CN110125341A - 一种随流孕育剂及其使用方法 - Google Patents

一种随流孕育剂及其使用方法 Download PDF

Info

Publication number
CN110125341A
CN110125341A CN201910498330.0A CN201910498330A CN110125341A CN 110125341 A CN110125341 A CN 110125341A CN 201910498330 A CN201910498330 A CN 201910498330A CN 110125341 A CN110125341 A CN 110125341A
Authority
CN
China
Prior art keywords
random inoculant
iron liquid
nodularization
iron
inoculant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910498330.0A
Other languages
English (en)
Inventor
吉万晟
许雨生
冷勇锋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Yulong Mold & Casting Co Ltd
Original Assignee
Anhui Yulong Mold & Casting Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Yulong Mold & Casting Co Ltd filed Critical Anhui Yulong Mold & Casting Co Ltd
Priority to CN201910498330.0A priority Critical patent/CN110125341A/zh
Publication of CN110125341A publication Critical patent/CN110125341A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种随流孕育剂及其使用方法，所述随流孕育剂的成份质量百分比为：Be4‑6％，Mg0.8‑1.5％，Re1‑1.5％,Si65‑70％,Ca1‑1.5％,Al1‑1.5％，余量为Fe，合计100％。所述随流孕育剂的使用方法为在铁液熔清完成后浇注时向铁液中加入铁液重量1.5％的所述随流孕育剂进行随流孕育处理。本发明在随流孕育剂中增加适量的具有球化作用的元素镁及稀有元素铼，同时具有瞬时球化和瞬时孕育作用，对铁液进行二次球化及孕育，补充一次球化中的球化衰退，通过二次球化孕育进一步提高球化率及石墨球数量，提升球铁件综合性能；同时通过控制镁及铼含量，避免加入过量导致二次球化爆发剧烈产生铁水紊流及大量的二次氧化渣缺陷，避免加入过少失去二次球化作用难以补偿球化衰退现象。

Description

一种随流孕育剂及其使用方法
技术领域
本发明涉及铸造技术领域，具体涉及一种随流孕育剂及其使用方法。
背景技术
随着行业技术进步，球化及孕育技术越来越先进，随流瞬时孕育技术在行业内得到大量的推广。但是生产球铁件时，球化孕育后的铁水因内含硫，暴露在空气中吸氧反应以及操作过程存在异常导致时间延长等不可避免的产生一定的球化衰退现象，会导致球铁件机械性能无法满足要求而报废。
本发明的目的在于研发一种在铁液最后浇注时加入的随流瞬时孕育剂，对铁液进行二次球化及孕育，补充一次球化中的球化衰退，通过二次球化孕育进一步提高球化率及石墨球数量，提升球铁件综合性能。
发明内容
为实现上述目的，本发明提供一种随流孕育剂及其使用方法。本发明所采用的技术方案为：
一种随流孕育剂，其成份质量百分比为：Be4-6％，Mg0.8-1.5％，Re1-1.5％,Si65-70％,Ca1-1.5％,Al1-1.5％，余量为Fe，合计100％。
进一步地，所述随流孕育剂的粒度为0.3-1mm。
所述随流孕育剂的使用方法为：在铁液熔清完成后浇注时向铁液中加入铁液重量1.5％的所述随流孕育剂进行随流孕育处理。
本发明的有益效果在于：本发明在随流孕育剂中增加适量的具有球化作用的元素镁及稀有元素铼，同时具有瞬时球化和瞬时孕育作用，对铁液进行二次球化及孕育，补充一次球化中的球化衰退，通过二次球化孕育进一步提高球化率及石墨球数量，提升球铁件综合性能。同时通过控制镁及铼含量，避免加入过量导致二次球化爆发剧烈产生铁水紊流及大量的二次氧化渣缺陷，避免加入过少失去二次球化作用难以补偿球化衰退现象。
具体实施方式
下面结合具体实施方式对本发明进行详细说明。
一种随流孕育剂，其成份质量百分比为：Be4-6％，Mg0.8-1.5％，Re1-1.5％,Si65-70％,Ca1-1.5％,Al1-1.5％，余量为Fe，合计100％。
所述随流孕育剂的粒度为0.3-1mm。
所述随流孕育剂的使用方法为：在铁液熔清完成后浇注时向铁液中加入铁液重量1.5％的所述随流孕育剂进行随流孕育处理。
实施例1：
一种随流孕育剂，其成份质量百分比为：Be5％，Mg1％，Re1％,Si67％,Ca1％,Al1％，余量为Fe；所述随流孕育剂的粒度为0.3-1mm；在铁液熔清完成后浇注时向铁液中加入铁液重量1.5％的所述随流孕育剂进行随流孕育处理，浇注后得球铁试块1。
实施例2：
一种随流孕育剂，其成份质量百分比为：Be5％，Mg1.5％，Re1.5％,Si67％,Ca1％,Al1％，余量为Fe；所述随流孕育剂的粒度为0.3-1mm；在铁液熔清完成后浇注时向铁液中加入铁液重量1.5％的所述随流孕育剂进行随流孕育处理，浇注后得球铁试块2。
上述实施例1、实施例2随流孕育处理后的球铁件试块进行金相组织检测，其结果如下：
从上述检测结果可知，通过实施1和实施例2对球铁铁液进行随流孕育处理时球化爆发较为平稳，制得的球铁试块的球化率大于95％，石墨球数量大于275，均处于高位水平，碳化物含量分别为无和极少，加工状态下无缺陷，球铁试块金相组织和内在质量优良。
以上所述是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也视为本发明的保护范围。

Claims (4)

1.一种随流孕育剂，其特征在于，所述随流孕育剂的成份质量百分比为：Be4-6％，Mg0.8-1.5％，Re1-1.5％,Si65-70％,Ca1-1.5％,Al1-1.5％，余量为Fe，合计100％。
2.根据权利要求1所述的一种随流孕育剂，其特征在于，所述随流孕育剂的成份质量百分比为：Be4-6％，Mg1％，Re1％,Si65-70％,Ca1-1.5％,Al1-1.5％，余量为Fe，合计100％。
3.根据权利要求1所述的一种随流孕育剂，其特征在于，所述随流孕育剂的粒度为0.3-1mm。
4.根据权利要求1所述的一种随流孕育剂，其特征在于，所述随流孕育剂的使用方法为：在铁液熔清完成后浇注时向铁液中加入铁液重量1.5％的所述随流孕育剂进行随流孕育处理。
CN201910498330.0A 2019-06-10 2019-06-10 一种随流孕育剂及其使用方法 Pending CN110125341A (zh)