CN110255906A - A kind of anion thickness throws glaze and its processing method - Google Patents
A kind of anion thickness throws glaze and its processing method Download PDFInfo
- Publication number
- CN110255906A CN110255906A CN201910712902.0A CN201910712902A CN110255906A CN 110255906 A CN110255906 A CN 110255906A CN 201910712902 A CN201910712902 A CN 201910712902A CN 110255906 A CN110255906 A CN 110255906A
- Authority
- CN
- China
- Prior art keywords
- parts
- anion
- glaze
- thickness
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of anion thickness to throw glaze, including following raw material: potassium feldspar, zinc oxide, calcination of talc, dolomite, barium sulfate, strontium carbonate, wollastonite, kaolin, quartz, frit, negative ion powder, the processing method that the thickness throws glaze, including step 1, stock;Step 2, filling;Step 3, mixing;Step 4 is examined;Step 5, packing processes.The anion thickness throws application method of the glaze in fired brick, includes the following steps: test proportion, according to anion number, color development, antifouling index preparation raw material;Pretreatment, sprays overglaze in adobe using bell jar slip shower;Ink-jet sprays ink pattern on brick face after the pre-treatment;Glazing is sprayed anion thickness in adobe using bell jar slip shower and throws glaze;It fires, the adobe after glazing is sent into kiln and is fired, a kind of anion thickness of the invention throws glaze and its processing method, is formulated using adjusting, to solve the problems, such as to combine anion and thick throwing advantage in background technique.
Description
Technical field
The present invention relates to a kind of tile product paint field, specifically a kind of anion thickness throws glaze and its processing method.
Background technique
Anion is a kind of negatively charged gas ion in air, and there is restraining and sterilizing bacteria, dedusting deodorization, raising body to exempt from
Epidemic disease power, the function of fresh air, be otherwise known as " air vitamin ", has highly important influence to human life activity.
When interior decoration, the pernicious gases such as the meeting such as furniture, plate, paint sustained release formaldehyde, ammonia, benzene influence people
Health.If anion technology can be introduced into ceramic tile, what ceramic tile when finishing using paving generated
Anion fine-purification air can greatly improve people's lives environmental quality.
Thickness throws glaze and can solve the problems, such as commonly to throw glaze " water ripples " entirely significantly, enhances the aesthetics of decoration.
It, then can be to a certain degree if a kind of Ceramic Tiles for decoration can be produced in conjunction with anion and thick the advantages of throwing glaze
Upper improvement people's lives quality.
Summary of the invention
The purpose of the present invention is to provide a kind of anion thickness to throw glaze and its processing method, is formulated using adjustment, to solve
Background technique combination anion and thick the problem of throwing advantage.
To achieve the above object, the invention provides the following technical scheme:
A kind of anion thickness throwing glaze, the raw material including following parts by weight are mixed: 20-40 parts of potassium feldspar, zinc oxide 2-8
Part, 5-15 parts of calcination of talc, 1-8 parts of dolomite, 5-12 parts of barium sulfate, 1-5 parts of strontium carbonate, 10-20 parts of wollastonite, kaolin 5-
10 parts, 1-5 parts of quartz, 10-20 parts of frit, 1-3 parts of negative ion powder.
Specifically, a kind of anion thickness throws glaze, the raw material including following parts by weight is made: 25-38 parts of potassium feldspar, zinc oxide
4-8 parts, 6-13 parts of calcination of talc, 2-7 parts of dolomite, 5-10 parts of barium carbonate, 2-5 parts of strontium carbonate, 10-18 parts of wollastonite, kaolinite
6-9 parts native, 1-3 parts of quartz, 10-18 parts of frit, 1-2 parts of negative ion powder.
Specifically, a kind of anion thickness throws glaze, the raw material including following parts by weight is made: 35 parts of potassium feldspar, zinc oxide 8
Part, 3 parts of quartz, is melted 10 parts of calcination of talc, 6 parts of dolomite, 8 parts of barium sulfate, 3 parts of strontium carbonate, 16 parts of wollastonite, 7 parts of kaolin
12 parts of block, 2 parts of negative ion powder.
A kind of processing method that anion thickness throws glaze, comprising the following steps:
S1, stock obtain constituent and its parts by weight that the anion thickness throws glaze;
Raw material in step 1 is grouped by S2, filling, wherein potassium feldspar be first group, kaolin, reoxidize zinc,
Burning talcum, dolomite, barium sulfate, strontium carbonate, frit and negative ion powder is second group, and calcined kaolin, quartz are third group, often
Kind of raw material with etc. parts by weight the above raw material is successively put into batch mixer according to order of packets, complete successively above-mentioned raw materials and put into
Afterwards, it repeats the above steps and surplus stock substep is added in batch mixer;
S3, mixing, starting mixing work, continuous mixing 40-50 minutes;
S4 is examined, is detected to the raw material after mixing;
S5, packing processes carry out discharging packaging to qualified products.
A kind of anion thickness of the invention throws glaze, by introducing anion technology, Ceramic Tiles anion burst size is enable to reach
To 2000~2500/cubic centimetre, in addition throwing glaze technology using thick, ideally solves and commonly throw lacking for glaze " water ripples " entirely
It falls into, after decorating Ceramic Tiles, can play the role of purifying air and space aesthetic feeling.
The processing method that a kind of anion thickness of the invention throws glaze, the beneficial effect is that, by adjusting filling step, make
The raw material of each ingredient is uniformly mixed, and guarantees that mixed anion thickness throws glaze balanced composition, and then improve the quality of product.(this
In description be duplication big plate dry granular content, inappropriate, I deletes front.Thickness is thrown glaze and is thrown as glaze with complete, is all
It is used alone, it is the full upgrade version for throwing glaze that thickness, which throws glaze,.)
Specific embodiment
Technical solution of the present invention is clearly and completely described below in conjunction with the embodiment of the present invention, it is clear that retouched
The embodiment stated is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, originally
Field those of ordinary skill every other embodiment obtained without making creative work, belongs to the present invention
The range of protection.
Embodiment one
A kind of anion thickness throwing glaze, the raw material including following parts by weight are mixed: 20-40 parts of potassium feldspar, zinc oxide 2-8
Part, 5-15 parts of calcination of talc, 1-8 parts of dolomite, 5-12 parts of barium sulfate, 1-5 parts of strontium carbonate, 10-20 parts of wollastonite, kaolin 5-
10 parts, 1-5 parts of quartz, 10-20 parts of frit, 1-3 parts of negative ion powder.
The following steps are included:
A1, stock obtain constituent and its parts by weight that the anion thickness throws glaze;
Raw material in step 1 is grouped by A2, filling, wherein potassium feldspar be first group, kaolin, reoxidize zinc,
Burning talcum, dolomite, barium sulfate, strontium carbonate, frit and negative ion powder is second group, and calcined kaolin, quartz are third group, often
Kind of raw material with etc. parts by weight the above raw material is successively put into batch mixer according to order of packets, complete successively above-mentioned raw materials and put into
Afterwards, it repeats the above steps and surplus stock substep is added in batch mixer;
A3, mixing, starting mixing work, continuous mixing 40-50 minutes;
A4 is examined, is detected to the raw material after mixing;
A5, packing processes carry out discharging packaging to qualified products.
Embodiment two
A kind of anion thickness throws glaze, and the raw material including following parts by weight is made: 25-38 parts of potassium feldspar, 4-8 parts of zinc oxide,
6-13 parts of calcination of talc, 2-7 parts of dolomite, 5-10 parts of barium carbonate, 2-5 parts of strontium carbonate, 10-18 parts of wollastonite, kaolin 6-9
Part, 1-3 parts of quartz, 10-18 parts of frit, 1-2 parts of negative ion powder.
The following steps are included:
B1, stock obtain constituent and its parts by weight that the anion thickness throws glaze;
Raw material in step 1 is grouped by B2, filling, wherein potassium feldspar be first group, kaolin, reoxidize zinc,
Burning talcum, dolomite, barium sulfate, strontium carbonate, frit and negative ion powder is second group, and calcined kaolin, quartz are third group, often
Kind of raw material with etc. parts by weight the above raw material is successively put into batch mixer according to order of packets, complete successively above-mentioned raw materials and put into
Afterwards, it repeats the above steps and surplus stock substep is added in batch mixer;
B3, mixing, starting mixing work, continuous mixing 40-50 minutes;
B4 is examined, is detected to the raw material after mixing;
B5, packing processes carry out discharging packaging to qualified products.
Embodiment three
A kind of anion thickness throwing glaze, the raw material including following parts by weight are made: 35 parts of potassium feldspar, 8 parts of zinc oxide, calcining are slided
10 parts of stone, 8 parts of barium sulfate, 3 parts of strontium carbonate, 16 parts of wollastonite, 7 parts of kaolin, 3 parts of quartz, 12 parts of frit, is born 6 parts of dolomite
2 parts of ion powder.
The following steps are included:
C1, stock obtain constituent and its parts by weight that the anion thickness throws glaze;
Raw material in step 1 is grouped by C2, filling, wherein potassium feldspar be first group, kaolin, reoxidize zinc,
Burning talcum, dolomite, barium sulfate, strontium carbonate, frit and negative ion powder is second group, and calcined kaolin, quartz are third group, often
Kind of raw material with etc. parts by weight the above raw material is successively put into batch mixer according to order of packets, complete successively above-mentioned raw materials and put into
Afterwards, it repeats the above steps and surplus stock substep is added in batch mixer;
C3, mixing, starting mixing work, continuous mixing 40-50 minutes;
C4 is examined, is detected to the raw material after mixing;
C5, packing processes carry out discharging packaging to qualified products.
Example IV
A kind of anion thickness throwing glaze, the raw material including following parts by weight are made: potassium feldspar 36g, zinc oxide 6g, calcination of talc
9g, dolomite 5g, barium sulfate 8g, strontium carbonate 4g, wollastonite 18g, kaolin 8g, quartz 2g, frit 14g, negative ion powder 2g.
The following steps are included:
D1, stock obtain and weigh constituent and its parts by weight that the anion thickness throws glaze;
Raw material in step 1 is grouped by D2, filling, wherein potassium feldspar be first group, kaolin, reoxidize zinc,
Burning talcum, dolomite, barium sulfate, strontium carbonate, frit and negative ion powder is second group, and calcined kaolin, quartz are third group, often
Kind of raw material with etc. parts by weight the above raw material is successively put into batch mixer according to order of packets, complete successively above-mentioned raw materials and put into
Afterwards, it repeats the above steps and surplus stock substep is added in batch mixer;
D3, mixing, starting mixing work, continuous mixing 40-50 minutes;
D4 is examined, is detected to the raw material after mixing;
D5, packing processes carry out discharging packaging to qualified products.
Embodiment five
A kind of anion thickness throwing glaze, the raw material including following parts by weight are made: potassium feldspar 35g, zinc oxide 7g, calcination of talc
9g, dolomite 7g, barium sulfate 10g, strontium carbonate 4g, wollastonite 18g, kaolin 7g, quartz 3g, frit 13g, negative ion powder 2g.
The following steps are included:
E1, stock obtain constituent and its parts by weight that the anion thickness throws glaze;
Raw material in step 1 is grouped by E2, filling, wherein potassium feldspar be first group, kaolin, reoxidize zinc,
Burning talcum, dolomite, barium sulfate, strontium carbonate, frit and negative ion powder is second group, and calcined kaolin, quartz are third group, often
Kind of raw material with etc. parts by weight the above raw material is successively put into batch mixer according to order of packets, complete successively above-mentioned raw materials and put into
Afterwards, it repeats the above steps and surplus stock substep is added in batch mixer;
E3, mixing, starting mixing work, continuous mixing 40-50 minutes;
E4 is examined, is detected to the raw material after mixing;
E5, packing processes carry out discharging packaging to qualified products.
Application Example one
Glaze glaze is thrown using the thickness as described in embodiment three, suitable quantity of water is added and ball milling obtains glaze slip, is drenching
The glaze slip is spooned in the adobe of overglaze, is fired into kiln, kiln discharge, and polishing detects anion number and " water ripples " situation.
Application Example two
Using the thick throwing glaze glaze as described in example IV kind, suitable quantity of water is added and ball milling obtains glaze slip, is drenching
The glaze slip is spooned in the adobe of overglaze, is fired into kiln, kiln discharge, and polishing detects anion number and " water ripples " situation.
Application Example three
Using the thick throwing glaze glaze as described in five kinds of embodiment, suitable quantity of water is added and ball milling obtains glaze slip, is drenching
The glaze slip is spooned in the adobe of overglaze, is fired into kiln, kiln discharge, and polishing detects anion number and " water ripples " situation.
Testing result
Table one
Project | Application Example one | Application Example two | Application Example three |
Anion number (a/cubic centimetre) | 2500 | 2200 | 2300 |
" water ripples " situation | Without " water ripples " | Without " water ripples " | Without " water ripples " |
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims
Variation is included within the present invention.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (4)
1. a kind of anion thickness throws glaze, which is characterized in that the raw material including following parts by weight is mixed: 20-40 parts of potassium feldspar,
2-8 parts of zinc oxide, 5-15 parts of calcination of talc, 1-8 parts of dolomite, 5-12 parts of barium sulfate, 1-5 parts of strontium carbonate, wollastonite 10-20
Part, 5-10 parts of kaolin, 1-5 parts of quartz, 10-20 parts of frit, 1-3 parts of negative ion powder.
2. a kind of anion thickness according to claim 1 throws glaze, which is characterized in that the raw material system including following parts by weight
At: 25-38 parts of potassium feldspar, 4-8 parts of zinc oxide, 6-13 parts of calcination of talc, 2-7 parts of dolomite, 5-10 parts of barium carbonate, strontium carbonate 2-
5 parts, 10-18 parts of wollastonite, 6-9 parts of kaolin, 1-3 parts of quartz, 10-18 parts of frit, 1-2 parts of negative ion powder.
3. a kind of anion thickness according to claim 1 throws glaze, which is characterized in that the raw material system including following parts by weight
At: 35 parts of potassium feldspar, 8 parts of zinc oxide, 10 parts of calcination of talc, 6 parts of dolomite, 8 parts of barium sulfate, 3 parts of strontium carbonate, wollastonite 16
Part, 7 parts of kaolin, quartzy 3 parts, 12 parts of frit, 2 parts of negative ion powder.
4. a kind of processing method for throwing glaze applied to a kind of any anion thickness of claims 1 to 3, which is characterized in that
The following steps are included:
S1, stock obtain constituent and its parts by weight that any one of claims 1 to 3 anion thickness throws glaze;
Raw material in step 1 is grouped by S2, filling, and wherein potassium feldspar is first group, and kaolin reoxidizes zinc, burns and slide
Stone, dolomite, barium sulfate, strontium carbonate, frit and negative ion powder are second group, and calcined kaolin, quartz are third group, every kind of original
Material with etc. parts by weight successively put into the above raw material into batch mixer according to order of packets, after completing successively above-mentioned raw materials investment, weight
Surplus stock substep is added in batch mixer by multiple above-mentioned steps;
S3, mixing, starting mixing work, continuous mixing 40-50 minutes;
S4 is examined, is detected to the raw material after mixing;
S5, packing processes carry out discharging packaging to qualified products.