CN110041589A - 一种防蚁色母 - Google Patents

一种防蚁色母 Download PDF

Info

Publication number
CN110041589A
CN110041589A CN201910197291.0A CN201910197291A CN110041589A CN 110041589 A CN110041589 A CN 110041589A CN 201910197291 A CN201910197291 A CN 201910197291A CN 110041589 A CN110041589 A CN 110041589A
Authority
CN
China
Prior art keywords
resin
ant proof
color masterbatch
parts
agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910197291.0A
Other languages
English (en)
Inventor
吴侠明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Zhongte Electric Material Co Ltd
Original Assignee
Suzhou Zhongte Electric Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Zhongte Electric Material Co Ltd filed Critical Suzhou Zhongte Electric Material Co Ltd
Priority to CN201910197291.0A priority Critical patent/CN110041589A/zh
Publication of CN110041589A publication Critical patent/CN110041589A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种防蚁色母，包括着色剂、载体树脂、分散剂、防蚁剂和其它填料，通过预先在着色母料中混合，在于着色母料一起与着色树脂混合，使得防蚁剂更好的融合在载体树脂中，提高防蚁效果，防止传统防蚁色母的由于重量份数过少，无法在载体树脂中混合均匀，本制备方法能够发挥材料的最佳性能，工艺简单，操作控制方便，质量稳定，生产效率高，可大规模工业化生产，能够有效利用防蚁剂的半衰期久的特点，提高了防蚁效果的持续时间，提高防护效果，所制备的产品具有很好的实用性，能够产生很好的经济效益和社会效应。

Description

一种防蚁色母
技术领域
本发明涉及一种色母，具体是一种防蚁色母。
背景技术
色母(ColorMasterBatch)的全称叫色母粒，也叫色种，是一种新型高分子材料专用 着色剂，亦称颜料制备物(PigmentPreparation)。色母主要用在塑料上。色母由颜料或染料、载体和添加剂三种基本要素所组成，是把超常量的颜料均匀载附于树脂之中而制得的聚集体，可称颜料浓缩物(PigmentConcentration)，所以它的着色力高于颜料本身。 加工时用少量色母料和未着色树脂掺混，就可达到设计颜料浓度的着色树脂或制品。
白蚁作为害虫之一，常常会损坏电缆，影响电力的输送以及信号的传输，在寒季，鼠 类对于线缆的相对危害较大，鼠类主要是老鼠及松鼠，它们具有锋利的牙齿，能将线缆的 护套甚至是钢、铝带保护层咬破，直接影响电缆的性能，同时，也造成了极大的安全隐患， 鼠群常常以某一鼠的成功为示例，进行集体效仿，进行磨牙及啃食；在夏季，蚁类对于线 缆的相对危害较大，尤其是白蚁，白蚁通过啃食线缆护套，并将蚁酸残留在线缆上，对于护套进行腐蚀，更基者，在护套破裂后，蚁类会钻入线缆内部，不断蚕食线缆的缆芯，因 此，市面上存在防蚁色母，但是由于防蚁色母与树脂的配比为2∶100，在这种配比下对防 蚁色母在树脂中很难分散，防蚁效果差。
发明内容
本发明的目的在于提供一种防蚁色母，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：
一种防蚁色母，包括着色剂、载体树脂、分散剂、防蚁剂和其它填料，着色剂的重量份数20至50份，根据需要调配的颜色选择调配，所述载体树脂是色母粒的基体，重量份 数为30至70份能够使着色剂、防蚁剂和其它填料均匀分布并使色母粒呈颗粒状，选择载 体树脂需考虑与被着色树脂的相容性，还要考虑色母粒应有良好的分散性，一般情况下载 体的流动性应大于被着色树脂，同时保证被着色后不影响产品质量，分散剂的重量份数为 分散剂6至10份，与着色剂和防蚁剂都有较好的亲和力，对着色剂、防蚁剂和其它填料 表面进行润湿，促使着色剂、防蚁剂和其它填料均匀分散，稳定于载体树脂中，不再凝聚， 分散剂的熔点应比载体树脂低，与载体树脂有良好的相容性，防蚁剂质量份数为20至40 份，用于毒杀和驱散白蚁，其它填料质量份数为3至12份，用于提高树脂的防老化和阻 燃能力。
作为本发明进一步的方案：所述着色剂为酞菁红、酞菁蓝、酞菁绿、耐晒大红、大分子红、大分子黄、永固黄、永固紫、偶氮红、镉红、镉黄、金红石型钛白粉、锐钛型钛白 粉、炭黑、氧化铁红、氧化铁黄、2030红、2001FG黄、H2GR黄、群青兰颜料中的一种或 几种调配而成。
作为本发明进一步的方案：所述载体树脂选自聚乙烯树脂、聚丙烯树脂、ABS树脂、尼龙树脂、PVC树脂、EVA树脂、GPPS聚苯乙烯树脂、HIPS聚苯乙烯树脂中的一种，根据 被着色树脂的种类具体选择。
作为本发明进一步的方案：所述分散剂由选自低分子量聚乙烯蜡、聚苯乙烯蜡、硬脂 酸钙、硬脂酸镁、无规聚丙烯和脂肪酸及衍生物中的一种或几种组成。
作为本发明进一步的方案：所述防蚁剂选用除虫菊酯、氨基甲酸酯类和新型有机磷药 物组成，拥有低毒、高效、半衰期久的特性。
作为本发明进一步的方案：所述其它填料由抗紫外线剂和抗氧剂组成的混合物。
作为本发明再进一步的方案：所述防蚁色母的制备方法为先按组成原料的重量份称取 着色剂、载体树脂、分散剂、防蚁剂和其它填料，将称量好的分量通过混合机混合，将混 合后的原料放入加热搅拌机中加热融化，并搅拌均匀，最后将搅拌均匀后的原料通过双螺 杆挤出机挤出造粒，在冷却干燥后制得色母颗粒。
作为本发明再进一步的方案：所述双螺杆挤出机的长径比为1∶36，色母的其熔融混 合分散挤出温度为100℃～280℃。
与现有技术相比，本发明的有益效果是：通过预先在着色母料中混合，在于着色母料 一起与着色树脂混合，使得防蚁剂更好的融合在载体树脂中，提高防蚁效果，防止传统防 蚁色母的由于重量份数过少，无法在载体树脂中混合均匀，本制备方法能够发挥材料的最 佳性能，工艺简单，操作控制方便，质量稳定，生产效率高，可大规模工业化生产，能够有效利用防蚁剂的半衰期久的特点，提高了防蚁效果的持续时间，提高防护效果，所制备的产品具有很好的实用性，能够产生很好的经济效益和社会效应。
具体实施方式
对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是 本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人 员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明实施例中，一种防蚁色母，包括着色剂、载体树脂、分散剂、防蚁剂和其它填料，着色剂的重量份数20至50份，根据需要调配的颜色选择调配，所述载体树脂是色母 粒的基体，重量份数为30至70份能够使着色剂、防蚁剂和其它填料均匀分布并使色母粒 呈颗粒状，选择载体树脂需考虑与被着色树脂的相容性，还要考虑色母粒应有良好的分散 性，一般情况下载体的流动性应大于被着色树脂，同时保证被着色后不影响产品质量，分 散剂的重量份数为分散剂6至10份，与着色剂和防蚁剂都有较好的亲和力，对着色剂、 防蚁剂和其它填料表面进行润湿，促使着色剂、防蚁剂和其它填料均匀分散，稳定于载体 树脂中，不再凝聚，分散剂的熔点应比载体树脂低，与载体树脂有良好的相容性，防蚁剂 质量份数为20至40份，用于毒杀和驱散白蚁，其它填料质量份数为3至12份，用于提 高树脂的防老化和阻燃能力。
优选的，所述着色剂为酞菁红、酞菁蓝、酞菁绿、耐晒大红、大分子红、大分子黄、永固黄、永固紫、偶氮红、镉红、镉黄、金红石型钛白粉、锐钛型钛白粉、炭黑、氧化铁 红、氧化铁黄、2030红、2001FG黄、H2GR黄、群青兰颜料中的一种或几种调配而成。
优选的，所述载体树脂选自聚乙烯树脂、聚丙烯树脂、ABS树脂、尼龙树脂、PVC树脂、EVA树脂、GPPS聚苯乙烯树脂、HIPS聚苯乙烯树脂中的一种，根据被着色树脂的种类 具体选择。
优选的，所述分散剂由选自低分子量聚乙烯蜡、聚苯乙烯蜡、硬脂酸钙、硬脂酸镁、无规聚丙烯和脂肪酸及衍生物中的一种或几种组成。
优选的，所述防蚁剂选用除虫菊酯、氨基甲酸酯类和新型有机磷药物组成，拥有低毒、 高效、半衰期久的特性。
优选的，所述其它填料由抗紫外线剂和抗氧剂组成的混合物。
优选的，所述防蚁色母的制备方法为先按组成原料的重量份称取着色剂、载体树脂、 分散剂、防蚁剂和其它填料，将称量好的分量通过混合机混合，将混合后的原料放入加热 搅拌机中加热融化，并搅拌均匀，最后将搅拌均匀后的原料通过双螺杆挤出机挤出造粒， 在冷却干燥后制得色母颗粒。
优选的，所述双螺杆挤出机的长径比为1∶36，色母的其熔融混合分散挤出温度为100℃ ～280℃。
本发明的工作原理是：通过预先在着色母料中混合，在于着色母料一起与着色树脂混 合，使得防蚁剂更好的融合在载体树脂中，提高防蚁效果，防止传统防蚁色母的由于重量 份数过少，无法在载体树脂中混合均匀，本制备方法能够发挥材料的最佳性能，工艺简单， 操作控制方便，质量稳定，生产效率高，可大规模工业化生产，能够有效利用防蚁剂的半 衰期久的特点，提高了防蚁效果的持续时间，提高防护效果，所制备的产品具有很好的实 用性，能够产生很好的经济效益和社会效应。
尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依 然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替 换，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本 发明的保护范围之内。

Claims (8)

1.一种防蚁色母，包括着色剂、载体树脂、分散剂、防蚁剂和其它填料，其特征在于，所述着色剂的重量份数20至50份，根据需要调配的颜色选择调配，所述载体树脂是色母粒的基体，重量份数为30至70份能够使着色剂、防蚁剂和其它填料均匀分布并使色母粒呈颗粒状，选择载体树脂需考虑与被着色树脂的相容性，还要考虑色母粒应有良好的分散性，所述分散剂的重量份数为分散剂6至10份，与着色剂和防蚁剂都有较好的亲和力，分散剂的熔点比载体树脂低，与载体树脂有良好的相容性，所述防蚁剂质量份数为20至40份，所述其它填料质量份数为3至12份。
2.根据权利要求1所述的防蚁色母，其特征在于，所述着色剂为酞菁红、酞菁蓝、酞菁绿、耐晒大红、大分子红、大分子黄、永固黄、永固紫、偶氮红、镉红、镉黄、金红石型钛白粉、锐钛型钛白粉、炭黑、氧化铁红、氧化铁黄、2030红、2001FG黄、H2GR黄、群青兰颜料中的一种或几种调配而成。
3.根据权利要求1所述的防蚁色母，其特征在于，所述载体树脂选自聚乙烯树脂、聚丙烯树脂、ABS树脂、尼龙树脂、PVC树脂、EVA树脂、GPPS聚苯乙烯树脂、HIPS聚苯乙烯树脂中的一种，根据被着色树脂的种类具体选择。
4.根据权利要求1所述的防蚁色母，其特征在于，所述分散剂由选自低分子量聚乙烯蜡、聚苯乙烯蜡、硬脂酸钙、硬脂酸镁、无规聚丙烯和脂肪酸及衍生物中的一种或几种组成。
5.根据权利要求1所述的防蚁色母，其特征在于，所述防蚁剂选用除虫菊酯、氨基甲酸酯类和新型有机磷药物组成。
6.根据权利要求1所述的防蚁色母，其特征在于，所述其它填料由抗紫外线剂和抗氧剂组成的混合物。
7.一种制备权利要求1所述的防蚁色母的方法，其特征在于，按组成原料的重量份称取着色剂、载体树脂、分散剂、防蚁剂和其它填料，将称量好的分量通过混合机混合，将混合后的原料放入加热搅拌机中加热融化，并搅拌均匀，最后将搅拌均匀后的原料通过双螺杆挤出机挤出造粒，在冷却干燥后制得色母颗粒。
8.根据权利要求7所述的防蚁色母的制备方法，其特征在于，所述双螺杆挤出机的长径比为1∶36，色母的其熔融混合分散挤出温度为100℃～280℃。
CN201910197291.0A 2019-03-08 2019-03-08 一种防蚁色母 Pending CN110041589A (zh)