CN110204982A - A kind of mosquito-proof coating of environmental protection and preparation method thereof - Google Patents
A kind of mosquito-proof coating of environmental protection and preparation method thereof Download PDFInfo
- Publication number
- CN110204982A CN110204982A CN201910510888.6A CN201910510888A CN110204982A CN 110204982 A CN110204982 A CN 110204982A CN 201910510888 A CN201910510888 A CN 201910510888A CN 110204982 A CN110204982 A CN 110204982A
- Authority
- CN
- China
- Prior art keywords
- mosquito
- environmental protection
- proof coating
- parts
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to mosquito-proof paint fields, more particularly to a kind of mosquito-proof coating of environmental protection, the mosquito-proof coating of environmental protection includes following components in parts by weight: 20-30 parts of water, 0.1-1 parts of dispersing agent, 0.1-1 parts of defoaming agent, 1-20 parts of titanium dioxide, 1-20 parts of calcium carbonate, 0.1-1 parts of coalescing agent, 0.1-1 parts of antifreeze, 0.1-1 parts of Ph buffer, thickener 0.1-1,20-40 parts of biology base acrylic emulsion, 1-10 parts of culicifuge.The mosquito-proof coating of environmental protection of the invention has environmental protection characteristic, is free of anaphylactogen, and mosquito repelling rate is high, fills up the domestic blank for lacking mosquito-proof coating.
Description
Technical field
The present invention relates to mosquito-proof paint fields, and in particular to a kind of mosquito-proof coating of environmental protection and preparation method thereof.
Background technique
Mosquito is a kind of fine winged insect with sucking mouth parts.Usually the text of female is using blood as food.It sucks blood
Female mosquito be the other pathogens such as dengue fever, malaria, yellow fever, filariasis, encephalitis B intermediate host.
The method of expelling mosquito mainly has mosquito-repellent incense, Mosquito killer lamp etc. at present.Contain up to 4 kinds of objects being harmful to the human body in mosquito-repellent incense
Matter, while other than these types of substance, also contain a large amount of organic filler, adhesive, fuel and other additives, can just make mosquito
Perfume (or spice) can be smouldered with nonflame.These substances contained in mosquito-repellent incense are not only harmful to human body, and polluted environment.Although Mosquito killer lamp is more
Environmental protection, but limitation is also more, needs again to use in dark, static environment.In the more hot summer of mosquito, nearly all
Can open fan or empty day, caused by air-flow variation will affect the trap effect of Mosquito killer lamp, while Mosquito killer lamp carries out continuing work
Energy consumption when making is also higher.Not yet there is the mosquito-proof coating with repelling effect in country's coating industry at present, exists in the field
Certain blank.
Summary of the invention
It is an object of that present invention to provide a kind of mosquito-proof coating of environmental protection, which has repelling effect, has filled up the field
Blank.
The technical scheme is that a kind of mosquito-proof coating of environmental protection, the mosquito-proof coating of environmental protection include in parts by weight with
Lower component:
Preferably, the dispersing agent is the dispersing agent of Dow Chemical's production, the model of the dispersing agent product are as follows:
731A。
Preferably, the defoaming agent is mineral oil defoaming agent.
Preferably, the coalescing agent is 12 coalescing agent of alcohol ester.12 coalescing agent of alcohol ester, chemistry entitled 2,2,
4- trimethyl -1,3- pentanediol mono isobutyrate, is colourless transparent liquid.
Preferably, the thickener is polyacrylate-type thickeners.
Preferably, the biology base acrylic emulsion is the lotion of Dow Chemical's production, the product type of the lotion
Number are as follows: RN1000V.
Preferably, the culicifuge is Permethrin.Permethrin is selected to have no stimulation of the skin as culicifuge.
The present invention also provides a kind of preparation method of mosquito-proof coating of environmental protection, the preparation method the following steps are included:
(1) it weighs: weighing water by the parts by weight, dispersing agent, defoaming agent, titanium dioxide, calcium carbonate, coalescing agent, resists
Freeze agent, Ph buffer, thickener, biological base emulsion, culicifuge；
(2) water, dispersing agent, defoaming agent of weighing are added into vessel, is mixed, mixing speed 400-
600rmp, when stirring, are 5 minutes a length of, obtain mixture A；
(3) continue the mixture A into the vessel and the thickener weighed, Ph buffer is added, titanium dioxide, carbon is then added
Sour calcium, is mixed, mixing speed 1100-1300rmp, and stirring duration is about 30 minutes, and temperature maintains less than 50 degree,
Until the mixture fineness in the vessel obtains mixture B less than 50 millimeters；
(4) continue the mixture B into the vessel and the coalescing agent weighed, antifreeze is added, be mixed, stirred
Speed is 700-900rmp, and when stirring is 5 minutes a length of, obtains mixture C；
(5) continue the mixture C into the vessel and the biological base emulsion weighed, culicifuge is added, be mixed, stirred
Mixing speed is 120-140rmp, and when stirring is 15 minutes a length of, obtains the mosquito-proof coating of environmental protection.
Compared with prior art, the present invention have it is following the utility model has the advantages that
1, the mosquito-proof coating of environmental protection of the invention has environmental protection characteristic, and formula material is free of formaldehyde, volatile organic matter, warp
Test can reach the standard of advanced U.S.'s green guardian gold medal certification；
2, the biology base acrylic emulsion that the present invention uses makes the anti-line coating of environmental protection have the low release of coating, anti-formaldehyde
Function, have higher Bio-based content, meet the requirement of high-performance coating, the effect of mosquito repellent is played in combination together with culicifuge
Fruit, the two are mutually mixed, and biology base acrylic emulsion plays the role of firm culicifuge, and mosquito repellent time is lasting, through testing to mosquito
The scattering ratio of worm is up to 95% or more；
3, the mosquito-proof coating of environmental protection of the invention is not added with the anaphylactogens such as anti-corrosion, mould proof, reduce people by skin contact or
Person's respiratory tract sucks so as to cause anaphylactoid probability.
Specific embodiment
The invention will be further described in conjunction with the embodiments.
Embodiment 1:
The present invention also provides a kind of preparation method of mosquito-proof coating of environmental protection, the preparation method the following steps are included:
(1) it weighs: weighing 20 parts of water, 0.1 part of dispersing agent, 0.1 part of defoaming agent, 1 part of titanium dioxide, calcium carbonate in parts by weight
1 part, 0.1 part of coalescing agent, 0.1 part of antifreeze, 0.1 part of Ph buffer, 0.1 part of thickener, biological 20 parts of base emulsion, culicifuge
1 part；
Wherein, dispersing agent is the dispersing agent 731A of Dow Chemical's production；Defoaming agent is mineral oil defoaming agent；Film forming
Auxiliary agent is 12 coalescing agent of alcohol ester；Thickener is polyacrylate-type thickeners；Biology base acrylic emulsion is DOW Chemical
The lotion of company's production, the product type of the lotion are as follows: RN1000V；Culicifuge is Permethrin, and the above raw material are buying
It obtains.
(2) water, dispersing agent, defoaming agent of weighing are added into vessel, is mixed, mixing speed 500rmp,
A length of 5 minutes when stirring, mixture A is obtained；
(3) continue the mixture A into the vessel and the thickener weighed, Ph buffer is added, titanium dioxide, carbon is then added
Sour calcium, is mixed, mixing speed 1200rmp, and stirring duration is about 30 minutes, and temperature maintains 45 degree, until the device
Mixture fineness in ware obtains mixture B less than 50 millimeters；
(4) continue the mixture B into the vessel and the coalescing agent weighed, antifreeze is added, be mixed, stirred
Speed is 800rmp, and when stirring is 5 minutes a length of, obtains mixture C；
(5) continue the mixture C into the vessel and the biological base emulsion weighed, culicifuge is added, be mixed, stirred
Mixing speed is 130rmp, and when stirring is 15 minutes a length of, obtains the mosquito-proof coating of environmental protection.
Embodiment 2:
The present embodiment 2 the difference from embodiment 1 is that: step (1) weigh: in parts by weight weighing 25 parts of water, dispersing agent
0.5 part, 0.5 part of defoaming agent, 10 parts of titanium dioxide, 10 parts of calcium carbonate, 0.5 part of coalescing agent, 0.5 part of antifreeze, Ph buffer 0.5
Part, 0.5 part of thickener, biological 30 parts of base emulsion, 5 parts of culicifuge.Remaining step is same as Example 1.
Embodiment 3:
The present embodiment 3 the difference from embodiment 1 is that: step (1) weigh: in parts by weight weighing 30 parts of water, dispersing agent 1
Part, 1 part of defoaming agent, 20 parts of titanium dioxide, 20 parts of calcium carbonate, 1 part of coalescing agent, 1 part of antifreeze, 1 part of Ph buffer, thickener 1
Part, biological 40 parts of base emulsion, 10 parts of culicifuge.Remaining step is same as Example 1.
Using embodiment 2 as test case, following test is carried out: one piece of blank template, one piece of painting are put into enclosed environment
There is the template of the mosquito-proof coating of the environmental protection of the embodiment of the present invention 2, is put into 107 mosquitoes, after 5 minutes, records and stopped on two pieces of templates
The quantity of mosquito subtracts mosquito-proof coating template number using the number of blank sample, and obtained result obtains mosquito repellent divided by blank template number
Rate is 96%, illustrates that the present invention has good repelling effect.
Finally it should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention, rather than the present invention is protected
Protect range limitation, those skilled in the art should understand that, can modify to technical solution of the present invention or
Equivalent replacement, without departing from the spirit and scope of technical solution of the present invention.
Claims (8)
1. a kind of mosquito-proof coating of environmental protection, which is characterized in that the mosquito-proof coating of environmental protection includes following components in parts by weight:
2. the mosquito-proof coating of environmental protection as described in claim 1, it is characterised in that:
The dispersing agent is the dispersing agent of Dow Chemical's production, the product type of the dispersing agent are as follows: 731A.
3. the mosquito-proof coating of environmental protection as described in claim 1, it is characterised in that:
The defoaming agent is mineral oil defoaming agent.
4. the mosquito-proof coating of environmental protection as described in claim 1, it is characterised in that:
The coalescing agent is 12 coalescing agent of alcohol ester.
5. the mosquito-proof coating of environmental protection as described in claim 1, it is characterised in that:
The thickener is polyacrylate-type thickeners.
6. the mosquito-proof coating of environmental protection as described in claim 1, it is characterised in that:
The biology base acrylic emulsion is the lotion of Dow Chemical's production, the product type of the lotion are as follows:
RN1000V。
7. the mosquito-proof coating of environmental protection as described in claim 1, it is characterised in that:
The culicifuge is Permethrin.
8. a kind of preparation method of such as described in any item mosquito-proof coating of environmental protection of claim 1-7, which is characterized in that including following
Step:
(1) weigh: by the parts by weight weigh water, dispersing agent, defoaming agent, titanium dioxide, calcium carbonate, coalescing agent, antifreeze,
Ph buffer, thickener, biological base emulsion, culicifuge；
(2) water, dispersing agent, defoaming agent of weighing are added into vessel, is mixed, mixing speed 400-600rmp,
A length of 5 minutes when stirring, mixture A is obtained；
(3) continue the mixture A into the vessel and the thickener weighed, Ph buffer is added, titanium dioxide, carbonic acid is then added
Calcium is mixed, mixing speed 1100-1300rmp, and stirring duration is about 30 minutes, and temperature maintains less than 50 degree, directly
Mixture fineness in the vessel obtains mixture B less than 50 millimeters；
(4) continue the mixture B into the vessel and the coalescing agent weighed, antifreeze is added, be mixed, mixing speed
For 700-900rmp, when stirring, is 5 minutes a length of, obtains mixture C；
(5) continue the mixture C into the vessel and the biological base emulsion weighed, culicifuge is added, be mixed, stirring speed
Degree is 120-140rmp, and when stirring is 15 minutes a length of, obtains the mosquito-proof coating of environmental protection.