CN110482863A - White opaque glaze, white opaque glaze ceramic and preparation method thereof - Google Patents
White opaque glaze, white opaque glaze ceramic and preparation method thereof Download PDFInfo
- Publication number
- CN110482863A CN110482863A CN201910864949.9A CN201910864949A CN110482863A CN 110482863 A CN110482863 A CN 110482863A CN 201910864949 A CN201910864949 A CN 201910864949A CN 110482863 A CN110482863 A CN 110482863A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- white opaque
- opaque glaze
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of white opaque glaze, white opaque glaze ceramic and preparation method thereof, the white opaque glaze includes the raw material of following parts by weight: 20~25 parts of potassium feldspar, 22~27 parts of albite, 8~12 parts of calcite, quartzy 16~20 parts, 10~14 parts of talcum powder, 4.5~5.5 parts of bentonite, 6~8 parts of strontium oxide strontia, 5~7 parts of barium monoxide, 6~9 parts of magnesia, 5~6 parts of titanium oxide, 2.5~3.5 parts of barium zirconium phthalate, 15~20 parts of zirconium silicate, 4~6 parts of yttrium oxide.The advantages that white opaque glaze ceramic produced by the present invention, glaze (opaque glaze) have opaque effect good, and glaze is flat and smooth, glossiness is good, exquisite beautiful, and whiteness is high, the wear-resisting property of glaze is good and hardness is high.
Description
Technical field
The present invention relates to ceramic fields, and in particular to white opaque glaze, white opaque glaze ceramic and its preparation
Method.
Background technique
Opaque glaze is a kind of method of common ceramic decoration, is widely used.Opaque glaze, that is, White-opalescent bright glaze.It
It is due to, there is the 2nd small phase of, volume different from host glass phase refractive index or the 3rd phase substance, working as light in glaze glass
When passing through glaze layer, milkiness particle makes light generate scattering process to cause the lighttight phenomenon of glaze layer.
According to the coherent condition of milkiness particle, opaque glaze can be divided into 3 classes: first is that there are a certain number of micro- in host glass
Small crystals, referred to as crystal phase opaque glaze;Second is that liquid-liquid split-phase occurs in cooling procedure for glaze melt, isolated in host glass
The higher 2nd phase glass of the small dispersion degree of volume, referred to as split-phase opaque glaze;Third is that being existed below in glaze surface layer of glass a large amount of micro-
Minute bubbles, referred to as gas phase opaque glaze.Wherein crystal phase opaque glaze is divided into 2 kinds of crystal grain opaque glaze of original grain opaque glaze and precipitation again.
The former is the milkiness that glaze is realized by additional infusibility substance, most common to have the turbid glaze of zirconium;The latter is in sintering process from glaze glass
Spontaneous precipitation milkiness particle causes milkiness in glass.
Ceramic is one of most common utensil in people's daily life, and ceramic development history is the one of Chinese civilization history
A important component part, wherein the invention and development of ceramics have more unique meaning, with the development of modern science technology,
Occur many new ceramic kinds again in the last hundred years, they do not use or be rarely employed the tradition pottery such as clay, feldspar, quartz
Porcelain raw material, but other special materials are used, or even be expanded to non-silicate, the range of non-oxidized substance, and there is many
New technique makes ceramics be provided with various specific functions.
Coloring, glazing are a kind of effective means for increasing ceramic texture and aesthetic feeling on the surface of ceramic, and
And the artistic effect that each glaze colours or pattern rise is different, have currently on the market various glaze colours, pattern or
Its combination of person.Glaze various types in the market, such as opaque glaze, but there is also some problems: glaze opaque effect is not good enough,
Whiteness is not high enough, and appearance is not exquisite enough;The wear-resisting property of glaze is poor and hardness is lower.
Summary of the invention
Based on the above situation, the purpose of the present invention is to provide white opaque glaze, white opaque glaze ceramic and its systems
Preparation Method can effectively solve problem above.
In order to solve the above technical problems, present invention provide the technical scheme that
A kind of white opaque glaze, the raw material including following parts by weight: 20~25 parts of potassium feldspar, 22~27 parts of albite, side
Solve 8~12 parts of stone, quartzy 16~20 parts, 10~14 parts of talcum powder, 4.5~5.5 parts of bentonite, 6~8 parts of strontium oxide strontia, barium monoxide 5
~7 parts, 6~9 parts of magnesia, 5~6 parts of titanium oxide, 2.5~3.5 parts of barium zirconium phthalate, 15~20 parts of zirconium silicate, yttrium oxide 4~6
Part.
Preferably, the white opaque glaze includes the raw material of following parts by weight: 22 parts of potassium feldspar, 24.5 parts of albite, side
Solve 10.5 parts of stone, quartzy 18.4 parts, 12 parts of talcum powder, 5 parts of bentonite, 7.5 parts of strontium oxide strontia, 6.2 parts of barium monoxide, magnesia 7.7
Part, 5.5 parts of titanium oxide, 3.1 parts of barium zirconium phthalate, 18 parts of zirconium silicate, 5 parts of yttrium oxide.
Preferably, the white opaque glaze further includes the raw material of following parts by weight: 4~7 parts of high boron frit.
Preferably, the white opaque glaze further includes the raw material of following parts by weight: 5.8 parts of high boron frit.
Preferably, the titanium oxide is nano-titanium dioxide.
Preferably, the boron content of the high boron frit is 10~15%, and lead content is less than 0.01%.
The present invention also provides a kind of white opaque glaze ceramics, including green body and the glaze for being covered in the billet surface
Layer, the glaze layer are foregoing white opaque glaze.
The present invention also provides the preparation methods of the white opaque glaze ceramic described in one kind, including the following steps:
A, following raw material: potassium feldspar, albite, calcite, quartz, talcum powder, bentonite, oxidation is weighed by weight
Strontium, barium monoxide, magnesia, titanium oxide, barium zirconium phthalate, zirconium silicate, yttrium oxide and high boron frit;
B, after mixing weighed each raw material, mixture is obtained, using ball mill 20~30min of ball milling, wherein when ball milling,
The weight ratio of mixture, ball and water are as follows: 1:2:(0.6~0.7);
C, 200 meshes are crossed, 20~25min of froth in vacuum is then carried out and obtains glaze slip, continue to stir and contain consolidating for glaze slip
Amount is adjusted to 60~65%;
D, the obtained glaze slip of step C is imposed on into billet surface, glazing is with a thickness of 0.7~0.8mm;It is warming up to 1190 again~
1250 DEG C, heating rate is 3 DEG C/min;It carries out glaze firing 70~90min hours, then is cooled to 250 DEG C of heat preservation 2h, be cooled to room
Temperature is to get white opaque glaze ceramic.
Compared with prior art, the present invention have the following advantages that and the utility model has the advantages that
White opaque glaze of the invention is made up of selected raw material, and rational proportion, selected appropriate proportion potassium feldspar,
Albite, calcite, quartz, talcum powder, bentonite, strontium oxide strontia, barium monoxide, magnesia, titanium oxide, barium zirconium phthalate, zirconium silicate,
Yttrium oxide and high boron frit, had not only given full play to respective advantage, but also be complementary to one another, had mutually promoted, and the quality for promoting product is stablized
Property, white opaque glaze ceramic obtained, glaze (opaque glaze) is good with opaque effect, and glaze is flat and smooth, glossiness is good,
The advantages that exquisite beautiful, and whiteness is high, the wear-resisting property of glaze is good and hardness is high.
The present invention selects titanium oxide, barium zirconium phthalate and zirconium silicate as compound opacifier, and potassium feldspar, the sodium suitably matched is long
Stone, calcite, quartz, talcum powder, bentonite, strontium oxide strontia, barium monoxide, magnesia, yttrium oxide and high boron frit, according to vitrifying
Basic principle prepares the opaque glaze of the compound crystal phase with titanium oxide and zirconium silicate, last white opaque glaze obtained
The advantages that ceramic, glaze (opaque glaze) have opaque effect good, and glaze is flat and smooth, glossiness is good, exquisite beautiful, and it is white
Degree is high, and the wear-resisting property of glaze is good and hardness is high.
Preparation method simple process of the invention, it is easy to operate.
Specific embodiment
It is right combined with specific embodiments below in order to make those skilled in the art more fully understand technical solution of the present invention
The preferred embodiments of the invention are described, but should not be understood as the limitation to this patent.
Test method described in following embodiments or test method are unless otherwise specified conventional method;The reagent
And material is obtained from routine business approach, or prepare in conventional manner unless otherwise specified.
Green body of the present invention can be made according to conventional method in that art, repeat no more its production method, and shape can be with
It is arbitrary shape;It can be used to carry out glazing using glaze slip of the invention, subsequently into lower one of work after sizing, air-drying
Sequence.
Embodiment 1:
A kind of white opaque glaze, the raw material including following parts by weight: 20~25 parts of potassium feldspar, 22~27 parts of albite, side
Solve 8~12 parts of stone, quartzy 16~20 parts, 10~14 parts of talcum powder, 4.5~5.5 parts of bentonite, 6~8 parts of strontium oxide strontia, barium monoxide 5
~7 parts, 6~9 parts of magnesia, 5~6 parts of titanium oxide, 2.5~3.5 parts of barium zirconium phthalate, 15~20 parts of zirconium silicate, yttrium oxide 4~6
Part.
Preferably, the white opaque glaze includes the raw material of following parts by weight: 22 parts of potassium feldspar, 24.5 parts of albite, side
Solve 10.5 parts of stone, quartzy 18.4 parts, 12 parts of talcum powder, 5 parts of bentonite, 7.5 parts of strontium oxide strontia, 6.2 parts of barium monoxide, magnesia 7.7
Part, 5.5 parts of titanium oxide, 3.1 parts of barium zirconium phthalate, 18 parts of zirconium silicate, 5 parts of yttrium oxide.
Preferably, the white opaque glaze further includes the raw material of following parts by weight: 4~7 parts of high boron frit.
Preferably, the white opaque glaze further includes the raw material of following parts by weight: 5.8 parts of high boron frit.
Preferably, the titanium oxide is nano-titanium dioxide.
Preferably, the boron content of the high boron frit is 10~15%, and lead content is less than 0.01%.
The present embodiment also provides a kind of white opaque glaze ceramic, including green body and the glaze for being covered in the billet surface
Layer, the glaze layer are foregoing white opaque glaze.
The present embodiment also provides the preparation method of white opaque glaze ceramic described in one kind, including the following steps:
A, following raw material: potassium feldspar, albite, calcite, quartz, talcum powder, bentonite, oxidation is weighed by weight
Strontium, barium monoxide, magnesia, titanium oxide, barium zirconium phthalate, zirconium silicate, yttrium oxide and high boron frit;
B, after mixing weighed each raw material, mixture is obtained, using ball mill 20~30min of ball milling, wherein when ball milling,
The weight ratio of mixture, ball and water are as follows: 1:2:(0.6~0.7);
C, 200 meshes are crossed, 20~25min of froth in vacuum is then carried out and obtains glaze slip, continue to stir and contain consolidating for glaze slip
Amount is adjusted to 60~65%;
D, the obtained glaze slip of step C is imposed on into billet surface, glazing is with a thickness of 0.7~0.8mm;It is warming up to 1190 again~
1250 DEG C, heating rate is 3 DEG C/min;It carries out glaze firing 70~90min hours, then is cooled to 250 DEG C of heat preservation 2h, be cooled to room
Temperature is to get white opaque glaze ceramic.
Embodiment 2:
It is a kind of white opaque glaze, the raw material including following parts by weight: 20 parts of potassium feldspar, 22 parts of albite, 8 parts of calcite,
Quartzy 16 parts, 10 parts of talcum powder, 4.5 parts of bentonite, 6 parts of strontium oxide strontia, 5 parts of barium monoxide, 6 parts of magnesia, 5 parts of titanium oxide, zirconium titanium
2.5 parts of sour barium, 15 parts of zirconium silicate, 4 parts of yttrium oxide.
In the present embodiment, the white opaque glaze further includes the raw material of following parts by weight: 4 parts of high boron frit.
In the present embodiment, the titanium oxide is nano-titanium dioxide.
In the present embodiment, the boron content of the high boron frit is 10%, and lead content is less than 0.01%.
The present invention also provides a kind of white opaque glaze ceramics, including green body and the glaze for being covered in the billet surface
Layer, the glaze layer are foregoing white opaque glaze.
In the present embodiment, the preparation method of the white opaque glaze ceramic, including the following steps:
A, following raw material: potassium feldspar, albite, calcite, quartz, talcum powder, bentonite, oxidation is weighed by weight
Strontium, barium monoxide, magnesia, titanium oxide, barium zirconium phthalate, zirconium silicate, yttrium oxide and high boron frit;
B, after mixing weighed each raw material, mixture is obtained, using ball mill ball milling 20min, wherein when ball milling, mixing
The weight ratio of material, ball and water are as follows: 1:2:0.6;
C, 200 meshes are crossed, froth in vacuum 20min is then carried out and obtains glaze slip, continue stirring and by the solid content tune of glaze slip
Section is 60%;
D, the obtained glaze slip of step C is imposed on into billet surface, glazing is with a thickness of 0.8mm;It is warming up to 1190 DEG C again, heating speed
Degree is 3 DEG C/min;Glaze firing 70min hours is carried out, then is cooled to 250 DEG C of heat preservation 2h, is cooled to room temperature to get white milkiness glazed pottery
Ceramic products.
Embodiment 3:
It is a kind of white opaque glaze, the raw material including following parts by weight: 25 parts of potassium feldspar, 27 parts of albite, 12 parts of calcite,
Quartzy 20 parts, 14 parts of talcum powder, 5.5 parts of bentonite, 8 parts of strontium oxide strontia, 7 parts of barium monoxide, 9 parts of magnesia, 6 parts of titanium oxide, zirconium titanium
3.5 parts of sour barium, 20 parts of zirconium silicate, 6 parts of yttrium oxide.
In the present embodiment, the white opaque glaze further includes the raw material of following parts by weight: 7 parts of high boron frit.
In the present embodiment, the titanium oxide is nano-titanium dioxide.
In the present embodiment, the boron content of the high boron frit is 15%, and lead content is less than 0.01%.
The present invention also provides a kind of white opaque glaze ceramics, including green body and the glaze for being covered in the billet surface
Layer, the glaze layer are foregoing white opaque glaze.
In the present embodiment, the preparation method of the white opaque glaze ceramic, including the following steps:
A, following raw material: potassium feldspar, albite, calcite, quartz, talcum powder, bentonite, oxidation is weighed by weight
Strontium, barium monoxide, magnesia, titanium oxide, barium zirconium phthalate, zirconium silicate, yttrium oxide and high boron frit;
B, after mixing weighed each raw material, mixture is obtained, using ball mill ball milling 30min, wherein when ball milling, mixing
The weight ratio of material, ball and water are as follows: 1:2:0.7;
C, 200 meshes are crossed, froth in vacuum 25min is then carried out and obtains glaze slip, continue stirring and by the solid content tune of glaze slip
Section is 65%;
D, the obtained glaze slip of step C is imposed on into billet surface, glazing is with a thickness of 0.7mm;It is warming up to 1250 DEG C again, heating speed
Degree is 3 DEG C/min;Glaze firing 90min hours is carried out, then is cooled to 250 DEG C of heat preservation 2h, is cooled to room temperature to get white milkiness glazed pottery
Ceramic products.
Embodiment 4:
A kind of white opaque glaze, the raw material including following parts by weight: 22 parts of potassium feldspar, 24.5 parts of albite, calcite
10.5 parts, quartzy 18.4 parts, 12 parts of talcum powder, 5 parts of bentonite, 7.5 parts of strontium oxide strontia, 6.2 parts of barium monoxide, 7.7 parts of magnesia, oxygen
Change 5.5 parts of titanium, 3.1 parts of barium zirconium phthalate, 18 parts of zirconium silicate, 5 parts of yttrium oxide.
In the present embodiment, the white opaque glaze further includes the raw material of following parts by weight: 5.8 parts of high boron frit.
In the present embodiment, the titanium oxide is nano-titanium dioxide.
In the present embodiment, the boron content of the high boron frit is 13%, and lead content is less than 0.01%.
The present invention also provides a kind of white opaque glaze ceramics, including green body and the glaze for being covered in the billet surface
Layer, the glaze layer are foregoing white opaque glaze.
In the present embodiment, the preparation method of the white opaque glaze ceramic, including the following steps:
A, following raw material: potassium feldspar, albite, calcite, quartz, talcum powder, bentonite, oxidation is weighed by weight
Strontium, barium monoxide, magnesia, titanium oxide, barium zirconium phthalate, zirconium silicate, yttrium oxide and high boron frit;
B, after mixing weighed each raw material, mixture is obtained, using ball mill ball milling 25min, wherein when ball milling, mixing
The weight ratio of material, ball and water are as follows: 1:2:0.67;
C, 200 meshes are crossed, froth in vacuum 22min is then carried out and obtains glaze slip, continue stirring and by the solid content tune of glaze slip
Section is 63%;
D, the obtained glaze slip of step C is imposed on into billet surface, glazing is with a thickness of 0.75mm;It is warming up to 1230 DEG C again, heating
Speed is 3 DEG C/min;Glaze firing 80min hours is carried out, then is cooled to 250 DEG C of heat preservation 2h, is cooled to room temperature to get white opaque glaze
Ceramic.
The white opaque glaze ceramic and common milkiness glazed pottery that the embodiment of the present invention 2 to embodiment 4 is obtained below
Ceramic products are tested for the property, and test result is as shown in table 1:
In table, the test result of mobility, crystal property and appearance is the consistent mirror of expert in 5 ceramic fields
Determine result.
Table 1
As can be seen from the above table, white opaque glaze of the invention is made up of selected raw material, and rational proportion, has been selected suitable
When the potassium feldspar of proportion, albite, calcite, quartz, talcum powder, bentonite, strontium oxide strontia, barium monoxide, magnesia, titanium oxide,
Barium zirconium phthalate, zirconium silicate, yttrium oxide and high boron frit, white opaque glaze ceramic obtained, glaze (opaque glaze) have cream
The advantages that turbid effect is good, and glaze is flat and smooth, glossiness is good, exquisite beautiful, and whiteness is high, the wear-resisting property of glaze is good and hardness
It is high;Its comprehensive performance is superior to common opaque glaze ceramic.
The above is only the preferred embodiment of the present invention, it is noted that above-mentioned preferred embodiment is not construed as pair
Limitation of the invention, protection scope of the present invention should be defined by the scope defined by the claims..For the art
For those of ordinary skill, without departing from the spirit and scope of the present invention, several improvements and modifications can also be made, these change
It also should be regarded as protection scope of the present invention into retouching.
Claims (8)
1. a kind of white opaque glaze, which is characterized in that the raw material including following parts by weight: 20~25 parts of potassium feldspar, albite 22
~27 parts, 8~12 parts of calcite, quartzy 16~20 parts, 10~14 parts of talcum powder, 4.5~5.5 parts of bentonite, strontium oxide strontia 6~8
Part, 5~7 parts of barium monoxide, 6~9 parts of magnesia, 5~6 parts of titanium oxide, 2.5~3.5 parts of barium zirconium phthalate, 15~20 parts of zirconium silicate,
4~6 parts of yttrium oxide.
2. white opaque glaze according to claim 1, which is characterized in that the white opaque glaze includes following parts by weight
Raw material: 22 parts of potassium feldspar, 24.5 parts of albite, 10.5 parts of calcite, quartzy 18.4 parts, 12 parts of talcum powder, 5 parts of bentonite, oxygen
Change 7.5 parts of strontium, 6.2 parts of barium monoxide, 7.7 parts of magnesia, 5.5 parts of titanium oxide, 3.1 parts of barium zirconium phthalate, 18 parts of zirconium silicate, oxidation
5 parts of yttrium.
3. white opaque glaze according to claim 1, which is characterized in that the white opaque glaze further includes following parts by weight
Raw material: 4~7 parts of high boron frit.
4. white opaque glaze according to claim 2, which is characterized in that the white opaque glaze further includes following parts by weight
Raw material: 5.8 parts of high boron frit.
5. white opaque glaze according to claim 1, which is characterized in that the titanium oxide is nano-titanium dioxide.
6. white opaque glaze according to claim 1, which is characterized in that the boron content of the high boron frit is 10~15%,
Lead content is less than 0.01%.
7. a kind of white opaque glaze ceramic, which is characterized in that including green body and the glaze layer for being covered in the billet surface, institute
Stating glaze layer is white opaque glaze as claimed in any one of claims 1 to 6.
8. a kind of preparation method of white opaque glaze ceramic as claimed in claim 7, which is characterized in that including following step
It is rapid:
A, weigh following raw material by weight: potassium feldspar, albite, calcite, quartz, talcum powder, bentonite, strontium oxide strontia,
Barium monoxide, magnesia, titanium oxide, barium zirconium phthalate, zirconium silicate, yttrium oxide and high boron frit;
B, after mixing weighed each raw material, mixture is obtained, using ball mill 20~30min of ball milling, wherein when ball milling, mixing
The weight ratio of material, ball and water are as follows: 1:2:(0.6~0.7);
C, 200 meshes are crossed, 20~25min of froth in vacuum is then carried out and obtains glaze slip, continue stirring and by the solid content tune of glaze slip
Section is 60~65%;
The obtained glaze slip of step C is imposed on into billet surface, glazing is with a thickness of 0.7~0.8mm;It is warming up to 1190~1250 DEG C again,
Heating rate is 3 DEG C/min;It carries out glaze firing 70~90min hours, then is cooled to 250 DEG C of heat preservation 2h, be cooled to room temperature to get arriving
White opaque glaze ceramic.