CN110330846A - A kind of color steel tile release rust priming paint - Google Patents
A kind of color steel tile release rust priming paint Download PDFInfo
- Publication number
- CN110330846A CN110330846A CN201910618362.XA CN201910618362A CN110330846A CN 110330846 A CN110330846 A CN 110330846A CN 201910618362 A CN201910618362 A CN 201910618362A CN 110330846 A CN110330846 A CN 110330846A
- Authority
- CN
- China
- Prior art keywords
- parts
- color steel
- steel tile
- rust
- priming paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of color steel tiles of color steel tile technical field to exempt rust priming paint, the color steel tile is exempted rust priming paint and is made of following material: original paint, dilute hydrochloric acid, substrate wetting agents, promotor, color preserving agent and ultraviolet absorbing agent, the production method that the color steel tile exempts rust priming paint is as follows: 10-20 parts of former paints are added 1-3 parts containing careless agent of becoming rusty, 1-3 parts of converting agent of iron rust, 0.5-1.5 parts of metal cleaners, 1-3 portions of surfactants, 2-6 parts of bonding agents, 0.5-1.5 parts of dilute hydrochloric acid, 1-3 parts of substrate wetting agents, 2-6 parts of promotors, 3-9 parts of color preserving agents and 3-9 parts of ultraviolet absorbing agents are stood after being stirred under 20-30 DEG C of environment temperature, the priming paint that derusts is sprayed on to the surface of color steel tile, brand-new oxidation film is generated with after the iron rust chemical reaction of corrosion, securely Paste on metal basal plane, more one layer of anti-corrosion protection reduce the problem of color steel tile is got rusty again.
Description
Technical field
The present invention relates to color steel tile technical field, specially a kind of color steel tile exempts rust priming paint.
Background technique
Most of domestic existing color steel tile derusting technology is manual polishing derusting and small part using strong acid as representative at present
Rust remover, manual polishing derusting working efficiency are very low.It is that derusting is extremely difficult that color steel tile, which renovates the biggest problem, it is known that color
Steel watt plate itself is than relatively thin, if derusted using traditional technique for grinding, easily punches plate and destroys original structure, and color steel
Shoe plate material inherently wave structure is uneven, and polishing derusting is difficult thoroughly clean.Strong acid rust remover be difficult derusting thoroughly and
And the powder produced after reflecting influences coating adhesion, remaining strong acid has corrosion impact, personnel's construction skin to coating below
Contact damages personnel very much, and residue is very big to environment especially soil damage, and iron rust, which still will appear, after processing returns rust and ask
Topic.
Summary of the invention
The purpose of the present invention is to provide a kind of color steel tiles to exempt rust priming paint, mentioned above in the background art existing to solve
There is technology to derust the problem of difficult and environmental pollution is serious color steel tile.
To achieve the above object, the invention provides the following technical scheme: a kind of color steel tile exempts rust priming paint, which exempts from
The priming paint that derusts is made of following material: painted containing careless agent of becoming rusty, converting agent of iron rust, metal cleaner, surfactant, bonding agent, original,
Dilute hydrochloric acid, substrate wetting agents, promotor, color preserving agent and ultraviolet absorbing agent.Preferably, which exempts the production of rust priming paint
Method is as follows:
10-20 parts of former paints are added 1-3 parts containing the careless agent, 1-3 parts of converting agent of iron rust, 0.5-1.5 parts of metal cleaners, 1- of becoming rusty
3 portions of surfactants, 2-6 parts of bonding agents, 0.5-1.5 parts of dilute hydrochloric acid, 1-3 parts of substrate wetting agents, 2-6 parts of promotors, 3-9 parts of guarantors
Toner and 3-9 parts of ultraviolet absorbing agents are stood after being stirred under 20-30 DEG C of environment temperature.
Preferably, a length of 30-40min when the stirring.
Preferably, the former paint is modified acroleic acid.
Preferably, the ultraviolet absorbing agent is benzotriazole absorbent.
Preferably, the substrate wetting agents are polyethylene glycol oxide alkanisation ether surfactant.
Preferably, the promotor uses ultra fast accelerator.
Preferably, the color preserving agent is sodium nitrite.
Preferably, the application method of color steel tile release rust priming paint is as follows:
Step 1: the color steel tile prepared derusting priming paint is poured into watering can；
Step 2: by the foreign matter on the surface for the color steel tile for needing to spray and floating rust cleaning；
Step 3: by the paint vehicle in watering can according to 10-12m2The spray area of/kg is sprayed in three times；
Step 4: the time interval sprayed three times is determined by environment temperature and humidity, when ambient humidity is below 70%,
For environment temperature at 15-35 DEG C, spray time interval is between 20-50min three times；
Step 5: it is dried 1 day in the state that humidity is lower than 40% after spraying.
Compared with prior art, the beneficial effects of the present invention are: by a kind of color steel tile release rust priming paint, in original paint
After dilute hydrochloric acid, substrate wetting agents, promotor, color preserving agent and ultraviolet absorbing agent is added, spray in color steel tile, it can be quickly right
The surface of color steel tile forms layer oxide film, the material water for improving rust cleaning efficiency, improving the antiseptic property of color steel tile, and use
Property is environment friendly and pollution-free.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
The invention provides the following technical scheme: a kind of color steel tile exempts rust priming paint, for improving the rustless property of color steel tile.
Embodiment 1
The color steel tile is exempted rust priming paint and is made of following material: containing the careless agent, converting agent of iron rust, metal cleaner, surface of becoming rusty
Activator, bonding agent, former paint, dilute hydrochloric acid, substrate wetting agents, promotor, color preserving agent and ultraviolet absorbing agent.
Wherein, the production method of color steel tile release rust priming paint is as follows:
10 parts of former paints are added 1 part containing the careless agent, 1 part of converting agent of iron rust, 0.5 part of metal cleaner, 1 part of surface active of becoming rusty
Agent, 2 parts of bonding agents, 0.5 part of dilute hydrochloric acid, 1 part of substrate wetting agents, 2 parts of promotors, 3 parts of color preserving agents and 3 parts of ultraviolet absorbing agents exist
It is stood after being stirred under 20-30 DEG C of environment temperature.
Wherein, a length of 30min when stirring.
Wherein, former paint is modified acroleic acid.
Wherein, ultraviolet absorbing agent is benzotriazole absorbent.
Wherein, substrate wetting agents are polyethylene glycol oxide alkanisation ether surfactant.
Wherein, promotor uses ultra fast accelerator.
Wherein, color preserving agent is sodium nitrite.
Wherein, the application method of color steel tile release rust priming paint is as follows:
Step 1: the color steel tile prepared derusting priming paint is poured into watering can；
Step 2: by the foreign matter on the surface for the color steel tile for needing to spray and floating rust cleaning；
Step 3: by the paint vehicle in watering can according to 10-12m2The spray area of/kg is sprayed in three times；
Step 4: the time interval sprayed three times is determined by environment temperature and humidity, when ambient humidity is below 70%,
For environment temperature at 15-35 DEG C, spray time interval is between 20-50min three times；
Step 5: it is dried 1 day in the state that humidity is lower than 40% after spraying.
Embodiment 2
The color steel tile is exempted rust priming paint and is made of following material: containing the careless agent, converting agent of iron rust, metal cleaner, surface of becoming rusty
Activator, bonding agent, former paint, dilute hydrochloric acid, substrate wetting agents, promotor, color preserving agent and ultraviolet absorbing agent.
Wherein, the production method of color steel tile release rust priming paint is as follows:
15 parts of former paints are added 2 parts containing the careless agent, 2 parts of converting agent of iron rust, 1 part of metal cleaner, 2 parts of surfactants, 4 of becoming rusty
Part bonding agent, 1 part of dilute hydrochloric acid, 2 parts of substrate wetting agents, 4 parts of promotors, 6 parts of color preserving agents and 6 parts of ultraviolet absorbing agents are in 20-30
DEG C environment temperature under be stirred after stand.
Wherein, a length of 35min when stirring.
Wherein, former paint is modified acroleic acid.
Wherein, ultraviolet absorbing agent is benzotriazole absorbent.
Wherein, substrate wetting agents are polyethylene glycol oxide alkanisation ether surfactant.
Wherein, promotor uses ultra fast accelerator.
Wherein, color preserving agent is sodium nitrite.
Wherein, the application method of color steel tile release rust priming paint is as follows:
Step 1: the color steel tile prepared derusting priming paint is poured into watering can；
Step 2: by the foreign matter on the surface for the color steel tile for needing to spray and floating rust cleaning；
Step 3: by the paint vehicle in watering can according to 10-12m2The spray area of/kg is sprayed in three times；
Step 4: the time interval sprayed three times is determined by environment temperature and humidity, when ambient humidity is below 70%,
For environment temperature at 15-35 DEG C, spray time interval is between 20-50min three times；
Step 5: it is dried 1 day in the state that humidity is lower than 40% after spraying.
Embodiment 3
The color steel tile is exempted rust priming paint and is made of following material: containing the careless agent, converting agent of iron rust, metal cleaner, surface of becoming rusty
Activator, bonding agent, former paint, dilute hydrochloric acid, substrate wetting agents, promotor, color preserving agent and ultraviolet absorbing agent.
Wherein, the production method of color steel tile release rust priming paint is as follows:
20 parts of former paints are added 3 parts containing the careless agent, 3 parts of converting agent of iron rust, 1.5 parts of metal cleaners, 3 parts of surface actives of becoming rusty
Agent, 6 parts of bonding agents, 1.5 parts of dilute hydrochloric acid, 3 parts of substrate wetting agents, 6 parts of promotors, 9 parts of color preserving agents and 9 parts of ultraviolet absorbing agents exist
It is stood after being stirred under 20-30 DEG C of environment temperature.
Wherein, a length of 40min when stirring.
Wherein, former paint is modified acroleic acid.
Wherein, ultraviolet absorbing agent is benzotriazole absorbent.
Wherein, substrate wetting agents are polyethylene glycol oxide alkanisation ether surfactant.
Wherein, promotor uses ultra fast accelerator.
Wherein, color preserving agent is sodium nitrite.
Wherein, the application method of color steel tile release rust priming paint is as follows:
Step 1: the color steel tile prepared derusting priming paint is poured into watering can；
Step 2: by the foreign matter on the surface for the color steel tile for needing to spray and floating rust cleaning；
Step 3: by the paint vehicle in watering can according to 10-12m2The spray area of/kg is sprayed in three times；
Step 4: the time interval sprayed three times is determined by environment temperature and humidity, when ambient humidity is below 70%,
For environment temperature at 15-35 DEG C, spray time interval is between 20-50min three times；
Step 5: it is dried 1 day in the state that humidity is lower than 40% after spraying.
Embodiment 1, embodiment 2, the embodiment 3 generated through the invention, and embodiment 1, embodiment 2, embodiment 3 are produced
Raw product and its service condition is detected, and when dilute hydrochloric acid is added in original paint, original paint is sprayed in color steel tile, can be with
Layer oxide film quickly is formed on the surface of color steel tile, has the function that protect the surface of color steel tile, while former paint
Middle mixed substrate wetting agents improve the viscosity between former paint and color steel tile, reduce the surface of color steel tile and air and water contact
It happens, compared to existing derusting mode, manual operation is reduced while reducing costs, economic and practical is strong.
Although hereinbefore having been made with reference to some embodiments, present invention is described, of the invention not departing from
In the case where range, various improvement can be carried out to it and can be with equivalent without replacement component therein.Especially, as long as not
There are structural conflict, the various features in presently disclosed each embodiment can be combined with each other by any way
It uses, the description for not carrying out exhaustion to the case where these combinations in the present specification is only to be in omit length and economize on resources
The considerations of.Therefore, the invention is not limited to specific embodiments disclosed herein, and including falling within the scope of the appended claims
All technical solutions.
Claims (9)
1. a kind of color steel tile exempts rust priming paint, it is characterised in that: the color steel tile is exempted rust priming paint and is made of following material: grass containing rust
Agent, metal cleaner, surfactant, bonding agent, former paint, dilute hydrochloric acid, substrate wetting agents, promotor, protects color at converting agent of iron rust
Agent and ultraviolet absorbing agent.
2. a kind of color steel tile according to claim 1 exempts rust priming paint, it is characterised in that: the color steel tile exempts rust priming paint
Production method is as follows:
10-20 parts of former paints are added 1-3 parts containing the careless agent, 1-3 parts of converting agent of iron rust, 0.5-1.5 parts of metal cleaners, 1-3 parts of becoming rusty
Surfactant, 2-6 part bonding agent, 0.5-1.5 parts of dilute hydrochloric acid, 1-3 parts of substrate wetting agents, 2-6 parts of promotors, 3-9 parts of guarantor's colors
Agent and 3-9 parts of ultraviolet absorbing agents are stood after being stirred under 20-30 DEG C of environment temperature.
3. a kind of color steel tile according to claim 1 exempts rust priming paint, it is characterised in that: a length of 30- when the stirring
40min。
4. a kind of color steel tile according to claim 1 exempts rust priming paint, it is characterised in that: the former paint is modified propylene
Acid.
5. a kind of color steel tile according to claim 1 exempts rust priming paint, it is characterised in that: the ultraviolet absorbing agent is benzene
And triazole type absorbent.
6. a kind of color steel tile according to claim 1 exempts rust priming paint, it is characterised in that: the substrate wetting agents are polyoxy
Change ethylene alkanisation ether surfactant.
7. a kind of color steel tile according to claim 1 exempts rust priming paint, it is characterised in that: the promotor is promoted using hypervelocity
Into agent.
8. a kind of color steel tile according to claim 1 exempts rust priming paint, it is characterised in that: the color preserving agent is nitrous acid
Sodium.
9. a kind of color steel tile according to any one of claims 1 to 8 exempts rust priming paint, it is characterised in that: the color steel tile is exempted from
The application method of derusting priming paint is as follows:
Step 1: the color steel tile prepared derusting priming paint is poured into watering can；
Step 2: by the foreign matter on the surface for the color steel tile for needing to spray and floating rust cleaning；
Step 3: by the paint vehicle in watering can according to 10-12m2The spray area of/kg is sprayed in three times；
Step 4: the time interval sprayed three times is determined by environment temperature and humidity, when ambient humidity is below 70%, environment
For temperature at 15-35 DEG C, spray time interval is between 20-50min three times；
Step 5: it is dried 1 day in the state that humidity is lower than 40% after spraying.