CN110318271A - It is a kind of for improving the toning size and preparation method thereof of casement face color - Google Patents
It is a kind of for improving the toning size and preparation method thereof of casement face color Download PDFInfo
- Publication number
- CN110318271A CN110318271A CN201910619168.3A CN201910619168A CN110318271A CN 110318271 A CN110318271 A CN 110318271A CN 201910619168 A CN201910619168 A CN 201910619168A CN 110318271 A CN110318271 A CN 110318271A
- Authority
- CN
- China
- Prior art keywords
- weight
- toning
- parts
- size
- improving
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of for improving the toning size and preparation method thereof of casement face color, its step are as follows: the titanium dioxide solution of the acrylic acid ester emulsion of 60~80 parts by weight and 10~20 parts by weight being mixed at room temperature, and carries out first time stirring in blender;Then, defoaming agent, the wetting agent of 0.5~1 parts by weight and the dispersing agent of 0.5~1 parts by weight of 2~3 parts by weight is added, and carries out second in blender and stirs;Then, the mill base of 0.5~2 parts by weight is added, and carries out third time stirring in blender;Then, the thickener of 4~5 parts by weight is added, and carries out the 4th stirring in blender, the toning size is finally made.Using finished product window curtain fabric made from this programme, cloth cover solid colour, and the more bright-coloured beauty of color.
Description
Technical field
The present invention relates to the coating treatment technical field of window curtain fabric, in particular to a kind of side for improving casement face color
Method.
Background technique
Curtain has the effects that shading, heat-insulated and protection privacy.It is varied to make fabric used by curtain, most windows
The manufacturing process of curtain fabric is: first dyeing fabric, then fabric wherein does functional coating treatment on one side, to reach
The functions such as the shading of curtain, heat-insulated, and the other one side of fabric retains the color after piece dyeing finishing, and with no treatment.
However, the color difference due to fabric in dyeing course, so that can exist in cloth face color in curtain finished product
The problems such as color difference or uneven color.
Summary of the invention
The technical problem to be solved by the present invention is existing window curtain fabric processing technology is easy to cause finished product window curtain fabric
Cloth face color is there are color difference or color are uneven, to seriously affect the weight of finished product curtain and the usage experience of client.
The technical solution adopted by the present invention to solve the technical problems is:
It is a kind of for improving the preparation method of the toning size of casement face color, comprise the technical steps that:
S1, the titanium dioxide solution of the acrylic acid ester emulsion of 60~80 parts by weight and 10~20 parts by weight is mixed at room temperature
It closes, and carries out first time stirring in blender, the first mixed solution is made;
S2, in first mixed solution obtained, the profit of the defoaming agents of 2~3 parts by weight, 0.5~1 parts by weight is added
The dispersing agent of humectant and 0.5~1 parts by weight, and carry out second in blender and stir, the second mixed solution is made;
S3, in second mixed solution obtained, the mill base of 0.5~2 parts by weight is added, and is carried out in blender
Third time stirs, and third mixed solution is made;
S4, in the third mixed solution obtained, the thickener of 4~5 parts by weight is added, and is carried out in blender
4th stirring, is finally made the toning size.
Technical solution is advanced optimized, before described 4th time stirring, the preparation method further includes following steps:
S41, after the thickener is added, the pH value of solution is measured;
If the pH value of S42, solution not between 5~6, is needed ammonium hydroxide is added and is adjusted, until the pH value of solution 5~
Between 6.
Advanced optimize technical solution, 1000~1200r/min of the blender revolving speed.
Advanced optimize technical solution, the first time stirring it is best when it is 10 minutes a length of;Second of stirring
It is 5 minutes a length of when best;Third time stirring it is best when it is 2 minutes a length of;It is described 4th time stirring it is best when a length of 10
Minute.
Technical solution is advanced optimized, the solid content of the acrylic acid ester emulsion is between 42%~45%.
Technical solution is advanced optimized, the wetting agent is silanol class nonionic surfactant, using BYK3455 series
Wetting agent, main function are to reduce substrate surface tension, our slurry is enable uniformly to be coated on substrate.
Technical solution is advanced optimized, the defoaming agent is organic silicon, specifically uses TEGO-815 or TEGO-825 system
Column defoaming agent.
Technical solution is advanced optimized, the thickener is acrylic ester thickener, and action principle is: being added after being watered
Enter in ammonium hydroxide and when, emulsion particle can expand, and lotion can retrogradation.
Technical solution is advanced optimized, the titanium dioxide solution is to be formulated by titanium dioxide and water by the weight ratio of 1:1.
It is a kind of for improving the toning size of casement face color, be made by the above method.
In the present solution, mixing time is extremely important, it is mainly to aid in dispersion, mixing time is too short so that component is dispersed
Uniformly, the too long temperature that can improve slurry of mixing time, to influence the stability of paste color.Do not have in preparation process to temperature
There is too many requirement, carries out at room temperature.
The beneficial effects of the present invention are:
1, the consistency of casement face color can be improved using this slurry.
2, the uniformity that color is dispersed in cloth cover can be improved using this slurry, makes the more bright-coloured beauty of cloth cover color.
3, using mill base included in this slurry, therefore when handling window curtain fabric base fabric, without in advance to base fabric
Soaking paste dyeing processing is carried out, the energy consumed by dyeing is greatly saved in this way, also reduces the pollution dyed for environment.
Specific embodiment
The present invention will be further described with reference to embodiments, but the scope of protection of present invention is not limited to reality
Apply the range of example statement.
Toning size obtained is primarily adapted for use in undyed window curtain fabric base fabric in this programme, and application method is: logical
Often by toning size blade coating in the one side of window curtain fabric base fabric, and another side scratches functional coating, for example, shading, every
Heat, uvioresistant etc..If not high to Functional Requirement, this toning size can also be scratched respectively to two in window curtain fabric base fabric
Face.
Embodiment 1: a kind of for improving the toning size of casement face color, the raw material proportioning of required preparation is as follows:
Based on parts by weight,
Acrylic acid ester emulsion --- --- --- --- -60;
Titanium dioxide solution --- --- --- --- --- 10;
Defoaming agent --- --- --- --- --- --- -2;
Wetting agent --- --- --- --- --- --- -0.5;
Dispersing agent --- --- --- --- --- --- -0.5;
Mill base --- --- --- --- --- --- --- 0.5;
Thickener --- --- --- --- --- --- -4;
It is specific the preparation method is as follows:
The titanium dioxide solution of the acrylic acid ester emulsion of 60 parts by weight and 10 parts by weight is mixed at room temperature, and in blender
Middle stirring 10 minutes, is made the first mixed solution;
In first mixed solution obtained, the defoaming agent of 2 parts by weight, the wetting agent and 0.5 of 0.5 parts by weight is added
The dispersing agent of parts by weight, and stirred 5 minutes in blender, the second mixed solution is made;
In second mixed solution obtained, the mill base of 0.5 parts by weight is added, and is stirred 2 minutes in blender,
Third mixed solution is made;
In the third mixed solution obtained, the thickener of 4 parts by weight is added;At this time, it may be necessary to carry out PH to solution
Value test, if pH value not between 5~6, is adjusted by adding appropriate ammonium hydroxide so that the pH value of solution positioned at 5~6 it
Between.Then, it is stirred 10 minutes in blender, required toning size is finally made.
Wherein, the revolving speed of blender is set as 1200r/min.
Wherein, the solid content of acrylic acid ester emulsion is between 42%~45%.
Wherein, wetting agent is silanol class nonionic surfactant, using BYK3455 series wetting agent, main function
It is to reduce substrate surface tension, our slurry is enable uniformly to be coated on substrate.
Wherein, defoaming agent is organic silicon, specifically uses TEGO-815 or TEGO-825 series defoaming agent.
Wherein, thickener is acrylic ester thickener, and action principle is: after being watered be added ammonium hydroxide in and when, lotion
Particle can expand, and lotion can retrogradation.
Wherein, titanium dioxide solution is to be formulated by titanium dioxide and water by the weight ratio of 1:1.
Embodiment 2: a kind of for improving the toning size of casement face color, the raw material proportioning of required preparation is as follows:
In parts by weight,
Acrylic acid ester emulsion --- --- --- --- -70;
Titanium dioxide solution --- --- --- --- --- 15;
Defoaming agent --- --- --- --- --- --- -2.5;
Wetting agent --- --- --- --- --- --- -0.7;
Dispersing agent --- --- --- --- --- --- -0.7;
Mill base --- --- --- --- --- --- --- 1.2;
Thickener --- --- --- --- --- --- -4.5;
It is specific the preparation method is as follows:
The titanium dioxide solution of the acrylic acid ester emulsion of 70 parts by weight and 15 parts by weight is mixed at room temperature, and in blender
Middle stirring 10 minutes, is made the first mixed solution;
In first mixed solution obtained, be added the defoaming agents of 2.5 parts by weight, 0.7 parts by weight wetting agent and
The dispersing agent of 0.7 parts by weight, and stirred 5 minutes in blender, the second mixed solution is made;
In second mixed solution obtained, the mill base of 1.2 parts by weight is added, and is stirred 2 minutes in blender,
Third mixed solution is made;
In the third mixed solution obtained, the thickener of 4.5 parts by weight is added;At this time, it may be necessary to be carried out to solution
PH value test, if pH value not between 5~6, is adjusted by adding appropriate ammonium hydroxide, so that the pH value of solution is located at 5~6
Between.Then, it is stirred 10 minutes in blender, required toning size is finally made.
Wherein, the revolving speed of blender is set as 1200r/min.
Wherein, the solid content of acrylic acid ester emulsion is between 42%~45%.
Wherein, wetting agent is silanol class nonionic surfactant, using BYK3455 series wetting agent, main function
It is to reduce substrate surface tension, our slurry is enable uniformly to be coated on substrate.
Wherein, defoaming agent is organic silicon, specifically uses TEGO-815 or TEGO-825 series defoaming agent.
Wherein, thickener is acrylic ester thickener, and action principle is: after being watered be added ammonium hydroxide in and when, lotion
Particle can expand, and lotion can retrogradation.
Wherein, titanium dioxide solution is to be formulated by titanium dioxide and water by the weight ratio of 1:1.
Embodiment 3: a kind of for improving the toning size of casement face color, the raw material proportioning of required preparation is as follows:
In parts by weight,
Acrylic acid ester emulsion --- --- --- --- -80;
Titanium dioxide solution --- --- --- --- --- 20;
Defoaming agent --- --- --- --- --- --- -3;
Wetting agent --- --- --- --- --- --- -1;
Dispersing agent --- --- --- --- --- --- -1;
Mill base --- --- --- --- --- --- --- 2;
Thickener --- --- --- --- --- --- -5;
It is specific the preparation method is as follows:
The titanium dioxide solution of the acrylic acid ester emulsion of 80 parts by weight and 20 parts by weight is mixed at room temperature, and in blender
Middle stirring 10 minutes, is made the first mixed solution;
In first mixed solution obtained, the defoaming agent of 3 parts by weight, the wetting agent and 1 weight of 1 parts by weight is added
The dispersing agent of part, and stirred 5 minutes in blender, the second mixed solution is made;
In second mixed solution obtained, the mill base of 2 parts by weight is added, and is stirred 2 minutes in blender, makes
Obtain third mixed solution;
In the third mixed solution obtained, the thickener of 5 parts by weight is added;At this time, it may be necessary to carry out PH to solution
Value test, if pH value not between 5~6, is adjusted by adding appropriate ammonium hydroxide so that the pH value of solution positioned at 5~6 it
Between.Then, it is stirred 10 minutes in blender, required toning size is finally made.
Wherein, the revolving speed of blender is set as 1200r/min.
Wherein, the solid content of acrylic acid ester emulsion is between 42%~45%.
Wherein, wetting agent is silanol class nonionic surfactant, using BYK3455 series wetting agent, main function
It is to reduce substrate surface tension, our slurry is enable uniformly to be coated on substrate.
Wherein, defoaming agent is organic silicon, specifically uses TEGO-815 or TEGO-825 series defoaming agent.
Wherein, thickener is acrylic ester thickener, and action principle is: after being watered be added ammonium hydroxide in and when, lotion
Particle can expand, and lotion can retrogradation.
Wherein, titanium dioxide solution is to be formulated by titanium dioxide and water by the weight ratio of 1:1.
The advantages of basic principles and main features and this programme of this programme have been shown and described above.The technology of the industry
Personnel are it should be appreciated that this programme is not restricted to the described embodiments, and the above embodiments and description only describe this
The principle of scheme, under the premise of not departing from this programme spirit and scope, this programme be will also have various changes and improvements, these changes
Change and improvement is both fallen within the scope of claimed this programme.This programme be claimed range by appended claims and its
Equivalent thereof.
Claims (10)
1. a kind of for improving the preparation method of the toning size of casement face color, which is characterized in that walked including following technique
It is rapid:
S1, the titanium dioxide solution of the acrylic acid ester emulsion of 60~80 parts by weight and 10~20 parts by weight is mixed at room temperature, and
First time stirring is carried out in blender, and the first mixed solution is made;
S2, in first mixed solution obtained, the wetting agent of the defoaming agents of 2~3 parts by weight, 0.5~1 parts by weight is added
With the dispersing agent of 0.5~1 parts by weight, and second being carried out in blender and is stirred, the second mixed solution is made;
S3, in second mixed solution obtained, the mill base of 0.5~2 parts by weight is added, and carries out third in blender
Third mixed solution is made in secondary stirring;
S4, in the third mixed solution obtained, be added 4~5 parts by weight thickener, and in blender carry out the 4th
The toning size is finally made in secondary stirring.
2. as described in claim 1 a kind of for improving the preparation method of the toning size of casement face color, feature exists
In before described 4th time stirring, the preparation method further includes following steps:
S41, after the thickener is added, the pH value of solution is measured;
If the pH value of S42, solution not between 5~6, need be added ammonium hydroxide be adjusted, until solution pH value 5~6 it
Between.
3. as described in claim 1 a kind of for improving the preparation method of the toning size of casement face color, feature exists
In 1000~1200r/min of the blender revolving speed.
4. as claimed in claim 3 a kind of for improving the preparation method of the toning size of casement face color, feature exists
In, first time stirring it is best when it is 10 minutes a length of;Second stirring it is best when it is 5 minutes a length of;The third
Secondary stirring it is best when it is 2 minutes a length of;It is described 4th time stirring it is best when it is 10 minutes a length of.
5. as described in claim 1 a kind of for improving the preparation method of the toning size of casement face color, feature exists
In the wetting agent is silanol class nonionic surfactant, using BYK3455 series wetting agent.
6. as described in claim 1 a kind of for improving the preparation method of the toning size of casement face color, feature exists
In the defoaming agent is organic silicon, specifically uses TEGO-815 or TEGO-825 series defoaming agent.
7. as described in claim 1 a kind of for improving the preparation method of the toning size of casement face color, feature exists
In the thickener is acrylic ester thickener.
8. a kind of for improving the toning size of casement face color, which is characterized in that as described in claim 1-7 any one
Preparation method is made.
9. as claimed in claim 8 a kind of for improving the toning size of casement face color, which is characterized in that the propylene
The solid content of acid esters lotion is between 42%~45%.
10. as claimed in claim 8 a kind of for improving the toning size of casement face color, which is characterized in that the titanium
Kalsomine is to be formulated by titanium dioxide and water by the weight ratio of 1:1.