CN110124968A - The solid wooden compound floor painting technology that aqueous UV is painted entirely - Google Patents

The solid wooden compound floor painting technology that aqueous UV is painted entirely Download PDF

Info

Publication number
CN110124968A
CN110124968A CN201910491898.XA CN201910491898A CN110124968A CN 110124968 A CN110124968 A CN 110124968A CN 201910491898 A CN201910491898 A CN 201910491898A CN 110124968 A CN110124968 A CN 110124968A
Authority
CN
China
Prior art keywords
aqueous
paint
infra
ultraviolet light
red drying
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910491898.XA
Other languages
Chinese (zh)
Inventor
郭祎鹏
钟伟
夏朝彦
龙玲
陈明贵
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
POWER DEKOR GROUP CO Ltd
GUANGZHOU HOMEBON TIMBER CO Ltd
Original Assignee
POWER DEKOR GROUP CO Ltd
GUANGZHOU HOMEBON TIMBER CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by POWER DEKOR GROUP CO Ltd, GUANGZHOU HOMEBON TIMBER CO Ltd filed Critical POWER DEKOR GROUP CO Ltd
Priority to CN201910491898.XA priority Critical patent/CN110124968A/en
Publication of CN110124968A publication Critical patent/CN110124968A/en
Pending legal-status Critical Current

Abstract

The invention belongs to building decoration technology fields, and be related to the solid wooden compound floor painting technology that aqueous UV is painted entirely: plain plate surface covers with paint, lacquer, colour wash, etc. the aqueous UV putty → infra-red drying of the aqueous UV putty → infra-red drying+ultraviolet light solidification → second of aqueous UV adhesive agent → infra-red drying → first+ultraviolet light and solidifies → first aqueous UV wear-resistant primer → infra-red drying+→ first aqueous aqueous UV sanding priming paint → infra-red drying of UV sanding priming paint → infra-red drying+ultraviolet light solidification → second of ultraviolet light solidification+→ first aqueous aqueous UV finishing coat → infra-red drying of UV finishing coat → infra-red drying+ultraviolet light solidification → second of ultraviolet light solidification+ultraviolet light solidification after cleaning out.The present invention solves the problems, such as current water-based paint covering with paint, and processing efficiency is low, ropy, and physicochemical property is much better than other water-based paint timber floors, and production efficiency is also apparently higher than traditional water-based paint timber floor.Obtained complete aqueous UV paint solid wooden compound floor surface effect is good, can more embody the texture of timber itself.

Description

The solid wooden compound floor painting technology that aqueous UV is painted entirely
Technical field
The invention belongs to building decoration technology field, production more particularly to a kind of solid wood for being related to solid wooden compound floor are multiple Close the floor painting technology that aqueous UV is painted entirely.
Background technique
In recent years, multi-layer solid wood composite floor with its good stability, enrich full surface style, health environment-friendly Characteristic, excellent physicochemical property, gradually by the favor of consumer.However how in the production process of floor to improve the feature of environmental protection Can, become an important research topic in current industry.Other than floor base material selection meets the material of environmental protection standard, also It needs to carry out green processing to solid wooden floor board top finishing technique.
Carrying out covering with paint processing in wood floor surface in industry at present mainly has: covering with paint, lacquer, colour wash, etc. vegetable oil and carries out natural drying or mechanical Simulation spontaneously dries, covering with paint UV paint (ultraviolet-cured paint) carries out ultraviolet light solidification and a small amount of PU is painted and covered with paint, lacquer, colour wash, etc..It wherein takes most More is painted using UV, and painting technology is usually 1~2 aqueous UV paint and 3~10 paint UV Qi Bingyong.
Summary of the invention
In view of the above-mentioned deficiencies in the prior art, entirely aqueous the purpose of the present invention is disclosing a kind of solid wooden compound floor The painting technology of UV paint.
Technical solution:
In all aqueous UV paints of coating that wood floor surface is covered with paint, lacquer, colour wash, etc., painted without using oiliness UV.
A kind of solid wooden compound floor painting technology that aqueous UV is painted entirely, includes the following steps:
Plain plate surface covers with paint, lacquer, colour wash, etc. aqueous UV adhesive agent (10~30g/m after cleaning out2) → infra-red drying → first is aqueous UV putty (15~50g/m2) → infra-red drying+aqueous UV putty (10~the 40g/m of ultraviolet light solidification → second2) → infrared is dry Dry+ultraviolet light solidifies → first aqueous UV wear-resistant primer (10~40g/m2) → infra-red drying+ultraviolet light solidification → first Aqueous UV sanding priming paint (10~40g/m2) → infra-red drying+aqueous UV sanding the priming paint of ultraviolet light solidification → second (10~ 40g/m2) → infra-red drying+ultraviolet light solidifies → first aqueous UV finishing coat (5~20g/m2) → infra-red drying+ultraviolet light solidification The aqueous UV finishing coat (5~20g/m of → second2) → infra-red drying+ultraviolet light solidification.
Wherein, according to different product performance demands, part painting and sequence can be replaced.
In the more excellent disclosed example of the present invention, the aqueous UV adhesive agent covering with paint amount 20g/m2。
In the more excellent disclosed example of the present invention, first of aqueous UV putty covering with paint amount 30g/m2。
In the more excellent disclosed example of the present invention, the aqueous UV putty covering with paint amount 25g/m of second2。
In the more excellent disclosed example of the present invention, first of aqueous UV wear-resistant primer covering with paint amount 25g/m2。
In the more excellent disclosed example of the present invention, first of aqueous UV sanding priming paint covering with paint amount 25g/m2。
In the more excellent disclosed example of the present invention, the aqueous UV sanding priming paint covering with paint amount 25g/m of second2。
In the more excellent disclosed example of the present invention, first of aqueous UV finishing coat covering with paint amount 12g/m2。
In the more excellent disclosed example of the present invention, the aqueous UV finishing coat covering with paint amount 12g/m of second2。
In the more excellent disclosed example of the present invention, first of the aqueous UV sanding priming paint, the aqueous UV sanding priming paint of second can change With aqueous UV dumb light priming paint, aqueous UV high filling primer or aqueous UV wear-resistant primer.
In the more excellent disclosed example of the present invention, first of the aqueous UV putty or the aqueous UV putty of second are covered with paint, lacquer, colour wash, etc. process and can be saved Slightly.
The present invention covers with paint, lacquer, colour wash, etc. aqueous UV adhesive agent in plain plate cleaning rear surface, using it to wood surface specifically stronger infiltration With adhesive ability, in addition with the similar compatibility of the materials such as the aqueous putty that is coated with above so that aqueous UV paint is in solid wood The Spraying technique of floor surface is good.
In painting technology of the present invention, institute is purchased from Jiangsu Himonia Technology Co., Ltd., specific product type using paint Number information is as follows: aqueous UV adhesive agent-FG109050M, aqueous UV putty-WUV208010, aqueous UV wear-resistant primer- WUV318030, aqueous UV sanding priming paint-WUV128030, aqueous UV dumb light priming paint-WUV128005, aqueous UV high fill bottom Paint-WUV138010, aqueous UV finishing coat --- WUV228005, WUV228020.
Major product matches when function:
(1) aqueous UV adhesive agent
Ingredient Percentage Remarks
Aqueous UV resin 85~95 Film forming matter
Photoinitiator 1.0~2 Solidify function
Auxiliary agent 5~15 Defoaming, wetting, enhancing adhesive force and tinctorial property etc.
Water In right amount Adjust working viscosity
(2) aqueous putty
Ingredient Percentage Remarks
Aqueous UV resin 70~80 Film forming matter
Photoinitiator 1.0~2 Solidify function
Auxiliary agent 0.5~3 The functions such as defoaming, wetting, anti-settling, thixotroping
Filler 10~20 Polishing, filling, mechanical performance
Water In right amount Adjust working viscosity
(3) aqueous UV priming paint
Ingredient Percentage Remarks
Aqueous UV resin 50~70 Film forming matter
Watery film-fomer 5~10 It adjusts viscosity, improve performance
Photoinitiator 1.0~3 Solidify function
Auxiliary agent 0.5~3 The functions such as defoaming, wetting, dispersion, anti-settling
Filler, functional powder 5~10 Polishing, delustring, mechanical performance
Water In right amount Adjust working viscosity
(4) aqueous UV wear-resistant primer
Ingredient Percentage Remarks
Aqueous UV resin 55~65 Film forming matter
Watery film-fomer 10~15 It adjusts viscosity, improve performance
Photoinitiator 1.0~2 Solidify function
Auxiliary agent 0.5~2 The functions such as defoaming, wetting, anti-settling
Wear resistant filler 15~20 Wear-resisting property
Water In right amount Adjust working viscosity
(5) aqueous UV finishing coat
Ingredient Percentage Remarks
Aqueous UV resin 40~80 Film forming matter
Watery film-fomer 5~10 It adjusts viscosity, improve performance
Photoinitiator 1.5~3 Solidify function
Auxiliary agent 0.5~2 The functions such as defoaming, wetting, anti-settling
Filler 1~5 Mechanical performance
Special powder material 1~8 Delustring, mechanical performance
Water In right amount Adjust working viscosity
Beneficial effect
The present invention complete aqueous UV paint solid wooden compound floor produced solve current water-based paint cover with paint, lacquer, colour wash, etc. processing efficiency is low, Ropy problem, physicochemical property are much better than other water-based paint timber floors.Production efficiency is also apparently higher than the aqueous oil of tradition Paint timber floor.The more traditional UV of complete aqueous UV paint solid wooden compound floor disclosed by the invention paints the surface effect of timber floor more preferably, more The grain effect of timber itself can be embodied.
Specific embodiment
The following describes the present invention in detail with reference to examples, so that those skilled in the art more fully understand this hair It is bright, but the invention is not limited to following embodiments.
Unless otherwise defined, term (including scientific and technical terminology) used herein above should be construed as having as belonging to the present invention The identical meaning that those skilled in the art are commonly understood by.It will also be understood that term used herein above should be explained To have the meaning consistent with their meanings in the content of this specification and the relevant technologies, and should not be with idealization Or excessive form is explained, unless expressly so limiting here.
Embodiment 1
(open)
After testing, it is as follows that paint film main performance is all satisfied national standard index to the product:
Detection project Standard requirements abstract Testing result
Paint film adhesion Score and score infall allow to have a small amount of discontinuously peeling It meets the requirements
Surface abrasion resistance ≤ 0.15g/100r, and paint film is not ground 0.0516
Paint film pencil hardness ≧H 2H
Embodiment 2
(closed)
After testing, it is as follows that paint film main performance is all satisfied national standard index to the product:
Detection project Standard requirements abstract Testing result
Paint film adhesion Score and score infall allow to have a small amount of discontinuously peeling It meets the requirements
Surface abrasion resistance ≤ 0.15g/100r, and paint film is not ground 0.0632
Paint film pencil hardness ≧H 3H
Embodiment 3
(closed hardening type)
After testing, it is as follows that paint film main performance is all satisfied national standard index to the product:
Detection project Standard requirements abstract Testing result
Paint film adhesion Score and score infall allow to have a small amount of discontinuously peeling It meets the requirements
Surface abrasion resistance ≤ 0.15g/100r, and paint film is not ground 0.0685
Paint film pencil hardness ≧H 5H
Upper described only the embodiment of the present invention, is not intended to limit the scope of the invention, all to utilize the present invention Equivalent structure or equivalent flow shift made by specification is applied directly or indirectly in other relevant technical fields, same Reason is included within the scope of the present invention.

Claims (10)

1. a kind of solid wooden compound floor painting technology that aqueous UV is painted entirely, which comprises the steps of:
Plain plate surface covers with paint, lacquer, colour wash, etc. 10~30g/m of aqueous UV adhesive agent after cleaning out2The aqueous UV putty 15 of → infra-red drying → first ~50g/m2→ infra-red drying+ultraviolet light solidification → 10~40g/m of the aqueous UV putty of second2→ infra-red drying+ultraviolet light solidification → first 10~40g/m of aqueous UV wear-resistant primer2→ infra-red drying+ultraviolet light solidifies → first aqueous UV sanding priming paint 10 ~40g/m2→ infra-red drying+ultraviolet light solidification → 10~40g/m of the aqueous UV sanding priming paint of second2→ infra-red drying+ultraviolet light Solidify → first 5~20g/m of aqueous UV finishing coat2→ infra-red drying+ultraviolet light solidification → 5~20g/ of the aqueous UV finishing coat of second m2→ infra-red drying+ultraviolet light solidification.
2. the solid wooden compound floor painting technology that aqueous UV is painted entirely according to claim 1, it is characterised in that: the aqueous UV Adhesive agent covering with paint amount 20g/m2。
3. the solid wooden compound floor painting technology that aqueous UV is painted entirely according to claim 1, it is characterised in that: described first Aqueous UV putty covering with paint amount 30g/m2。
4. the solid wooden compound floor painting technology that aqueous UV is painted entirely according to claim 1, it is characterised in that: the second Aqueous UV putty covering with paint amount 25g/m2。
5. the solid wooden compound floor painting technology that aqueous UV is painted entirely according to claim 1, it is characterised in that: described first Aqueous UV wear-resistant primer covering with paint amount 25g/m2。
6. the solid wooden compound floor painting technology that aqueous UV is painted entirely according to claim 1, it is characterised in that: described first Aqueous UV sanding priming paint covering with paint amount 25g/m2。
7. the solid wooden compound floor painting technology that aqueous UV is painted entirely according to claim 1, it is characterised in that: the second Aqueous UV sanding priming paint covering with paint amount 25g/m2。
8. the solid wooden compound floor painting technology that aqueous UV is painted entirely according to claim 1, it is characterised in that: described first Aqueous UV finishing coat covering with paint amount 12g/m2；The aqueous UV finishing coat covering with paint amount 12g/m of second2。
9. the solid wooden compound floor painting technology that aqueous UV is painted entirely according to claim 1, it is characterised in that: described first Aqueous UV sanding priming paint, the aqueous UV sanding priming paint of second can use aqueous UV dumb light priming paint, aqueous UV high filling primer or water instead Property UV wear-resistant primer.
10. the solid wooden compound floor painting technology that aqueous UV is painted entirely according to claim 1, it is characterised in that: described first The aqueous UV putty in road or the aqueous UV putty of second, which cover with paint, lacquer, colour wash, etc. process, to be omitted.
CN201910491898.XA 2019-06-06 2019-06-06 The solid wooden compound floor painting technology that aqueous UV is painted entirely Pending CN110124968A (en)