CN110343474A - 一种抗蓝紫光保护膜及其制作方法 - Google Patents
一种抗蓝紫光保护膜及其制作方法 Download PDFInfo
- Publication number
- CN110343474A CN110343474A CN201910686831.1A CN201910686831A CN110343474A CN 110343474 A CN110343474 A CN 110343474A CN 201910686831 A CN201910686831 A CN 201910686831A CN 110343474 A CN110343474 A CN 110343474A
- Authority
- CN
- China
- Prior art keywords
- layer
- protective film
- blue violet
- substrate
- violet light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及保护膜技术领域，更具体地说，它涉及一种抗蓝紫光保护膜，包括基材，所述基材的一侧涂布有用于贴合屏幕的高粘胶层，另一侧涂布有抗蓝紫层；所述抗蓝紫层远离基材的一侧依次涂布有隔离层和OCA层，所述OCA层远离隔离层的一侧覆盖有离型膜。该抗蓝紫光保护膜通过在抗蓝紫层与OCA层增加一层隔离层，能够很好的隔绝抗蓝紫层中的蓝紫光吸收助剂与OCA层接触，进而避免OCA层侵蚀蓝紫光吸收助剂，从而增加了该抗蓝紫光保护膜的紫光阻隔率和紫光光泽度，提高了抗蓝紫光保护膜的抗蓝紫光效果；使用时，将高粘胶层粘贴于电子产品的屏幕表面即可，透光率达到94％以上，雾度小于0.5％，对蓝紫光，尤其是410nm波长的光阻隔率能达到40％以上。
Description
技术领域
本发明涉及保护膜技术领域，特别是涉及一种抗蓝紫光保护膜及其制作方法。
背景技术
随着人们对电子产品的使用频率越来越高，眼睛注视屏幕的时间越来越长，因此对眼睛的保护越来越重要。通常，电子产品的显示屏的光源会产生不同波段的光源，其中蓝紫光是电磁波谱中波长从360nm-480nm辐射的总称，对人眼睛的伤害很大，因此市面上出现了抗蓝紫光膜。一般的抗蓝紫光膜包括基材、涂布于基材上的抗蓝紫层、涂布于抗蓝紫层上的OCA层和覆盖于OCA层上的离型膜，其中，OCA层的主要特点是透明性好，光透过率在90％以上，塑性较好和粘接强度适中，方便抗蓝紫层与离型膜之间的填充与粘接，并且在需要的时候可剥离而不残胶无污染；另外，一般的抗蓝紫层内均添加有蓝紫光吸收助剂，然而，蓝紫光吸收助剂在与OCA层接触后，容易被OCA层侵蚀，从而损伤抗蓝紫层，降低了抗蓝紫光效果。
发明内容
针对上述现有技术的不足，本发明的目的是提供一种抗蓝紫光保护膜及制作该保护膜的方法，该保护膜能隔离抗蓝紫层和OCA层，从而避免抗蓝紫层中的蓝紫光吸收助剂被OCA层侵蚀，进而提高抗蓝紫光效果。
本发明的上述技术目的是通过以下技术方案得以实现的：一种抗蓝紫光保护膜，包括基材，所述基材的一侧涂布有用于贴合屏幕的高粘胶层，另一侧涂布有抗蓝紫层；所述抗蓝紫层远离基材的一侧依次涂布有隔离层和OCA层，所述OCA层远离隔离层的一侧覆盖有离型膜。
进一步，所述隔离层为UV涂层。
进一步，所述UV涂层为混合有紫外光引发剂的丙烯酸酯涂层。
进一步，所述紫外光引发剂为光引发剂184、光引发剂907、光引发剂1173或二苯甲酮中的一种或多种。
进一步，所述紫外光引发剂的含量范围为1％-6％。
进一步，所述隔离层中含有抗氧化剂。
进一步，所述隔离层中含有稳定剂。
进一步，所述OCA层为丙烯酸酯、聚酯丙烯酸酯、聚醚丙烯酸酯酯、聚氨酯丙烯酸酯、环氧丙烯酸酯、聚噻吩中的一种或多种组合。
进一步，所述高粘胶层远离基材的一侧覆盖有剥离膜。
一种抗蓝紫光保护膜的制造方法，包括有以下步骤：步骤A、取基材，在基材的一面涂布UV胶层，所述UV胶层混合有蓝紫光吸收助剂；经UV光固化后，使基材表面形成抗蓝紫层；步骤B、在抗蓝紫层上继续进行UV光油涂布，经UV光固化下后得到UV涂层，该UV涂层形成抗侵蚀的隔离层；步骤C、在基材背离抗蓝紫层的一面涂布高粘胶，以形成高粘胶层；然后将剥离层与高粘胶层粘接后烘干，使剥离层固定在基材的另一表面；步骤D、在隔离层上涂布高粘胶水材料形成OCA层，并在OCA层上附上离型膜，最后通过紫外光固化。
本发明的有益效果是：本发明通过在抗蓝紫层与OCA层增加一层隔离层，能够很好的隔绝抗蓝紫层中的蓝紫光吸收助剂与OCA层接触，进而避免OCA层侵蚀蓝紫光吸收助剂，从而增加了该抗蓝紫光保护膜的紫光阻隔率和紫光光泽度，提高了保护膜的抗蓝紫光效果。
附图说明
为了更清楚地说明本发明实施例中的技术方案，下面将对实施例或现有技术描述中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本发明的一些实施例，对于本领域普通技术人员来讲，在不付出创造性劳动性的前提下，还可以根据这些附图获得其他的附图。
图1是本发明实施例的结构示意图。
附图标记：1、基材；2、抗蓝紫层；3、隔离层；4、OCA层；5、离型膜；6、高粘胶层；7、剥离膜。
具体实施方式
为了使本发明所要解决的技术问题、技术方案及有益效果更加清楚明白，以下结合附图及实施例，对本发明进行进一步详细说明。应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
需说明的是，当部件被称为“固定于”或“设置于”另一个部件，它可以直接在另一个部件上或者间接在该另一个部件上。当一个部件被称为是“连接于”另一个部件，它可以是直接或者间接连接至该另一个部件上。
需要理解的是，术语“长度”、“宽度”、“上”、“下”、“前”、“后”、“左”、“右”、“竖直”、“水平”、“顶”、“底”“内”、“外”等指示的方位或位置关系为基于附图所示的方位或位置关系，仅是为了便于描述本发明和简化描述，而不是指示或暗示所指的装置或元件必须具有特定的方位、以特定的方位构造和操作，因此不能理解为对本发明的限制。
此外，术语“第一”、“第二”仅用于描述目的，而不能理解为指示或暗示相对重要性或者隐含指明所指示的技术特征的数量。由此，限定有“第一”、“第二”的特征可以明示或者隐含地包括一个或者更多个该特征。在本发明的描述中，“多个”的含义是两个或两个以上，除非另有明确具体的限定。
一种抗蓝紫光保护膜，参见图1，包括基材1，所述基材1的一侧涂布有用于贴合屏幕的高粘胶层6，另一侧涂布有抗蓝紫层2；所述抗蓝紫层2远离基材1的一侧依次涂布有隔离层3和OCA层4，所述OCA层4远离隔离层3的一侧覆盖有离型膜5。
该抗蓝紫光保护膜通过在抗蓝紫层2与OCA层4增加一层隔离层3，能够很好的隔绝抗蓝紫层2中的蓝紫光吸收助剂与OCA层4接触，进而避免OCA层4侵蚀蓝紫光吸收助剂，从而增加了该抗蓝紫光保护膜的紫光阻隔率和紫光光泽度，提高了抗蓝紫光保护膜的抗蓝紫光效果；使用时，将高粘胶层粘贴于电子产品的屏幕表面即可，且透光率达到94％以上，雾度小于0.5％，对蓝紫光，尤其是410nm波长的光阻隔率能达到40％以上。
具体的，基材1的厚度为50μm，抗蓝紫层2的厚度范围为1-2μm，表面硬度为4H，在本实施例中，所述抗蓝紫层2为UV胶层，且具体为混合有蓝紫光吸收助剂的丙烯酸酯胶层，抗蓝紫层2的厚度为2μm。具体地，蓝紫光吸收助剂可以是荧光增白剂OB、UV-9626等。
具体的，所述隔离层3为UV涂层(图中未示出)。UV涂层的固化方式是采用紫外线进行照射固化，方便生产加工。
具体的，所述UV涂层为混合有紫外光引发剂的丙烯酸酯涂层。在本实施例中，所述丙烯酸酯可以是环氧丙烯酸酯、聚氨酯丙烯酸酯、聚醚丙烯酸酯、聚酯丙烯酸酯和丙烯酸树脂中的一种或多种组合。
所述紫外光引发剂可以选择采用光引发剂184、光引发剂907、光引发剂1173和二苯甲酮中的一种或多种，在本实施例中，优选地采用光引发剂184。
具体的，所述紫外光引发剂的含量范围为1％-6％，在本实施例中，优选地紫外光引发剂的含量为4％。
在本实施例中，所述隔离层3中含有抗氧化剂(图中未示出)和稳定剂(图中未示出)。抗氧化剂为抗氧剂1010和抗氧剂1076中的任意一种或多种，优选采用抗氧剂1010，稳定剂为热稳定剂和光稳定剂，光稳定剂为光稳定剂292、光稳定剂622和光稳定剂770中的任意一种或多种，优选采用光稳定剂292。具体的，隔离层3的厚度范围为1-2μm，在本实施例中，隔离层3的厚度为2μm。
具体的，所述OCA层4为丙烯酸酯、聚酯丙烯酸酯、聚醚丙烯酸酯酯、聚氨酯丙烯酸酯、环氧丙烯酸酯、聚噻吩中的一种或多种组合，在本实施例中，OCA层4为丙烯酸酯，且OCA层4的厚度范围为20-100μm，在本实施例中，OCA层4的厚度为68μm。
具体的，所述高粘胶层6远离基材1的一侧覆盖有剥离膜7，剥离膜7便于保护膜存放，用于保护高粘胶层6不受外界杂质灰尘污染。
具体的，高粘胶层6为硅胶层或亚克力胶层，在本实施例中，高粘胶层6优选硅胶层。
以下为抗蓝紫光保护膜的制造方法，包括有以下步骤：
步骤A、取基材1，在基材1的一面涂布UV胶层，具体地，所述UV胶层为混合有蓝紫光吸收助剂的丙烯酸酯胶层；经UV光固化后，使基材1表面形成抗蓝紫层2；UV光固化紫外光强为300mj/cm 2，固化时间为13s；
步骤B、在抗蓝紫层2上继续进行UV光油涂布，经UV光固化下固化15S后得到UV涂层，该UV涂层形成抗侵蚀的隔离层3；且具体地，UV涂层为混合有紫外光引发剂的丙烯酸酯；
步骤C、在基材1背离抗蓝紫层2的一面涂布高粘胶，以形成高粘胶层6；然后将剥离层7与高粘胶层6粘接后烘干，使剥离层7固定在基材1的另一表面；且具体地，上述高粘胶为硅胶或亚克力胶，优选地采用硅胶。
步骤D、在隔离层3上涂布高粘胶水材料形成OCA层4，并在OCA层4上附上离型膜，最后通过主波长为253.7nm的UVC波段紫外光固化。具体的，所述OCA层4为丙烯酸酯、聚酯丙烯酸酯、聚醚丙烯酸酯酯、聚氨酯丙烯酸酯、环氧丙烯酸酯、聚噻吩中的一种或多种组合，在本实施例中，OCA层优选采用为丙烯酸酯。
上述实施例仅仅是对本发明的解释，其并不是对本发明的限制，本领域技术人员在阅读完本说明书后可以根据需要对本实施例做出没有创造性贡献的修改，但只要在本发明的权利要求范围内都受到专利法的保护。
Claims (10)
1.一种抗蓝紫光保护膜，其特征是：包括基材(1)，所述基材(1)的一侧涂布有用于贴合屏幕的高粘胶层(6)，另一侧涂布有抗蓝紫层(2)；所述抗蓝紫层(2)远离基材(1)的一侧依次涂布有隔离层(3)和OCA层(4)，所述OCA层(4)远离隔离层(3)的一侧覆盖有离型膜(5)。
2.根据权利要求1所述的一种抗蓝紫光保护膜，其特征是：所述隔离层(3)为UV涂层。
3.根据权利要求2所述的一种抗蓝紫光保护膜，其特征是：所述UV涂层为混合有紫外光引发剂的丙烯酸酯涂层。
4.根据权利要求3所述的一种抗蓝紫光保护膜，其特征是：所述紫外光引发剂为光引发剂184、光引发剂907、光引发剂1173和二苯甲酮中的一种或多种组合。
5.根据权利要求3所述的一种抗蓝紫光保护膜，其特征是：所述紫外光引发剂的含量范围为1％-6％。
6.根据权利要求1-5任一项所述的一种抗蓝紫光保护膜，其特征是：所述隔离层(3)中含有抗氧化剂。
7.根据权利要求1-5任一项所述的一种抗蓝紫光保护膜，其特征是：所述隔离层(3)中含有稳定剂。
8.根据权利要求1-5任一项所述的一种抗蓝紫光保护膜，其特征是：所述OCA层(4)为丙烯酸酯、聚酯丙烯酸酯、聚醚丙烯酸酯酯、聚氨酯丙烯酸酯、环氧丙烯酸酯、聚噻吩中的一种或多种组合。
9.根据权利要求1-5任一项所述的一种抗蓝紫光保护膜，其特征是：所述高粘胶层(6)远离基材(1)的一侧覆盖有剥离膜(7)。
10.一种抗蓝紫光保护膜的制造方法，其特征在于，包括有以下步骤：
步骤A、取基材(1)，在基材(1)的一面涂布UV胶层，所述UV胶层混合有蓝紫光吸收助剂；经UV光固化后，使基材(1)表面形成抗蓝紫层(2)；
步骤B、在抗蓝紫层(2)上继续进行UV光油涂布，经UV光固化下后得到UV涂层，该UV涂层形成抗侵蚀的隔离层(3)；
步骤C、在基材(1)背离抗蓝紫层(2)的一面涂布高粘胶，以形成高粘胶层(6)；然后将剥离层(7)与高粘胶层(6)粘接后烘干，使剥离层(7)固定在基材(1)的另一表面；
步骤D、在隔离层(3)上涂布高粘胶水材料形成OCA层(4)，并在OCA层(4)上附上离型膜(5)，最后通过紫外光固化。