CN110372213A - One kind is unglazed protection glaze modelled after an antique and its processing method - Google Patents
One kind is unglazed protection glaze modelled after an antique and its processing method Download PDFInfo
- Publication number
- CN110372213A CN110372213A CN201910713640.XA CN201910713640A CN110372213A CN 110372213 A CN110372213 A CN 110372213A CN 201910713640 A CN201910713640 A CN 201910713640A CN 110372213 A CN110372213 A CN 110372213A
- Authority
- CN
- China
- Prior art keywords
- parts
- unglazed
- antique
- raw material
- kaolin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of unglazed protection glaze modelled after an antique, including following raw material: potassium feldspar, albite, zinc oxide, calcination of talc, barium carbonate, calcined kaolin, kaolin, quartz, frit powder.The processing method modelled after an antique for protecting glaze that this is unglazed, including step 1, stock；Step 2, filling；Step 3, mixing；Step 4 is examined；Step 5, packing processes, and the application method in fired brick include the following steps: test proportion, according to glossiness, antifouling, color development, feel index preparation raw material；Pretreatment, sprays overglaze in adobe using glaze spraying cabinet or bell jar slip shower；Ink-jet, according to design spraying ink pattern and color on brick face after the pre-treatment；Protection glaze is sprayed in glazing using glaze spraying cabinet in adobe；Fire, the adobe after glazing be sent into kiln and is fired, and it is an object of the present invention to provide a kind of unglazed protection glaze modelled after an antique and its processing method, make the protection glaze with glossiness it is low, antifouling it is good, color development is good, the good effect such as soft touch.
Description
Technical field
The present invention relates to a kind of tile product paint field, specifically a kind of unglazed protection glaze modelled after an antique and its processing method.
Background technique
For Antique Imitation Tiles design subject matter substantially based on natural-like stone, timber, fabrics etc., these material materials are basic
Unglazed, so Antique Imitation Tiles glaze accomplishes that no light condition could be copied more true to nature as far as possible, but common glaze be transferred to it is unglazed
State, color development is poor, it is antifouling it is poor, feel is coarse.
Summary of the invention
The purpose of the present invention is to provide a kind of unglazed protection glaze modelled after an antique and its processing methods, to solve above-mentioned background technique
The problem of middle proposition.
To achieve the above object, the invention provides the following technical scheme:
A kind of unglazed protection glaze modelled after an antique, the raw material including following parts by weight: 20-40 parts of potassium feldspar, 10-20 parts of albite,
Zinc oxide 1-5,5-15 parts of calcination of talc, 10-20 parts of barium carbonate, 5-15 parts of calcined kaolin, 10-20 parts of kaolin, quartz 1-5
Part, 10-20 parts of frit powder.
Specifically, a kind of unglazed protection glaze modelled after an antique, the raw material including following parts by weight: 25-35 parts of potassium feldspar, albite
10-15 parts, zinc oxide 2-5,8-12 parts of calcination of talc, 12-18 parts of barium carbonate, 5-12 parts of calcined kaolin, kaolin 12-19
Part, 2-4 parts of quartz, 10-18 parts of frit powder.
Specifically, a kind of unglazed protection glaze modelled after an antique, the raw material including following parts by weight: 30 parts of potassium feldspar, 12 parts of albite,
3 parts of zinc oxide, 10 parts of calcination of talc, 18 parts of barium carbonate, 10 parts of calcined kaolin, 15 parts of kaolin, quartzy 3 parts, frit powder 12
Part.
A kind of processing method applied to the unglazed protection glaze modelled after an antique of the described in any item one kind of claims 1 to 3, including with
Lower step:
Step 1, stock obtain constituent and its weight that any one of claims 1 to 3 anion thickness throws glaze
Part；
Raw material in step 1 is grouped by step 2, filling, and wherein potassium feldspar and albite are first group, kaolinite
Soil is second group, and zinc oxide, calcination of talc, barium carbonate and frit powder are third group, and calcined kaolin and quartz are the 4th group, often
Kind of raw material with etc. parts by weight the above raw material is successively put into batch mixer according to order of packets, complete successively above-mentioned raw materials and put into
Afterwards, it repeats the above steps and surplus stock substep is added in batch mixer；
Step 3, mixing, starting mixing work, continuous mixing 40-50 minutes；
Step 4 is examined, is detected to the raw material after mixing；
Step 5, packing processes carry out discharging packaging to qualified products.
The unglazed protection glaze modelled after an antique of one kind of the invention, the beneficial effect is that: by adjusting formula and material rate, by adding
Add barium carbonate and quartz and adjustment mass ratio, realizes and the glossiness of the protection glaze is adjusted, by adjusting the addition ratio of zinc oxide
The full color development for throwing glaze can be adjusted in example, can carry out to the full anti-fouling effect for throwing glaze by adjusting calcination of talc adding proportion
Improvement realizes that the adobe made of the glaze has good feel using frit powder and its adding proportion.
The processing method modelled after an antique for protecting glaze that one kind of the invention is unglazed, the beneficial effect is that: by adjusting filling step, make
The raw material of each ingredient is uniformly mixed, and guarantees mixed unglazed protection glaze balanced composition, and then improve the quality of product.
Specific embodiment
Technical solution of the present invention is clearly and completely described below in conjunction with the embodiment of the present invention, it is clear that retouched
The embodiment stated is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, originally
Field those of ordinary skill every other embodiment obtained without making creative work, belongs to the present invention
The range of protection.
Embodiment one
A kind of unglazed protection glaze modelled after an antique, the raw material including following parts by weight: 20-40 parts of potassium feldspar, 10-20 parts of albite,
Zinc oxide 1-5,5-15 parts of calcination of talc, 10-20 parts of barium carbonate, 5-15 parts of calcined kaolin, 10-20 parts of kaolin, quartz 1-5
Part, 10-20 parts of frit powder.
The following steps are included:
A1, stock obtain the constituent and its parts by weight of unglazed protection glaze modelled after an antique；
Raw material in A1 is grouped by A2, filling, and wherein potassium feldspar and albite are first group, kaolin second
Group, zinc oxide, calcination of talc, barium carbonate and frit powder be third group, calcined kaolin and quartz be the 4th group, every kind of raw material with
Etc. parts by weight successively put into the above raw material into batch mixer according to order of packets, after completing successively above-mentioned raw materials investment, in repetition
It states step surplus stock substep is added in batch mixer；
A3, mixing, starting mixing work, continuous mixing 40-50 minutes；
A4 is examined, is detected to the raw material after mixing；
A5, packing processes carry out discharging packaging to qualified products.
Embodiment two
A kind of unglazed protection glaze modelled after an antique, the raw material including following parts by weight: 25-35 parts of potassium feldspar, 10-15 parts of albite,
Zinc oxide 2-5,8-12 parts of calcination of talc, 12-18 parts of barium carbonate, 5-12 parts of calcined kaolin, 12-19 parts of kaolin, quartz 2-4
Part, 10-18 parts of frit powder.
The following steps are included:
B1, stock obtain the constituent and its parts by weight of unglazed protection glaze modelled after an antique；
Raw material in B1 is grouped by B2, filling, and wherein potassium feldspar and albite are first group, kaolin second
Group, zinc oxide, calcination of talc, barium carbonate and frit powder be third group, calcined kaolin and quartz be the 4th group, every kind of raw material with
Etc. parts by weight successively put into the above raw material into batch mixer according to order of packets, after completing successively above-mentioned raw materials investment, in repetition
It states step surplus stock substep is added in batch mixer；
B3, mixing, starting mixing work, continuous mixing 40-50 minutes；
B4 is examined, is detected to the raw material after mixing；
B5, packing processes carry out discharging packaging to qualified products.
Embodiment three
A kind of unglazed protection glaze modelled after an antique, the raw material including following parts by weight: 30 parts of potassium feldspar, 12 parts of albite, zinc oxide 3
Part, 10 parts of calcination of talc, 18 parts of barium carbonate, 10 parts of calcined kaolin, 15 parts of kaolin, 3 parts, 12 parts of frit powder of quartz.
The following steps are included:
C1, stock obtain the constituent and its parts by weight of unglazed protection glaze modelled after an antique；
Raw material in C1 is grouped by C2, filling, and wherein potassium feldspar and albite are first group, kaolin second
Group, zinc oxide, calcination of talc, barium carbonate and frit powder be third group, calcined kaolin and quartz be the 4th group, every kind of raw material with
Etc. parts by weight successively put into the above raw material into batch mixer according to order of packets, after completing successively above-mentioned raw materials investment, in repetition
It states step surplus stock substep is added in batch mixer；
C3, mixing, starting mixing work, continuous mixing 40-50 minutes；
C4 is examined, is detected to the raw material after mixing；
C5, packing processes carry out discharging packaging to qualified products.
Application Example one
Using the unglazed protection glaze modelled after an antique as described in embodiment one, suitable quantity of water is added and ball milling obtains glaze slip,
It has sprayed and has sprayed the glaze slip in the adobe of overglaze, fired into kiln, kiln discharge, detection glossiness, anti-fouling effect and feel.
Application Example two
Using the unglazed protection glaze modelled after an antique as described in embodiment two, suitable quantity of water is added and ball milling obtains glaze slip,
It has sprayed and has sprayed the glaze slip in the adobe of overglaze, fired into kiln, kiln discharge, detection glossiness, anti-fouling effect and feel.
Application Example three
Using the unglazed protection glaze modelled after an antique as described in embodiment three, suitable quantity of water is added and ball milling obtains glaze slip,
It has sprayed and has sprayed the glaze slip in the adobe of overglaze, fired into kiln, kiln discharge, detection glossiness, anti-fouling effect and feel.
Testing result
Table one
| Project | Application Example one | Application Example two | Application Example three |
| Glossiness | 0.5 | 1 | 0.5 |
| Anti-fouling effect | It is excellent | It is excellent | It is excellent |
| Feel | It is soft | It is soft | It is soft |
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims
Variation is included within the present invention.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (4)
1. a kind of unglazed protection glaze modelled after an antique, which is characterized in that the raw material including following parts by weight: 20-40 parts of potassium feldspar, albite
10-20 parts, zinc oxide 1-5,5-15 parts of calcination of talc, 10-20 parts of barium carbonate, 5-15 parts of calcined kaolin, kaolin 10-20
Part, 1-5 parts of quartz, 10-20 parts of frit powder.
2. the unglazed protection glaze modelled after an antique of one kind according to claim 1, which is characterized in that the raw material including following parts by weight:
25-35 parts of potassium feldspar, 10-15 parts of albite, zinc oxide 2-5,8-12 parts of calcination of talc, 12-18 parts of barium carbonate, calcined kaolin
5-12 parts, 12-19 parts of kaolin, 2-4 parts of quartz, 10-18 parts of frit powder.
3. the unglazed protection glaze modelled after an antique of one kind according to claim 1, which is characterized in that the raw material including following parts by weight:
30 parts of potassium feldspar, 12 parts of albite, 3 parts of zinc oxide, 10 parts of calcination of talc, 18 parts of barium carbonate, 10 parts of calcined kaolin, kaolin
15 parts, 3 parts, 12 parts of frit powder of quartz.
4. a kind of processing method applied to the unglazed protection glaze modelled after an antique of the described in any item one kind of claims 1 to 3, feature exist
In, comprising the following steps:
Step 1, stock obtain the constituent and its parts by weight of any one of claims 1 to 3 unglazed protection glaze modelled after an antique；
Raw material in step 1 is grouped by step 2, filling, and wherein potassium feldspar and albite are first group, and kaolin is
Second group, zinc oxide, calcination of talc, barium carbonate and frit powder are third group, and calcined kaolin and quartz are the 4th group, every kind of original
Material with etc. parts by weight successively put into the above raw material into batch mixer according to order of packets, after completing successively above-mentioned raw materials investment, weight
Surplus stock substep is added in batch mixer by multiple above-mentioned steps；
Step 3, mixing, starting mixing work, continuous mixing 40-50 minutes；
Step 4 is examined, is detected to the raw material after mixing；
Step 5, packing processes carry out discharging packaging to qualified products.