CN102400161A - Cleaning agent for stainless steel bright piece and preparation method thereof - Google Patents
Cleaning agent for stainless steel bright piece and preparation method thereof Download PDFInfo
- Publication number
- CN102400161A CN102400161A CN2011103822659A CN201110382265A CN102400161A CN 102400161 A CN102400161 A CN 102400161A CN 2011103822659 A CN2011103822659 A CN 2011103822659A CN 201110382265 A CN201110382265 A CN 201110382265A CN 102400161 A CN102400161 A CN 102400161A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- percent
- stirring
- weight percent
- bright
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to the technical field of chemical cleaning, in particular to a cleaning agent suitable for a stainless steel bright piece and a preparation method thereof. The cleaning agent for the stainless steel bright piece is manufactured at normal temperature by mixing the following raw materials by weight percentage: 86.4 percent to 93.2 percent of water, 0.5 percent to 1 percent of citric acid, 2 percent to 4 percent of fatty alcohol-polyoxyethylene ether, 1 percent to 2 percent of triethanolamine, 0.1 percent to 0.2 percent of sodium molybdate, 0.1 percent to 0.2 percent of hydrochloric acid, 0.1 percent to 0.2 percent of hydrofluoric acid and the balance of alkylphenol ethoxylates. The chemical cleaning and the preparation method have the advantages that the operation is simple, the cleaning effect is good, warming is not needed, the surface of the stainless steel bright piece cannot be corroded at the same time, and the glossiness of the stainless steel bright piece is maintained; the cleaning agent for the stainless steel bright piece can be repeatedly used and cannot harm skin when being contacted with the skin; and as not containing zinc or phosphorus, the cleaning agent is low-carbon and environmentally friendly, and the cost is saved.
Description
Technical field
The present invention relates to the chemical cleaning technique field, especially a kind of clean-out system that is applicable to bright of stainless steel and preparation method thereof.
Background technology
For spationautics field and outlet businessman, bright equipment of making of stainless steel and product had not only required clean but also had required to keep the brightness of bright inside and outside of stainless steel.But at present, bright of stainless steel is difficult to clean up after being made into product, careless slightlyly just can produce excessive corrosion, causes bright loss of gloss of stainless steel.
Summary of the invention
The technical problem that the present invention will solve is: overcome the deficiency in the prior art; A kind of dirt that can clean on bright workpiece surface of stainless steel is provided; The gloss that can keep workpiece surface again; Long soaking time can not make bright surface of stainless steel rotten excessively yet, bright clean-out system of stainless steel simultaneously harmless and free from environmental pollution and preparation method thereof.
The technical solution adopted for the present invention to solve the technical problems is: bright clean-out system of a kind of stainless steel is mixed and made into by following raw materials by weight percent:
Preferred bright clean-out system of stainless steel is bright cleaning liquid of stainless steel, and bright cleaning liquid of described stainless steel is mixed and made into by following raw materials by weight percent:
After bright cleaning liquid of stainless steel used for some time, cleaning performance was not obvious, needed to add bright of stainless steel this moment and cleaned annex solution, and bright of described stainless steel cleans annex solution and is mixed and made into by following raw materials by weight percent:
The preparation method of bright clean-out system of stainless steel of the present invention has following steps:
(1), under the normal temperature, in stirrer, adding weight percent is the water of 86.4%-93.2%;
(2), throw in the Hydrocerol A that weight percent is 0.5%-1% while stirring;
(3), throw in the AEO that weight percent is 2%-4% while stirring;
(4), throw in the trolamine that weight percent is 1%-2% while stirring;
(5), throw in the Sodium orthomolybdate that weight percent is 0.1%-0.2% while stirring;
(6), throw in the hydrofluoric acid that weight percent is 0.1%-0.2% while stirring;
(7), throw in the hydrochloric acid that weight percent is 0.1%-0.2% while stirring;
(8), throw in the TX10 that weight percent is a surplus while stirring;
(9), all reinforced back restir that finishes was finished product in 20-30 minute.
Principle of work of the present invention is: TX10 has played the effect of oil removing degreasing, cleans the dirt and the grease on bright surface of stainless steel; Hydrocerol A can prolong the work-ing life of bright clean-out system of stainless steel, uses repeatedly, also can play the effect that hides flavor; The AEO ability will be attached to the obstinate dirt and the grease bull pine on bright surface of stainless steel; Add that dirt that hydrochloric acid, hydrofluoric acid and Hydrocerol A make its bull pine is fast from bright sur-face peeling of stainless steel; Sodium orthomolybdate and trolamine are in bright surface adsorption of the stainless steel that cleans up and generate one deck passive film.
The invention has the beneficial effects as follows: the present invention is simple to operate, and cleaning performance is good, need not to heat the surface of not corroding bright of stainless steel simultaneously, the glossiness that the maintenance stainless steel is bright; And bright clean-out system of stainless steel can reuse, and skin exposure is not had injury, owing to do not contain zinc and phosphorus, low-carbon environment-friendly is practiced thrift cost.
Embodiment
In conjunction with the preferred embodiments the present invention is further described now, AEO is the JFC permeate agent among the embodiment, and TX10 is an emulsifier op-10.
Embodiment 1
The preparation method of bright clean-out system of a kind of stainless steel has following steps: under (1), the normal temperature, the adding weight percent is 932 kilograms a water in stirrer; (2), throwing in content while stirring is 5 kilograms of 99.3% Hydrocerol As; (3), throw in 20 kilograms of JFC permeate agents while stirring; (4), throwing in content while stirring is 10 kilograms of 85% trolamines; (5), throwing in content while stirring is 1 kilogram of 99% Sodium orthomolybdate; (6), throwing in content while stirring is 1 kilogram in 44% hydrofluoric acid; (7), throwing in content while stirring is 1 kilogram of 31% hydrochloric acid; (8), throw in 30 kilograms emulsifier op-10 while stirring; (9), all reinforced back restir that finishes was finished product in 20-30 minute.
Embodiment 2
The preparation method of bright clean-out system of a kind of stainless steel has following steps: under (1), the normal temperature, the adding weight percent is 910.5 kilograms a water in stirrer; (2), throwing in content while stirring is 6 kilograms of 99.3% Hydrocerol As; (3), throw in 25 kilograms of JFC permeate agents while stirring; (4), throwing in content while stirring is 14 kilograms of 85% trolamines; (5), throwing in content while stirring is 1.5 kilograms of 99% Sodium orthomolybdates; (6), throwing in content while stirring is 1.2 kilograms in 44% hydrofluoric acid; (7), throwing in content while stirring is 1.8 kilograms of 31% hydrochloric acid; (8), throw in 40 kilograms emulsifier op-10 while stirring; (9), all reinforced back restir that finishes was finished product in 20-30 minute.
Embodiment 3
The preparation method of bright clean-out system of a kind of stainless steel has following steps: under (1), the normal temperature, the adding weight percent is 884.2 kilograms a water in stirrer; (2), throwing in content while stirring is 8 kilograms of 99.3% Hydrocerol As; (3), throw in 35 kilograms of JFC permeate agents while stirring; (4), throwing in content while stirring is 18 kilograms of 85% trolamines; (5), throwing in content while stirring is 1.8 kilograms of 99% Sodium orthomolybdates; (6), throwing in content while stirring is 1.8 kilograms in 44% hydrofluoric acid; (7), throwing in content while stirring is 1.2 kilograms of 31% hydrochloric acid; (8), throw in 50 kilograms emulsifier op-10 while stirring; (9), all reinforced back restir that finishes was finished product in 20-30 minute.
Embodiment 4
The preparation method of bright clean-out system of a kind of stainless steel has following steps: under (1), the normal temperature, the adding weight percent is 864 kilograms a water in stirrer; (2), throwing in content while stirring is 10 kilograms of 99.3% Hydrocerol As; (3), throw in 40 kilograms of JFC permeate agents while stirring; (4), throwing in content while stirring is 20 kilograms of 85% trolamines; (5), throwing in content while stirring is 2 kilograms of 99% Sodium orthomolybdates; (6), throwing in content while stirring is 2 kilograms in 44% hydrofluoric acid; (7), throwing in content while stirring is 2 kilograms of 31% hydrochloric acid; (8), throw in 60 kilograms emulsifier op-10 while stirring; (9), all reinforced back restir that finishes was finished product in 20-30 minute.
The finished product that embodiment 1 obtains is bright cleaning liquid of stainless steel, and the finished product that embodiment 4 obtains is that bright of stainless steel cleans annex solution.During use, bright cleaning liquid of stainless steel is poured in the clean groove, soaked the workpiece of required processing, need not to heat; Rinse well with High Pressure Gun after totally going out groove when workpiece soaks, dry or oven drying at low temperature gets final product.After bright cleaning liquid of stainless steel uses for some time, must add bright of stainless steel and clean annex solution.
The foregoing description only is explanation technical conceive of the present invention and characteristics; Its purpose is to let the personage that is familiar with this technology can understand content of the present invention and implements; Can not limit protection scope of the present invention with this; All equivalences that spirit is done according to the present invention change or modify, and all should be encompassed in protection scope of the present invention.
Claims (4)
1. bright clean-out system of a stainless steel, it is characterized in that: bright clean-out system of described stainless steel is mixed and made into by following raw materials by weight percent:
2. bright clean-out system of stainless steel according to claim 1 is characterized in that: bright clean-out system of described stainless steel is mixed and made into by following raw materials by weight percent:
3. bright clean-out system of stainless steel according to claim 1 is characterized in that: bright clean-out system of described stainless steel is mixed and made into by following raw materials by weight percent:
4. the preparation method of bright clean-out system of a stainless steel according to claim 1 is characterized in that: have following steps:
(1), under the normal temperature, in stirrer, adding weight percent is the water of 86.4%-93.2%;
(2), throw in the Hydrocerol A that weight percent is 0.5%-1% while stirring;
(3), throw in the AEO that weight percent is 2%-4% while stirring;
(4), throw in the trolamine that weight percent is 1%-2% while stirring;
(5), throw in the Sodium orthomolybdate that weight percent is 0.1%-0.2% while stirring;
(6), throw in the hydrofluoric acid that weight percent is 0.1%-0.2% while stirring;
(7), throw in the hydrochloric acid that weight percent is 0.1%-0.2% while stirring;
(8), throw in the TX10 that weight percent is a surplus while stirring;
(9), all reinforced back restir that finishes was finished product in 20-30 minute.