CN110330793A - 用于中空玻璃的暖边间隔条及其合成方法 - Google Patents

用于中空玻璃的暖边间隔条及其合成方法 Download PDF

Info

Publication number
CN110330793A
CN110330793A CN201910612604.4A CN201910612604A CN110330793A CN 110330793 A CN110330793 A CN 110330793A CN 201910612604 A CN201910612604 A CN 201910612604A CN 110330793 A CN110330793 A CN 110330793A
Authority
CN
China
Prior art keywords
parts
side spacer
warm side
spacer bar
hollow glass
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910612604.4A
Other languages
English (en)
Inventor
孙祯彬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Yaoxing Safety Glass Co Ltd
Original Assignee
Jiangsu Yaoxing Safety Glass Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Yaoxing Safety Glass Co Ltd filed Critical Jiangsu Yaoxing Safety Glass Co Ltd
Priority to CN201910612604.4A priority Critical patent/CN110330793A/zh
Publication of CN110330793A publication Critical patent/CN110330793A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种用于中空玻璃的暖边间隔条及其合成方法，将聚苯硫醚、玻璃纤维增强聚酯树脂、磷硅酸盐按重量份混合均匀，送入棒销式砂磨机磨细到细度小于50μm；然后加入定量氧化锌晶须、增强剂、玻璃纤维及加工助剂混合均匀，再由双螺杆挤出机造粒。该用于中空玻璃的暖边间隔条及其合成方法采用聚聚苯硫醚及玻璃纤维增强聚酯树脂为基材，另外添加了磷硅酸盐，并与其余辅料相配合，所得到的暖边间隔条具有较高的强度和隔热性，使用寿命较长，具有推广使用价值。

Description

用于中空玻璃的暖边间隔条及其合成方法
技术领域：
本发明涉及中空玻璃材料技术领域，尤其涉及一种用于中空玻璃的暖边间隔条及其合成方法。
背景技术：
具有隔热保温功能的中空玻璃已经越来越受到人们的重视。暖边间隔条是影响整个中空玻璃隔热性能的重要部件，而暖边间隔条的隔热性和高强度是考虑的主要因素。现有的用于中空玻璃的暖边间隔条综合性能并不理想。
发明内容：
为了解决上述存在的问题，本发明的目的是提供一种用于中空玻璃的暖边间隔条及其合成方法，具有高强度、高隔热性、耐化学性，使用寿命较长。其具体技术方案如下：
一种用于中空玻璃的暖边间隔条，由下列重量份的原料制成：
聚苯硫醚30-40份，
玻璃纤维增强聚酯树脂20-30份，
磷硅酸盐5-10份，
氧化锌晶须5-10份，
增强剂10-20份，
余量为玻璃纤维。
在本发明一较佳实施例中，所述用于中空玻璃的暖边间隔条最好由下列重量份的原料制成：
聚苯硫醚38.2份，
玻璃纤维增强聚酯树脂23.1份，
磷硅酸盐6.9份，
氧化锌晶须6.3份，
增强剂16.3份，
余量为玻璃纤维。
作为优选，所述磷硅酸盐为SW111磷硅酸盐。
作为优选，所述增强剂为多孔石英粉。
本发明还提供一种用于中空玻璃的暖边间隔条的合成方法，包括如下步骤：
将聚苯硫醚、玻璃纤维增强聚酯树脂、磷硅酸盐按重量份混合均匀，送入棒销式砂磨机磨细到细度小于50μm；
然后加入定量氧化锌晶须、增强剂、玻璃纤维及加工助剂混合均匀，再由双螺杆挤出机造粒。
其中，加工助剂可选用抗氧剂、增粘树脂、分散剂等。
本发明的有益效果是：该用于中空玻璃的暖边间隔条及其合成方法采用聚聚苯硫醚及玻璃纤维增强聚酯树脂为基材，另外添加了磷硅酸盐，并与其余辅料相配合，所得到的暖边间隔条具有较高的强度和隔热性，使用寿命较长，具有推广使用价值。
具体实施方式：
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易被本领域人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
实施例1
将聚苯硫醚38.2份、玻璃纤维增强聚酯树脂23.1份、磷硅酸盐6.9份混合均匀，送入棒销式砂磨机磨细到细度小于50μm；
然后加入氧化锌晶须6.3份、多孔石英粉16.3份、玻璃纤维5.7份及加工助剂3.5份混合均匀，再由双螺杆挤出机造粒，测得其拉伸强度为155.3MPa，弯曲强度为171.1MPa，导热系数为0.26w/mk。
实施例2
将聚苯硫醚40份、玻璃纤维增强聚酯树脂20份、磷硅酸盐5份混合均匀，送入棒销式砂磨机磨细到细度小于50μm；
然后加入氧化锌晶须10份、钛白粉10份、玻璃纤维10份及加工助剂5份混合均匀，再由双螺杆挤出机造粒，测得其拉伸强度为132.1MPa，弯曲强度为149.8.1MPa，导热系数为0.30w/mk。
实施例3
将聚苯硫醚35份、玻璃纤维增强聚酯树脂25份、磷硅酸盐7份混合均匀，送入棒销式砂磨机磨细到细度小于50μm；
然后加入氧化锌晶须7份、钛白粉15份、玻璃纤维7份及加工助剂4份混合均匀，再由双螺杆挤出机造粒，测得其拉伸强度为136.6MPa，弯曲强度为151.3MPa，导热系数为0.29w/mk。
最后应说明的是：以上实施例仅用以说明本发明而并非限制本发明所描述的技术方案；因此，尽管本说明书参照上述的各个实施例对本发明已进行了详细的说明，但是，本领域的普通技术人员应当理解，仍然可以对本发明进行修改或等同替换；而一切不脱离本发明的精神和范围的技术方案及其改进，其均应涵盖在本发明的权利要求范围中。

Claims (5)

1.一种用于中空玻璃的暖边间隔条，其特征在于，由下列重量份的原料制成：
聚苯硫醚30-40份，
玻璃纤维增强聚酯树脂20-30份，
磷硅酸盐5-10份，
氧化锌晶须5-10份，
增强剂10-20份，
余量为玻璃纤维。
2.根据权利要求1所述的用于中空玻璃的暖边间隔条，其特征在于，所述用于中空玻璃的暖边间隔条由下列重量份的原料制成：
聚苯硫醚38.2份，
玻璃纤维增强聚酯树脂23.1份，
磷硅酸盐6.9份，
氧化锌晶须6.3份，
增强剂16.3份，
余量为玻璃纤维。
3.根据权利要求1所述的用于中空玻璃的暖边间隔条，其特征在于，所述磷硅酸盐为SW111磷硅酸盐。
4.根据权利要求1所述的用于中空玻璃的暖边间隔条，其特征在于，所述增强剂为多孔石英粉。
5.一种如权利要求1-4任一项所述的用于中空玻璃的暖边间隔条的合成方法，其特征在于，包括如下步骤：
将聚苯硫醚、玻璃纤维增强聚酯树脂、磷硅酸盐按重量份混合均匀，送入棒销式砂磨机磨细到细度小于50μm；
然后加入定量氧化锌晶须、增强剂、玻璃纤维及加工助剂混合均匀，再由双螺杆挤出机造粒。
CN201910612604.4A 2019-07-09 2019-07-09 用于中空玻璃的暖边间隔条及其合成方法 Pending CN110330793A (zh)