CN108178950A - A kind of highlight water-based gloss oil - Google Patents
A kind of highlight water-based gloss oil Download PDFInfo
- Publication number
- CN108178950A CN108178950A CN201711361010.8A CN201711361010A CN108178950A CN 108178950 A CN108178950 A CN 108178950A CN 201711361010 A CN201711361010 A CN 201711361010A CN 108178950 A CN108178950 A CN 108178950A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- gloss oil
- based gloss
- highlight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention is print field, and in particular to a kind of highlight water-based gloss oil, by the component of following parts by weight meter：35~37 parts of styrene-acrylic emulsion, 18~20 parts of water-soluble acrylic epoxy resin, 15~17 parts of poly adipate succinic acid ester, 6~8 parts of wax emulsion, 2 4~4.6 parts of aminoethylamino ethanesulfonic acid sodium, 4.5~5 parts of isophorone diisocyanate, 2.8~3 parts of diethanol amine, 2~2.2 parts of auxiliary agent are configured；The water-soluble acrylic epoxy resin is copolymerized by the component of following parts by weight meter：25 parts of epoxy resin, 8 parts of acrylic acid, 8 parts of maleic anhydride, 5 parts of ethylenediamine.The present invention has the advantages that glossiness is high, cost is relatively low, product is stablized.
Description
Technical field
The present invention is print field, and in particular to a kind of highlight water-based gloss oil.
Technical background
In recent years, environmental requirement is higher and higher on packaging material, and the process of surface treatment requirement of product packaging is very high, especially
It is the glazing process after print, both coated (or spray, print) one layer of water white transparency coating in printed matter surface, protection and increasing are played after dry
Add the effect of printed matter gloss.The coating of (or spray, print) last layer water white transparency is applied in printed matter surface, through levelling, drying, pressure
A kind of thin and even transparent bright layer is formed in printed matter surface after light, curing, plays enhancing carrier surface smoothness, protection print
The technique of the finish machining function of map brushing text.
Mainly there are two kinds of glazing modes of the aqueous glazing of line and off line UV glazings, traditional off line UV glazings currently on the market
It is most commonly used, although off line UV gloss oil brightness can reach 85 degree, since UV gloss oil is comprising many harmful
Solvent, and pollute the environment seriously, such production technology has not met the development trend of society；More environmentally friendly company at present
The aqueous glazing process of line also obtains the use of more and more enterprises, but since such technique is using water as the solvent of aqueous glazing
Also there is shortcoming, such as volatilizing, bad, rate of drying is slower, and it is unstable to be easy to cause product, and the brightness of line water-based gloss oil is only
70 degree or so can be reached.
In consideration of it, the highlight water-based gloss oil that a kind of cost of present invention offer is relatively low, product is stablized.
Invention content
It is an object of the invention to overcome above-mentioned the deficiencies in the prior art, a kind of highlight water-based gloss oil is provided.
Purpose to realize the present invention, the technical solution adopted by the present invention are：
A kind of highlight water-based gloss oil, by the component of following parts by weight meter：35~37 parts of styrene-acrylic emulsion, water-soluble acrylic ring
18~20 parts of oxygen resin, 15~17 parts of poly adipate succinic acid ester, 6~8 parts of wax emulsion, 2- aminoethylamino ethanesulfonic acids sodium 4
~4.6 parts, 4.5~5 parts of isophorone diisocyanate, 2.8~3 parts of diethanol amine, 2~2.2 parts of auxiliary agent be configured.
The water-soluble acrylic epoxy resin is copolymerized by the component of following parts by weight meter：25 parts of epoxy resin,
8 parts of acrylic acid, 8 parts of maleic anhydride, 5 parts of ethylenediamine.
Preferably, the wax emulsion is babassu wax emulsion.
Preferably, the auxiliary agent includes levelling agent, dispersant, optical brightener, antifoaming agent and plasticizer.
Preferably, the levelling agent is carboxymethyl cellulose.
Preferably, the dispersant is polyacrylic acid sodium salt.
Preferably, the optical brightener is organosiloxane.
Preferably, the antifoaming agent is dimethyl silicone polymer.
Preferably, the plasticizer is ditridecyl phthalate.
Relative to the prior art, the application achieves following advantageous effect：
Highlight water-based gloss oil wearability of the present invention is good, and adhesion is strong, cracking resistance, and there is good printing to adapt to
Property.
Specific embodiment
Embodiment 1
A kind of highlight water-based gloss oil, by the component of following parts by weight meter：35 parts of styrene-acrylic emulsion, water-soluble acrylic asphalt mixtures modified by epoxy resin
20 parts of fat, 17 parts of poly adipate succinic acid ester, 8 parts of wax emulsion, 4.2 parts of 2- aminoethylamino ethanesulfonic acids sodium, isophorone two
5 parts of isocyanates, 2.8 parts of diethanol amine, 2 parts of auxiliary agent are configured.
The water-soluble acrylic epoxy resin is copolymerized by the component of following parts by weight meter：25 parts of epoxy resin,
8 parts of acrylic acid, 8 parts of maleic anhydride, 5 parts of ethylenediamine.
The wax emulsion is babassu wax emulsion.
The auxiliary agent includes levelling agent, dispersant, optical brightener, antifoaming agent and plasticizer.
The levelling agent is carboxymethyl cellulose.
The dispersant is polyacrylic acid sodium salt.
The optical brightener is organosiloxane.
The antifoaming agent is dimethyl silicone polymer.
The plasticizer is ditridecyl phthalate.
Embodiment 2
A kind of highlight water-based gloss oil, by the component of following parts by weight meter：37 parts of styrene-acrylic emulsion, water-soluble acrylic asphalt mixtures modified by epoxy resin
18 parts of fat, 16 parts of poly adipate succinic acid ester, 7 parts of wax emulsion, 4.6 parts of 2- aminoethylamino ethanesulfonic acids sodium, isophorone two
4.5 parts of isocyanates, 3 parts of diethanol amine, 2.1 parts of auxiliary agent are configured.
The water-soluble acrylic epoxy resin is copolymerized by the component of following parts by weight meter：25 parts of epoxy resin,
8 parts of acrylic acid, 8 parts of maleic anhydride, 5 parts of ethylenediamine.
The wax emulsion is babassu wax emulsion.
The auxiliary agent includes levelling agent, dispersant, optical brightener, antifoaming agent and plasticizer.
The levelling agent is carboxymethyl cellulose.
The dispersant is polyacrylic acid sodium salt.
The optical brightener is organosiloxane.
The antifoaming agent is dimethyl silicone polymer.
The plasticizer is ditridecyl phthalate.
Embodiment 3
A kind of highlight water-based gloss oil, by the component of following parts by weight meter：36 parts of styrene-acrylic emulsion, water-soluble acrylic asphalt mixtures modified by epoxy resin
20 parts of fat, 15 parts of poly adipate succinic acid ester, 6 parts of wax emulsion, 4 parts of 2- aminoethylamino ethanesulfonic acids sodium, isophorone two are different
4.7 parts of cyanate, 2.8 parts of diethanol amine, 2.2 parts of auxiliary agent are configured.
The water-soluble acrylic epoxy resin is copolymerized by the component of following parts by weight meter：25 parts of epoxy resin,
8 parts of acrylic acid, 8 parts of maleic anhydride, 5 parts of ethylenediamine.
The wax emulsion is babassu wax emulsion.
The auxiliary agent includes levelling agent, dispersant, optical brightener, antifoaming agent and plasticizer.
The levelling agent is carboxymethyl cellulose.
The dispersant is polyacrylic acid sodium salt.
The optical brightener is organosiloxane.
The antifoaming agent is dimethyl silicone polymer.
The plasticizer is ditridecyl phthalate.
Embodiment 4
Highlight water-based gloss oil performance test
The water-based gloss oil for buying comparative example at random with Examples 1 to 3 and on the market respectively is tested for the property, acquired results
As shown in table 1.
Table 1
Glossiness：It is measured by the regulation of GB/T9754, incidence angle is 60 °.
Wearability：It is tested using friction machine, under 4 pounds of load, example edition is cut into wide 50mm* long 220mm, and with pressure
Paper device is fixed in rubbing table, and 80 grams of A4 copy papers are cut into wide 50mm* long 220mm, and be fixed on and rubbed with eccentric pinch roller
On rub body, 80 grams of A4 copy papers smooth surfaces wear number when exposing ink to represent to example edition coated surface with film.
Scratch resistance：Apply middle pressure with thumbnail, scraped back and forth on water oil dry film, observe the serious of scratch
Degree；Evaluation result is divided into 1~5 grade, and 1 grade worst, and 5 grades best.
From the above results, highlight water-based gloss oil of the present invention has preferable glossiness, wearability and anti-scratch
Wound property.
Claims (8)
1. a kind of highlight water-based gloss oil, by the component of following parts by weight meter：35~37 parts of styrene-acrylic emulsion, water-soluble acrylic epoxy
18~20 parts of resin, 15~17 parts of poly adipate succinic acid ester, 6~8 parts of wax emulsion, 2- aminoethylamino ethanesulfonic acids sodium 4~
4.6 parts, 4.5~5 parts of isophorone diisocyanate, 2.8~3 parts of diethanol amine, 2~2.2 parts of auxiliary agent be configured；The water
Soluble acrylic epoxy resin is copolymerized by the component of following parts by weight meter：25 parts of epoxy resin, 8 parts of acrylic acid, suitable fourth
8 parts of enedioic acid acid anhydride, 5 parts of ethylenediamine.
2. highlight water-based gloss oil according to claim 1, which is characterized in that the wax emulsion is babassu wax emulsion.
3. highlight water-based gloss oil according to claim 1, which is characterized in that the auxiliary agent includes levelling agent, dispersant, increasing
Photo etching, antifoaming agent and plasticizer.
4. highlight water-based gloss oil according to claim 1, which is characterized in that the levelling agent is carboxymethyl cellulose.
5. highlight water-based gloss oil according to claim 4, which is characterized in that the dispersant is polyacrylic acid sodium salt.
6. highlight water-based gloss oil according to claim 4, which is characterized in that the optical brightener is organosiloxane.
7. highlight water-based gloss oil according to claim 4, which is characterized in that the antifoaming agent is dimethyl silicone polymer.
8. highlight water-based gloss oil according to claim 4, which is characterized in that the plasticizer is ditridecyl phthalate.