CN110423424A - 一种高耐热、抗老化的cpvc电力电缆保护管及其制备方法 - Google Patents
一种高耐热、抗老化的cpvc电力电缆保护管及其制备方法 Download PDFInfo
- Publication number
- CN110423424A CN110423424A CN201910622915.9A CN201910622915A CN110423424A CN 110423424 A CN110423424 A CN 110423424A CN 201910622915 A CN201910622915 A CN 201910622915A CN 110423424 A CN110423424 A CN 110423424A
- Authority
- CN
- China
- Prior art keywords
- parts
- aging
- cpvc
- power cable
- heat resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高耐热、抗老化的CPVC电力电缆保护管，它包括以下重量份的原料：CPVC 450‑550份、PVC 200‑300份、钙粉150‑200份、增韧剂30‑50份、丁腈橡胶3‑15份、稳定剂20‑30份、阻燃剂10‑20份、硬脂酸1‑5份、石蜡12‑18份。本发明的高耐热、抗老化的CPVC电力电缆保护管，耐受热变形温度98℃以上，具有优良的耐高温性能，可适应高温的恶劣环境；阻燃性能达到FV‑0级；同时具有柔性好、不易断裂和老化、使用寿命长、无放射污染，重量轻等特点。另外，本发明的制备方法简单可控，生产易操作。
Description
技术领域
本发明属于电力电缆保护管技术领域，具体涉及一种高耐热、抗老化的CPVC电力电缆保护管及其制备方法。
背景技术
CPVC电力管通常用作电缆保护管，具有优良的耐腐蚀性能，近些年来广泛应用于钢铁、冶金、石油、化工、化肥、染料、制药、电力、环境保护及污水处理等行业中，具有柔韧性好、绝缘性能良好、无污染、施工方便等特点，是传统的石棉电缆排管及普通PVC管材理想的替代品。CPVC电力管以CPVC（氯化聚乙烯树脂）为主要原料挤出成型，CPVC树脂由PVC（聚氯乙烯）树脂氯化改性制得，PVC树脂经过氯化后，分子键的不规则性增加，极性增加，使树脂的溶解性增大，化学稳定性增加，从而提高了材料的耐酸、碱、盐、氧化剂等的腐蚀。但现有的CPVC电力管仍然存在耐热性、抗老化性能有待提高的问题。
发明内容
本发明要解决的技术问题在于，提供所述的一种高耐热、抗老化的CPVC电力电缆保护管。
本发明更进一步要解决的技术问题在于，提供一种简单可控、生产操作方便的高耐热、抗老化的CPVC电力电缆保护管的制备方法。
本发明解决所采用的技术方案是：一种高耐热、抗老化的CPVC电力电缆保护管，它包括以下重量份的原料：CPVC 450-550份、PVC 200-300份、钙粉 150-200份、增韧剂 30-50份、丁腈橡胶 3-15份、稳定剂 20-30份、阻燃剂 10-20份、硬脂酸 1-5份、石蜡 12-18份。
优选地，它包括以下重量份的原料：CPVC 450-500份、PVC 250-300份、钙粉 150-180份、增韧剂 40-50份、丁腈橡胶3-10份、稳定剂 25-30份、阻燃剂 10-16份、硬脂酸 1-3份、石蜡 15-18份。
优选地，它包括以下重量份的原料：CPVC 500-550份、PVC 250-300份、钙粉 180-200份、增韧剂 30-40份、丁腈橡胶10-15份、稳定剂 20-25份、阻燃剂 16-20份、硬脂酸 3-5份、石蜡 15-18份。
优选地，它还包括钼铬红 0.2-0.8份、耐晒大红0.2-0.8份。
优选地，所述增韧剂为甲基丙烯酸甲酯、丁二烯、苯乙烯三元共聚物。
优选地，所述稳定剂为木糖醇、柠檬酸铈、甘油锌按2：1：1混合的混合物。
优选地，所述阻燃剂为水滑石、硼酸锌、碳黑按5：1：0.5混合的混合物。
高耐热、抗老化的CPVC电力电缆保护管的制备方法，它包括以下制备步骤：
（1）按照重量份数称取原料 ；
（2）将按照重量份数称取的原料混合10-30分钟；
（3）将步骤（2）混合后的原料用真空上料机上到料斗中，经料筒和模具升温塑化后，由模具挤出，真空定型，最后冷却定型，料筒温度160-190℃，模具温度170-190℃。
本发明的有益效果：本发明采用CPVC、PVC、钙粉、增韧剂、丁腈橡胶、稳定剂、阻燃剂、硬脂酸、石蜡制备高耐热、抗老化的CPVC电力电缆保护管；丁腈橡胶与CPVC、PVC有极好的相溶性，可提高产品的耐油、耐寒、抗老化抗湿滑等性能，保持良好的理机械性能；增韧剂甲基丙烯酸甲酯、丁二烯、苯乙烯三元共聚物与CPVC、PVC相容性好，在室温或低温下具有很高的抗冲击性，可提高的抗冲击强度，同时还可以改善制品的耐寒性和加工流动性，实现了良好的增韧效果，提高CPVC电力电缆保护管的拉伸强度和冲击韧性；加入剂木糖醇、柠檬酸铈、甘油锌，提高了体系的塑化速度，改善了体系的加工性能，从而提高CPVC电力电缆保护管热稳定性和力学性能，使其具有很好的耐热温性能和抵抗变形的能力；加入水滑石、硼酸锌、碳黑制备的阻燃剂，使各原料的性能协同，热释放历程发生改变,平均热释放降低明显，烟释放速率和总烟释放都降低，到了阻燃的效果，抑烟效果明显。
另外，本发明的制备方法简单可控，生产易操作。
具体实施方式
为了便于本领域技术人员的理解，下面结合实施例对本发明作进一步的说明，实施方式提及的内容并非对本发明的限定。
实施例1
一种高耐热、抗老化的CPVC电力电缆保护管，它包括以下重量份的原料：CPVC 450份、PVC 300份、钙粉 150份、增韧剂 50份、丁腈橡胶 3份、稳定剂 30份、阻燃剂 10份、硬脂酸5份、石蜡12份。增韧剂为甲基丙烯酸甲酯、丁二烯、苯乙烯三元共聚物；稳定剂为木糖醇、柠檬酸铈、甘油锌按2：1：1混合的混合物；阻燃剂为水滑石、硼酸锌、碳黑按5：1：0.5混合的混合物。
高耐热、抗老化的CPVC电力电缆保护管的制备方法，它包括以下制备步骤：
（1）按照重量份数称取原料 ；
（2）将按照重量份数称取的原料混合10分钟；
（3）将步骤（2）混合后的原料用真空上料机上到料斗中，经料筒和模具升温塑化后，由模具挤出，真空定型，最后冷却定型，料筒温度160℃，模具温度170℃。
实施例2
一种高耐热、抗老化的CPVC电力电缆保护管，它包括以下重量份的原料：CPVC 550份、PVC 200份、钙粉200份、增韧剂30份、丁腈橡胶15份、稳定剂 20份、阻燃剂20份、硬脂酸 1份、石蜡 18份。增韧剂为甲基丙烯酸甲酯、丁二烯、苯乙烯三元共聚物；稳定剂为木糖醇、柠檬酸铈、甘油锌按2：1：1混合的混合物；阻燃剂为水滑石、硼酸锌、碳黑按5：1：0.5混合的混合物。
高耐热、抗老化的CPVC电力电缆保护管的制备方法，它包括以下制备步骤：
（1）按照重量份数称取原料 ；
（2）将按照重量份数称取的原料混合20分钟；
（3）将步骤（2）混合后的原料用真空上料机上到料斗中，经料筒和模具升温塑化后，由模具挤出，真空定型，最后冷却定型，料筒温度170℃，模具温度180℃。
实施例3
一种高耐热、抗老化的CPVC电力电缆保护管，它包括以下重量份的原料：CPVC 500份、PVC 250份、钙粉 180份、增韧剂35份、丁腈橡胶 5份、稳定剂 25份、阻燃剂 15份、硬脂酸 3份、石蜡 15份。增韧剂为甲基丙烯酸甲酯、丁二烯、苯乙烯三元共聚物；稳定剂为木糖醇、柠檬酸铈、甘油锌按2：1：1混合的混合物；阻燃剂为水滑石、硼酸锌、碳黑按5：1：0.5混合的混合物。
高耐热、抗老化的CPVC电力电缆保护管的制备方法，它包括以下制备步骤：
（1）按照重量份数称取原料 ；
（2）将按照重量份数称取的原料混合15分钟；
（3）将步骤（2）混合后的原料用真空上料机上到料斗中，经料筒和模具升温塑化后，由模具挤出，真空定型，最后冷却定型，料筒温度180℃，模具温度185℃。
实施例4
一种高耐热、抗老化的CPVC电力电缆保护管，它包括以下重量份的原料：CPVC 550份、PVC 280份、钙粉 160份、增韧剂40份、丁腈橡胶 8份、稳定剂 28份、阻燃剂 16份、硬脂酸 3份、石蜡 16份、钼铬红 0.5份、耐晒大红0.3份。增韧剂为甲基丙烯酸甲酯、丁二烯、苯乙烯三元共聚物；稳定剂为木糖醇、柠檬酸铈、甘油锌按2：1：1混合的混合物；阻燃剂为水滑石、硼酸锌、碳黑按5：1：0.5混合的混合物。
高耐热、抗老化的CPVC电力电缆保护管的制备方法，它包括以下制备步骤：
（1）按照重量份数称取原料 ；
（2）将按照重量份数称取的原料混合20分钟；
（3）将步骤（2）混合后的原料用真空上料机上到料斗中，经料筒和模具升温塑化后，由模具挤出，真空定型，最后冷却定型，料筒温度190℃，模具温度190℃。
实施例5
一种高耐热、抗老化的CPVC电力电缆保护管，它包括以下重量份的原料：CPVC 520份、PVC 230份、钙粉 170份、增韧剂45份、丁腈橡胶 12份、稳定剂 28份、阻燃剂 18份、硬脂酸4份、石蜡 12份。增韧剂为甲基丙烯酸甲酯、丁二烯、苯乙烯三元共聚物；稳定剂为木糖醇、柠檬酸铈、甘油锌按2：1：1混合的混合物；阻燃剂为水滑石、硼酸锌、碳黑按5：1：0.5混合的混合物。
高耐热、抗老化的CPVC电力电缆保护管的制备方法，它包括以下制备步骤：
（1）按照重量份数称取原料 ；
（2）将按照重量份数称取的原料混合10分钟；
（3）将步骤（2）混合后的原料用真空上料机上到料斗中，经料筒和模具升温塑化后，由模具挤出，真空定型，最后冷却定型，料筒温度160℃，模具温度175℃。
性能评价方式及实行标准
本发明的实施例1-5制备的高耐热、抗老化的CPVC电力电缆保护管的指标参数如下：
| 项目 | 指标参数 |
| 扁平实验 | 压至1/2无破裂 |
| 维卡软化度 | ≥93 |
| 纵向回缩率% | ≤5.0 |
| 环片热压缩KN | ≥1.26 |
| 阻燃性能 | FV-0级 |
| 体积电阻系数Ω.cm | ≥1×10 |
| 线膨胀系数C | ≤8×10 |
| 落锤冲击(0℃) | 10次冲击无破裂 |
| 弯曲强度MPa | ≥70 |
| 耐热性 | 耐受热变形温度98℃以上 |
从上表可以看出，本发明的高耐热、抗老化的CPVC电力电缆保护管，耐受热变形温度98℃以上，具有优良的耐高温性能，可适应高温的恶劣环境；阻燃性能达到FV-0级；弯曲强度≥70Mpa，纵向回缩率≤5.0%，同时具有柔性好、不易断裂和老化、使用寿命长、无放射污染，重量轻等特点。本发明可广泛用于市镇电网建设和改造、城市市政改造工程、民航机场建设工程、工程园区、小区工程建设、交通、路桥工程建设、城市路灯埋地电缆敷设，对电线电缆起到引导和保护作用。
上述实施例为本发明较佳的实现方案，除此之外，本发明还可以其它方式实现，在不脱离本发明构思的前提下任何显而易见的替换均在本发明的保护范围之内。
Claims (8)
1.一种高耐热、抗老化的CPVC电力电缆保护管，其特征在于，它包括以下重量份的原料：CPVC 450-550份、PVC 200-300份、钙粉 150-200份、增韧剂 30-50份、丁腈橡胶 3-15份、稳定剂 20-30份、阻燃剂 10-20份、硬脂酸 1-5份、石蜡 12-18份。
2.根据权利要求1所述的高耐热、抗老化的CPVC电力电缆保护管，其特征在于，它包括以下重量份的原料：CPVC 450-500份、PVC 250-300份、钙粉 150-180份、增韧剂 40-50份、丁腈橡胶3-10份、稳定剂 25-30份、阻燃剂 10-16份、硬脂酸 1-3份、石蜡 15-18份。
3.根据权利要求1所述的高耐热、抗老化的CPVC电力电缆保护管，其特征在于，它包括以下重量份的原料：CPVC 500-550份、PVC 250-300份、钙粉 180-200份、增韧剂 30-40份、丁腈橡胶10-15份、稳定剂 20-25份、阻燃剂 16-20份、硬脂酸 3-5份、石蜡 15-18份。
4.根据权利要求1所述的高耐热、抗老化的CPVC电力电缆保护管，其特征在于，它还包括钼铬红 0.2-0.8份、耐晒大红0.2-0.8份。
5.根据权利要求1所述的高耐热、抗老化的CPVC电力电缆保护管，其特征在于，所述增韧剂为甲基丙烯酸甲酯、丁二烯、苯乙烯三元共聚物。
6.根据权利要求1所述的高耐热、抗老化的CPVC电力电缆保护管，其特征在于，所述稳定剂为木糖醇、柠檬酸铈、甘油锌按2：1：1混合的混合物。
7.根据权利要求1所述的高耐热、抗老化的CPVC电力电缆保护管，其特征在于，所述阻燃剂为水滑石、硼酸锌、碳黑按5：1：0.5混合的混合物。
8.权利要求1所述的高耐热、抗老化的CPVC电力电缆保护管的制备方法，其特征在于，它包括以下制备步骤：
（1）按照重量份数称取原料 ；
（2）将按照重量份数称取的原料混合10-30分钟；
（3）将步骤（2）混合后的原料用真空上料机上到料斗中，经料筒和模具升温塑化后，由模具挤出，真空定型，最后冷却定型，料筒温度160-190℃，模具温度170-190℃。