CN109439113A - A kind of water-based metal rust-proof anti-corrosive paint - Google Patents
A kind of water-based metal rust-proof anti-corrosive paint Download PDFInfo
- Publication number
- CN109439113A CN109439113A CN201811212468.1A CN201811212468A CN109439113A CN 109439113 A CN109439113 A CN 109439113A CN 201811212468 A CN201811212468 A CN 201811212468A CN 109439113 A CN109439113 A CN 109439113A
- Authority
- CN
- China
- Prior art keywords
- water
- based metal
- parts
- proof anti
- metal rust
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of water-based metal rust-proof anti-corrosive paints, are composed of the following parts by weight: 1-3 parts of water, 60-65 parts of silicone acrylic emulsion, 2-5 parts of aluminum phosphate, 0.1 part of emulsifier, 0.2 part of dispersing agent, 0.2 part of mould inhibitor, 1-3 parts of preservative, 5-10 parts of trbasic zinc phosphate, 1.5 parts of C-12,0.3 part of wetting agent, 0.1 part of defoaming agent, 0.1 part of thickener, 1-5 parts of titanium dioxide, 8-15 parts of antirust agent, 0.5 part of APM-95.Water-based metal rust-proof anti-corrosive paint provided by the invention is suitable for all metal surface materials, can round brush, spraying, it is easy for construction, to metal material surface without derusting dedusting, there is excellent adhesive force.
Description
Technical field
The invention belongs to technical field of chemical paint, and in particular to a kind of water-based metal rust-proof anti-corrosive paint.
Background technique
In recent years, with the raising of China's expanding economy and living standards of the people, the propulsion of urbanization process, real estate
It quickly grows, the environmental consciousness and health requirements of people is increasingly enhanced, and the harmful and noxious substance in building decoration materials is to environment
Caused by pollute, influence also to become increasingly conspicuous caused by human health.Harmful substance is mainly derived from all solvent based coatings
The formaldehyde that material releases, the pollutants such as benzene, ammonia.These ornament materials environmental pollutions of waterproof field are the biggest problem, because
A kind of this water-based metal rust-proof anti-corrosive paint substitution solvent based coating for developing safety and environmental protection in the art is urgent need to resolve
Problem.
Summary of the invention
To solve the above-mentioned problems, the invention proposes a kind of water-based metal rust-proof anti-corrosive paints.
A kind of water-based metal rust-proof anti-corrosive paint, is composed of the following parts by weight:
Further, each component content are as follows:
Further, the emulsifier is cationic emulsifier.
Further, dispersing agent is ammonium sulfate.
Further, the thickener is polyurethane thickener.
Water-based metal rust-proof anti-corrosive paint provided by the invention be suitable for all metal surface materials, can round brush, spraying, apply
Work is convenient, to metal material surface without the dedusting that derusts, has excellent adhesive force.High temperature resistant, it is corrosion-resistant, ageing-resistant, it is weather-proof
Property, stain resistance, cracking resistance, low temperature stretching force and good film-forming property.Su Yinqi substrate transport cold to thermal expansions such as steel construction, color steel tiles, under
There is good base to deform ability to bear for heavy, transfer etc., provide antirust, anti-corrosive defencive function for metal material surface.Prolong very well
The service life of long normal steel structure.Water-tolerant, 150um film thickness salt spray resistance impregnate in water usually up to 300-500 hours
It is without exception after 7-10 weeks.It is nontoxic and pollution-free, it is a kind of environmentally protective safe water-based metal rust-proof anti-corrosive paint.
Specific embodiment
The present invention will be further described combined with specific embodiments below.
Embodiment 1
A kind of water-based metal rust-proof anti-corrosive paint, is composed of the following parts by weight:
The water-based metal rust-proof anti-corrosive paint of the present embodiment is tested for the property, the results show that the water-based metal antirust
Anticorrosive paint antiseepage, high temperature resistant, color inhibition, acid and alkali-resistance, weatherability, stain resistant, cracking resistance, low temperature stretching force and film forming water resistance
Good, 50um film thickness acid and alkali-resistance is without exception after impregnating in water 8 weeks usually up to 450 hours.
Embodiment 2
A kind of water-based metal rust-proof anti-corrosive paint, is composed of the following parts by weight:
The water-based metal rust-proof anti-corrosive paint of the present embodiment is tested for the property, the results show that the water-based metal antirust
Anticorrosive paint antiseepage, high temperature resistant is corrosion-resistant, ageing-resistant, weatherability, stain resistance, cracking resistance, low temperature stretching force and film forming water resistance
Good, 50um film thickness salt spray resistance is without exception after impregnating in water 8 weeks usually up to 470 hours.
Embodiment 3
A kind of water-based metal rust-proof anti-corrosive paint, is composed of the following parts by weight:
The water-based metal rust-proof anti-corrosive paint of the present embodiment is tested for the property, the results show that the water-based metal antirust
Anticorrosive paint antiseepage, high temperature resistant is corrosion-resistant, ageing-resistant, weatherability, stain resistance, cracking resistance, low temperature stretching force and film forming water resistance
Good, 50um film thickness salt spray resistance is without exception after impregnating in water 9 weeks usually up to 480 hours.
Embodiment 4
A kind of water-based metal rust-proof anti-corrosive paint, is composed of the following parts by weight:
The water-based metal rust-proof anti-corrosive paint of the present embodiment is tested for the property, the results show that the water-based metal antirust
Anticorrosive paint antiseepage, high temperature resistant is corrosion-resistant, ageing-resistant, weatherability, stain resistance, cracking resistance, low temperature stretching force and film forming water resistance
Good, 50um film thickness salt spray resistance is without exception after impregnating in water 10 weeks usually up to 500 hours.
Comparative example 1
It is grouped as in the comparative example water-based metal rust-proof anti-corrosive paint by the group of following parts by weight:
This comparative example water-based metal rust-proof anti-corrosive paint is tested for the property, the results show that the water-based metal antirust is anti-
The 50um film thickness salt spray resistance of rotten coating is without exception after impregnating in water 7 weeks usually up to 260 hours.
Comparative example 2:
Heavy water metal rust preventing anticorrosive paint is grouped as by the group of following amount part in the comparative example:
This comparative example water-based metal rust-proof anti-corrosive paint is tested for the property, the results show that the water-based metal antirust is anti-
The 50um film thickness salt spray resistance of rotten coating is without exception after impregnating in water 7 weeks usually up to 250 hours.
Comparative example 3:
Water-based metal rust-proof anti-corrosive paint is grouped as by the group of following parts by weight in the comparative example:
This implementation water-based metal rust-proof anti-corrosive paint is tested for the property, the results show that the water-based metal antirust, anti-corrosive
The 50um film thickness salt spray resistance of coating is without exception after impregnating in water 7 weeks usually up to 300 hours.
Comparative example 4:
Water-based metal rust-proof anti-corrosive paint is grouped as by the group of following parts by weight in the comparative example:
This comparative example rust-proof anti-corrosive paint is tested for the property, the results show that the water-based metal rust-proof anti-corrosive paint
50um film thickness salt spray resistance is without exception after impregnating in water 7 weeks usually up to 310 hours
It can be seen that dosage of each component control water-based metal rust-proof anti-corrosive paint system of the invention within the scope of the present invention may be used
Function admirable is obtained, such as embodiment 1-4 water-based metal rust-proof anti-corrosive paint, but if some of amounts of components are beyond this
The range of invention, then the water-based metal rust-proof anti-corrosive paint performance that can make substantially reduce, and such as comparative example 1-4, this illustrates this hair
Bright mutual cooperation achieves the preferable effect of water-based metal rust-proof anti-corrosive paint.
Therefore, water-based metal rust-proof anti-corrosive paint provided by the invention has excellent physical and mechanical property, has excellent
Adhesive force.High temperature resistant, corrosion-resistant, ageing-resistant, weatherability, stain resistance, cracking resistance, low temperature stretching force and good film-forming property.To steel construction,
There is good base to deform ability to bear for the cold Su Yinqi substrate transport of the thermal expansions such as color steel tile, sinking, transfer etc., be metal material
Surface provides antirust, anti-corrosive defencive function.Extend the service life of normal steel structure very well.Water-tolerant, 50um film thickness salt spray resistance
It is without exception after impregnating 8-10 weeks in water usually up to 400-500 hours.It is nontoxic and pollution-free, it is a kind of environmentally protective safe
Water-based metal rust-proof anti-corrosive paint.
Claims (5)
1. a kind of water-based metal rust-proof anti-corrosive paint, which is characterized in that be composed of the following parts by weight:
2. a kind of water-based metal rust-proof anti-corrosive paint according to claim 1, which is characterized in that each component content are as follows:
3. a kind of water-based metal rust-proof anti-corrosive paint according to claim 1, which is characterized in that the emulsifier be sun from
Sub- emulsifier.
4. a kind of water-based metal rust-proof anti-corrosive paint according to claim 1, which is characterized in that dispersing agent is ammonium sulfate.
5. according to claim 1, which is characterized in that the thickener is polyurethane thickener.