CN110317515A - 一种导电粉末涂料以及导电涂层 - Google Patents

一种导电粉末涂料以及导电涂层 Download PDF

Info

Publication number
CN110317515A
CN110317515A CN201910493992.9A CN201910493992A CN110317515A CN 110317515 A CN110317515 A CN 110317515A CN 201910493992 A CN201910493992 A CN 201910493992A CN 110317515 A CN110317515 A CN 110317515A
Authority
CN
China
Prior art keywords
parts
powder paint
conductive powder
agent
conductive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910493992.9A
Other languages
English (en)
Inventor
张�林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Xunxuan Textile Co Ltd
Original Assignee
Suzhou Xunxuan Textile Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Xunxuan Textile Co Ltd filed Critical Suzhou Xunxuan Textile Co Ltd
Priority to CN201910493992.9A priority Critical patent/CN110317515A/zh
Publication of CN110317515A publication Critical patent/CN110317515A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种导电粉末涂料以及导电涂层，其中，导电粉末涂料按重量计包括如下组分：50‑70份的树脂，5‑10份的填料，1‑3份的固化剂，1‑3份的助剂，0.5‑1.5份的流平剂，0.1‑0.5份的砂纹剂，所述填料按重量百分比计包括如下组分：10‑15％的石墨烯、10‑20％的钛白粉、40‑45％的聚四氟乙烯蜡、20‑40％的硫酸钡。本发明通过引入石墨烯作为导电填料，利用石墨烯的优异导电性，在用量较少的情况下就能够显著增加涂料的导电性，避免对涂层的力学性能造成影响，形成的涂层附着力、硬度、耐磨等性能表现良好。

Description

一种导电粉末涂料以及导电涂层
技术领域
本发明涉及导电粉末技术领域，具体是一种导电粉末涂料以及导电涂层。
背景技术
导电涂层是加涂在绝缘材料表面具有一定导电能力的薄膜或涂层。使用导电粉末涂料一般是掺和型导电涂层，掺合型导电涂层是将细颗粒的导电材料掺人到涂层的填料中，与有机或无机黏结剂、稀释剂一道涂刷或喷涂到绝缘材料表面，形成具有某种导电能力的导电层。它可以用喷涂、印刷、刷涂等工艺加涂在刚性或柔性底材上。根据使用要求，调节填料中导电粉末的含量，或用不同电阻率的导电材料则可调节导电涂层的电阻率。这类涂层主要用作电极、电加热膜，也可用来消除静电干扰。目前的导电粉末涂料存在导电炭黑填充量大、分散不均、形成的涂层力学性能较差等问题。
发明内容
本发明的目的在于提供一种导电粉末涂料以及导电涂层，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：
一种导电粉末涂料，按重量计包括如下组分：50-70份的树脂，5-10份的填料，1-3份的固化剂，1-3份的助剂，0.5-1.5份的流平剂，0.1-0.5份的砂纹剂。
作为本发明进一步的方案：所述树脂为环氧树脂、聚酯树脂中的任一种。
作为本发明进一步的方案：所述固化剂为三环氧丙基异氰尿酸酯、双氰胺、异氰尿酸三缩水甘油酯中的任一种。
作为本发明进一步的方案：所述填料按重量百分比计包括如下组分：10-15％的石墨烯、10-20％的钛白粉、40-45％的聚四氟乙烯蜡、20-40％的硫酸钡。
作为本发明进一步的方案：所述助剂为甲基丙烯酸甲酯均聚物、有机膨润土、亚磷酸酯按重量比例1：1：2混合而成。
作为本发明进一步的方案：所述流平剂为丙烯酸酯共聚物、丙烯酸酯均聚物、有机硅改性丙烯酸酯聚合物中的任一种。
作为本发明进一步的方案：所述砂纹剂按重量百分比计包括如下组分：1-10％的纳米铝、50-73％的二甘醇双氯甲酸酯、1-5％的三聚氰胺氰尿酸盐、10-15％的甲基丙烯酸甲酯、15-20％的月桂醇聚氧乙烯醚。
一种导电涂层，由上述的导电粉末涂料涂覆固化而成。
与现有技术相比，本发明的有益效果是：
本发明通过引入石墨烯作为导电填料，利用石墨烯的优异导电性，在用量较少的情况下就能够显著增加涂料的导电性，避免对涂层的力学性能造成影响，形成的涂层附着力、硬度、耐磨等性能表现良好。
具体实施方式
下面对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例一：
一种导电粉末涂料，按重量计包括如下组分：50份的树脂，5份的填料，1份的固化剂，1份的助剂，0.5份的流平剂，0.1份的砂纹剂。
所述树脂为环氧树脂。
所述固化剂为三环氧丙基异氰尿酸酯。
所述填料按重量百分比计包括如下组分：10％的石墨烯、10％的钛白粉、40％的聚四氟乙烯蜡、40％的硫酸钡。
所述助剂为甲基丙烯酸甲酯均聚物、有机膨润土、亚磷酸酯按重量比例1：1：2混合而成。
所述流平剂为丙烯酸酯共聚物。
所述砂纹剂按重量百分比计包括如下组分：1％的纳米铝、73％的二甘醇双氯甲酸酯、1％的三聚氰胺氰尿酸盐、10％的甲基丙烯酸甲酯、15％的月桂醇聚氧乙烯醚。
一种导电涂层，由上述的导电粉末涂料涂覆固化而成。
实施例二：
一种导电粉末涂料，按重量计包括如下组分：60份的树脂，7份的填料，2份的固化剂，2份的助剂，1份的流平剂，0.3份的砂纹剂。
所述树脂为环氧树脂。
所述固化剂为双氰胺。
所述填料按重量百分比计包括如下组分：13％的石墨烯、17％的钛白粉、40％的聚四氟乙烯蜡、30％的硫酸钡。
所述助剂为甲基丙烯酸甲酯均聚物、有机膨润土、亚磷酸酯按重量比例1：1：2混合而成。
所述流平剂为丙烯酸酯均聚物。
所述砂纹剂按重量百分比计包括如下组分：5％的纳米铝、62％的二甘醇双氯甲酸酯、3％的三聚氰胺氰尿酸盐、13％的甲基丙烯酸甲酯、17％的月桂醇聚氧乙烯醚。
一种导电涂层，由上述的导电粉末涂料涂覆固化而成。
实施例三：
一种导电粉末涂料，按重量计包括如下组分：70份的树脂，10份的填料，3份的固化剂，3份的助剂，1.5份的流平剂，0.5份的砂纹剂。
所述树脂为聚酯树脂。
所述固化剂为异氰尿酸三缩水甘油酯。
所述填料按重量百分比计包括如下组分：15％的石墨烯、20％的钛白粉、45％的聚四氟乙烯蜡、20％的硫酸钡。
所述助剂为甲基丙烯酸甲酯均聚物、有机膨润土、亚磷酸酯按重量比例1：1：2混合而成。
所述流平剂为有机硅改性丙烯酸酯聚合物。
所述砂纹剂按重量百分比计包括如下组分：10％的纳米铝、50％的二甘醇双氯甲酸酯、5％的三聚氰胺氰尿酸盐、15％的甲基丙烯酸甲酯、20％的月桂醇聚氧乙烯醚。
一种导电涂层，由上述的导电粉末涂料涂覆固化而成。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。

Claims (8)

1.一种导电粉末涂料，其特征在于，按重量计包括如下组分：50-70份的树脂，5-10份的填料，1-3份的固化剂，1-3份的助剂，0.5-1.5份的流平剂，0.1-0.5份的砂纹剂。
2.根据权利要求1所述的一种导电粉末涂料，其特征在于，所述树脂为环氧树脂、聚酯树脂中的任一种。
3.根据权利要求1所述的一种导电粉末涂料，其特征在于，所述固化剂为三环氧丙基异氰尿酸酯、双氰胺、异氰尿酸三缩水甘油酯中的任一种。
4.根据权利要求1所述的一种导电粉末涂料，其特征在于，所述填料按重量百分比计包括如下组分：10-15％的石墨烯、10-20％的钛白粉、40-45％的聚四氟乙烯蜡、20-40％的硫酸钡。
5.根据权利要求1所述的一种导电粉末涂料，其特征在于，所述助剂为甲基丙烯酸甲酯均聚物、有机膨润土、亚磷酸酯按重量比例1：1：2混合而成。
6.根据权利要求1所述的一种导电粉末涂料，其特征在于，所述流平剂为丙烯酸酯共聚物、丙烯酸酯均聚物、有机硅改性丙烯酸酯聚合物中的任一种。
7.根据权利要求1所述的一种导电粉末涂料，其特征在于，所述砂纹剂按重量百分比计包括如下组分：1-10％的纳米铝、50-73％的二甘醇双氯甲酸酯、1-5％的三聚氰胺氰尿酸盐、10-15％的甲基丙烯酸甲酯、15-20％的月桂醇聚氧乙烯醚。
8.一种导电涂层，其特征在于，由权利要求1-7任一所述的导电粉末涂料涂覆固化而成。
CN201910493992.9A 2019-06-08 2019-06-08 一种导电粉末涂料以及导电涂层 Pending CN110317515A (zh)