CN109986673A - A kind of tossa 3E coconut palm plate and preparation method thereof - Google Patents
A kind of tossa 3E coconut palm plate and preparation method thereof Download PDFInfo
- Publication number
- CN109986673A CN109986673A CN201910296207.0A CN201910296207A CN109986673A CN 109986673 A CN109986673 A CN 109986673A CN 201910296207 A CN201910296207 A CN 201910296207A CN 109986673 A CN109986673 A CN 109986673A
- Authority
- CN
- China
- Prior art keywords
- tossa
- monofilament
- coconut palm
- hot melting
- melting wool
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of tossa 3E coconut palm plates and preparation method thereof, including blanket, tossa 10-20%, monofilament 55% and hot melting wool 25%-35%, beneficial effects of the present invention: present invention process step is rigorously orderly, hot melting wool compression moulding is added after the material of traditional coconut palm monofilament bed board configures certain proportion jute, only not traditional coconut palm monofilament bed board provides moisture-proof, outside insect prevention and the function of eliminating the unusual smell, it ensure that the toughness of its script, pliability is moderate simultaneously, comfort level when using user improves, also has the advantages that low cost, coconut palm monofilament bed board is set to have Arenga engleri Beccari silk bed board costly insect-free, the advantages of free from extraneous odour, avoid the growth of bed board bacterium, it is more environmentally protective.
Description
Technical field
The present invention relates to coconut palm plate technical field, specially a kind of tossa 3E coconut palm plate and preparation method thereof.
Background technique
The more materials of mattress at present on the market are single, and bed board hardness made of only being suppressed as monofilament is big, irritant smell,
Comfort is poor, while breeding and being easy mouldy ask using skin disease, acarid caused by being easy to produce because of humidity for a long time
Topic generates threat to the health of user, and carries out coconut palm monofilament and the polyester fiber to merge mattress made of compacting on the market more
Not after debugging because of ratio, the mattress produced is not soft or hard still moderate, not only results in discomfort when user uses, or even meeting
So that its original durable advantage of coconut palm monofilament material is disappeared, causes the bed board produced more existing in the case where more expending working hour
Without substantial advance for technology, hence it is evident that without benefit, desocialization needs.
Summary of the invention
The object of the invention is that providing a kind of jute 3E coconut palm plate and preparation method thereof to solve the above-mentioned problems.
To solve the above-mentioned problems, the present invention provides a kind of technical solutions:
A kind of tossa 3E coconut palm plate and preparation method thereof, including blanket, tossa 10-20%, monofilament 55% and hot melt
Cotton 25%-35%.
Preferably, being thoroughly mixed between the tossa and hot melting wool by industrial mixer.
Preferably, the polyester fiber material that the hot melting wool uses heat to melt.
Preferably, the monofilament uses coconut palm monofilament material.
Preferably, the following steps are included:
A. stir: tossa, monofilament and hot melting wool respectively with certain proportion addition blender, allow tossa, monofilament with
And it is stirred between hot melting wool；
B. be laminated: the mixture thickness of tossa, monofilament and hot melting wool is uniformly layered in conveyer belt blanket by carding machine
On, specified thickness is laminated to again in one layer of blanket of mixture upper cover；
C. dry: conveyer belt, which is sent to mixture oven and toast, melts hot melting wool, bonds monofilament and tossa, and
Mixture degreasing, desugar and de-oiling are sterilized；
D. it is compacted: mixture being compacted with press before mixture oven out.
Preferably, hot melting wool polyester as made of organic dibasic acid and dihydric alcohol polycondensation in the step a is through spinning
Resulting synthetic fibers.
Preferably, oven temperature will control between 170 DEG C -185 DEG C in the step c, baking time is 5-8 points
Clock.
Preferably, the ratio of tossa, monofilament and hot melting wool is respectively 10-20%, 55%, 25%- in the step a
35%。
Beneficial effects of the present invention: present invention process step is rigorously orderly, configures in the material of traditional coconut palm monofilament bed board
Hot melting wool compression moulding is added after certain proportion jute, is not only that traditional coconut palm monofilament bed board provides moisture-proof, insect prevention and except different
Outside the function of taste, the toughness of its script ensure that, while pliability is moderate, comfort level when using user improves, and also has
There is the advantages of low cost, so that coconut palm monofilament bed board is had the advantages that Arenga engleri Beccari silk bed board costly is insect-free, free from extraneous odour, avoid
The growth of bed board bacterium, it is more environmentally protective.
Specific embodiment:
Embodiment 1:
A kind of tossa 3E coconut palm plate and preparation method thereof, including blanket, tossa 10%, monofilament 55% and hot melting wool
35%。
Wherein, it is thoroughly mixed between the tossa and hot melting wool by industrial mixer, optimizes overall structure.
Wherein, the polyester fiber material that the hot melting wool uses heat to melt, conveniently mixes tossa and monofilament.
Wherein, the monofilament uses coconut palm monofilament material, economical and practical, low cost.
Wherein, comprising the following steps:
A. stir: tossa, monofilament and hot melting wool respectively with certain proportion addition blender, allow tossa, monofilament with
And it is stirred between hot melting wool；
B. be laminated: the mixture thickness of tossa, monofilament and hot melting wool is uniformly layered in conveyer belt blanket by carding machine
On, specified thickness is laminated to again in one layer of blanket of mixture upper cover；
C. dry: conveyer belt, which is sent to mixture oven and toast, melts hot melting wool, bonds monofilament and tossa, and
Mixture degreasing, desugar and de-oiling are sterilized；
D. it is compacted: mixture being compacted with press before mixture oven out.
Wherein, hot melting wool polyester as made of organic dibasic acid and dihydric alcohol polycondensation in the step a is through obtained by spinning
Synthetic fibers.
Wherein, oven temperature will control between 170 DEG C -185 DEG C in the step c, and baking time is 5-8 minutes.
Wherein, the ratio of tossa, monofilament and hot melting wool is respectively 10%, 55%, 35% in the step a.
| Material | Tossa | Monofilament | Hot melting wool |
| Ratio | 10% | 55% | 35% |
Embodiment 2:
A kind of tossa 3E coconut palm plate and preparation method thereof, including blanket, tossa 15%, monofilament 55% and hot melting wool
30%。
Wherein, it is thoroughly mixed between the tossa and hot melting wool by industrial mixer, optimizes overall structure.
Wherein, the polyester fiber material that the hot melting wool uses heat to melt, conveniently mixes tossa and monofilament.
Wherein, the monofilament uses coconut palm monofilament material, economical and practical, low cost.
Wherein, comprising the following steps:
A. stir: tossa, monofilament and hot melting wool respectively with certain proportion addition blender, allow tossa, monofilament with
And it is stirred between hot melting wool；
B. be laminated: the mixture thickness of tossa, monofilament and hot melting wool is uniformly layered in conveyer belt blanket by carding machine
On, specified thickness is laminated to again in one layer of blanket of mixture upper cover；
C. dry: conveyer belt, which is sent to mixture oven and toast, melts hot melting wool, bonds monofilament and tossa, and
Mixture degreasing, desugar and de-oiling are sterilized；
D. it is compacted: mixture being compacted with press before mixture oven out.
Wherein, hot melting wool polyester as made of organic dibasic acid and dihydric alcohol polycondensation in the step a is through obtained by spinning
Synthetic fibers.
Wherein, oven temperature will control between 170 DEG C -185 DEG C in the step c, and baking time is 5-8 minutes.
Wherein, the ratio of tossa, monofilament and hot melting wool is respectively 15%, 55%, 30% in the step a.
| Material | Tossa | Monofilament | Hot melting wool |
| Ratio | 15% | 55% | 30% |
Embodiment 3:
A kind of tossa 3E coconut palm plate and preparation method thereof, including blanket, tossa 20%, monofilament 55% and hot melting wool
25%。
Wherein, it is thoroughly mixed between the tossa and hot melting wool by industrial mixer, optimizes overall structure.
Wherein, the polyester fiber material that the hot melting wool uses heat to melt, conveniently mixes tossa and monofilament.
Wherein, the monofilament uses coconut palm monofilament material, economical and practical, low cost.
Wherein, comprising the following steps:
A. stir: tossa, monofilament and hot melting wool respectively with certain proportion addition blender, allow tossa, monofilament with
And it is stirred between hot melting wool；
B. be laminated: the mixture thickness of tossa, monofilament and hot melting wool is uniformly layered in conveyer belt blanket by carding machine
On, specified thickness is laminated to again in one layer of blanket of mixture upper cover；
C. dry: conveyer belt, which is sent to mixture oven and toast, melts hot melting wool, bonds monofilament and tossa, and
Mixture degreasing, desugar and de-oiling are sterilized；
D. it is compacted: mixture being compacted with press before mixture oven out.
Wherein, hot melting wool polyester as made of organic dibasic acid and dihydric alcohol polycondensation in the step a is through obtained by spinning
Synthetic fibers.
Wherein, oven temperature will control between 170 DEG C -185 DEG C in the step c, and baking time is 5-8 minutes.
Wherein, the ratio of tossa, monofilament and hot melting wool is respectively 20%, 55%, 25% in the step a.
| Material | Tossa | Monofilament | Hot melting wool |
| Ratio | 20% | 55% | 25% |
Beneficial effects of the present invention: present invention process step is rigorously orderly, certain in the material configuration of traditional coconut palm monofilament bed board
Hot melting wool compression moulding is added after ratio jute, is not only that traditional coconut palm monofilament bed board provides moisture-proof, insect prevention and eliminates the unusual smell
Outside function, the toughness of its script ensure that, while pliability is moderate, comfort level when using user improves, and also has and makes
The low advantage of valence makes coconut palm monofilament bed board have the advantages that Arenga engleri Beccari silk bed board costly is insect-free, free from extraneous odour, avoids bed board
The growth of bacterium, it is more environmentally protective.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention, the technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention, the claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (8)
1. a kind of tossa 3E coconut palm plate and preparation method thereof, which is characterized in that including blanket, tossa 10-20%, palm fibre
55% and hot melting wool 25%-35% of silk.
2. a kind of tossa 3E coconut palm plate according to claim 1, it is characterised in that: the tossa and hot melting wool
Between be thoroughly mixed by industrial mixer.
3. a kind of tossa 3E coconut palm plate according to claim 1, it is characterised in that: the hot melting wool is melted using heat
The polyester fiber material of change.
4. a kind of tossa 3E coconut palm plate according to claim 1, it is characterised in that: the monofilament uses coconut palm monofilament material
Matter.
5. a kind of tossa 3E coconut palm plate production method according to claim 1, which is characterized in that including following step
It is rapid:
A. stir: tossa, monofilament and hot melting wool respectively with certain proportion addition blender, allow tossa, monofilament with
And it is stirred between hot melting wool；
B. be laminated: the mixture thickness of tossa, monofilament and hot melting wool is uniformly layered in conveyer belt blanket by carding machine
On, specified thickness is laminated to again in one layer of blanket of mixture upper cover；
C. dry: conveyer belt, which is sent to mixture oven and toast, melts hot melting wool, bonds monofilament and tossa, and
Mixture degreasing, desugar and de-oiling are sterilized；
D. it is compacted: mixture being compacted with press before mixture oven out.
6. a kind of tossa 3E coconut palm plate production method according to claim 1, which is characterized in that in the step a
Hot melting wool polyester as made of organic dibasic acid and dihydric alcohol polycondensation through the resulting synthetic fibers of spinning.
7. a kind of tossa 3E coconut palm plate production method according to claim 1, which is characterized in that in the step c
Oven temperature will control between 170 DEG C -185 DEG C, and baking time is 5-8 minutes.
8. a kind of tossa 3E coconut palm plate production method according to claim 1, which is characterized in that in the step a
The ratio of tossa, monofilament and hot melting wool is respectively 10-20%, 55%, 25%-35%.