CN109929954A - 化渣消泡剂 - Google Patents
化渣消泡剂 Download PDFInfo
- Publication number
- CN109929954A CN109929954A CN201711356024.0A CN201711356024A CN109929954A CN 109929954 A CN109929954 A CN 109929954A CN 201711356024 A CN201711356024 A CN 201711356024A CN 109929954 A CN109929954 A CN 109929954A
- Authority
- CN
- China
- Prior art keywords
- parts
- defoaming agent
- slugging
- best number
- wollastonite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明涉及消泡剂技术领域,尤其是一种化渣消泡剂。一种化渣消泡剂,按照重量份数包括:萤石,5‑8份;工业碱,2‑7份;硅灰石,40‑50份;水泥,10‑15份;焦炭,2‑5份;碘化钾,1‑4份。这种化渣消泡剂在使用的时候,能够满足使用需求。
Description
技术领域
本发明涉及消泡剂技术领域,尤其是一种化渣消泡剂。
背景技术
高炉出铁不可避免的产生大量铁渣并起泡,这些铁渣固有的物理性质决定了它非常容易粘结沉积在沉铁式铁水沟壁、铁水罐、鱼雷罐内,加大工人的劳动强度,降低设备利用率,严重影响生产和铁水质量。
发明内容
为了克服现有的消泡剂存在的不足,本发明提供了一种化渣消泡剂。
本发明解决其技术问题所采用的技术方案是:一种化渣消泡剂,按照重量份数包括:
萤石,5-8份;
工业碱,2-7份;
硅灰石,40-50份;
水泥,10-15份;
焦炭,2-5份;
碘化钾,1-4份。
根据本发明的另一个实施例,进一步包括,萤石最佳份数为6份。
根据本发明的另一个实施例,进一步包括,工业碱最佳份数为4份。
根据本发明的另一个实施例,进一步包括,硅灰石最佳份数为45份。
根据本发明的另一个实施例,进一步包括,水泥最佳份数为12份。
根据本发明的另一个实施例,进一步包括,焦炭最佳份数为3份。
根据本发明的另一个实施例,进一步包括,碘化钾最佳份数为3份。
本发明的有益效果是,这种化渣消泡剂在使用的时候,能够满足使用需求。
具体实施方式
一种化渣消泡剂,按照重量份数包括:
萤石,5-8份;
工业碱,2-7份;
硅灰石,40-50份;
水泥,10-15份;
焦炭,2-5份;
碘化钾,1-4份。
根据本发明的另一个实施例,进一步包括,萤石最佳份数为6份。
根据本发明的另一个实施例,进一步包括,工业碱最佳份数为4份。
根据本发明的另一个实施例,进一步包括,硅灰石最佳份数为45份。
根据本发明的另一个实施例,进一步包括,水泥最佳份数为12份。
根据本发明的另一个实施例,进一步包括,焦炭最佳份数为3份。
根据本发明的另一个实施例,进一步包括,碘化钾最佳份数为3份。
本发明的实施例一:
一种化渣消泡剂,按照重量份数包括:
萤石, 8份;
工业碱, 7份;
硅灰石, 50份;
水泥, 15份;
焦炭, 5份;
碘化钾, 4份。
本发明的实施例二:
一种化渣消泡剂,按照重量份数包括:
萤石,5份;
工业碱,2份;
硅灰石,40份;
水泥,10份;
焦炭,2份;
碘化钾,1份。
本发明的实施例三:
一种化渣消泡剂,按照重量份数包括:
萤石,6份;
工业碱,3份;
硅灰石,42份;
水泥,12份;
焦炭,3份;
碘化钾,2份。
本发明的实施例四:
一种化渣消泡剂,按照重量份数包括:
萤石,7份;
工业碱,6份;
硅灰石,48份;
水泥,14份;
焦炭,4份;
碘化钾,3份。
以上说明对本发明而言只是说明性的,而非限制性的,本领域普通技术人员理解,在不脱离所附权利要求所限定的精神和范围的情况下,可做出许多修改、变化或等效,但都将落入本发明的保护范围内。
Claims (7)
1.一种化渣消泡剂,其特征是,按照重量份数包括:
萤石,5-8份;
工业碱,2-7份;
硅灰石,40-50份;
水泥,10-15份;
焦炭,2-5份;
碘化钾,1-4份。
2.根据权利要求1所述的化渣消泡剂,其特征是,萤石最佳份数为6份。
3.根据权利要求1所述的化渣消泡剂,其特征是,工业碱最佳份数为4份。
4.根据权利要求1所述的化渣消泡剂,其特征是,硅灰石最佳份数为45份。
5.根据权利要求1所述的化渣消泡剂,其特征是,水泥最佳份数为12份。
6.根据权利要求1所述的化渣消泡剂,其特征是,焦炭最佳份数为3份。
7.根据权利要求1所述的化渣消泡剂,其特征是,碘化钾最佳份数为3份。