CN103131286A - Normal temperature dust-bonding agent - Google Patents
Normal temperature dust-bonding agent Download PDFInfo
- Publication number
- CN103131286A CN103131286A CN2011103769765A CN201110376976A CN103131286A CN 103131286 A CN103131286 A CN 103131286A CN 2011103769765 A CN2011103769765 A CN 2011103769765A CN 201110376976 A CN201110376976 A CN 201110376976A CN 103131286 A CN103131286 A CN 103131286A
- Authority
- CN
- China
- Prior art keywords
- normal temperature
- bonding agent
- dust
- temperature dust
- dust adhering
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
An object of the invention is to provide a normal temperature dust-bonding agent that surface viscosity of the dust-bonding agent can maintain for about one month at a temperature of 30-45 DEG C, has no damage to a substrate of a coating workshop and cannot cause shrinkage cavity of a sample sprayed by the dust-bonding agent. The normal temperature dust-bonding agent is composed by using polyacrylate, alkali, deionized water and glycerol as main raw materials and adding a thickening agent and a surfactant. Appearance of a product is a colorless, transparent and water-soluble liquid. The dust-bonding agent is soluble in water and biodegradable, can effectively adsorb the dust floating in a paint spray booth and over-sprayed paint particles, further purifies air of the paint spray booth, increases spraying quality, has an effective isolation protective effect for paint shop walls, equipment, pipelines and the like, and prolongs service life of the equipment.
Description
Technical field:
The present invention relates to a kind of normal temperature dust adhering agent, under 30 ℃~45 ℃ normal temperature, surface viscosity can be kept one month; To the base material not damaged of Painting Shop, can not cause institute's spray exemplar shrinkage cavity; Namely spray i.e. use, need not to wait for; Take water as primary solvent; During cleaning, water can directly rinse; Easy construction can spray or brush.
Technical problem solved by the invention is:
(1) pollution of the paint of spray to the Painting Shop wall excessively in coating process, the clean environment degree of protection Painting Shop have been solved.
(2) solve pad pasting and the inconvenient problem of cleaning in the traditional type of pasting protective film, reduced site operation amount and labour intensity.
(3) solved in general provisional protective coating take solvent or diluent as solvent, to the harm of environment and operator's health.
(4) solved general provisional protection coating under 30 ℃~45 ℃ drying conditionss, the problem that surface viscosity cannot not held time longly.
Background technology:
The height of the clean environment degree of Painting Shop is the important factor that directly affects the surface spraying quality.Understand in spraying process that the airborne paint particles that floats dirt and spray excessively is blended in paint, thereby reduce coating quality.
Adopting protective film or temporary protective coating is common guard technology measure both at home and abroad, but this method has a lot of defectives, and at first traditional protective film is pasted type, and this needs a large amount of site operations; Secondly remove inconveniently, and waste is to environment, and last traditional protective film or temporary protective coating great majority adopt solvent or diluents for dissolving, damage can be arranged the base material of Painting Shop, and easily cause institute's spray exemplar shrinkage cavity.
Outstanding feature of the present invention is: mainly take water as solvent, do not contain " triphen " solvent, be Green Product.The present invention can be under 30 ℃~45 ℃ environment, and surface viscosity was kept about one month; To the base material not damaged of Painting Shop, can not cause institute's spray exemplar shrinkage cavity; Easy construction can spray or brush use; It is convenient to remove, and can directly rinse by water less manpower.This normal temperature dust adhering agent is water-soluble, biodegradable.The wall of Painting Shop, equipment, pipeline etc. are played effective barrier property protective effect, the work-ing life of extension device.
Summary of the invention:
The purpose of this invention is to provide a kind of water-based flushable type normal temperature dust adhering agent.
Another object of the present invention is to provide the preparation method of this normal temperature dust adhering agent.
Normal temperature dust adhering agent of the present invention is main raw material by polyacrylic ester, alkali, deionized water, glycerol, adds thickening material and tensio-active agent and forms, and product is apparent is the water white transparency water soluble liq.
Described alkaline conditioner can be: trolamine, ammoniacal liquor or 3% sodium hydroxide.
Described thickening material can be: Natvosol, xanthan gum, sodium alginate or sodium polyacrylate.
Described tensio-active agent can be: polyoxyethylene nonylphenol ether, polyoxyethylene octylphenol ether or sucrose fatty ester.
Embodiment:
The preparation method of normal temperature dust adhering agent of the present invention comprises following processing step:
Add deionized water in reactor: 60.0%~70.0%, open and stir, controlling stirring velocity is 600 rev/mins, adds alkali: 0.2%~1.0%, stirred 30 minutes; Add polyacrylic ester: 3%~4%, stirred 2 hours, add thickening material: 0.1%~1%, stirred 1 o'clock; Add glycerol 26.0%~40.0%, stirred 30 minutes; Add tensio-active agent: 0.1%~0.8%, stirred at last 30 minutes, be finished product.
Embodiment 1
The present invention forms (mass percent): deionized water: 67%, trolamine: 0.5%, polyacrylic ester: 2.5%, xanthan gum 0.5%, enter glycerol: 29%, polyoxyethylene nonylphenol ether: 0.5%.
Embodiment 2
29%,, polyoxyethylene nonylphenol ether the present invention forms (mass percent): deionized water: 68%, ammoniacal liquor: 0.5%, polyacrylic ester: 1.8%, Natvosol: 0.2%, glycerol:: 0.5%.
Embodiment 3
The present invention forms (mass percent): deionized water: 67%, trolamine: 0.5%, polyacrylic ester: 2.8%, sodium alginate: 0.2%, glycerol: 29%, polyoxyethylene nonylphenol ether: 0.5%.
Embodiment 4
2%,, Natvosol the present invention forms (mass percent): deionized water: 68%, 3% sodium hydroxide: 0.2%, polyacrylic ester:: 0.8%, glycerol: 28.5%, sucrose fatty ester: 0.5%.
Embodiment 5
The present invention forms (mass percent): deionized water: 66.9%, trolamine: 0.8%, polyacrylic ester: 2.8%, Natvosol: 0.5%, glycerol: 28.5%, polyoxyethylene octylphenol ether: 0.5%.
Embodiment 6
The present invention forms (mass percent): deionized water: 66%, 3% sodium hydroxide: 0.5%, polyacrylic ester: 2.2%, Natvosol: 0.8%, glycerol: 30%, polyoxyethylene octylphenol ether: 0.5%.
Embodiment 7
The present invention forms (mass percent): deionized water: 66.9%, trolamine: 0.5%, polyacrylic ester: 2.8%, sodium polyacrylate: 0.3%, glycerol: 29%, polyoxyethylene nonylphenol ether: 0.5%.
Claims (6)
1. a normal temperature dust adhering agent, is characterized in that: each constituent mass per-cent: polyacrylic ester 3%~4%, deionized water 60%~70%, thickening material 0.1%~1%, alkaline conditioner 0.2%~1%, glycerol 26%~40%, tensio-active agent 0.1%~0.8%.
2. the normal temperature dust adhering agent described according to claim 1, its feature is being: thickening material wherein can be: Natvosol, xanthan gum, sodium alginate or sodium polyacrylate.
3. the normal temperature dust adhering agent described according to claim 1, it is characterized in that: alkaline conditioner wherein can be: trolamine, ammoniacal liquor or 3% sodium hydroxide.
4. the normal temperature dust adhering agent described according to claim 1, it is characterized in that: tensio-active agent wherein can be: polyoxyethylene nonylphenol ether, polyoxyethylene octylphenol ether or sucrose fatty ester.
5. the normal temperature dust adhering agent described according to claim 1, it is characterized in that: form of construction work can be spraying or brush.
6. the normal temperature dust adhering agent described according to claim 1, it is characterized in that: its surface viscosity can be kept about one month at 30 ℃~45 ℃ temperature, and used water is directly rinsed removing.