CN109053227A - Ceramic solid crack glaze and preparation method thereof - Google Patents
Ceramic solid crack glaze and preparation method thereof Download PDFInfo
- Publication number
- CN109053227A CN109053227A CN201811040501.7A CN201811040501A CN109053227A CN 109053227 A CN109053227 A CN 109053227A CN 201811040501 A CN201811040501 A CN 201811040501A CN 109053227 A CN109053227 A CN 109053227A
- Authority
- CN
- China
- Prior art keywords
- component
- coat enamel
- parts
- ground coat
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses three-dimensional crack glaze of a kind of ceramics and preparation method thereof, ceramics solid crack glaze contains ground coat enamel and overglaze；Wherein, the component and each component mass parts that ground coat enamel contains are as follows: 20 parts of dispersions of polyurethanes；78 parts of emulsion acrylic resin, 0.5 part of dispersing agent；0.6 part of wetting agent, 0.3 part of defoaming agent；0.6 part of thickener；The component and each component mass parts that overglaze contains are as follows: 80 parts of water-based acrylic resin；15 parts of green toner；5 parts of white titanium dioxide.Crackle of the present invention is changeful, in picturesque disorder, has art stereo aesthetic feeling, is particularly suitable for ceramic simulated decorative modelled after an antique, is suitable for low-firing.
Description
Technical field
The present invention relates to three-dimensional crack glazes of a kind of ceramics and preparation method thereof.
Background technique
Currently, the moulding of porcelain billet is the basis of quality product in porcelain industry, the allotment of glaze keeps porcelain more gorgeous
Colorful, the porcelain billet of same moulding often because of the difference of glaze paint, and generates different influences to the vision of consumer, the prior art
Ceramic crack glaze need 1200 degree of high temperature firing or more, used cost of material and firing gas cost are all very high.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies of existing technologies, a kind of three-dimensional crack glaze of ceramics is provided,
Its crackle is changeful, in picturesque disorder, has art stereo aesthetic feeling, is particularly suitable for ceramic simulated decorative modelled after an antique, is suitable for low
Temperature is fired.
In order to solve the above technical problems, the technical scheme is that a kind of three-dimensional crack glaze of ceramics, it contains ground coat enamel
And overglaze；Wherein,
The component and each component mass parts that ground coat enamel contains are as follows:
20 parts of dispersions of polyurethanes；78 parts of emulsion acrylic resin, 0.5 part of dispersing agent；0.6 part of defoaming agent 0.3 of wetting agent
Part；0.6 part of thickener；
The component and each component mass parts that overglaze contains are as follows:
80 parts of water-based acrylic resin；
15 parts of green toner；
5 parts of white titanium dioxide.
The present invention also provides a kind of preparation method of three-dimensional crack glaze of ceramics, the step of method contains, is as follows:
S1: ground coat enamel material is prepared according to the component and each component mass parts of ground coat enamel, according to the component and each component quality of overglaze
Part prepares glaze material；
S2: cleaning ceramic surface；
S3: ground coat enamel material is sprayed on ceramic surface；
S4: by ceramic first drying；
S5: the ceramic surface after first drying sprays a glaze material again；
S6: ceramics are dried again, obtain finished product.
Further, in step sl, the preparation step of ground coat enamel material is as follows:
D1: it stocks up according to each component and each component mass parts of ground coat enamel；
D2: ground coat enamel each component is added in dispersion tank and is uniformly dispersed, ground coat enamel material is obtained.
Further, in step sl, the preparation step of glaze material is as follows:
M1: it stocks up according to each component and each component mass parts of overglaze；
M2: overglaze each component is added in dispersion tank and is uniformly dispersed, glaze material is obtained.
Further, in step s3, the glaze film thickness of ground coat enamel material is controlled at 11~19 μm.
Further, in step s 4, the condition of first drying are as follows: temperature is 100 DEG C~120 DEG C, and the time is 10~20 points
Clock.
Further, in step s 5, the glaze film thickness of glaze material is controlled at 15 μm.
Further, in step s 6, the condition dried again are as follows: 160 DEG C~180 DEG C of temperature, the time is 25 minutes~35
Minute.
After above-mentioned technical proposal, the three-dimensional crack glaze crackle of ceramics of the invention is changeful, in picturesque disorder, has
Art stereo aesthetic feeling is particularly suitable for ceramic simulated decorative modelled after an antique, is suitable for low-firing.
Specific embodiment
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, to the present invention make into
One step detailed description.
Embodiment one
A kind of three-dimensional crack glaze of ceramics, it contains ground coat enamel and overglaze；Wherein,
The component and each component mass parts that ground coat enamel contains are as follows:
20 parts of dispersions of polyurethanes；78 parts of emulsion acrylic resin, 0.5 part of dispersing agent；0.6 part of defoaming agent 0.3 of wetting agent
Part；0.6 part of thickener；
The component and each component mass parts that overglaze contains are as follows:
80 parts of water-based acrylic resin；
15 parts of green toner；
5 parts of white titanium dioxide.
The step of preparation method of ceramics solid crack glaze, method contains, is as follows:
S1: ground coat enamel material is prepared according to the component and each component mass parts of ground coat enamel, according to the component and each component quality of overglaze
Part prepares glaze material；
S2: cleaning ceramic surface；
S3: ground coat enamel material is sprayed on ceramic surface；
S4: by ceramic first drying；
S5: the ceramic surface after first drying sprays a glaze material again；
S6: ceramics are dried again, obtain finished product.
In step sl, the preparation step of ground coat enamel material is as follows:
D1: it stocks up according to each component and each component mass parts of ground coat enamel；
D2: ground coat enamel each component is added in dispersion tank and is uniformly dispersed, ground coat enamel material is obtained.
In step sl, the preparation step of glaze material is as follows:
M1: it stocks up according to each component and each component mass parts of overglaze；
M2: overglaze each component is added in dispersion tank and is uniformly dispersed, glaze material is obtained.
In step s3, the glaze film thickness of ground coat enamel material is controlled at 11 μm.
In step s 4, the condition of first drying are as follows: temperature is 100 DEG C, and the time is 10 minutes.
In step s 5, the glaze film thickness of glaze material is controlled at 15 μm.
In step s 6, the condition dried again are as follows: 160 DEG C of temperature, the time is 25 minutes.
Embodiment two
The component and each component mass parts contained in overglaze used in the three-dimensional crack glaze of the ceramics of the present embodiment and ground coat enamel
Identical with embodiment one, preparation method is also essentially identical, unlike:
In step s3, the glaze film thickness of ground coat enamel material is controlled at 19 μm.
In step s 4, the condition of first drying are as follows: temperature is 120 DEG C, and the time is 20 minutes.
In step s 6, the condition dried again are as follows: 180 DEG C of temperature, the time is 35 minutes.
Embodiment three
The component and each component mass parts contained in overglaze used in the three-dimensional crack glaze of the ceramics of the present embodiment and ground coat enamel
Identical with embodiment one, preparation method is also essentially identical, unlike:
In step s3, the glaze film thickness of ground coat enamel material is controlled at 15 μm.
In step s 4, the condition of first drying are as follows: temperature is 110 DEG C, and the time is 15 minutes.
In step s 5, the glaze film thickness of glaze material is controlled at 15 μm.
In step s 6, the condition dried again are as follows: 170 DEG C of temperature, the time is 30 minutes.
For the three-dimensional crack glaze of the ceramics that three above embodiment is prepared by observation discovery, glaze paint crackle is changeful,
It is in picturesque disorder, and pass through easy fired, high temperature firing is not needed, design requirement is met.
Particular embodiments described above has carried out further in detail the purpose of the present invention, technical scheme and beneficial effects
It describes in detail bright, it should be understood that the above is only a specific embodiment of the present invention, is not intended to restrict the invention, it is all
Within the spirit and principles in the present invention, any modification, equivalent substitution, improvement and etc. done should be included in guarantor of the invention
Within the scope of shield.
Claims (8)
1. a kind of three-dimensional crack glaze of ceramics, it is characterised in that it contains ground coat enamel and overglaze；Wherein,
The component and each component mass parts that ground coat enamel contains are as follows:
20 parts of dispersions of polyurethanes；78 parts of emulsion acrylic resin, 0.5 part of dispersing agent；0.6 part of wetting agent, 0.3 part of defoaming agent；Increase
Thick dose 0.6 part；
The component and each component mass parts that overglaze contains are as follows:
80 parts of water-based acrylic resin；
15 parts of green toner；
5 parts of white titanium dioxide.
2. a kind of preparation method of the three-dimensional crack glaze of ceramics as described in claim 1, it is characterised in that the step of method contains
It is as follows:
S1: ground coat enamel material is prepared according to the component and each component mass parts of ground coat enamel, according to the component and each component mass parts system of overglaze
Standby glaze material；
S2: cleaning ceramic surface；
S3: ground coat enamel material is sprayed on ceramic surface；
S4: by ceramic first drying；
S5: the ceramic surface after first drying sprays a glaze material again；
S6: ceramics are dried again, obtain finished product.
3. preparation method according to claim 2, it is characterised in that: in step sl, the preparation step of ground coat enamel material is as follows:
D1: it stocks up according to each component and each component mass parts of ground coat enamel；
D2: ground coat enamel each component is added in dispersion tank and is uniformly dispersed, ground coat enamel material is obtained.
4. preparation method according to claim 2, it is characterised in that: in step sl, the preparation step of glaze material is as follows:
M1: it stocks up according to each component and each component mass parts of overglaze；
M2: overglaze each component is added in dispersion tank and is uniformly dispersed, glaze material is obtained.
5. preparation method according to claim 2, it is characterised in that: in step s3, the glaze film thickness of ground coat enamel material controls
At 11~19 μm.
6. preparation method according to claim 2, it is characterised in that: in step s 4, the condition of first drying are as follows: temperature
It is 100 DEG C~120 DEG C, the time is 10~20 minutes.
7. preparation method according to claim 2, it is characterised in that: in step s 5, the glaze film thickness of glaze material controls
At 15 μm.
8. preparation method according to claim 2, it is characterised in that: in step s 6, the condition dried again are as follows: temperature
160 DEG C~180 DEG C, the time is 25 minutes~35 minutes.