CN110406287A - The highlighted color face oil glazing process of one kind - Google Patents
The highlighted color face oil glazing process of one kind Download PDFInfo
- Publication number
- CN110406287A CN110406287A CN201910802782.3A CN201910802782A CN110406287A CN 110406287 A CN110406287 A CN 110406287A CN 201910802782 A CN201910802782 A CN 201910802782A CN 110406287 A CN110406287 A CN 110406287A
- Authority
- CN
- China
- Prior art keywords
- oil
- glazing
- color face
- parts
- printed matter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the highlighted color face oil glazing process of one kind, and printed matter surface is first carried out oil polish, carries out overlay film to its surface again after the completion, at a certain temperature throw off the film layer in the upper color face for crossing gloss oil, obtain the printed matter with more high brightness coloured silk face oil.The color face performance that gloss oil is crossed on present invention process is especially bright, brightness of the mixed gloss oil on color face surface, it substantially can achieve the standard of UV, it is even higher, significantly increase the commodity value of printed matter, glazing process of the present invention is simple to equipment requirement at the same time, without redesigning production line, it can be operated on original glazing and coating production line, and production process environmental protection, lower production temperature reduces energy consumption, meets printing industry currently to environmental protection, efficiency, cost, high standard of quality demand in production process, has a vast market foreground.
Description
Technical field
The invention belongs to printing technologies, more particularly to a kind of highlighted color face oil glazing process.
Background technique
Glazing is one of a procedure and printed matter surface ornamenting processing technology of post-press finishing.Generically explain,
Glazing is exactly can be in printed matter surface shape after levelling, drying, press polish in printed matter surface one layer of colorless and transparent coating of coating
At thin and even transparent bright layer.Glazing can not only increase the surface smoothness of printed matter, show printed product stronger
Gloss, and can play a protective role to printing image-text, thus be widely used in packing and decorating, Front cover of book and periodical, picture album,
Trade mark, advertisement, wall calendar, substantially the printed matters such as decoration, pictorial poster surface finish processing in.Glazing technology is as printing process
Extend the important means with printed matter finishing, be widely used by numerous printing factories, have become realization and improves printing
A kind of important means of product class.
Different by glazing paint type, glazing process can be mainly divided into solvent type glazing, aqueous glazing, UV glazing etc.,
Wherein solvent type glazing be using benzene class, esters, alcohols as solvent, using thermoplastic resin as the glazing process method of film-forming resin,
Feature is that equipment investment is small, at low cost, but solvent volatilizees and remains on printed matter the pollution that will cause to environment, and to human body
Nocuousness, therefore its application range is just gradually reduced;Aqueous glazing is with water-soluble resin or different types of water-dispersed resin
As the method for lustering of film forming matter, feature is the non-stimulated smell of upper photoreduction process, and no pollution to the environment is harmless, therefore
Just gradually promoted the use of;The dry glazing of UV glazing, that is, ultraviolet radiation was caused using the moment of ultraviolet light irradiation oil polish
Photochemical reaction occurs rapidly for oil polish, the light coating with netted chemical structure is formed in printed matter surface, feature is light
Pool is good, heat-resisting, wear-resisting property is strong, safety and environmental protection, there is wide market development prospect.
It praises highly although world's environmental protection prints industry using easy aqueous glazing, and water lustering oil is quickly grown at home,
With environment-friendly advantage, and cheap is widely used, but the glossiness after its glazing is about 60-70, and the glossiness of UV glazing
About 95, although there is certain competitiveness to UV glazing with aqueous glazing, but in printing industry, many people think that due on UV
Light exquisite appearance, therefore aqueous glazing will not also constitute UV glazing very big prestige association at present.In view of this, the present inventor is logical
Improvement glazing process is crossed, brightness on water lustering oil is enabled to be significantly increased, improves the exquisite degree of glazing, while can be effectively reduced
Light cost, to extend the application field of water lustering oil.
Summary of the invention
The object of the invention is to remedy the disadvantages of known techniques, provides a kind of highlighted color face oil glazing process, enables water
Brightness is significantly increased on property oil polish, the exquisite degree of glazing is improved, while can effectively reduce glazing cost, to extend on aqueous
The application field of gloss oil.
In order to achieve the above purpose, the present invention the following technical schemes are provided:
The highlighted color face oil glazing process of one kind, first carries out oil polish for printed matter surface, carries out again to its surface after the completion
The film layer in the upper color face for crossing gloss oil is thrown off at a certain temperature, obtains the printed matter with more high brightness coloured silk face oil by overlay film.
The oil polish process the following steps are included:
(1) oil polish is diluted with diluent, controlling its viscosity is at 25 DEG C within the scope of No. 4 cup 30-40s;
(2) the online carry out glazing of offset printing is used, and is dried with short infrared, glazing speed control is 55-65m/
min。
The oil polish is composed of the following components in parts by weight: 15-20 parts of water-soluble acrylic dispersion resin, polyacrylic acid
10-12 parts of ester lotion, 5-8 parts of urethane acrylate, 1-2 parts of defoaming agent, 2-3 parts of levelling agent, 1-2 parts of surfactant, water
45-55 parts.
During oil polish, the diluent is water and ethyl alcohol 1:(1-1.1 by volume) mixed liquor that is mixed to form.
Further, the defoaming agent is organic silicon defoamer;The levelling agent is organic silicon modified by polyether levelling agent;Institute
Stating surfactant is that neopelex mixes gained with nonylphenol polyoxyethylene ether 1:1.5 in mass ratio.
The coating process the following steps are included:
(1) binder is spread evenly across Plastic film surface using glue spreader, and will be molten in binder through drying device
Agent evaporation, obtains to coating layer;
(2) the upper printed matter for crossing gloss oil is drawn into laminating machine, it will be to coating layer and printed matter pressure by roll-forming
It closes, film layer is enabled to be overlying on light oil reservoir.
Further, the laminating machine carries out roll-forming by overlay film roller, and the temperature control of overlay film roller is 80-90 DEG C.
The described highlighted color face oil glazing process throws off film layer at control temperature is maintained at 80-90 DEG C after the overlay film
.
The invention has the advantages that
The present invention uses water lustering oil, on the basis of conventional glazing process, improves oil polish component, increases simultaneously
Overlay film and the process for taking off film after oil polish, wherein the color face for going up gloss oil (is no more than 90 DEG C) at a certain temperature after overlay film,
Part composition in gloss oil part composition and PVC light film is indissoluble under high temperature action, enables film layer easily open, and open
Color face performance afterwards is especially bright, and mixed gloss oil substantially can achieve the standard of UV, even in the brightness on color face surface
It is higher, the commodity value of printed matter is significantly increased, glazing process of the present invention is simple to equipment requirement at the same time, without weight
New design production line, can be operated on original glazing and coating production line, and production process environmental protection, lower production temperature contracting
Small energy consumption meets printing industry currently to environmental protection, efficiency, cost, high standard of quality demand in production process, has wide
Market prospects.
Specific embodiment
Below in conjunction with specific example, technical scheme is described further:
Embodiment 1
The highlighted color face oil glazing process of one kind, first carries out oil polish for printed matter surface, carries out again to its surface after the completion
The film layer in the upper color face for crossing gloss oil is thrown off at a certain temperature, obtains the printed matter with more high brightness coloured silk face oil by overlay film.
The oil polish process the following steps are included:
(1) oil polish is diluted with diluent, controlling its viscosity is No. 4 cup 35s at 25 DEG C;
(2) the online carry out glazing of offset printing is used, and is dried with short infrared, glazing speed control is 60m/min.
The oil polish is composed of the following components in parts by weight: 18 parts of water-soluble acrylic dispersion resin, polyacrylate
11 parts of lotion, 7 parts of urethane acrylate, 1.5 parts of defoaming agent, 2.5 parts of levelling agent, 1.5 parts of surfactant, 50 parts of water.
During oil polish, the diluent is water and the ethyl alcohol mixed liquor that 1:1.05 is mixed to form by volume.
Further, the defoaming agent is organic silicon defoamer;The levelling agent is organic silicon modified by polyether levelling agent;Institute
Stating surfactant is that neopelex mixes gained with nonylphenol polyoxyethylene ether 1:1.5 in mass ratio.
The coating process the following steps are included:
(1) binder is spread evenly across Plastic film surface using glue spreader, and will be molten in binder through drying device
Agent evaporation, obtains to coating layer;
(2) the upper printed matter for crossing gloss oil is drawn into laminating machine, it will be to coating layer and printed matter pressure by roll-forming
It closes, film layer is enabled to be overlying on light oil reservoir.
Further, the laminating machine carries out roll-forming by overlay film roller, and the temperature control of overlay film roller is 85 DEG C.
The described highlighted color face oil glazing process throws off film layer i.e. at control temperature is maintained at 85 DEG C after the overlay film
It can.
Embodiment 2
The highlighted color face oil glazing process of one kind, first carries out oil polish for printed matter surface, carries out again to its surface after the completion
The film layer in the upper color face for crossing gloss oil is thrown off at a certain temperature, obtains the printed matter with more high brightness coloured silk face oil by overlay film.
The oil polish process the following steps are included:
(1) oil polish is diluted with diluent, controlling its viscosity is No. 4 cup 30s at 25 DEG C;
(2) the online carry out glazing of offset printing is used, and is dried with short infrared, glazing speed control is 55m/min.
The oil polish is composed of the following components in parts by weight: 15 parts of water-soluble acrylic dispersion resin, polyacrylate
10 parts of lotion, 5 parts of urethane acrylate, 1 part of defoaming agent, 2 parts of levelling agent, 1 part of surfactant, 45 parts of water.
During oil polish, the diluent is water and the ethyl alcohol mixed liquor that 1:1 is mixed to form by volume.
Further, the defoaming agent is organic silicon defoamer;The levelling agent is organic silicon modified by polyether levelling agent;Institute
Stating surfactant is that neopelex mixes gained with nonylphenol polyoxyethylene ether 1:1.5 in mass ratio.
The coating process the following steps are included:
(1) binder is spread evenly across Plastic film surface using glue spreader, and will be molten in binder through drying device
Agent evaporation, obtains to coating layer;
(2) the upper printed matter for crossing gloss oil is drawn into laminating machine, it will be to coating layer and printed matter pressure by roll-forming
It closes, film layer is enabled to be overlying on light oil reservoir.
Further, the laminating machine carries out roll-forming by overlay film roller, and the temperature control of overlay film roller is 80 DEG C.
The described highlighted color face oil glazing process throws off film layer i.e. at control temperature is maintained at 80 DEG C after the overlay film
It can.
Embodiment 3
The highlighted color face oil glazing process of one kind, first carries out oil polish for printed matter surface, carries out again to its surface after the completion
The film layer in the upper color face for crossing gloss oil is thrown off at a certain temperature, obtains the printed matter with more high brightness coloured silk face oil by overlay film.
The oil polish process the following steps are included:
(1) oil polish is diluted with diluent, controlling its viscosity is No. 4 cup 40s at 25 DEG C;
(2) the online carry out glazing of offset printing is used, and is dried with short infrared, glazing speed control is 65m/min.
The oil polish is composed of the following components in parts by weight: 20 parts of water-soluble acrylic dispersion resin, polyacrylate
12 parts of lotion, 8 parts of urethane acrylate, 2 parts of defoaming agent, 3 parts of levelling agent, 2 parts of surfactant, 55 parts of water.
During oil polish, the diluent is water and the ethyl alcohol mixed liquor that 1:1.1 is mixed to form by volume.
Further, the defoaming agent is organic silicon defoamer;The levelling agent is organic silicon modified by polyether levelling agent;Institute
Stating surfactant is that neopelex mixes gained with nonylphenol polyoxyethylene ether 1:1.5 in mass ratio.
The coating process the following steps are included:
(1) binder is spread evenly across Plastic film surface using glue spreader, and will be molten in binder through drying device
Agent evaporation, obtains to coating layer;
(2) the upper printed matter for crossing gloss oil is drawn into laminating machine, it will be to coating layer and printed matter pressure by roll-forming
It closes, film layer is enabled to be overlying on light oil reservoir.
Further, the laminating machine carries out roll-forming by overlay film roller, and the temperature control of overlay film roller is 90 DEG C.
The described highlighted color face oil glazing process throws off film layer i.e. at control temperature is maintained at 90 DEG C after the overlay film
It can.
The upper optical property of above-mentioned 3 embodiments and performance of the common UV gloss oil after conventional glazing process are subjected to test pair
Than the results are shown in Table 1:
1 glazing performance test comparing result of table
As can be seen from the table, glazing process of the present invention has higher upper brightness on the basis of water lustering oil,
It has been even up to UV glazing luminance standard, to aqueous glazing competitiveness is improved, enterprise's production cost has been reduced, improves printing quality all
With significant facilitation.
Above-described embodiments are merely to illustrate the technical scheme, rather than its limitations;Although referring to before
Stating embodiment, invention is explained in detail, those skilled in the art should understand that: it still can be to preceding
It states technical solution documented by embodiment to modify, or part of or all technical features is equivalently replaced;And
These modifications or substitutions, the range for technical solution of various embodiments of the present invention that it does not separate the essence of the corresponding technical solution.
Claims (8)
1. the highlighted color face oil glazing process of one kind, which is characterized in that printed matter surface is first carried out oil polish, after the completion again to it
Surface carries out overlay film, at a certain temperature throws off the film layer in the upper color face for crossing gloss oil, obtains with more high brightness coloured silk face oil
Printed matter.
2. highlighted color face oil glazing process according to claim 1, which is characterized in that the oil polish process includes following
Step:
(1) oil polish is diluted with diluent, controlling its viscosity is at 25 DEG C within the scope of No. 4 cup 30-40s;
(2) the online carry out glazing of offset printing is used, and is dried with short infrared, glazing speed control is 55-65m/min.
3. highlighted color face oil glazing process according to claim 2, which is characterized in that the oil polish is by following parts by weight
At being grouped as: 15-20 parts of water-soluble acrylic dispersion resin, 10-12 parts of polyacrylate dispersion, urethane acrylate 5-
8 parts, 1-2 parts of defoaming agent, 2-3 parts of levelling agent, 1-2 parts of surfactant, 45-55 parts of water.
4. highlighted color face oil glazing process according to claim 2, which is characterized in that the diluent is that water and ethyl alcohol are pressed
Volume ratio 1:(1-1.1) mixed liquor that is mixed to form.
5. highlighted color face oil glazing process according to claim 4, which is characterized in that the defoaming agent is organosilicon defoaming
Agent;The levelling agent is organic silicon modified by polyether levelling agent;The surfactant is neopelex and nonyl phenol
Polyoxyethylene ether 1:1.5 in mass ratio mixing gained.
6. highlighted color face oil glazing process according to claim 1, which is characterized in that the coating process includes following step
It is rapid:
(1) binder is spread evenly across Plastic film surface using glue spreader, and steams solvent in binder through drying device
Hair, obtains to coating layer;
(2) the upper printed matter for crossing gloss oil is drawn into laminating machine, will be pressed, and will be enabled to coating layer and printed matter by roll-forming
Film layer is overlying on light oil reservoir.
7. highlighted color face oil glazing process according to claim 6, which is characterized in that the laminating machine by overlay film roller into
The temperature control of row roll-forming, overlay film roller is 80-90 DEG C.
8. highlighted color face oil glazing process according to claim 1, which is characterized in that control temperature after overlay film and keep
At 80-90 DEG C, film layer is thrown off.