CN110028883A - 一种可有效改善结皮性的气干性涂料及其制备方法 - Google Patents
一种可有效改善结皮性的气干性涂料及其制备方法 Download PDFInfo
- Publication number
- CN110028883A CN110028883A CN201910367827.9A CN201910367827A CN110028883A CN 110028883 A CN110028883 A CN 110028883A CN 201910367827 A CN201910367827 A CN 201910367827A CN 110028883 A CN110028883 A CN 110028883A
- Authority
- CN
- China
- Prior art keywords
- parts
- air
- drying property
- coating
- effectively improved
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种可有效改善结皮性的气干性涂料，按质量份数计，所述涂料包括如下组分：气干性树脂：40‑60份；酚类单体：1.0‑2.0份；有机膨润土0.3‑0.5份；着色颜料：5‑20份；体质颜料：17‑25份；200#溶剂油0.5‑1.0份；锰干料：0.3‑0.5份；稀土干料：0.8‑1.2份。本发明所公开的气干性涂料从性能上与市面所售传统涂料相比，不使用传统抗结皮剂，利用酚类单体代替传统的甲乙酮肟作为防结皮剂，从而达到有效改善气干性涂料易结皮的性能效果。
Description
技术领域
本发明属于涂料技术领域，具体涉及一种可有效改善结皮性的气干性涂料及其制备方法。
背景技术
气干性涂料一直以来都占据着工业涂料用量的绝对霸主地位，随着世界资源枯竭，可再生性资源的利用会更加被重视。中长半干性植物油及干性植物油改性的醇酸树脂和腰果壳油改性的酚醛树脂等富含共轭双键或经重排后能形成共轭双键的半干性油、干性油的高分子化合物作为气干性涂料的成膜物将越加得到社会认可。而气干性涂料的开罐效果长期受结皮严重所困扰，目前，本领域技术人员认为这类涂料因为通过成膜物中的共轭双键与空气中的氧气接触发生游离基聚合形成漆膜的原理，那就不可避免存在产生结皮的现象。但申请人研究发现了一种可改善气干性涂料结皮性的方法。
发明内容
有鉴于此，本发明目的在于提供一种可有效改善结皮性的气干性涂料及其制备方法。
具体提供了如下所述技术方案：
1、一种可有效改善结皮性的气干性涂料，按质量份数计，所述涂料包括如下组分：气干性树脂：40-60份；酚类单体：1.0-2.0份；有机膨润土0.3-0.5份；着色颜料：5-20份；体质颜料：17-25份；200#溶剂油0.5-1.0份；锰干料：0.3-0.5份；稀土干料：0.8-1.2份。
进一步，所述气干性树脂包括半干性植物油改性醇酸树脂、干性植物油改性的醇酸树脂以及腰果壳油改性的酚醛树脂中的一种或几种。
进一步，所述酚类单体包括苯酚、对叔丁酚、对苯基苯酚中的一种或几种。
进一步，所述有机膨润土包括BP-183有机膨润土、JF-38有机膨润土中的一种或几种。
进一步，所述着色颜料包括钛白粉、炭黑、中铬黄、酞菁蓝、氧化铁红、大红粉中的一种或几种；所述体质颜料包括沉淀硫酸钡、轻质碳酸钙、滑石粉中的一种或几种。
进一步，所述锰干料包括环烷酸锰、异辛酸锰中的一种或几种，所述稀土干料包括环烷酸稀土、异辛酸稀土中的一种或几种。
进一步优选的，按质量份数计，所述涂料包括如下组分：气干性树脂：50份；酚类单体：1.5份；有机膨润土0.4份；着色颜料：15份；体质颜料：20份；200#溶剂油0.8份；锰干料：0.4份；稀土干料：1.0份。
2、一种可有效改善结皮性的气干性涂料的制备方法如下：气干性树脂入搅拌缸，开启低速搅拌，慢慢依次加入有机膨润土着色颜料、体质颜料、溶剂后提至高速搅拌，均匀后过研磨机至细度小于25μm得漆浆，漆浆入调漆缸，加入锰干料、稀土干料、酚类单体，搅匀、过滤、包装。
本发明的有益效果在于:
1、本发明所公开的气干性涂料组分中利用酚类单体代替传统的甲乙酮肟作为防结皮剂，其能与空气中的氧气作用，使氧原子失去产生游离基的活性，从而避免涂料结皮；
2、本发明所公开的气干性涂料组分中所使用的酚类单体利用其弱酸性，与中长半干性植物油及干性植物油改性的醇酸树脂和腰果壳油改性的酚醛树脂相容性好，并且在漆膜干燥过程中，常温下能够相互作用形成漆膜，甚至有助于漆膜的表干和实干；
3、本技术方案所采用组分去掉传统使用的金属钴类表干催干剂，其有利于消除气干性涂料储存过程中诱导涂料上表面的氧气产生氧游离基的风险，也就杜绝了引发共轭双键链增长的可能，进一步达到防结皮的效果。
具体实施方式
下面将结合具体实施例对本发明做详细说明：以下实施例按照如下所述方法进行制备：气干性树脂入搅拌缸，开启低速搅拌，慢慢依次加入有机膨润土着色颜料、体质颜料、溶剂后提至高速搅拌，均匀后过研磨机至细度小于25μm得漆浆，漆浆入调漆缸，加入锰干料、稀土干料、酚类单体，搅匀、过滤、包装。而对比实施例的制备方法的区别在于：不加入酚类单体，而在调漆缸中另加钴干料、防结皮剂。
实施例1
一种可有效改善结皮性的气干性涂料，按质量份数计，所述涂料包括如下组分：气干性树脂：50份；酚类单体：1.5份；有机膨润土0.4份；着色颜料：15份；体质颜料：20份；200#溶剂油0.8份；锰干料：0.4份；稀土干料：1.0份。
以上组分中，气干性树脂为半干性植物油改性醇酸树脂、干性植物油改性的醇酸树脂以及腰果壳油改性的酚醛树脂中的一种或几种；所述酚类单体为苯酚；所述有机膨润土为BP-183有机膨润土；所述着色颜料为钛白粉；所述体质颜料为沉淀硫酸钡；
所述锰干料为环烷酸锰；所述稀土干料为环烷酸稀土。
实施例2
一种可有效改善结皮性的气干性涂料，按质量份数计，所述涂料包括如下组分：气干性树脂：40份；酚类单体：2.0份；有机膨润土0.3份；着色颜料：20份；体质颜料：17份；200#溶剂油1.0份；锰干料：0.3份；稀土干料：1.2份。
以上组分中所述气干性树脂为半干性植物油改性醇酸树脂、干性植物油改性的醇酸树脂以及腰果壳油改性的酚醛树脂按质量比1:1:1混合而成；所述酚类单体为对叔丁酚；所述有机膨润土为JF-38有机膨润土；所述着色颜料酞菁蓝；所述体质颜料为滑石粉；所述锰干料为异辛酸锰中；所述稀土干料为异辛酸稀土。
实施例3
一种可有效改善结皮性的气干性涂料，按质量份数计，所述涂料包括如下组分：气干性树脂：60份；酚类单体：1.0份；有机膨润土0.5份；着色颜料：5份；体质颜料：25份；200#溶剂油0.5份；锰干料：0.5份；稀土干料：0.8份。
以上组分中，所述气干性树脂为腰果壳油改性的酚醛树脂；所述酚类单体为对苯基苯酚；所述有机膨润土由BP-183有机膨润土和JF-38有机膨润土按质量比1:1混合而成；所述着色颜料为中铬黄；所述体质颜料为轻质碳酸钙；所述锰干料为异辛酸锰；所述稀土干料为异辛酸稀土。
下面以市面上传统的气干性涂料作为对比实施例。
对比实施例1
与实施例1不同在于，本实施例气干性涂料组分中不包括酚类单体，另外还包括极性溶剂0.2质量份、钴干料0.4质量份；防结皮剂0.25质量份。并且200#溶剂油用量为2.5质量份；
其中极性溶剂为甲醇；钴干料为环烷酸钴；防结皮剂为甲乙酮肟。
对比实施例2
与实施例2不同在于，本实施例气干性涂料组分中不包括酚类单体，另外还包括极性溶剂0.3质量份、钴干料0.5质量份；防结皮剂0.23质量份。并且200#溶剂油用量为3质量份；
其中极性溶剂为乙醇；钴干料为异辛酸钴；防结皮剂为甲乙酮肟。
对比实施例3
与实施例3不同在于，本实施例气干性涂料组分中不包括酚类单体，另外还包括极性溶剂0.1质量份、钴干料0.3质量份；防结皮剂0.2质量份。并且200#溶剂油用量为2质量份；
其中极性溶剂为丙酮；钴干料为异辛酸钴；防结皮剂为甲乙酮肟。
性能验证：
下面将对实施例1～3及对比实施例1～3所制备的气干性涂料进行性能检测，试样检测标准参照GB6753.3-86涂料储存稳定性试验方法执行，记录于表1所示：
表1气干性涂料质量状况
由以上实施例可发现，本发明所公开的气干性涂料从性能上与市面所售传统涂料相比，从表干、实干、是否沉淀以及施工性能方面差别不大，基本所实现性能一样，但是从结皮性来看，明显实施例1～3所列涂料优于对比实施例1～3。
从而可验证，本发明所公开技术方案在不使用防结皮剂的基础上，还能实现所制备得到的气干性涂料在防结皮性能上有效改善。本发明所公开的气干性涂料组分中利用酚类单体代替传统的甲乙酮肟作为防结皮剂，其能与空气中的氧气作用，使氧原子失去产生游离基的活性，从而避免涂料结皮；并且酚类单体利用其弱酸性，与中长半干性植物油及干性植物油改性的醇酸树脂和腰果壳油改性的酚醛树脂相容性好，并且在漆膜干燥过程中，常温下能够相互作用形成漆膜，甚至有助于漆膜的表干和实干；另外本技术方案所采用组分去掉传统使用的金属钴类表干催干剂，其有利于消除气干性涂料储存过程中诱导涂料上表面的氧气产生氧游离基的风险，也就杜绝了引发共轭双键链增长的可能，进一步达到防结皮的效果。
最后说明的是，对所公开的实施例的上述说明，使本领域技术人员能够实现或使用本发明。对这些实施例的多种修改对本领域技术人员来说将是显而易见的，本文中所定义的一般原理可以在不脱离本发明的精神或范围的情况下，在其它实施例中实现。因此，本发明将不会被限制于本文所示的这些实施例，而是要符合与本文所公开的原理和新颖特点相一致的最宽的范围。
Claims (8)
1.一种可有效改善结皮性的气干性涂料，其特征在于，按质量份数计，所述涂料包括如下组分：气干性树脂：40-60份；酚类单体：1.0-2.0份；有机膨润土0.3-0.5份；着色颜料：5-20份；体质颜料：17-25份；200#溶剂油0.5-1.0份；锰干料：0.3-0.5份；稀土干料：0.8-1.2份。
2.根据权利要求1所述一种可有效改善结皮性的气干性涂料，其特征在于，所述气干性树脂包括半干性植物油改性醇酸树脂、干性植物油改性的醇酸树脂以及腰果壳油改性的酚醛树脂中的一种或几种。
3.根据权利要求1所述一种可有效改善结皮性的气干性涂料，其特征在于，所述酚类单体包括苯酚、对叔丁酚、对苯基苯酚中的一种或几种。
4.根据权利要求1所述一种可有效改善结皮性的气干性涂料，其特征在于，所述有机膨润土包括BP-183有机膨润土、JF-38有机膨润土中的一种或几种。
5.根据权利要求1所述一种可有效改善结皮性的气干性涂料，其特征在于，所述着色颜料包括钛白粉、炭黑、中铬黄、酞菁蓝、氧化铁红、大红粉中的一种或几种；所述体质颜料包括沉淀硫酸钡、轻质碳酸钙、滑石粉中的一种或几种。
6.根据权利要求1所述一种可有效改善结皮性的气干性涂料，其特征在于，所述锰干料包括环烷酸锰、异辛酸锰中的一种或几种，所述稀土干料包括环烷酸稀土、异辛酸稀土中的一种或几种。
7.根据权利要求1所述一种可有效改善结皮性的气干性涂料，其特征在于，按质量份数计，所述涂料包括如下组分：气干性树脂：50份；酚类单体：1.5份；有机膨润土0.4份；着色颜料：15份；体质颜料：20份；200#溶剂油0.8份；锰干料：0.4份；稀土干料：1.0份。
8.根据权利要求1所述一种可有效改善结皮性的气干性涂料，其特征在于，所述涂料的制备方法如下：按质量份配比，首先气干性树脂入搅拌缸，开启低速搅拌，依次加入有机膨润土着色颜料、体质颜料、溶剂后提至高速搅拌，均匀后过研磨机至细度小于25μm得漆浆，漆浆入调漆缸，加入锰干料、稀土干料、酚类单体，搅匀、过滤、包装。