry chitosan processing;It is mixed after vaseline is heated with paraffin oil, kuh-seng seed flavones sustained release pellet, high pressure sterilization, the oxidation degreasing cotton gauze of chitosan processing is immersed, taking-up drains, and ethane via epoxyethane handles to obtain the antibacterial degreasing cotton gauze of sustained release;Polyvinyl alcohol water solution and the modified high hydroscopic resin of water-absorbent material, graphene oxide are mixed and heated, antibacterial degreasing cotton gauze will be sustained and be immersed, taking-up is placed on stamp scraper plate, after scraper is scraped three times back and forth, dries to obtain the antibacterial high imbibition degreasing cotton gauze of sustained release.
Description
Technical field
The invention belongs to gauze fields, and in particular to a kind of antibacterial-high imbibition method for sorting of the sustained release of degreasing cotton gauze.
Background technique
Gauze is widely used in wound as a kind of main medical dressing.Traditional cotton gauze cannot effectively absorb wound
The sepage in face, hemostasis is slow, is unfavorable for wound healing.In addition, needing to frequently replace gauze because gauze imbibition ability is limited, increase
The workload of medical worker.Therefore, a kind of gauze that absorbent is high is prepared to have a very important significance.
Kuh-seng is a kind of traditional Chinese medicine, has significant antibacterial activity, can be used for a certain extent instead of antibiotic
Clinical treatment bacterial infection disease has Small side effects, is not likely to produce the advantages such as drug resistance, thus to its Antibacterial mechanism
And the research of related preparations is drawn great attention.But since natural resources of Chinese medicinal materials destroys seriously, as traditional medication in recent years
The kuh-seng Root yield at position has been unable to meet clinical needs, thus studies the antibacterial activity and its preparation at other positions of kuh-seng plant
Have become trend of the times.
Summary of the invention
The purpose of the present invention is being directed to existing problem, antibacterial-high imbibition of sustained release for providing a kind of degreasing cotton gauze is whole
Reason method, the modified absorben cotton gauze according to this method preparation have excellent antibacterial bacteriostatic performance and absorbent.
The present invention is achieved by the following technical solutions:
A kind of antibacterial-high imbibition method for sorting of the sustained release of degreasing cotton gauze, includes the following steps, following raw materials by weight:
(1) oxidation treatment method of degreasing cotton gauze:
100-200 parts of SODIUM PERCARBONATE solution water-baths are heated to 40-45 DEG C, 10-20 parts of degreasing cotton gauzes are put into wherein, are adjusted
PH is 9, oxidation processes 1-2h, takes out, is neutralized to neutrality with hydrochloric acid solution, sufficiently washing, drying, obtains the degreasing of oxidation processes
Cotton gauze;
Oxidation modification processing first is carried out to degreasing cotton gauze with SODIUM PERCARBONATE, fibre diameter becomes larger after oxidation, and swollen occurs in fiber
Effect, SODIUM PERCARBONATE oxidation cotton gauze can preferably improve the absorbent of gauze, and ultimate strength, elongation at break meet yarn
Cloth application requirement;
(2) the antibacterial processing of the sustained release of degreasing cotton gauze:
6-12 parts of chitosan 1:30 are dissolved in acetum, magnetic agitation mixes, filtration sterilization, at (1) middle gained oxidation
Wherein 2-4h, the drying in 60-65 DEG C of drying box obtain the oxidation degreasing cotton yarn of chitosan processing to the degreasing cotton gauze dipping of reason
Cloth;After 4-8 parts of medical ventolin heating are in a liquid state, with 2-4 parts of medical paraffin oil, 8-16 parts of kuh-seng seed flavones sustained release pellets
The oxidation degreasing cotton gauze of chitosan processing is immersed 5-10min by mixing, high pressure sterilization, and taking-up drains, ethane via epoxyethane
Handle to obtain the antibacterial degreasing cotton gauze of sustained release;
Using glycerin monostearate as adhesive, using lactose as filler, it is yellow that kuh-seng seed is prepared by high-speed molten paddling process
Ketone sustained release pellet, kuh-seng seed flavones has preferable antibacterial activity, and gained sustained release pellet has excellent sustained release biocidal property
Energy;
The degreasing cotton gauze of oxidation processes is sufficiently impregnated the oxidation absorbent cotton of chitosan processing is made in chitosan-acetic acid solution
Gauze;Vaseline, paraffin oil, kuh-seng seed flavones sustained release pellet mixed liquor are configured, then with mixed liquor package chitosan processing
Degreasing cotton gauze is aoxidized, preparation is sustained antibacterial degreasing cotton gauze, has good biocidal property and moisture retention;
(3) the dip coating processing method of degreasing cotton gauze:
27-30 parts of polyvinyl alcohol are added in 90-100 parts of water, are dissolved by heating, 5-9 parts of water-absorbent materials, 1-2 parts of oxidation stones are added
The modified high hydroscopic resin of black alkene stirs evenly, and gained coating agent is heated to 50-55 DEG C, and gained in (2) is sustained antibacterial degreasing
Cotton gauze, which is put into, wherein impregnates 2-3min, and taking-up is placed on stamp scraper plate, and after scraper is scraped three times back and forth, the gauze handled well is put down
It is layered on and bakes on oilpaper, be put into 50-55 DEG C of baking oven and dry, obtain being sustained antibacterial high imbibition degreasing cotton gauze;
Using stalk cellulose, PERFORMANCE OF MODIFIED VERMICULITE as raw material, citric acid is crosslinking agent, prepares water-absorbent material, stalk cellulose and modification
Vermiculite forms rough surface, has concave-convex level and a large amount of folds, loose porous, the biggish composite material of specific surface area, these
Design feature is all the structure internal cause of the composition good water absorbing properties of water-absorbent material, meanwhile, water-absorbent material has good salt tolerant energy
Power;
To obtain comprehensive performance preferably super absorbent resin, using graphene oxide to Sodium Polyacrylate system high hydroscopic resin into
Row is modified, and special structure plays inhibition to the loss of the Free water in system to graphene oxide in the polymer, is made
Modified resin shows good water-retaining property, and the addition of graphene oxide effectively improves the water absorbing capacity of resin, improves its salt tolerant
Property, improve the thermal stability of resin;
Polyvinyl alcohol is compounded into prepares coating agent with water-absorbent material, the modified high hydroscopic resin of graphene oxide, will be sustained antibacterial de-
Rouge cotton gauze carries out coating treatment, improves the absorbent of medical cotton gauze, the imbibition of modified gauze, ventilative, softness is good;
Further, the concentration of SODIUM PERCARBONATE solution is 0.1-0.2g/L, concentration of hydrochloric acid solution 6-9% in step (1).
Further, step (2) high speed melting paddling process prepares kuh-seng seed flavones sustained release pellet: 9-11 parts are bonded
Agent glycerin monostearate is mixed with 4-6 parts of filler lactose, adds 7-8 parts of kuh-seng seed chromocor extracts, and mixing speed is
300rpm, high-speed molten stirring granulation, is cooled to room temperature, obtains kuh-seng seed flavones sustained release pellet at 50-58 DEG C;
Acetum concentration is 1-2%.
Further, in step (3) water-absorbent material preparation: 5-10 parts of stalk cellulose 1:20 are dissolved in -5 DEG C of hydrogen-oxygen
Change sodium-urea liquid, stirring, microwave is gelatinized 2-4min, 2-4 parts of PERFORMANCE OF MODIFIED VERMICULITEs, 8-16 parts of citric acid-trisodium citrates are added,
Magnetic agitation 50-70min, the cross-linking reaction 50-60min at 70-75 DEG C are washed 3-5 times, and drying to constant weight, are crushed, are crossed 100
Mesh obtains water-absorbent material;
The method of modifying of vermiculite: 2-4 parts of expanded vermiculites are mixed with 8% hydrochloric acid 1:20, in 80-85 DEG C of stirred in water bath 1-2h, water
It is washed till neutrality, PERFORMANCE OF MODIFIED VERMICULITE is dried to obtain at 60-65 DEG C;
The concentration of sodium hydroxide is 6% in sodium hydroxide-urea liquid, the concentration of urea is 10%, and citric acid-trisodium citrate rubs
You are than being 1:1.
Further, in step (3) the modified high hydroscopic resin of graphene oxide preparation: be to 10-20 parts of mass fractions
1-2 parts of Sodium Polyacrylate system high hydroscopic resins are added in the graphene oxide solution of 0.1-0.2%, are stirred to react to obtain graphite oxide
Alkene is modified high hydroscopic resin.
The present invention has the advantage that compared with prior art
(1) oxidation modification processing first is carried out to degreasing cotton gauze with SODIUM PERCARBONATE, fibre diameter becomes larger after oxidation, and fiber moistens
Swollen effect, SODIUM PERCARBONATE oxidation cotton gauze can preferably improve the absorbent of gauze, and ultimate strength, elongation at break meet
Gauze application requirement.
(2) using glycerin monostearate as adhesive, using lactose as filler, kuh-seng is prepared by high-speed molten paddling process
Seed flavones sustained release pellet, kuh-seng seed flavones has preferable antibacterial activity, and gained sustained release pellet has excellent sustained release
Bacteriostasis property;
The degreasing cotton gauze of oxidation processes is sufficiently impregnated the oxidation absorbent cotton of chitosan processing is made in chitosan-acetic acid solution
Gauze;Vaseline, paraffin oil, kuh-seng seed flavones sustained release pellet mixed liquor are configured, then with mixed liquor package chitosan processing
Degreasing cotton gauze is aoxidized, preparation is sustained antibacterial degreasing cotton gauze, has good biocidal property and moisture retention.
(2) using stalk cellulose, PERFORMANCE OF MODIFIED VERMICULITE as raw material, citric acid is crosslinking agent, prepares water-absorbent material, stalk cellulose
Rough surface is formd with PERFORMANCE OF MODIFIED VERMICULITE, has concave-convex level and a large amount of folds, loose porous, the biggish composite wood of specific surface area
Material, these design features are all the structure internal causes of the composition good water absorbing properties of water-absorbent material, meanwhile, water-absorbent material has good
Salt resistance ability;
To obtain comprehensive performance preferably super absorbent resin, using graphene oxide to Sodium Polyacrylate system high hydroscopic resin into
Row is modified, and special structure plays inhibition to the loss of the Free water in system to graphene oxide in the polymer, is made
Modified resin shows good water-retaining property, and the addition of graphene oxide effectively improves the water absorbing capacity of resin, improves its salt tolerant
Property, improve the thermal stability of resin;
Polyvinyl alcohol is compounded into prepares coating agent with water-absorbent material, the modified high hydroscopic resin of graphene oxide, will be sustained antibacterial de-
Rouge cotton gauze carries out coating treatment, improves the absorbent of medical cotton gauze, the imbibition of modified gauze, ventilative, softness is good.
Specific embodiment
Embodiment 1
A kind of antibacterial-high imbibition method for sorting of the sustained release of degreasing cotton gauze, which is characterized in that include the following steps, following raw materials
By weight:
(1) oxidation treatment method of degreasing cotton gauze:
100 parts of SODIUM PERCARBONATE solution water-baths are heated to 40 DEG C, 10 parts of degreasing cotton gauzes are put into wherein, adjusting pH is 9, oxidation
2h is handled, takes out, be neutralized to neutrality with hydrochloric acid solution, sufficiently washing, drying, obtains the degreasing cotton gauze of oxidation processes;
Wherein, the concentration of SODIUM PERCARBONATE solution is 0.1g/L, concentration of hydrochloric acid solution 6%;
(2) the antibacterial processing of the sustained release of degreasing cotton gauze:
6 parts of chitosan 1:30 are dissolved in acetum, magnetic agitation mixes, filtration sterilization, by gained oxidation processes in (1)
Wherein 2h, the drying in 60 DEG C of drying boxes obtain the oxidation degreasing cotton gauze of chitosan processing to degreasing cotton gauze dipping;By 4 parts
After medical ventolin heating is in a liquid state, mixed with 2 parts of medical paraffin oil, 8 parts of kuh-seng seed flavones sustained release pellets, high pressure sterilization,
The oxidation degreasing cotton gauze of chitosan processing is immersed 5min, taking-up drains, and ethane via epoxyethane handles to be sustained antibacterial de-
Rouge cotton gauze;
Wherein, high-speed molten paddling process prepares kuh-seng seed flavones sustained release pellet: by 9 parts of adhesive glycerin monostearates and 4
Part filler lactose mixing, adds 7 parts of kuh-seng seed chromocor extracts, mixing speed 300rpm, high-speed molten is stirred at 50 DEG C
Mixing grain, is cooled to room temperature, and obtains kuh-seng seed flavones sustained release pellet;
Acetum concentration is 1%;
(3) the dip coating processing method of degreasing cotton gauze:
27 parts of polyvinyl alcohol are added in 90 parts of water, are dissolved by heating, the modified high suction of 5 parts of water-absorbent materials, 1 part of graphene oxide is added
Water-resin stirs evenly, and gained coating agent is heated to 50 DEG C, and gained in (2) is sustained antibacterial degreasing cotton gauze and is put into and is wherein soaked
3min is steeped, taking-up is placed on stamp scraper plate, after scraper is scraped three times back and forth, the gauze handled well is laid in and is baked on oilpaper, is put
Enter and dried in 50 DEG C of baking oven, obtains being sustained antibacterial high imbibition degreasing cotton gauze;
Wherein, 5 parts of stalk cellulose 1:20: being dissolved in -5 DEG C of sodium hydroxide-urea liquid by the preparation of water-absorbent material, stirring,
Microwave is gelatinized 2min, 2 parts of PERFORMANCE OF MODIFIED VERMICULITEs, 8 parts of citric acid-trisodium citrates is added, magnetic agitation 50min is crosslinked at 70 DEG C
60min is reacted, is washed 3 times, drying to constant weight, crushes, sieves with 100 mesh sieve to obtain water-absorbent material;
The method of modifying of vermiculite: 2 parts of expanded vermiculites are mixed with 8% hydrochloric acid 1:20, in 80 DEG C of stirred in water bath 2h, are washed to
Property, PERFORMANCE OF MODIFIED VERMICULITE is dried to obtain at 60 DEG C;
The concentration of sodium hydroxide is 6% in sodium hydroxide-urea liquid, the concentration of urea is 10%, and citric acid-trisodium citrate rubs
You are than being 1:1;
The preparation of the modified high hydroscopic resin of graphene oxide: it is added in the graphene oxide solution for being 0.1% to 10 parts of mass fractions
1 part of Sodium Polyacrylate system high hydroscopic resin is stirred to react to obtain the modified high hydroscopic resin of graphene oxide.
Embodiment 2
A kind of antibacterial-high imbibition method for sorting of the sustained release of degreasing cotton gauze, which is characterized in that include the following steps, following raw materials
By weight:
(1) oxidation treatment method of degreasing cotton gauze:
200 parts of SODIUM PERCARBONATE solution water-baths are heated to 45 DEG C, 20 parts of degreasing cotton gauzes are put into wherein, adjusting pH is 9, oxidation
1h is handled, takes out, be neutralized to neutrality with hydrochloric acid solution, sufficiently washing, drying, obtains the degreasing cotton gauze of oxidation processes;
Wherein, the concentration of SODIUM PERCARBONATE solution is 0.2g/L, concentration of hydrochloric acid solution 9%;
(2) the antibacterial processing of the sustained release of degreasing cotton gauze:
12 parts of chitosan 1:30 are dissolved in acetum, magnetic agitation mixes, filtration sterilization, by gained oxidation processes in (1)
Degreasing cotton gauze dipping wherein 4h, it is dry in 65 DEG C of drying boxes, obtain the oxidation degreasing cotton gauze of chitosan processing;By 8
After part medical ventolin heating is in a liquid state, mixed with 4 parts of medical paraffin oil, 16 parts of kuh-seng seed flavones sustained release pellets, high pressure is gone out
The oxidation degreasing cotton gauze of chitosan processing is immersed 10min by bacterium, and taking-up drains, and ethane via epoxyethane handles to obtain sustained release suppression
Bacterium degreasing cotton gauze;
Wherein, high-speed molten paddling process prepares kuh-seng seed flavones sustained release pellet: by 11 parts of adhesive glycerin monostearates and 6
Part filler lactose mixing, adds 8 parts of kuh-seng seed chromocor extracts, mixing speed 300rpm, high-speed molten is stirred at 58 DEG C
Mixing grain, is cooled to room temperature, and obtains kuh-seng seed flavones sustained release pellet;
Acetum concentration is 2%;
(3) the dip coating processing method of degreasing cotton gauze:
30 parts of polyvinyl alcohol are added in 100 parts of water, are dissolved by heating, it is modified high that 9 parts of water-absorbent materials, 2 parts of graphene oxides are added
Water-absorbing resin stirs evenly, and gained coating agent is heated to 55 DEG C, and gained in (2) is sustained antibacterial degreasing cotton gauze and is put into wherein
2min is impregnated, taking-up is placed on stamp scraper plate, and after scraper is scraped three times back and forth, the gauze handled well is laid in and is baked on oilpaper,
It is put into 55 DEG C of baking oven and dries, obtain being sustained antibacterial high imbibition degreasing cotton gauze;
Wherein, 10 parts of stalk cellulose 1:20: being dissolved in -5 DEG C of sodium hydroxide-urea liquid by the preparation of water-absorbent material, stirring,
Microwave is gelatinized 4min, 4 parts of PERFORMANCE OF MODIFIED VERMICULITEs, 16 parts of citric acid-trisodium citrates is added, magnetic agitation 70min is crosslinked at 75 DEG C
50min is reacted, is washed 5 times, drying to constant weight, crushes, sieves with 100 mesh sieve to obtain water-absorbent material;
The method of modifying of vermiculite: 4 parts of expanded vermiculites are mixed with 8% hydrochloric acid 1:20, in 85 DEG C of stirred in water bath 1h, are washed to
Property, PERFORMANCE OF MODIFIED VERMICULITE is dried to obtain at 65 DEG C;
The concentration of sodium hydroxide is 6% in sodium hydroxide-urea liquid, the concentration of urea is 10%, and citric acid-trisodium citrate rubs
You are than being 1:1;
The preparation of the modified high hydroscopic resin of graphene oxide: it is added in the graphene oxide solution for being 0.2% to 20 parts of mass fractions
2 parts of Sodium Polyacrylate system high hydroscopic resins are stirred to react to obtain the modified high hydroscopic resin of graphene oxide.
Comparative example 1
This comparative example 1 compared with Example 1, is not added in step (1) using kuh-seng seed flavones sustained release pellet, removes this
Outer method and step is all the same.
Comparative example 2
This comparative example 2 compared with Example 2, is not added in step (3) using water-absorbent material, method and step in addition to this
It is all the same.
Blank degreasing cotton gauze of the control group without any modification
In order to compare the performance of modified absorben cotton gauze prepared by the present invention, to above-described embodiment 1, embodiment 2, comparative example
1,2 method of comparative example corresponding obtained modified absorben cotton gauze and control group are corresponding without any modification
Blank degreasing cotton gauze carries out performance detection according to professional standard, and specific correlation data is as shown in table 1 below:
Bacteria resistance detection: taking staphylococcus aureus and Escherichia coli, and turbidity containing bacterium number is the bacteria suspension of 0.5mcf, with doctor
Bacterium is evenly coated in put down with cotton swab and is pulled, every kind of bacterium repeats 3 pieces of plates, on the super-clean bench, will be obtained de- with sterile mirror
Rouge cotton gauze is attached on ware containing bacterium, and the antibacterial bacteriostatic rate around degreasing cotton gauze is surveyed after cultivating 24 hours in insulating box;
The test of gauze absorbent: it referring to the hygroscopic method of surface of a wound dressing is commonly tested in the world, is weighed using moisture absorption
Method tests the absorbent of gauze, concrete operations are as follows: tailor 5cm × 5cm gauze, accurately weigh up its dry weight W0, it is put into 100mL
In deionized water, imbibition 30min takes out gauze, naturally flatly after vertical hanging 30s, weighs cotton gauze weight W at once1, yarn
Imbibition rate Q=(W of cloth1−W0)/W0;
Table 1
There is excellent antibacterial bacteriostatic performance and absorbent according to the modified absorben cotton gauze of present invention method preparation,
Air penetrability is 3890mm/s, and the imbibition of modified absorben cotton gauze, ventilative, softness is good;
It is not added in comparative example 1 using kuh-seng seed flavones sustained release pellet, causes modified absorben cotton gauze to golden yellow
The antibacterial bacteriostatic performance of staphylococcus and Escherichia coli reduces, but presses down still better than the antibacterial of control group blank degreasing cotton gauze
Bacterium performance;Be not added in comparative example 2 causes the imbibition rate of modified absorben cotton gauze to reduce using water-absorbent material, still
Still better than the absorbent of control group blank degreasing cotton gauze.
Claims (5)
1. a kind of antibacterial-high imbibition method for sorting of the sustained release of degreasing cotton gauze, which is characterized in that include the following steps, Xia Shuyuan
Expect by weight:
(1) oxidation treatment method of degreasing cotton gauze:
100-200 parts of SODIUM PERCARBONATE solution water-baths are heated to 40-45 DEG C, 10-20 parts of degreasing cotton gauzes are put into wherein, are adjusted
PH is 9, oxidation processes 1-2h, takes out, is neutralized to neutrality with hydrochloric acid solution, sufficiently washing, drying, obtains the degreasing of oxidation processes
Cotton gauze;
The antibacterial processing of the sustained release of degreasing cotton gauze:
6-12 parts of chitosan 1:30 are dissolved in acetum, magnetic agitation mixes, filtration sterilization, at (1) middle gained oxidation
Wherein 2-4h, the drying in 60-65 DEG C of drying box obtain the oxidation degreasing cotton yarn of chitosan processing to the degreasing cotton gauze dipping of reason
Cloth;After 4-8 parts of medical ventolin heating are in a liquid state, with 2-4 parts of medical paraffin oil, 8-16 parts of kuh-seng seed flavones sustained release pellets
The oxidation degreasing cotton gauze of chitosan processing is immersed 5-10min by mixing, high pressure sterilization, and taking-up drains, ethane via epoxyethane
Handle to obtain the antibacterial degreasing cotton gauze of sustained release;
(3) the dip coating processing method of degreasing cotton gauze:
27-30 parts of polyvinyl alcohol are added in 90-100 parts of water, are dissolved by heating, 5-9 parts of water-absorbent materials, 1-2 parts of oxidation stones are added
The modified high hydroscopic resin of black alkene stirs evenly, and gained coating agent is heated to 50-55 DEG C, and gained in (2) is sustained antibacterial degreasing
Cotton gauze, which is put into, wherein impregnates 2-3min, and taking-up is placed on stamp scraper plate, and after scraper is scraped three times back and forth, the gauze handled well is put down
It is layered on and bakes on oilpaper, be put into 50-55 DEG C of baking oven and dry, obtain being sustained antibacterial high imbibition degreasing cotton gauze.
2. a kind of antibacterial-high imbibition method for sorting of the sustained release of degreasing cotton gauze according to claim 1, which is characterized in that
The concentration of SODIUM PERCARBONATE solution is 0.1-0.2g/L, concentration of hydrochloric acid solution 6-9% in step (1).
3. a kind of antibacterial-high imbibition method for sorting of the sustained release of degreasing cotton gauze according to claim 1, which is characterized in that
Step (2) high speed melting paddling process prepares kuh-seng seed flavones sustained release pellet: by 9-11 parts of adhesive glycerin monostearates
It is mixed with 4-6 parts of filler lactose, adds 7-8 parts of kuh-seng seed chromocor extracts, mixing speed 300rpm, at 50-58 DEG C
High-speed molten stirring granulation, is cooled to room temperature, obtains kuh-seng seed flavones sustained release pellet;
Acetum concentration is 1-2%.
4. a kind of antibacterial-high imbibition method for sorting of the sustained release of degreasing cotton gauze according to claim 1, which is characterized in that
The preparation of water-absorbent material in step (3): 5-10 parts of stalk cellulose 1:20 are dissolved in -5 DEG C of sodium hydroxide-urea liquid, are stirred
It mixes, microwave gelatinization 2-4min, addition 2-4 parts of PERFORMANCE OF MODIFIED VERMICULITEs, 8-16 parts of citric acid-trisodium citrates, magnetic agitation 50-70min,
The cross-linking reaction 50-60min at 70-75 DEG C is washed 3-5 times, and drying to constant weight, crushes, sieves with 100 mesh sieve to obtain water-absorbent material;
The method of modifying of vermiculite: 2-4 parts of expanded vermiculites are mixed with 8% hydrochloric acid 1:20, in 80-85 DEG C of stirred in water bath 1-2h, water
It is washed till neutrality, PERFORMANCE OF MODIFIED VERMICULITE is dried to obtain at 60-65 DEG C;
The concentration of sodium hydroxide is 6% in sodium hydroxide-urea liquid, the concentration of urea is 10%, and citric acid-trisodium citrate rubs
You are than being 1:1.
5. a kind of antibacterial-high imbibition method for sorting of the sustained release of degreasing cotton gauze according to claim 1, which is characterized in that
The preparation of the modified high hydroscopic resin of graphene oxide in step (3): the graphite oxide for being 0.1-0.2% to 10-20 parts of mass fractions
1-2 parts of Sodium Polyacrylate system high hydroscopic resins are added in alkene solution, are stirred to react to obtain the modified high hydroscopic resin of graphene oxide.