CN110306352A - 一种皮毛一体服装革的制备工艺 - Google Patents

一种皮毛一体服装革的制备工艺 Download PDF

Info

Publication number
CN110306352A
CN110306352A CN201910692513.6A CN201910692513A CN110306352A CN 110306352 A CN110306352 A CN 110306352A CN 201910692513 A CN201910692513 A CN 201910692513A CN 110306352 A CN110306352 A CN 110306352A
Authority
CN
China
Prior art keywords
leather
coating
double
face
preparation process
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910692513.6A
Other languages
English (en)
Inventor
张鸣霆
张一木
王体坤
周文发
何建武
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Baideli Leather Co Ltd
Original Assignee
Zhejiang Baideli Leather Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Baideli Leather Co Ltd filed Critical Zhejiang Baideli Leather Co Ltd
Priority to CN201910692513.6A priority Critical patent/CN110306352A/zh
Publication of CN110306352A publication Critical patent/CN110306352A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种皮毛一体服装革的制备工艺，涉及人造革制备的技术领域，包括以下工艺步骤：S1：配制PU树脂涂料、发泡涂料和胶黏涂料；S2：将PU树脂涂料均匀涂覆到离型纸上，然后在100～130℃下烘干，得到面膜层；S3：在面膜层上涂覆发泡涂料，然后再170～200℃下烘干，得到发泡层；S4：在发泡层上涂覆胶黏涂料，然后在150～160℃下烘干，得到胶粘层；S5：将基布热压到胶粘层上，然后将离型纸剥除后收卷，得到成品服装革。本发明具有提高人造革保温性能的效果。

Description

一种皮毛一体服装革的制备工艺
技术领域
本发明涉及服装革制备工艺的技术领域，尤其是涉及一种皮毛一体服装革的制备工艺。
背景技术
人造革是一种外观、手感似皮革并可代替其使用的塑料制品。通常以织物为底基，涂覆合成树脂及各种塑料添加制成。现有的大多数服装上的皮革都是采用人造革进行裁剪制作。
现有的人造服装革制作工艺通常采用离型纸法生产工艺，是将配制好的面膜层、发泡层和黏合层依次涂覆到离型纸表面，然后再将基布贴合到黏合层上，使其塑化发泡后再将离型纸剥离，然后再经过表面处理进行修饰后得到成品。
上述中的现有技术方案存在以下缺陷：采用现有技术制备得到的人造服装革虽然与皮革在手感和质地上近似，但是由于现有的人造服装革的材料采用聚氨酯或者聚氯乙烯等有机高分子材料，与动物皮革相比，其舒适度尤其是保温性能上有所不及。
发明内容
针对现有技术存在的不足，本发明的目的在于提供一种皮毛一体服装革的制备工艺，通过在配制人造革的PU树脂涂料、发泡涂料和胶黏涂料中添加可以发生协同效果的物质，从隔热以及保温的不同效果上对人造革的保温性能进行提升。
本发明的上述目的是通过以下技术方案得以实现的：
一种皮毛一体服装革的制备工艺，包括以下工艺步骤：
S1：配制PU树脂涂料、发泡涂料和胶黏涂料；
S2：将PU树脂涂料均匀涂覆到离型纸上，然后在100～130℃下烘干，得到面膜层；
S3：在面膜层上涂覆发泡涂料，然后再170～200℃下烘干，得到发泡层；
S4：在发泡层上涂覆胶黏涂料，然后在150～160℃下烘干，得到胶粘层；
S5：将基布热压到胶粘层上，然后将离型纸剥除后收卷，得到成品服装革。
通过采用上述技术方案，人造革在制作过程中先在待转印的离型纸上一次涂覆上不同的涂料形成面膜层、发泡层和胶黏层，然后再将基布与胶黏层进行热压粘合，从而得到可用于服装制作的人造革材料。面膜层中添加有隔热粉料，使得人造革在用于制作服装时，其最外侧的面膜层一方面可以在一定程度上隔绝内层与外界环境之间的热量交换，从而减少热量的传递，提高人造革的保温效果。而胶粘层中添加有保温粉料，使得人体自身产生的热量可以得到保留，提高升温效果，而且保温粉料中含有远红外物质，其散发的远红外线可以渗透到人体表皮下，通过介质传导和血液循环产生热量，活化细胞组织，从而起到保温升温的效果。
本发明进一步设置为：所述PU树脂涂料包括以下重量份数的组分：
本发明进一步设置为：所述隔热粉料包括以下重量百分比的组分：
本发明进一步设置为：所述润湿剂包括以下重量百分比的组分：
钛酸酯偶联剂 30～45％；
硅烷偶联剂 20～35％；
十二烷基硫酸钠 10～60％。
通过采用上述技术方案，聚氨酯粉末为面膜层的主要成分成膜物质，二甲基甲酰胺和甲乙酮为溶剂，其与聚氨酯粉末以及其他添加的有机材料具有较好的相容性，在面膜层涂覆完成后进行加热烘干时，溶剂挥发使得面膜层固化。色料用于调节聚氯乙烯膜层的颜色，使得其颜色与皮料相似。隔热粉料中海泡石一种纤维状的含水硅酸镁，其拥有贯穿整个结构的孔隙，具有很强的吸附能力，其可以将二氧化硅气凝胶粉体、氧化镁粉体吸附，从而提高在面膜层中二氧化硅气凝胶粉体、氧化镁粉体可添加量，二氧化硅气凝胶粉体是一种由二氧化硅胶体粒子通过相互桥联构成的具有三维空间网络结构的纳米多孔非晶固体材料，能有效抑制气体对流传热和降低固态热传导，具有极低的热导率，硅酸镁粉体也是具有低热导率的物质，从而使得面膜层与外界环境中的热传导降低，减少热量的散失。无机玻化微珠可以反射热辐射，使得内层产生的热量可以被部分反射回去，从而减少热量的损失。
钛酸酯偶联剂、硅烷偶联剂和十二烷基硫酸钠三者是表面活性剂，三者复配后可以提高降低隔热粉料的表面张力，从而使得隔热粉料中的固体粉料的分散均匀性得到提高。
本发明进一步设置为：所述发泡涂料包括以下重量份数的组分：
本发明进一步设置为：所述稳定剂中包括以下重量百分比的组分：
硬脂酸铝 30～40％；
硬脂酸钾 20～30％；
稀土稳定剂 30～50％。
通过采用上述技术方案，聚氯乙烯粉末作为发泡涂料中的主要成分，邻苯二甲酸二辛酯、邻苯二甲酸二辛酯和邻苯二甲酸丁基苄酯三者作为增塑剂成分，对聚氯乙烯树脂起到削弱聚合物分子之间的范德华力的作用，使得分子链之间的移动性增加，降低结晶性，提高塑性和柔韧性。硬脂酸铝、硬脂酸钾和稀土稳定剂三者可以抑制聚氯乙烯在加热时抑制其热分解作用，以防止其产生氯化氢气体而对聚氯乙烯的固化产生开裂等不良影响。
本发明进一步设置为：所述胶黏涂料包括以下重量份数的组分；
本发明进一步设置为：所述保温粉料包括以下重量百分比的组分：
二氧化钛粉末 30～40％；
珍珠岩粉末 10～20％；
胶粉苯颗粒 30～55％。
通过采用上述技术方案，聚氨酯粘合剂在胶黏层中起到主要的粘合作用，其中的甲乙酮用作溶剂，在加热烘干的过程中，其挥发而使得聚氨酯树脂发生固化交联，与基布中纤维链进行结合，从而将基布粘合。碳酸钙作为树脂的填充料，可以增加烘干后的表面硬度以及减小烘干时的体积变化，从而以防止开裂。保温粉料中，二氧化钛粉末是一种远红外物质，可以吸收太阳光中的远红外线，转化为自身的热能进行储存，然后不断地向内散发远红外线物质，从而对人体进行保温。
与现有技术相比，本发明的有益效果是：
1、通过在配制人造革的PU树脂涂料、发泡涂料和胶黏涂料中添加可以发生协同效果的物质，从隔热以及保温的不同效果上对人造革的保温性能进行提升；
2、通过对隔热粉料进行表面处理使得隔热粉料在PU树脂涂料中的分散更加均匀，并通过海泡石粉末对粉料进行吸附提高隔热粉料的添加上限，从而提高隔热效果。
附图说明
图1为本发明的工艺流程图。
具体实施方式
下面结合附图和实施例，对本发明进行详细描述。
实施例1：
参照图1，本发明公开的一种皮毛一体服装革的制备工艺，包括以下工艺步骤：
S1：配制PU树脂涂料：按重量份数将聚氨酯粉末80份、二甲基甲酰胺10份、甲乙酮10份、色料4份、隔热粉料2份和润湿剂0.5份加热混合搅拌均匀。
其中，隔热粉料包括以下重量百分比的组分：
其中，润湿剂包括以下重量百分比的组分：
钛酸酯偶联剂 30％；
硅烷偶联剂 20％；
十二烷基硫酸钠 50％。
配制发泡涂料:按重量份数将聚氯乙烯粉末80份、邻苯二甲酸二辛酯40份、邻苯二甲酸二辛酯10份、邻苯二甲酸丁基苄酯10份、稳定剂1份、发泡剂2份、整泡剂8份、填充料1份、色浆4份加热混合搅拌均匀。
其中，稳定剂中包括以下重量百分比的组分：
硬脂酸铝 30％；
硬脂酸钾 30％；
稀土稳定剂 40％。
配制胶黏涂料:按重量份数将聚氨酯粘合剂80份、稳定剂2份、甲乙酮40份、碳酸钙3份、保温粉料5份加热混合搅拌均匀。
其中，保温粉料包括以下重量百分比的组分：
二氧化钛粉末 40％；
珍珠岩粉末 20％；
胶粉苯颗粒 40％。
S2：将PU树脂涂料均匀涂覆到离型纸上，然后在130℃下烘干，得到面膜层；
S3：在面膜层上涂覆发泡涂料，然后再200℃下烘干，得到发泡层；
S4：在发泡层上涂覆胶黏涂料，然后在160℃下烘干，得到胶粘层；
S5：将基布热压到胶粘层上，然后将离型纸剥除后收卷，得到成品服装革。
实施例2～5与实施例1的区别在于：PU树脂涂料中各组分按重量份数计为下表。
实施例6～9与实施例1的区别在于：隔热粉料中各组分按重量百分比计为下表。
实施例10～13与实施例1的区别在于：润湿剂中各组分按重量百分比计为下表。
实施例 钛酸酯偶联剂 硅烷偶联剂 十二烷基硫酸钠
实施例10 33.75 23.75 42.5
实施例11 37.5 27.5 35
实施例12 41.25 31.25 27.5
实施例13 45 35 20
实施例14～17与实施例1的区别在于：发泡涂料中各组分按重量百分比计为下表。
实施例18～21与实施例1的区别在于：稳定剂中各组分按重量百分比计为下表。
实施例 硬脂酸铝 硬脂酸钾 稀土稳定剂
实施例18 32.5 22.5 45
实施例19 35 25 40
实施例20 37.5 27.5 35
实施例21 40 30 30
实施例22～25与实施例1的区别在于：胶黏涂料中各组分按重量份数计为下表。
实施例26～29与实施例1的区别在于：保温粉料中各组分按重量百分比计为下表。
对比例
对比例1与实施例1的区别在于：面膜层中未添加隔热粉料；
对比例2与实施例1的区别在于：胶黏层中未添加保温粉料；
对比例3与实施例1的区别在于：面膜层中未添加隔热粉料，胶黏层中也未添加保温粉料。
检测方法
保温性能检测
将直径为5cm的纯铁球加热至50摄氏度，然后用人造革将其包覆，并在人造革与纯铁球之间插入温度传感器，然后将人造革包覆的纯铁求放入5℃的环境中，然后每隔五分钟记录温度传感器的读数。
结果如下表：
结论：通过上表的数据可以看出，实施例1在1h内，其温度的变化化范围很低，而对比例1、对比例2和对比例3中的温度变化较快，下降很快，说明在人造革在添加有隔热粉料和保温粉料后其保温能力得到较大的提升。
以上所述仅是本发明的优选实施方式，本发明的保护范围并不仅局限于上述实施例，凡属于本发明思路下的技术方案均属于本发明的保护范围。应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理前提下的若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (8)

1.一种皮毛一体服装革的制备工艺，其特征在于：包括以下工艺步骤：
S1：配制PU树脂涂料、发泡涂料和胶黏涂料；
S2：将PU树脂涂料均匀涂覆到离型纸上，然后在100～130℃下烘干，得到面膜层；
S3：在面膜层上涂覆发泡涂料，然后再170～200℃下烘干，得到发泡层；
S4：在发泡层上涂覆胶黏涂料，然后在150～160℃下烘干，得到胶粘层；
S5：将基布热压到胶粘层上，然后将离型纸剥除后收卷，得到成品服装革。
2.根据权利要求1所述的一种皮毛一体服装革的制备工艺，其特征在于：所述PU树脂涂料包括以下重量份数的组分：
3.根据权利要求2所述的一种皮毛一体服装革的制备工艺，其特征在于：所述隔热粉料包括以下重量百分比的组分：
4.根据权利要求2所述的一种皮毛一体服装革的制备工艺，其特征在于：所述润湿剂包括以下重量百分比的组分：
钛酸酯偶联剂 30～45％；
硅烷偶联剂 20～35％；
十二烷基硫酸钠 10～60％。
5.根据权利要求1所述的一种皮毛一体服装革的制备工艺，其特征在于：所述发泡涂料包括以下重量份数的组分：
6.根据权利要求5所述的一种皮毛一体服装革的制备工艺，其特征在于：所述稳定剂中包括以下重量百分比的组分：
硬脂酸铝 30～40％；
硬脂酸钾 20～30％；
稀土稳定剂 30～50％。
7.根据权利要求1所述的一种皮毛一体服装革的制备工艺，其特征在于：所述胶黏涂料包括以下重量份数的组分；
8.根据权利要求7所述的一种皮毛一体服装革的制备工艺，其特征在于：所述保温粉料包括以下重量百分比的组分：
二氧化钛粉末 30～40％；
珍珠岩粉末 10～20％；
胶粉苯颗粒 30～55％。
CN201910692513.6A 2019-07-30 2019-07-30 一种皮毛一体服装革的制备工艺 Pending CN110306352A (zh)