CN110016261A - A kind of heat-insulated radiation protection water-repellent paint and preparation method thereof - Google Patents
A kind of heat-insulated radiation protection water-repellent paint and preparation method thereof Download PDFInfo
- Publication number
- CN110016261A CN110016261A CN201910284290.XA CN201910284290A CN110016261A CN 110016261 A CN110016261 A CN 110016261A CN 201910284290 A CN201910284290 A CN 201910284290A CN 110016261 A CN110016261 A CN 110016261A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- heat
- repellent paint
- radiation protection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of heat-insulated radiation protection water-repellent paint, the component including following parts by weight: 10~20 parts of styrene-acrylic emulsion, 10~15 parts of silicone acrylic emulsion, 10~15 parts of styrene-butadiene emulsion, 10~20 parts of weather-proof powder, 5~10 parts of modified powder, 2~7 parts of sepiolite powder, 5~10 parts of cenosphere, 4~9 parts of mica powder, 2~7 parts of attapulgite powder and 0.5~3 part of styrenated phenol.The synergistic effect that coating in the present invention passes through several components, and by adjusting the weight ratio between each component, the waterproof and dampproof performance for not only increasing coating, improves the adhesive property of coating, also improves the heat insulation property, uvioresistant, anti-aging and heat reflection of coating.The present invention also provides a kind of preparation methods of heat-insulated radiation protection water-repellent paint.
Description
Technical field
The invention belongs to technical field of coatings, and in particular to a kind of heat-insulated radiation protection water-repellent paint and preparation method thereof.
Background technique
The leakage problems of building are generally existing, and buildings waterproof becomes question of common concern in architectural engineering, especially
After modern architecture tends to high stratification, assembling, the requirement to waterproofing work is higher, and water-repellent paint is often made in waterproofing work
One of primary roofing material.
Currently, the functionality of water-repellent paint is more single, have the function of waterproof water proof, and heat-insulated, radiation protection effect
It is poor.Existing water-repellent paint mainly uses Styrene And Chloroalkyl Acrylates (SAE) or acetic acid-vinyl acetate (EVA) copolymer emulsion, this
Two kinds of materials all have preferable workability and compatibility with cement, are capable of forming preferable continuous waterproof membrane.Both waterproofs
Material is only coated in a thin layer on the inside of the surface layer or building of building, after the completion of molding, the heating conduction of water-repellent paint
It combines together substantially with the heating conduction of building, but both water-repellent paint light albedoes and weatherability are poor, use the longevity
Life is shorter, and the irradiation of daylight, and the temperature of Indoor environment can be made to increase rapidly, and indoor ventilation effect is poor, causes to dissipate
Thermal effect is bad, but the inside of building needs to be heated up or cooled down using some equipment, consume generally there are heat-insulated demand
It can be serious.
In view of this, promoting the benign development of friendly environment society to reduce carbon emission, it is necessary to provide a kind of tool
There is heat-insulated and radiation-proof effect water-repellent paint.
Summary of the invention
It is an object of the invention to overcome above-mentioned technical deficiency, a kind of heat-insulated radiation protection water-repellent paint is proposed, which applies
Material has heat-insulated and radiation-proof effect；The purpose of another aspect of the present invention is, provides a kind of preparation of heat-insulated radiation shielding coating
Method.
To reach above-mentioned technical purpose, technical solution of the present invention provides a kind of heat-insulated radiation protection water-repellent paint, including such as
The component of lower parts by weight: 10~20 parts of styrene-acrylic emulsion, 10~15 parts of silicone acrylic emulsion, 10~15 parts of styrene-butadiene emulsion, weather-proof powder 10
~20 parts, 5~10 parts of modified powder, 2~7 parts of sepiolite powder, 5~10 parts of cenosphere, 4~9 parts of mica powder, attapulgite powder
2~7 parts and 0.5~3 part of styrenated phenol.
Technical solution of the present invention additionally provides a kind of preparation method of heat-insulated radiation protection water-repellent paint, including walks as follows
It is rapid:
S1, it stocks up by weight；
S2, weather-proof powder, modified powder, sepiolite powder, cenosphere, mica powder, attapulgite powder and water are mixed
It is even, obtain mixed liquor A；Styrene-acrylic emulsion, silicone acrylic emulsion, styrene-butadiene emulsion and styrenated phenol are uniformly mixed, mixed liquor is obtained
B；The mixed liquor A and the mixed liquid B are uniformly mixed, finished product is obtained.
Compared with prior art, the beneficial effect comprise that
1, in the present invention styrene-acrylic emulsion that adds can continuous film forming, improve the extensibility at water-repellent paint interface；Silicon third
Lotion can improve the intensity of water-repellent paint；Styrene-butadiene emulsion can improve the heat resistance of water-repellent paint；Weather-proof powder and modified powder
It is adjustable the rheological property of water-repellent paint, not only improves and improves the boundary strength and compactness of water-repellent paint, enhance anti-
The mechanical performance of water paint, and improve the weatherability of water-repellent paint；Sepiolite powder can improve the heat-proof quality of coating, and it has
There is certain rheological characteristic, improves the thixotropy and suspension of coating；Cenosphere have hollow structure, can improve coating every
Thermal effect makes light diffusion and scattering, improves coating to the obstructing capacity of infrared heat ray；Mica powder can assist hollow micro-
Pearl further promotes coating to the albedo of sunlight；Attapulgite powder can promote the deformability of coating, it may have heat-insulated guarantor
The effect of temperature；Styrenated phenol is able to ascend the ageing resistance of coating；
2, the coating in the present invention is by the synergistic effects of several components, and by adjusting the weight ratio between each component
Example, not only increases the waterproof and dampproof performance of coating, improves the adhesive property of coating, also improve the insulation of coating
Property, uvioresistant, anti-aging and heat reflection；
3, the preparation method of coating is simple in the present invention, and each component mixes more uniform, is suitable for industrial mass
Production.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that embodiment described herein is only used to explain the present invention, it is not used to limit
The present invention.
The embodiment provides a kind of heat-insulated radiation protection water-repellent paint, the components including following parts by weight: phenylpropyl alcohol
10~20 parts of lotion, 10~15 parts of silicone acrylic emulsion, 10~15 parts of styrene-butadiene emulsion, 10~20 parts of weather-proof powder, modified powder 5~10
Part, 2~7 parts of sepiolite powder, 5~10 parts of cenosphere, 4~9 parts of mica powder, 2~7 parts of attapulgite powder and styrenated phenol
0.5~3 part.
In the present invention, weather-proof powder is rutile titanium white powder；Its dispersibility with higher, high covering power and preferable steady
It is qualitative, it plays a protective role to the stability of water-repellent paint, and enhance the mechanical strength and adhesive force of film, prevents crackle, prevent
Only ultraviolet light and moisture penetrate, to extend the service life of film；If water-repellent paint is colored, moreover it is possible to color after making water-repellent paint form a film
It is color bright-coloured.
In the present invention, modified powder is precipitated calcium carbonate；It is adjustable viscosity, rheological property and the curability of coating, from
And the heat resistance, wearability and glossiness of coating are improved, and improve the processing performance of coating.
In the present invention, partial size≤50um of cenosphere promotes the heat-insulated effect of coating to increase the surface area of cenosphere
Fruit, and enhance the diffusion and scattering of light, to enhance the radiation-proof effect of coating.
In the present invention, which further includes the common auxiliary agent of paint field and/or carrier, including but
It is not limited at least one of defoaming agent, foam inhibitor, dispersing agent, coalescing agent, fungicide, thickener, colorant, solvent；Its
Middle solvent is organic solvent, vegetable oil solvent or water.
In some preferred embodiments of the invention, the heat-insulated radiation protection water-repellent paint further include: defoaming agent, foam inhibition
Agent, dispersing agent, coalescing agent, fungicide, thickener, aqueous color paste and water.Wherein, defoaming agent can eliminate the bubble of generation, mention
The compactness of high film forming；Foam inhibitor can inhibit the generation of bubble to defoam rapidly in a longer period of time；Dispersing agent energy
It is uniformly mixed water-repellent paint system, suspendability increases, and does not precipitate, the physico-chemical property of whole system more stable uniform；At
Film auxiliary agent can preferably promote water-repellent paint surface to form a tunic, and accelerate the formation of film；Fungicide can play antibacterial and mouldproof
Effect；Thickener can increase the consistency of water-repellent paint, improve spreading property；Aqueous color paste, which plays, adjusts water-repellent paint color
Effect；The carrier that water is fused as each component, merges each component sufficiently.Defoaming agent in the present invention, foam inhibitor, dispersing agent, at
Film auxiliary agent, fungicide, thickener and which kind of specifically used type of aqueous color paste, those skilled in the art can be according to practical feelings
Condition is selected.
It is highly preferred that the heat-insulated radiation protection water-repellent paint includes the auxiliary agent of following parts by weight: 0.1~0.2 part of defoaming agent, suppression
0.15~0.3 part of infusion, 0.5~2 part of dispersing agent, 0.8~2 part of coalescing agent, 0.1~0.2 part of fungicide, thickener 1~2
Part, 0.4~0.6 part of aqueous color paste and 5~10 parts of water.By the amount of auxiliary agent in optimization water-repellent paint, preferably to improve waterproof
The performance of coating, and avoid the waste of raw material.
In the present invention, the pH value of the heat-insulated radiation protection water-repellent paint is 8.5~9.5.
Embodiments of the present invention additionally provide a kind of preparation method of heat-insulated radiation protection water-repellent paint, including walk as follows
It is rapid:
(1) it stocks up by weight；
(2) weather-proof powder, modified powder, sepiolite powder, cenosphere, mica powder, attapulgite powder and water are mixed equal
It is even, obtain mixed liquor A；Styrene-acrylic emulsion, silicone acrylic emulsion, styrene-butadiene emulsion and styrenated phenol are uniformly mixed, mixed liquor is obtained
B；Mixed liquor A and mixed liquid B are uniformly mixed, finished product is obtained.
In the present invention, prepare mixed liquor A when be also added into defoaming agent, foam inhibitor, dispersing agent, coalescing agent, fungicide and
Aqueous color paste, mixed liquor A are specifically prepared with the following method: water and aqueous color paste being uniformly mixed, mill base liquid is obtained；It will defoaming
Agent, foam inhibitor, dispersing agent, coalescing agent, fungicide and mill base liquid are uniformly mixed, and obtain cosolvent；Again by cosolvent, weather-proof powder
Body, modified powder, sepiolite powder, cenosphere, mica powder and attapulgite powder are uniformly mixed, and obtain mixed liquor A.
In the present invention, after mixing by mixed liquor A and mixed liquid B, thickener also joined into mixed liquor, to adjust
The consistency of finished product.
In order to make the objectives, technical solutions, and advantages of the present invention clearer, below in conjunction with specific embodiment, to this
Invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, not
For limiting the present invention.
Experimental method in the present invention is unless otherwise specified conventional method.Experimental material used in the present invention is such as
It is that market is commercially available without specified otherwise.
Embodiment 1:
The embodiment of the present invention 1 provides a kind of heat-insulated radiation protection water-repellent paint, the component including following parts by weight: phenylpropyl alcohol
15 parts of lotion, 12.5 parts of silicone acrylic emulsion, 13 parts of styrene-butadiene emulsion, 15 parts of weather-proof powder, 7 parts of modified powder, 4.5 parts of sepiolite powder,
8 parts of cenosphere, 6 parts of mica powder, 5 parts of attapulgite powder, 1.7 parts of styrenated phenol, 0.15 part of defoaming agent, foam inhibitor 0.2
Part, 1.2 parts of dispersing agent, 1.5 parts of coalescing agent, 0.15 part of fungicide, 1.5 parts of thickener, 0.5 part of aqueous color paste and 7 parts of water.
The heat-insulated radiation protection water-repellent paint is prepared with the following method:
(1) water and aqueous color paste are uniformly mixed, obtain mill base liquid；By defoaming agent, foam inhibitor, dispersing agent, film forming
Auxiliary agent, fungicide and mill base liquid are uniformly mixed, and obtain cosolvent；Again by cosolvent, weather-proof powder, modified powder, Hai Pao
Mountain flour, cenosphere, mica powder and attapulgite powder are uniformly mixed, and obtain mixed liquor A；
(2) styrene-acrylic emulsion, silicone acrylic emulsion, styrene-butadiene emulsion and styrenated phenol are uniformly mixed, obtain mixed liquor
B；
(3) thickener and mixed liquid B are added in mixed liquor A, after being uniformly mixed, the pH value of mixed liquor are transferred to 9,
Obtain finished product.
Embodiment 2:
The embodiment of the present invention 2 provides a kind of heat-insulated radiation protection water-repellent paint, the component including following parts by weight: phenylpropyl alcohol
It is 12 parts of lotion, 11 parts of silicone acrylic emulsion, 11 parts of styrene-butadiene emulsion, 13 parts of weather-proof powder, 6 parts of modified powder, 3 parts of sepiolite powder, hollow
6 parts of microballon, 5 parts of mica powder, 4 parts of attapulgite powder, 1 part of styrenated phenol, 0.15 part of defoaming agent, 0.2 part of foam inhibitor, dispersion
1 part of agent, 1 part of coalescing agent, 0.15 part of fungicide, 1.5 parts of thickener, 0.5 part of aqueous color paste and 8 parts of water.
The preparation method of the heat-insulated radiation protection water-repellent paint is identical as the preparation method in embodiment 1, and difference is step
(3) finished product is obtained after the pH value of mixed liquor is transferred to 8.5 in.
Embodiment 3:
The embodiment of the present invention 3 provides a kind of heat-insulated radiation protection water-repellent paint, the component including following parts by weight: phenylpropyl alcohol
It is 18 parts of lotion, 13 parts of silicone acrylic emulsion, 14 parts of styrene-butadiene emulsion, 17 parts of weather-proof powder, 8 parts of modified powder, 5 parts of sepiolite powder, hollow
9 parts of microballon, 8 parts of mica powder, 6 parts of attapulgite powder, 2 parts of styrenated phenol, 0.15 part of defoaming agent, 0.2 part of foam inhibitor, dispersion
1.5 parts of agent, 1.5 parts of coalescing agent, 0.15 part of fungicide, 1.5 parts of thickener, 0.5 part of aqueous color paste and 8 parts of water.
The preparation method of the heat-insulated radiation protection water-repellent paint is identical as the preparation method in embodiment 1, and difference is step
(3) finished product is obtained after the pH value of mixed liquor is transferred to 9.5 in.
Embodiment 4:
The embodiment of the present invention 4 provides a kind of heat-insulated radiation protection water-repellent paint, the component including following parts by weight: phenylpropyl alcohol
It is 10 parts of lotion, 10 parts of silicone acrylic emulsion, 10 parts of styrene-butadiene emulsion, 10 parts of weather-proof powder, 5 parts of modified powder, 2 parts of sepiolite powder, hollow
5 parts of microballon, 4 parts of mica powder, 2 parts of attapulgite powder, 0.5 part of styrenated phenol, 0.1 part of defoaming agent, foam inhibitor 0.15 part, point
0.5 part of powder, 0.8 part of coalescing agent, 0.1 part of fungicide, 1 part of thickener, 0.4 part of aqueous color paste and 5 parts of water.
The preparation method of the heat-insulated radiation protection water-repellent paint is identical as the preparation method in embodiment 1.
Embodiment 5:
The embodiment of the present invention 5 provides a kind of heat-insulated radiation protection water-repellent paint, the component including following parts by weight: phenylpropyl alcohol
It is 20 parts of lotion, 15 parts of silicone acrylic emulsion, 15 parts of styrene-butadiene emulsion, 20 parts of weather-proof powder, 10 parts of modified powder, 7 parts of sepiolite powder, hollow
10 parts of microballon, 9 parts of mica powder, 7 parts of attapulgite powder, 3 parts of styrenated phenol, 0.2 part of defoaming agent, 0.3 part of foam inhibitor, dispersion
2 parts of agent, 2 parts of coalescing agent, 0.2 part of fungicide, 2 parts of thickener, 0.6 part of aqueous color paste and 10 parts of water.
The preparation method of the heat-insulated radiation protection water-repellent paint is identical as the preparation method in embodiment 1.
The performance of heat-insulated radiation protection water-repellent paint obtained in the embodiment of the present invention 1~5 is tested, performance test knot
Fruit is as shown in table 1:
The heat-insulated radiation protection water-repellent paint performance comparison of 1 Examples 1 to 5 of table
As can be seen from Table 1, the adhesion strength of heat-insulated radiation protection water-repellent paint obtained in the embodiment of the present invention 1~5, draw
It stretches intensity, fracture elongation and heat-proof quality and is superior to commercially available conventional waterproof coating, drying time is also than commercially available conventional waterproof
Coating is shorter.
The above described specific embodiments of the present invention are not intended to limit the scope of the present invention..Any basis
Any other various changes and modifications that technical concept of the invention is made should be included in the guarantor of the claims in the present invention
It protects in range.
Claims (10)
1. a kind of heat-insulated radiation protection water-repellent paint, which is characterized in that the component including following parts by weight: styrene-acrylic emulsion 10~20
Part, 10~15 parts of silicone acrylic emulsion, 10~15 parts of styrene-butadiene emulsion, 10~20 parts of weather-proof powder, 5~10 parts of modified powder, sepiolite
2~7 parts of powder, 5~10 parts of cenosphere, 4~9 parts of mica powder, 2~7 parts of attapulgite powder and 0.5~3 part of styrenated phenol.
2. heat-insulated radiation protection water-repellent paint according to claim 1, which is characterized in that the weather-proof powder is rutile titanium
White powder.
3. heat-insulated radiation protection water-repellent paint according to claim 1, which is characterized in that the modified powder is lightweight carbonic acid
Calcium.
4. heat-insulated radiation protection water-repellent paint according to claim 1, which is characterized in that the partial size of the cenosphere≤
50um。
5. heat-insulated radiation protection water-repellent paint according to claim 1, which is characterized in that the heat-insulated radiation protection water-repellent paint
It further include defoaming agent, foam inhibitor, dispersing agent, coalescing agent, fungicide, thickener, aqueous color paste and water.
6. heat-insulated radiation protection water-repellent paint according to claim 5, which is characterized in that the heat-insulated radiation protection water-repellent paint
It further include 0.1~0.2 part of defoaming agent, 0.15~0.3 part of foam inhibitor, 0.5~2 part of dispersing agent, 0.8~2 part of coalescing agent, sterilization
0.1~0.2 part of agent, 1~2 part of thickener, 0.4~0.6 part of aqueous color paste and 5~10 parts of water.
7. heat-insulated radiation protection water-repellent paint according to claim 1, which is characterized in that the heat-insulated radiation protection water-repellent paint
PH value be 8.5~9.5.
8. a kind of preparation method of heat-insulated radiation protection water-repellent paint as described in any one of claims 1 to 7, which is characterized in that
Include the following steps:
S1, it stocks up by weight；
S2, weather-proof powder, modified powder, sepiolite powder, cenosphere, mica powder, attapulgite powder and water are uniformly mixed, are obtained
To mixed liquor A；Styrene-acrylic emulsion, silicone acrylic emulsion, styrene-butadiene emulsion and styrenated phenol are uniformly mixed, mixed liquid B is obtained；By institute
It states mixed liquor A and the mixed liquid B is uniformly mixed, obtain finished product.
9. the preparation method of heat-insulated radiation protection water-repellent paint according to claim 8, which is characterized in that preparation mixed liquor A
When be also added into defoaming agent, foam inhibitor, dispersing agent, coalescing agent, fungicide and aqueous color paste, the mixed liquor A specifically uses
Following method preparation: water and aqueous color paste are uniformly mixed, mill base liquid is obtained；Defoaming agent, foam inhibitor, dispersing agent, film forming are helped
Agent, fungicide and mill base liquid are uniformly mixed, and obtain cosolvent；Again by cosolvent, weather-proof powder, modified powder, sepiolite powder, sky
Heart microballon, mica powder and attapulgite powder are uniformly mixed, and obtain mixed liquor A.
10. the preparation method of heat-insulated radiation protection water-repellent paint according to claim 8, which is characterized in that mixed liquor A and mixed
It closes liquid B after mixing, also joined thickener into mixed liquor.