CN109987871A - 混凝土砂浆抗裂外加剂及其制备方法和使用 - Google Patents
混凝土砂浆抗裂外加剂及其制备方法和使用 Download PDFInfo
- Publication number
- CN109987871A CN109987871A CN201811597851.3A CN201811597851A CN109987871A CN 109987871 A CN109987871 A CN 109987871A CN 201811597851 A CN201811597851 A CN 201811597851A CN 109987871 A CN109987871 A CN 109987871A
- Authority
- CN
- China
- Prior art keywords
- concrete
- additive
- crack
- mortar
- concrete mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了混凝土砂浆抗裂外加剂及其制备方法和使用，本外加剂通过在常用的丁腈乳胶(增韧剂)中加入丙烯酸进行共聚，主链中引入羧基活化基团，能够改善混凝土中砂浆的抗渗性和疏水性。且支链上加入羧基和腈基，可调节砂浆的保水能力。应用于水泥基人造石方料成型中，适用于批荡、涂层、堵漏、界面和粘贴，可解决砂浆混凝土水化过程产生的放热，消除应力所产生的裂缝，从而达到方料的利用率，降低方料在制造过程的损耗。
Description
技术领域
本发明涉及混凝土外加剂领域，具体涉及一种混凝土砂浆抗裂外加剂。
背景技术
普通混凝土是由水泥作胶凝材料，砂、石作集料，与水(加或不加外加剂和掺合料)按一定比例配合，经搅拌、成型、养护、硬化而得的具有一定结构强度的结构或者构件。水泥是混凝土的主要成分，决定着混凝土的基本性质，混凝土外加剂则可弥补和改善混凝土性能方面的不足，赋予某些新的性能，是砂浆混凝土的重要组成部分。砂浆混凝土在硅酸盐水化固结时，由于剧烈的放热所产生的应力、微膨胀和伸缩，导致砂浆混凝土出现应力缝。
混凝土外加剂奠定了现代混凝土技术的基础，成为混凝土不可或缺的重要组成之一。外加剂则有减水剂、缓凝剂、防冻剂、引气剂和防锈剂等，目前品种多样、功能各异的外加剂的广泛应用，有效地改善了混凝土的工作性能、力学性能和耐久性能，由于有了高效减水剂，大流动度混凝土、自密实混凝土、高强混凝土得到应用；由于有了增稠剂，使混凝土抗离析性和保水性增强，水下混凝土的性能得以改善；由于有了缓凝剂，水泥的凝结时间得以延长，才有可能减少坍落度损失，延长施工操作时间；混凝土添加某些具有抗裂功能的外加剂则能改善混凝土的抗裂性能。
发明内容
本发明提出了一种外加剂应用于水泥基人造石方料成型中，解决砂浆混凝土水化过程产生的放热的问题，消除应力所产生的裂缝，从而达到方料的利用率，降低方料在制造过程的损耗。
为了实现上述目的，本发明是通过以下技术方案来实现的：
一种混凝土砂浆抗裂外加剂，分子式为：
优选的，所述n为≥1的自然数。
优选的，所述n为5-20的自然数。
混凝土砂浆抗裂外加剂的制备方法为：将丙烯酸和丁腈乳液在35-60℃温度下搅拌混合并充分反应，得到外加剂。
上述所述丙烯酸和丁腈乳液在35-40℃温度。
混凝土砂浆抗裂外加剂的使用为，适用于批荡、涂层、堵漏、界面和粘贴。
上述所述用于批荡时，外加剂与砂浆的重量比为1：(9-10)。
上述所述砂浆的为水泥和沙的混合物，且所述水泥和沙的重量比为1:2。
上述所述用于涂层时，外加剂与水泥的重量比为1：2。
本发明混凝土砂浆抗裂外加剂及其制备方法和使用，其有益效果在于：
(1)本外加剂通过在常用的丁腈乳胶(增韧剂)中加入丙烯酸进行共聚，主链中引入羧基活化基团，能够改善混凝土中砂浆的抗渗性和疏水性。且支链上加入羧基和腈基，可调节砂浆的保水能力。
(2)应用于水泥基人造石方料成型中，可解决砂浆混凝土水化过程产生的放热，消除应力所产生的裂缝，从而达到方料的利用率，降低方料在制造过程的损耗。
(3)粘接力强，渗透力强，抗拉强度高，延伸性好，和易性好、隔潮、抗老化，抗紫外线、耐酸碱，耐盐，耐温变。无毒，无味，无有害挥发物，无污染，无腐蚀。不燃烧，不爆炸。
具体实施方式
下面结合具体实施例来进一步详细说明本发明。
实施例1
一种混凝土砂浆抗裂外加剂，分子式为：
n为5-20的自然数。
混凝土砂浆抗裂外加剂的制备方法为，将丙烯酸和丁腈乳液在50-60℃温度下搅拌混合并充分反应，得到外加剂。
混凝土砂浆抗裂外加剂适用于批荡、涂层、堵漏、界面和粘贴，用于批荡时，外加剂与砂浆(水泥和沙的重量比为1:2)的重量比为1：10。
用于涂层时，外加剂与水泥的重量比为1：2。
实施例2
混凝土砂浆抗裂外加剂的制备方法为，将丙烯酸和丁腈乳液在35-40℃温度下搅拌混合并充分反应，得到外加剂。
混凝土砂浆抗裂外加剂适用于批荡、涂层、堵漏、界面和粘贴，用于批荡时，外加剂与砂浆(水泥和沙的重量比为1:2)的重量比为1：9。
用于涂层时，外加剂与水泥的重量比为1：2。
实施例3
混凝土砂浆抗裂外加剂的制备方法为，将丙烯酸和丁腈乳液在35-40℃温度下搅拌混合并充分反应，得到外加剂。
混凝土砂浆抗裂外加剂适用于批荡、涂层、堵漏、界面和粘贴，用于批荡时，外加剂与砂浆(水泥和沙的重量比为1:2)的重量比为1：9。
用于涂层时，外加剂与水泥的重量比为1：2。
实施例4
外加剂的操作方法为：
1、先将基面用水清洗干净。
2、涂层：刷一遍之后，待不粘手即可刷第二遍(总厚度不超过2mm)。
3、批荡：批一遍之后，待压指不粘即可批第二遍(总厚度不超过2cm)。
4、注意事项：水泥为普硅325#(含)以上。初凝为45分钟；终凝为10小时。保质期12个月，存储温度不低于摄氏0°。
以上对本发明实施例所提供的技术方案进行了详细介绍，本文中应用了具体个例对本发明实施例的原理以及实施方式进行了阐述，以上实施例的说明只适用于帮助理解本发明实施例的原理；同时，对于本领域的一般技术人员，依据本发明实施例，在具体实施方式以及应用范围上均会有改变之处，综上所述，本说明书内容不应理解为对本发明的限制。
Claims (9)
1.一种混凝土砂浆抗裂外加剂，其特征在于：分子式为：
2.根据权利要求1所述混凝土砂浆抗裂外加剂，其特征在于：所述n为≥1的自然数。
3.根据权利要求2所述混凝土砂浆抗裂外加剂，其特征在于：所述n为5-20的自然数。
4.一种根据权利要求1所述的混凝土砂浆抗裂外加剂的制备方法，其特征在于：将丙烯酸和丁腈乳液在35-60℃温度下搅拌混合并充分反应，得到外加剂。
5.根据权利要求4所述混凝土砂浆抗裂外加剂，其特征在于：所述丙烯酸和丁腈乳液在35-40℃温度。
6.一种根据权利要求1所述的混凝土砂浆抗裂外加剂的使用，其特征在于：适用于批荡、涂层、堵漏、界面和粘贴。
7.根据权利要求6所述混凝土砂浆抗裂外加剂的使用，其特征在于：所述用于批荡时，外加剂与砂浆的重量比为1：(9-10)。
8.根据权利要求7所述混凝土砂浆抗裂外加剂的使用，其特征在于：所述砂浆的为水泥和沙的混合物，且所述水泥和沙的重量比为1:2。
9.根据权利要求6所述混凝土砂浆抗裂外加剂的使用，其特征在于：所述用于涂层时，外加剂与水泥的重量比为1：2。