CN110080008A - It is a kind of can both-sided adhesive double-point lining cloth processing technology - Google Patents
It is a kind of can both-sided adhesive double-point lining cloth processing technology Download PDFInfo
- Publication number
- CN110080008A CN110080008A CN201910457250.0A CN201910457250A CN110080008A CN 110080008 A CN110080008 A CN 110080008A CN 201910457250 A CN201910457250 A CN 201910457250A CN 110080008 A CN110080008 A CN 110080008A
- Authority
- CN
- China
- Prior art keywords
- point
- coating
- base fabric
- lining cloth
- sided adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses it is a kind of can both-sided adhesive double-point lining cloth processing technology, overall flow includes: a, water repellent finish；B, single side coating；C, cured；D, cooling, winding；E, coated on both sides；F, cured again；G, cooling, winding again.The present invention is by improving the means such as technological parameter, step and product formula, the double-point lining cloth with both-sided adhesive function can be produced, the technical issues of at high cost, feel caused by the technique can solve the two-sided clothing of tradition due to using two layers of lining cloth and poor air permeability, and water-tolerant, will not degumming, be suitable for large-scale promotion application.
Description
Technical field
The present invention relates to a kind of processing technology, more particularly to it is a kind of can both-sided adhesive double-point lining cloth processing technology.
Background technique
Lining cloth is using woven fabric, knitted fabric and non-woven cloth as base fabric, using thermoplastic high molecular compound, by special
Machinery carry out Special Finishing processing, the internal layer for clothes play reinforcement, it is well-pressed the effects of, with fabric bonding spe-cial-purpose uniform
Auxiliary material, it plays skeleton function on clothes.Lining cloth can be divided into sizing point padding cloth cloth, powder spot lining cloth, two point according to the difference of coating process
Lining cloth, the glue that wherein sizing point padding cloth cloth uses is melt, the glue that powder spot lining cloth uses be it is solid, and double-point lining cloth using
Slurry point plus the coating way of dusting, i.e., first apply prime cement dusting again, form two kinds of different medium rubber powders, wherein prime cement plays protection resistance
Bonding effect is played in gear effect, dusting.Double-point lining cloth is compared with other two lining cloth, because with elasticity is good, plasticity is high, not will cause
The superior performances such as seep through and adhesive effect are good and obtain industry and unanimously affirm, quickly grow, it has also become the lining cloth of mainstream at present
Form processing.
With the development of the social economy, more and more people start to pursue practical multifunctional product.Some can
Positive and negative two clothings worn have obtained the widespread love of people because of the design of its uniquenessization and the characteristics of can reducing expenses.But it is existing can be double
The clothing that face is worn all needs to use using two layers of lining cloth substantially, and no matter two layers of lining cloth all can to the cost, feel, gas permeability of clothes
It has a negative impact.Therefore, if can develop it is a kind of it is novel can both-sided adhesive double-point lining cloth processing technology, to improving people
Usage experience will have very positive Practical significance.But both-sided adhesive technology is due to two-sided dispensing, that there are difficulty of processing is big,
Reverse side is easy the defect of degumming, this is also the difficult point place being still developed at present without such technique.
Summary of the invention
In order to solve shortcoming present in above-mentioned technology, the present invention provides it is a kind of can both-sided adhesive double-point lining cloth
Processing technology.
In order to solve the above technical problems, the technical solution adopted by the present invention is that: it is a kind of can both-sided adhesive double-point lining cloth
Processing technology, overall flow are as follows:
A, water repellent finish:
To water repellent finish before base fabric progress technique, make base fabric that there is the feel and water repellency of soft comfortable；
B, single side coating:
Coating machine is served as a contrast by two point first and carries out slurry point coating on one side in base fabric；Then it is spread on the basis of starching point
Powder coating, the point-type density of dusting coating are 180/cm2, the Circularhole diameter of powder point is 0.15mm；
C, cured:
The good base fabric of single side coating is sent into the drying unit that temperature setting is 170~260 DEG C, in 170~260 DEG C of temperature
It heats up, base fabric is carried out cured step by step in three times in degree range；Keep the speed of base fabric transmission in 30~40m/s, always admittedly
The change time is 20~30s；
D, cooling, winding:
Base fabric after solidification passes through water cooled rolls rolling after cooling；Room temperature overnight is placed, and keeps base fabric completely cooling；
E, coated on both sides:
Base fabric after single side coating is reversely unfolded, keeps coating face-down；Slurry point coating is carried out to the upper surface of base fabric again,
Coating amount when single side coating is less than the coating amount of this secondary coating；Then dusting coating is carried out on the basis of starching point, dusting applies
The point-type density of layer is 130/cm2, the Circularhole diameter of powder point is 0.2mm；
Coating is carried out to another side since the base fabric after single side coating will turn after step e, single side dusting applies
Point-type density when layer is greater than point-type density when coated on both sides, it is ensured that overall leveling of the product after turning
Property, it avoids applying and does not glue or gluing is irregular.
F, cured again:
The good base fabric of coated on both sides is sent into the drying unit that temperature setting is 150~205 DEG C, in 150~205 DEG C of temperature
It heats up, base fabric is carried out again cured step by step in three times in degree range；Keep the speed of base fabric transmission in 30~40m/s,
Total curing time is 20~30s；
G, cooling, winding again:
Base fabric after solidification is passed through into water cooled rolls rolling after cooling；It is placed at room temperature for completely cooling to base fabric.
Further, the material of base fabric is low elastic polyester filament.
Further, step b, in step e, the material starched a little is thermosetting acrylic resin complex liquid, the material of powder point
Matter is polyamide.
Further, thermosetting acrylic resin complex liquid is made of thermosetting acrylic resin, thickener, adhesive；
The mass fraction of thickener is 5%, and the mass fraction of adhesive is 1.5%.It is final that the addition of adhesive can improve product
Water-wash resistance makes it meet water-fastness 40~90 degree and dry-cleaning.
Further, adhesive is rosin resin；Thickener is acrylic thickener.
Further, single side coating uses the polyamide that melting temperature is high and melting means is low；Coated on both sides is using melting
Temperature is low and polyamide that melting means is high.When in view of coated on both sides, the one side of base fabric has been completed to be coated with, in order to avoid
When cured again, polyamide degumming due to high-temperature fusion of base fabric bottom, so that selects when the second secondary coating is poly-
Amide resin will have that the melting temperature of the polyamide than selecting when the first secondary coating is low and characteristic that melting means is high.Polyamide
The nylon of resin also known as nylon, above-mentioned characteristic can be debugged out according to different nylon product models.
Further, the melting temperature for the polyamide that single side coating uses is 120~140 DEG C；Coated on both sides uses
Polyamide melting temperature be 100~130 DEG C.Correspondingly, second of cured temperature will be lower than roasting for the first time
Solidification is dried, degumming due to high-temperature fusion of the polyamide of base fabric bottom is avoided.
Further, each coating amount of slurry point coating is every square metre of 2~3g.
Further, in step b single side coating, the coating amount of slurry point coating is every square metre of 2g；Step e coated on both sides
In, the coating amount of slurry point coating is every square metre of 3g.Coating amount when single side coating is less than the coating amount of coated on both sides, can keep away
It is blocked up and fall off to exempt from base fabric bottom surface glue-line, and thus the difference on bring structural strength and water resistance can pass through two sides
Point-type density and powder spot diameter make up, have the advantages that technique and parameter amount are arranged scientific and reasonable.
Further, step e, in f, g, when forwarding, bottom surface should be noted that be avoided serving as a contrast coating machine by two point base fabric
The parts depreciation of lower part and fall glue.
For the present invention by improving the means such as technological parameter, step and product formula, can produce has the function of both-sided adhesive
Double-point lining cloth, at high cost, feel and gas permeability caused by which can solve the two-sided clothing of tradition due to using two layers of lining cloth
Difference technical problem, and water-tolerant, will not degumming, be suitable for large-scale promotion application.
Specific embodiment
The present invention will be further described in detail with reference to the specific embodiments.
[embodiment one]
It is a kind of can both-sided adhesive double-point lining cloth processing technology, overall flow are as follows:
A, water repellent finish:
To water repellent finish before base fabric progress technique, make base fabric that there is the feel and water repellency of soft comfortable；The material of base fabric
Preferably low elastic polyester filament.
B, single side coating:
Coating machine is served as a contrast by two point first and carries out slurry point coating on one side in base fabric, coating amount is that every square metre of 2g starches point；
Then dusting coating is carried out on the basis of starching point, the point-type density of dusting coating is 180/cm2, the Circularhole diameter of powder point is
0.15mm；
C, cured:
The good base fabric of single side coating is sequentially sent in the drying unit that temperature setting is 170-195-260 DEG C, to base fabric
It carries out cured；Keep the speed of base fabric transmission in 30m/s, total curing time is 20s；
D, cooling, winding:
Base fabric after solidification passes through water cooled rolls rolling after cooling；Room temperature overnight is placed, and keeps base fabric completely cooling；
E, coated on both sides:
Base fabric after single side coating is reversely unfolded, keeps coating face-down；Slurry point coating is carried out to the upper surface of base fabric again,
Coating amount is 3g/m2Slurry point；Then dusting coating is carried out on the basis of starching point, the point-type density of dusting coating is 130/
cm2, the Circularhole diameter of powder point is 0.2mm；
In step b single side coating and step e coated on both sides, the material starched a little is thermosetting acrylic resin complex liquid.
Thermosetting acrylic resin complex liquid is made of thermosetting acrylic resin, thickener, adhesive；The mass fraction of thickener is
5%, the mass fraction of adhesive is 1.5%.Adhesive is rosin resin；Thickener is acrylic thickener.
The material of powder point is polyamide, but single side coating uses the polyamide resin that melting temperature is high and melting means is low
Rouge, melting temperature are 120~140 DEG C；And coated on both sides uses the polyamide that melting temperature is low and melting means is high, melting
Temperature is 100~130 DEG C.
F, cured again:
The good base fabric of coated on both sides is sequentially sent in the drying unit that temperature setting is 150-175-205 DEG C, it is right again
Base fabric carries out cured；Keep the speed of base fabric transmission in 30m/s, total curing time is 20s；
G, cooling, winding again:
Base fabric after solidification is passed through into water cooled rolls rolling after cooling；It is placed at room temperature for completely cooling to base fabric.
Step e, in f, g, since there is glue in the bottom surface of base fabric, base fabric when forwarding, bottom surface should be noted that avoid it is double
Point serves as a contrast the part friction of coating machine lower part and falls glue.
[embodiment two]
It is a kind of can both-sided adhesive double-point lining cloth processing technology, overall flow are as follows:
A, water repellent finish:
To water repellent finish before base fabric progress technique, make base fabric that there is the feel and water repellency of soft comfortable；The material of base fabric
Preferably low elastic polyester filament.
B, single side coating:
Coating machine is served as a contrast by two point first and carries out slurry point coating on one side in base fabric, coating amount is that every square metre of 2g starches point；
Then dusting coating is carried out on the basis of starching point, the point-type density of dusting coating is 180/cm2, the Circularhole diameter of powder point is
0.15mm；
C, cured:
The good base fabric of single side coating is sequentially sent in the drying unit that temperature setting is 170-195-260 DEG C, to base fabric
It carries out cured；Keep the speed of base fabric transmission in 40m/s, total curing time is 30s；
D, cooling, winding:
Base fabric after solidification passes through water cooled rolls rolling after cooling；Room temperature overnight is placed, and keeps base fabric completely cooling；
E, coated on both sides:
Base fabric after single side coating is reversely unfolded, keeps coating face-down；Slurry point coating is carried out to the upper surface of base fabric again,
Coating amount is 3g/m2Slurry point；Then dusting coating is carried out on the basis of starching point, the point-type density of dusting coating is 130/
cm2, the Circularhole diameter of powder point is 0.2mm；
In step b single side coating and step e coated on both sides, the material starched a little is thermosetting acrylic resin complex liquid.
Thermosetting acrylic resin complex liquid is made of thermosetting acrylic resin, thickener, adhesive；The mass fraction of thickener is
5%, the mass fraction of adhesive is 1.5%.Adhesive is rosin resin；Thickener is acrylic thickener.
The material of powder point is polyamide, but single side coating uses the polyamide resin that melting temperature is high and melting means is low
Rouge, melting temperature are 120~140 DEG C；And coated on both sides uses the polyamide that melting temperature is low and melting means is high, melting
Temperature is 100~130 DEG C.
F, cured again:
The good base fabric of coated on both sides is sequentially sent in the drying unit that temperature setting is 150-175-205 DEG C, it is right again
Base fabric carries out cured；Keep the speed of base fabric transmission in 40m/s, total curing time is 30s；
G, cooling, winding again:
Base fabric after solidification is passed through into water cooled rolls rolling after cooling；It is placed at room temperature for completely cooling to base fabric.
Step e, in f, g, since there is glue in the bottom surface of base fabric, base fabric when forwarding, bottom surface should be noted that avoid it is double
Point serves as a contrast the part friction of coating machine lower part and falls glue.
Above embodiment is not limitation of the present invention, and the present invention is also not limited to the example above, this technology neck
The variations, modifications, additions or substitutions that the technical staff in domain is made within the scope of technical solution of the present invention, also belong to this hair
Bright protection scope.
Claims (10)
1. one kind can both-sided adhesive double-point lining cloth processing technology, it is characterised in that: the overall flow of the technique are as follows:
A, water repellent finish:
To water repellent finish before base fabric progress technique, make base fabric that there is the feel and water repellency of soft comfortable；
B, single side coating:
Coating machine is served as a contrast by two point first and carries out slurry point coating on one side in base fabric；Then dusting painting is carried out on the basis of starching point
Layer, the point-type density of dusting coating are 180/cm2, the Circularhole diameter of powder point is 0.15mm；
C, cured:
The good base fabric of single side coating is sent into the drying unit that temperature setting is 170~260 DEG C, in 170~260 DEG C of temperature models
It heats up, base fabric is carried out cured step by step in three times in enclosing；Keep the speed of base fabric transmission in 30~40m/s, total solidification
Between be 20~30s；
D, cooling, winding:
Base fabric after solidification passes through water cooled rolls rolling after cooling；Room temperature overnight is placed, and keeps base fabric completely cooling；
E, coated on both sides:
Base fabric after single side coating is reversely unfolded, keeps coating face-down；Slurry point coating, single side are carried out to the upper surface of base fabric again
Coating amount when coating is less than the coating amount of this secondary coating；Then dusting coating is carried out on the basis of starching point, dusting coating
Point-type density is 130/cm2, the Circularhole diameter of powder point is 0.2mm；
F, cured again:
The good base fabric of coated on both sides is sent into the drying unit that temperature setting is 150~205 DEG C, in 150~205 DEG C of temperature models
It heats up, base fabric is carried out again cured step by step in three times in enclosing；Keep the speed of base fabric transmission in 30~40m/s, always admittedly
The change time is 20~30s；
G, cooling, winding again:
Base fabric after solidification is passed through into water cooled rolls rolling after cooling；It is placed at room temperature for completely cooling to base fabric.
2. it is according to claim 1 can both-sided adhesive double-point lining cloth processing technology, it is characterised in that: the base fabric
Material is low elastic polyester filament.
3. it is according to claim 2 can both-sided adhesive double-point lining cloth processing technology, it is characterised in that: the step b,
In step e, the material starched a little is thermosetting acrylic resin complex liquid, and the material of powder point is polyamide.
4. it is according to claim 3 can both-sided adhesive double-point lining cloth processing technology, it is characterised in that: the thermosetting property
Acrylic resin complex liquid is made of thermosetting acrylic resin, thickener, adhesive；The mass fraction of the thickener is
5%, the mass fraction of adhesive is 1.5%.
5. it is according to claim 4 can both-sided adhesive double-point lining cloth processing technology, it is characterised in that: the adhesive
For rosin resin；The thickener is acrylic thickener.
6. it is according to claim 5 can both-sided adhesive double-point lining cloth processing technology, it is characterised in that: the single side applies
Layer uses the polyamide that melting temperature is high and melting means is low；The coated on both sides uses the polyamides that melting temperature is low and melting means is high
Polyimide resin.
7. it is according to claim 6 can both-sided adhesive double-point lining cloth processing technology, it is characterised in that: the single side applies
The melting temperature for the polyamide that layer uses is 120~140 DEG C；The melting temperature for the polyamide that the coated on both sides uses
Degree is 100~130 DEG C.
8. it is according to claim 7 can both-sided adhesive double-point lining cloth processing technology, it is characterised in that: the slurry spot printing
The each coating amount of layer is every square metre of 2~3g.
9. it is according to claim 7 can both-sided adhesive double-point lining cloth processing technology, it is characterised in that: the step b
In single side coating, the coating amount of slurry point coating is every square metre of 2g；In the step e coated on both sides, the coating amount of slurry point coating
For every square metre of 3g.
10. according to claim 8 or claim 9 can both-sided adhesive double-point lining cloth processing technology, it is characterised in that: the step
In rapid e, f, g, when forwarding, bottom surface should be noted that be avoided being served as a contrast the parts depreciation of coating machine lower part by two point and being fallen base fabric
Glue.