CN110279205A - 一种电铸镶嵌宝石工艺 - Google Patents
一种电铸镶嵌宝石工艺 Download PDFInfo
- Publication number
- CN110279205A CN110279205A CN201910722431.1A CN201910722431A CN110279205A CN 110279205 A CN110279205 A CN 110279205A CN 201910722431 A CN201910722431 A CN 201910722431A CN 110279205 A CN110279205 A CN 110279205A
- Authority
- CN
- China
- Prior art keywords
- wax
- copper
- gold
- jewel
- silver
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种电铸镶嵌宝石工艺,解决现有宝石镶嵌不能与电铸金或K金一体成型的问题。包括有如下步骤:A:银模制作:用金属银制作腔体模具;B:蜡模制作:用硅胶包裹银模,制造出硅模腔体模具,在硅模腔体内浇灌蜡,凝固后形成蜡模;C:在蜡模表面刷一层铜油形成一层软质铜油层;D:在铜油表面电铸铜形成一层硬质铜外壳;E:在铜外壳表面电镀一层保护银;F:将液态蜡以滴蜡的方式覆盖在宝石表面,直至完全包裹宝石;G:将包裹蜡的宝石镶进银镀层的镶口内;H:将整个产品进行电铸金或K金固定宝石;I:在产品上打孔,孔的深度能深及蜡层;J:除蜡;K:去除铜油层,铜以及银;L:对金或K金表面处理。从而宝石与金或者K金一体成型,不会破坏宝石的整体外观造型,外观美观。
Description
技术领域
本发明涉及首饰领域,尤其涉及一种电铸镶嵌宝石工艺。
背景技术
传统用的宝石镶嵌通常是通过爪镶配件用物理性方法,把宝石固定在金或者K金表面,配件的焊接的工艺具有局限性,对饰品的结构有要求,另外饰品一般比较小巧,不好控制焊接点的尺寸;对于爪镶容易破环宝石整个的外观完整,影响美观,从而宝石镶嵌不能与金或K金一体成型,影响美观。
发明内容
本发明的目的在于解决现有宝石镶嵌不能与电铸金或K金一体成型的问题。
为解决本发明所提出的技术问题采用的技术方案为:本发明的电铸镶嵌宝石工艺包括有如下步骤:
A:银模制作:用金属银制作腔体模具;
B:蜡模制作:用硅胶包裹银模,制造出硅模腔体模具,在硅模腔体内浇灌蜡,凝固后形成蜡模;
C:在蜡模表面刷一层铜油形成一层软质铜油层;
D:在铜油表面电铸铜形成一层硬质铜外壳;
E:在铜外壳表面电镀一层保护银;
F:将液态蜡以滴蜡的方式覆盖在宝石表面,直至完全包裹宝石;
G:将包裹蜡的宝石镶进银镀层的镶口内;
H:将整个产品进行电铸金或K金,电铸金或K金在宝石安装位的上下两侧形成阻挡块将宝石固定;
I:在产品上打孔,孔的深度能深及蜡层;
J:除蜡;
K:去除铜油层,铜以及银;
L:对金或K金表面处理。
对本发明作进一步限定的技术方案包括:
所述的步骤B中,蜡模形成后对蜡模进行修整,用白电油进行抛光。
所述的步骤F中,用热风枪对包裹蜡的宝石进行加热。
所述的步骤G中,宝石的镶嵌可以为包镶、爪镶或迫镶。
所述的步骤J中,除蜡用热碱水除蜡。
所述的步骤K中,热硝酸去除铜油层,铜和银。
所述的步骤L中,表面处理为对金或K金表面抛光。
通过上述技术方案,本发明的有益效果为:本发明的电铸镶嵌宝石工艺,电铸层会把宝石与镶口金属层之间的空歇填满,并且在宝石安装位的上下两侧形成阻挡块,从而把宝石固定,防止宝石晃动脱落,从而宝石与金或者K金一体成型,不会破坏宝石的整体外观造型,外观美观。
附图说明
图1为本发明一种电铸镶嵌宝石工艺的剖切结构示意图。
具体实施方式
以下结合附图对本发明的结构做进一步说明。
参照图1,一种电铸镶嵌宝石工艺包括有如下步骤:
A:银模制作:用金属银制作腔体模具;
B:蜡模制作:用硅胶包裹银模,制造出硅模腔体模具,在硅模腔体内浇灌蜡,凝固后形成蜡模;本实施例中,蜡模形成后对蜡模进行修整,用白电油进行抛光。
C:在蜡模表面刷一层铜油形成一层软质铜油层;铜油层可以导电,从而可以进行电铸。
D:在铜油表面电铸铜形成一层硬质铜外壳;硬质外壳层在操作时不容易损坏,能够更好的进行后续的工艺操作。
E:在铜外壳表面电镀一层保护银;银的导电性比较好,铜在空气中容易氧化,在铜外壳表面电铸银,能够防止铜的氧化;同时银导电性能好,从而可以进行电铸。
F:将液态蜡以滴蜡的方式覆盖在宝石表面,直至完全包裹宝石;本实施例中,用热风枪对包裹蜡的宝石进行加热,可以把蜡的分布得更均匀,更薄,同时把残留在边位上多余的蜡清除出来。
G:将包裹蜡的宝石1镶进银镀层的镶口2内;本实施例中,宝石的镶嵌可以为包镶、爪镶或迫镶。
H:将整个产品进行电铸金或K金,电铸金或K金在宝石安装位的上下两侧形成阻挡块将宝石固定;蜡因防水及防渗透特征,有效保护宝石避免电铸液的化学侵蚀,影响石头的颜色及光泽度。薄蜡有助稳固石头避免受水阻及摇摆的外力而脱落。电铸过程中,电铸层会把宝石1与镶口金属层之间的空歇填满,并且在宝石的上下两侧形成阻挡块3,从而把宝石固定,防止宝石晃动脱落。
I:在产品上打孔,孔的深度能深及蜡层;为除蜡和除铜油层,铜以及银做好准备。
J:除蜡;本实施例中,将产品整个放在热碱水使蜡溶解从孔内流出去除。
K:去除铜油层,铜以及银;本实施例中,将产品整个放在硝酸液中,铜离子和银离子与硝酸反应从孔内流出去除。
L:对金或K金表面处理。即对金或K金表面抛光达到一定的亮度。
通过上述技术方案,本发明的有益效果为:本发明的电铸镶嵌宝石工艺,电铸层会把宝石与镶口金属层之间的空歇填满,并且在宝石安装位的上下两侧形成阻挡块,从而把宝石固定,防止宝石晃动脱落,从而宝石与金或者K金一体成型,不会破坏宝石的整体外观造型,外观美观。
虽然结合附图对本发明的具体实施方式进行了详细地描述,但不应理解为对本发明的保护范围的限定。在权利要求书所描述的范围内,本领域技术人员不经创造性劳动即可做出的各种修改和变形仍属于本发明的保护范围。
Claims (7)
1.一种电铸镶嵌宝石工艺,其特征在于:包括有如下步骤:
A:银模制作:用金属银制作腔体模具;
B:蜡模制作:用硅胶包裹银模,制造出硅模腔体模具,在硅模腔体内浇灌蜡,凝固后形成蜡模;
C:在蜡模表面刷一层铜油形成一层软质铜油层;
D:在铜油表面电铸铜形成一层硬质铜外壳;
E:在铜外壳表面电镀一层保护银;
F:将液态蜡以滴蜡的方式覆盖在宝石表面,直至完全包裹宝石;
G:将包裹蜡的宝石镶进银镀层的镶口内;
H:将整个产品进行电铸金或K金,电铸金或K金在宝石安装位的上下两侧形成阻挡块将宝石固定;
I:在产品上打孔,孔的深度能深及蜡层;
J:除蜡;
K:去除铜油层,铜以及银;
L:对金或K金表面处理。
2.如权利要求1所述的一种电铸镶嵌宝石工艺,其特征在于:所述的步骤B中,蜡模形成后对蜡模进行修整,用白电油进行抛光。
3.如权利要求1所述的一种电铸镶嵌宝石工艺,其特征在于:所述的步骤F中,用热风枪对包裹蜡的宝石进行加热。
4.如权利要求1所述的一种电铸镶嵌宝石工艺,其特征在于:所述的步骤G中,宝石的镶嵌可以为包镶、爪镶或迫镶。
5.如权利要求1所述的一种电铸镶嵌宝石工艺,其特征在于:所述的步骤J中,除蜡用热碱水除蜡。
6.如权利要求1所述的一种电铸镶嵌宝石工艺,其特征在于:所述的步骤K中,热硝酸去除铜油层,铜和银。
7.如权利要求1所述的一种电铸镶嵌宝石工艺,其特征在于:所述的步骤L中,表面处理为对金或K金表面抛光。