CN109929353A - 一种会议室用信号干扰涂料及其制备方法 - Google Patents
一种会议室用信号干扰涂料及其制备方法 Download PDFInfo
- Publication number
- CN109929353A CN109929353A CN201910301220.0A CN201910301220A CN109929353A CN 109929353 A CN109929353 A CN 109929353A CN 201910301220 A CN201910301220 A CN 201910301220A CN 109929353 A CN109929353 A CN 109929353A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- thickener
- signal interference
- meeting room
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种会议室用信号干扰涂料及其制备方法，由以下重量份数的各原料制备而成：丙烯酸合成树脂30～35份、水18～22份、偶联剂0.4～0.5份、分散剂0.6～0.8份、乙二醇2～2.5份、十六碳双酯2.5～3份、十二碳醇酯10～15份、二氧化钛粉体12～15份、氧化铝粉体8～12份、导电金属氧化物粉体10～13份、石墨烯粉体4～6份、增稠剂0.3～0.4份、有机硅消泡剂0.4～0.6份、乙基纤维素0.3～0.4份、PH调节剂0.1～0.15份、卡松杀菌剂0.15～0.2份、B@T剂0.2～0.25份，具备信号屏蔽功能。
Description
技术领域
本发明涉及涂料技术领域，尤其涉及一种信号干扰涂料。
背景技术
信息时代，通信技术高速成发展，移动通讯工具已成为人们日常工作和生活不可缺少的重要工具。随着移动移动通讯工具的广泛应用，也产生了一些不容忽视的问题：例如通常情况下，开会时应保持一定的严肃气氛、但有时因为与会人员的手机在会议期间，由于忘记将手机转为静音，手机突然响起，一是给自己招来尴尬，二是给会场秩序带来不必要的干扰。特别是有部分人员的手机更是自制了搞笑或者搞怪的铃声，这种情况容易打断会议进程，甚至让会议出现跑题现象。一些大型会议上，与会者往往都是属于外单位的有级别有身份的人物，他们往往会因自己的工作或个人事务不原意在开会期间关闭手机，但又不会自觉的将自己的手机调至静音，结果导致开会时手机来电声此起彼伏，不注意的人甚至直接接打手机，稍加注意的会掐断来电但又因来电而放心不心，遂起身至会场外回拔电话。如此一来，会场进进出出、喧哗不断，会场秩序难以维持；因此如何有效防止会议室上手机滥用的情形，保护会场秩序，使得正常的会议在安静、严肃的中继续成为需要解决的难题。
发明内容
本发明的目的是解决现有会议室中容易受到手机干扰的问题，提供一种会议室用信号干扰涂料，具备信号屏蔽功能。
为了实现以上目的，本发明采用的技术方案是：一种会议室用信号干扰涂料，由以下重量份数的各原料制备而成：丙烯酸合成树脂35～40份、水18～22份、偶联剂0.4～0.5份、分散剂0.6～0.8份、乙二醇2～2.5份、十六碳双酯2.5～3份、十二碳醇酯10～15份、二氧化钛粉体12～15份、氧化铝粉体8～12份、导电金属氧化物粉体10～13份、石墨烯粉体4～6份、闭合性增稠剂0.3～0.4份、有机硅消泡剂0.4～0.6份、乙基纤维素0.3～0.4份、PH调节剂0.1～0.15份、卡松杀菌剂0.15～0.2份、耐高温抑菌BIT剂0.2～0.25份。
为了进一步优化本发明，可优选以下技术方案：
优选的，由以下重量份数的各原料制备而成：丙烯酸合成树脂38份、水20份、偶联剂0.5份、分散剂0.7份、乙二醇2份、十六碳双酯3份、十二碳醇酯12份、二氧化钛粉体13份、氧化铝粉体10份、导电金属氧化物粉体12份、石墨烯粉体6份、闭合性增稠剂0.4份、有机硅消泡剂0.5份、乙基纤维素0.4份、PH调节剂0.15份、卡松杀菌剂0.15份、耐高温抑菌BIT剂0.2份。
优选的，所述偶联剂采用钛酸酯偶联剂、铝酸酯偶联剂、锆酸酯偶联剂中的一种或者它们的混合物。
优选的，所述分散剂采用导电炭黑分散剂。
优选的，所述二氧化钛采用改性包裹处理后的导电二氧化钛。
优选的，所述导电金属氧化物粉体采用掺锑二氧化锡粉体、掺铝氧化锌粉体或掺铟氧化锡粉体中的一种。
优选的，所述导电金属氧化物粉体采用掺锑二氧化锡粉体。
优选的，所述闭合性增稠剂采用纤维素增稠剂、聚氨酯增稠剂、聚丙烯酸酯增稠剂中的一种或者它们的混合物。
一种会议室用信号干扰涂料的制备方法，包括以下步骤：
步骤一：在高速分散机中依次加入水、偶联剂、分散剂、乙二醇、十六碳双酯在转速为500r/min的条件下，搅拌2～5分钟；
步骤二：在步骤一中制得的原料中依次加入十二碳醇酯、二氧化钛粉体、氧化铝粉体、掺锑二氧化锡、石墨烯粉体、闭合性增稠剂、有机硅消泡剂，提高高速分散机转速至700r/min的条件下，搅拌3～6分钟；
步骤三：在步骤二中制得的原料中依次加入乙基纤维素、PH调节剂，提高高速分散机转速至1500r/min的条件下，分散10～25分钟，直至涂料粒径达到50um以下；
步骤四：在步骤三中制得的原料中加入丙烯酸合成树脂，保持高速分散机转速在1500r/min的条件下，分散直至涂料粒径达到40～50um；
步骤五：在步骤四中制得的原料降温至50℃以下后中加入卡松杀菌剂、耐高温抑菌BIT剂制成成品涂料，灌装存储。
本发明的有益效果是：
本发明的会议室用信号屏蔽涂料采用959w丙烯酸乳液采用细粒径金属离子熬合技术搭配氧化物粉体、填充导电石墨烯形成更致密的导电涂膜，利用静电屏蔽的原理使其内部形成封闭的信号屏蔽腔室，可有效的降低开会期间、电话干扰的情况，保证会议的有序进行；本发明的涂料原料采用粉体氧化物填充粉料石墨烯、氧化铝等，因而无释放性挥发物；同时959w丙烯酸乳液属于环保型物质低于VOC<2水性树脂，低于国家检查线，安全环保、配比科学合理，各原料间的相容性较好，体系稳定性好、有利于长期储存。
具体实施方式
在本发明的描述中，还需要说明的是，除非另有明确的规定和限定，术语“设置”、“安装”、“相连”、“连接”应做广义理解，例如，可以是固定连接，也可以是可拆卸连接，或一体地连接；可以是机械连接，也可以是电连接；可以是直接相连，也可以通过中间媒介间接相连，可以是两个元件内部的连通。对于本领域的普通技术人员而言，可以具体情况理解上述术语在本发明中的具体含义。
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
导电材料是一种新型功能材料，已被广泛应用于电子、航空航天、通信、印刷、包装等领域。目前导电粉体主要以填料为主要应用形式，使基体材料具有导电性、抗静电、屏蔽电磁波等功能。导电材料根据化学成分的不同可以分为碳系、金属系、金属氧化物系、结构高分子系以及复合型等五类；根据导电材料功能不同，又可分为防静电材料、导电材料、电极材料、发热体材料、电磁波屏蔽材料。
1、碳系导电材料
碳系导电材料包括导电炭黑、石墨、碳纤维等，具有导电性好、着色力强、化学稳定性高、密度小、价格低廉等特点，以其制备的导电油墨、导电胶等广泛应用于电子、化工等领域。碳系导电材料存在的不足主要是分散稳定性差、颜色深，因此，实际应用中受到一定的限制。目前，碳纳米管材料、石墨烯等新材料，已被探索作为新型的碳系导电材料使用，石墨烯就是一种神奇的材料，只要添加一点进入其它材料就有可能产生神奇的效果，不愧为材料界的“超级材料”。石墨烯不仅“最薄、最强”，作为热导体，它比目前任何其它材料的导热效果都好。利用石墨烯，科学家能够研发一系列具有特殊性能的新材料。因为它的电阻率极低，电子迁移的速度极快，因此被期待可用来发展出更薄、导电速度更快的芯片，取代硅材料。由于石墨烯实质上是一种透明、良好的导体，也适合用来制造透明触控屏幕、光板，甚至是太阳能电池。超级电容和芯片，是全世界研究石墨烯的重点领域，也是未来石墨烯革命的决胜点。石墨烯的应用必然是一个由低端向高端延伸的过程。利用石墨烯的导电导热性的低端应用这两三年内将会崛起，而应用于光电转换的电池以及代替硅材料的芯片领域，仍需要较长的时间。”
2、金属系导电材料
金属系导电材料主要包括银系、铜系、镍系等导电材料，具有良好的导电性和延展性，颜色相对较浅，因此，应用较为广泛。其中，以银系导电材料的导电性能最佳，抗氧化能力最强，但价格高昂，使用过程中容易发生银离子迁移造成短路；镍和铜价格较金属银便宜很多，但这两种材料制备成粉体后，容易发生氧化反应，造成电阻的急剧上升，影响导电性能，用有机磷化合物、偶联剂、杂环类化合物或羰基化技术等处理可以提高其抗氧化能力，但相对较高的使用成本，并且限制其在应用领域。
3、金属氧化物系导电材料
金属氧化物系导电材料以其熔点高、抗氧化能力强、价格适中等优点，受到下游应用企业的喜爱。目前比较常见的导电金属氧化物有掺锑二氧化锡（ATO）、掺铝氧化锌（ZAO）、掺铟氧化锡（ITO）。
（1）掺锑二氧化锡（ATO）；掺杂了锑的二氧化锡（简称ATO）的导电性明显提高，且具有颜色浅、稳定性好等优良特性。在一定的锑掺杂量范围内，掺锑量越多，导电性能越好，但粉体颜色越深。目前，现有技术采用的是用少量锑均匀地掺杂于二氧化锡的粉体中，能够克服了粉体颜色深的问题，同时保证导电性能。
（2）掺铝氧化锌（ZAO）；掺铝氧化锌（ZAO）是氧化锌与氧化铝形成的置换型固溶体。掺铝氧化锌（ZAO）不仅紫外线吸收性能好、化学稳定性高，而且具有颜色浅、可见光透过率高、导电性好等优良特性，可以广泛应用在抗静电涂料、橡胶和塑料等领域，有取代导电性好但价格昂贵的 ITO材料的趋势。
（3）掺铟氧化锡（ITO）
掺铟氧化锡（ITO）具有低电阻率、高可见光透射率等性能优势。掺铟氧化锡可以切断对人体有害的电子辐射、紫外线及远红外线，被广泛应用于各种平板显示器、传感器、气敏 元件之中。
4、结构型导电高分子材料
结构型导电高分子材料又称为本征型导电高分子材料，与传统的复合导电高分子材料相比具有质轻、环境稳定性好、结构可设计、电导率可调、可弥补金属填料的缺陷等特点，同时还具有抗静电、电磁屏蔽或吸收电磁波以及电致发光、光致变色和能发生非线性光学效应等不同特征。在诸多领域都有着潜在的应用价值，如在导电、防腐、电磁干扰屏蔽、芯片制造、微电子、液晶显示器等领域得到了应用。
5、复合型导电材料
随着信息工业的发展，对于具有导电功能的复合材料的需求越来越迫切。复合导电材料是采用导电材料与成型材料填充复合。
偶联剂是一类具有两不同性质官能团的物质，其分子结构的最大特点是分子中含有化学性质不同的两个基团，一个是亲无机物的基团，易与无机物表面起化学反应；另一个是亲有机物的基团，能与合成树脂或其它聚合物发生化学反应或生成氢键溶于其中。因此偶联剂被称作“分子桥”，用以改善无机物与有机物之间的界面作用，从而大大提高复合材料的性能，如物理性能、电性能、热性能、光性能等。偶联剂用于橡胶工业中，可提高轮胎、胶板、胶管、胶鞋等产品的耐磨性和耐老化性能，并且能减小NR用量，从而降低成本。偶联剂在复合材料中的作用在于它既能与增强材料表面的某些基团反应，又能与基体树脂反应，在增强材料与树脂基体之间形成一个界面层，界面层能传递应力，从而增强了增强材料与树脂之间粘合强度，提高了复合材料的性能，同时还可以防止其它介质向界面渗透，改善界面状态，有利于制品的耐老化、耐应力及电绝缘性能。
二氧化钛又称钛白，是自然界白度较高的基础无机颜料。二氧化钛经过表面化学改性以后可以成为具有导电性能的钛白粉，这样使二氧化钛既能保持颜料特性又具备了导电性能，导电二氧化钛可以用于塑料、橡胶、纤维等材料的抗静电剂、电磁屏蔽涂层或表面发热体；二氧化钛本身不导电，它之所以成为导电粉，是因为在其颗粒表面包裹了一层掺锑的二氧化锡导电膜，根据二氧化钛超细粉体的导电机理，要制得性能较好的二氧化钛导电粉体，首先要使Sn4+和Sb3+在水解过程中共沉淀，均匀地沉积在二氧化钛超细粉颗粒表面成膜；其次，将已经表面成膜的二氧化钛在一定温度下煅烧，使Sb3+成为Sb5+，取代Sn4+形成缺陷固溶体，由Sb5+提供载流子。
卡松是由两种活性组分：2-甲基-4-异噻唑啉-3-酮（MIT）和5-氯-2-甲基-4-异噻唑啉-3-酮（CMIT）组成的混合物，是一种高效的广谱抑菌剂。卡松具有很强的生物活性，既能抑菌，又能杀菌，可以解决因菌类感染而引起的产品发酵、发霉、变质、细菌超标等问题，而且由于其对粘液有穿透作用，不仅能应用于化妆品、洗涤剂，还可用于工业杀菌环水、机床冷却液、油漆等，是用途极为广泛的一类环保型“绿色产品”杀菌剂，是一种值得大力开发的产品、具有较高的附加值。异噻唑啉酮类化合物是一种新型、广谱、高效的非氧化性杀菌剂，是目前性价比最具优势的防腐杀菌剂之一，其对酵母菌、真菌、革兰氏菌、异氧菌、藻类等具有较好的抑制效果，目前广泛应用于纺织、造纸、炼油、化妆品、清洗剂及油田注水、污水处理等领域的杀菌防腐处理。
乙二醇能将涂料中的成膜物质溶解或分散为均匀的液态，以便于施工成膜，当施工后又能从漆膜中挥发至大气的物质，原则上溶剂不构成涂膜，也不应存留在涂膜中。
实施例1
一种会议室用信号干扰涂料，由以下重量份数的各原料制备而成：丙烯酸合成树脂35g、水22g、偶联剂0.4g、导电炭黑分散剂0.6g、乙二醇2g、十六碳双酯2.5g、十二碳醇酯10g、二氧化钛粉体12g、氧化铝粉体8g、掺锑二氧化锡粉体10g、石墨烯粉体4g、闭合性增稠剂0.3g、有机硅消泡剂0.4g、乙基纤维素0.3g、amp95型号PH调节剂0.1g、卡松杀菌剂0.15g、耐高温抑菌BIT剂0.2g。其中偶联剂采用钛酸酯偶联剂、铝酸酯偶联剂、锆酸酯偶联剂中的任意一种或者它们的混合物；二氧化钛采用改性包裹处理后的导电二氧化钛；闭合性增稠剂采用纤维素闭合性增稠剂、聚氨酯闭合性增稠剂、聚丙烯酸酯闭合性增稠剂中的任意一种或者它们的混合物，丙烯酸合成树脂采用955W丙烯酸合成树脂。
实施例2
一种会议室用信号干扰涂料，由以下重量g数的各原料制备而成：丙烯酸合成树脂38g、水20g、偶联剂0.5g、导电炭黑分散剂0.7g、乙二醇2g、十六碳双酯3g、十二碳醇酯12g、二氧化钛粉体13g、氧化铝粉体10g、掺锑二氧化锡粉体12g、石墨烯粉体6g、闭合性增稠剂0.4g、有机硅消泡剂0.5g、乙基纤维素0.4g、amp95型号PH调节剂0.15g、卡松杀菌剂0.15g、耐高温抑菌BIT剂0.2g；其中偶联剂采用钛酸酯偶联剂、铝酸酯偶联剂、锆酸酯偶联剂中的任意一种或者它们的混合物；二氧化钛采用改性包裹处理后的导电二氧化钛；闭合性增稠剂采用纤维素闭合性增稠剂、聚氨酯闭合性增稠剂、聚丙烯酸酯闭合性增稠剂中的任意一种或者它们的混合物。
实施例3
一种会议室用信号干扰涂料，由以下重量g数的各原料制备而成：丙烯酸合成树脂39g、水19g、偶联剂0.5g、导电炭黑分散剂0.8g、乙二醇2.5g、十六碳双酯3g、十二碳醇酯15g、二氧化钛粉体13g、氧化铝粉体12g、掺锑二氧化锡粉体13g、石墨烯粉体5g、闭合性增稠剂0.4g、有机硅消泡剂0.5g、乙基纤维素0.4g、amp95型号PH调节剂0.1g、卡松杀菌剂0.2g、耐高温抑菌BIT剂0.25g；其中偶联剂采用钛酸酯偶联剂、铝酸酯偶联剂、锆酸酯偶联剂中的任意一种或者它们的混合物；二氧化钛采用改性包裹处理后的导电二氧化钛；闭合性增稠剂采用纤维素闭合性增稠剂、聚氨酯闭合性增稠剂、聚丙烯酸酯闭合性增稠剂中的任意一种或者它们的混合物。
实施例4
一种会议室用信号干扰涂料，由以下重量g数的各原料制备而成：丙烯酸合成树脂40g、水18g、偶联剂0.5g、导电炭黑分散剂0.8g、乙二醇2.5g、十六碳双酯3g、十二碳醇酯15g、二氧化钛粉体15g、氧化铝粉体12g、掺锑二氧化锡粉体13g、石墨烯粉体6g、闭合性增稠剂0.4g、有机硅消泡剂0.6g、乙基纤维素0.4g、amp95型号PH调节剂0.15g、卡松杀菌剂0.2g、耐高温抑菌BIT剂0.25g；其中偶联剂采用钛酸酯偶联剂、铝酸酯偶联剂、锆酸酯偶联剂中的任意一种或者它们的混合物；二氧化钛采用改性包裹处理后的导电二氧化钛；闭合性增稠剂采用纤维素闭合性增稠剂、聚氨酯闭合性增稠剂、聚丙烯酸酯闭合性增稠剂中的任意一种或者它们的混合物。
上述会议室用信号干扰涂料的制备方法，包括以下步骤：
步骤一：在高速分散机中依次加入水、偶联剂、分散剂、乙二醇、十六碳双酯在转速为500r/min的条件下，搅拌5分钟；
步骤二：在步骤一中制得的原料中依次加入十二碳醇酯、二氧化钛粉体、氧化铝粉体、掺锑二氧化锡、石墨烯粉体、闭合性增稠剂、有机硅消泡剂，提高高速分散机转速至700r/min的条件下，搅拌6分钟；
步骤三：在步骤二中制得的原料中依次加入乙基纤维素、PH调节剂，提高高速分散机转速至1500r/min的条件下，分散25分钟，直至涂料粒径达到50um以下；
步骤四：在步骤三中制得的原料中加入丙烯酸合成树脂，保持高速分散机转速在1500r/min的条件下，分散直至涂料粒径达到50um；
步骤五：在步骤四中制得的原料降温至50℃以下后中加入卡松杀菌剂、耐高温抑菌BIT剂制成成品涂料，灌装存储。
为了针对实施例中涂料的效果进行说明，分别在不同的实验条件下，观察信号干扰强度。实验1中采用信号干扰涂料涂覆在会议室墙面上，观察室内手机信号干扰强度；实验2中将信号干扰涂料搭配金属网，观察室内手机信号干扰强度；实验3中用金属板制成金属密闭室，观察室内手机信号干扰强度；实验4内采用普通涂料涂覆在会议室墙面上，观察观察室内手机信号干扰强度。
信号干扰实验数据表：
| 实验序号 | 实验条件 | 会议室内手机屏蔽状态 |
| 1 | 将上述制得的信号干扰涂料分别涂至会议室墙面，拨打会议室内电话，观察信号干扰强度。 | 信号干扰强度≥50% |
| 2 | 将墙体底材修铺金属网格，然后使用内墙普通腻子，将信号干扰涂料分别涂至会议室墙面，拨打会议室内电话，观察信号干扰强度。 | 信号干扰强度≥80% |
| 3 | 制备一个金属密闭室，拨打金属密闭室内电话，观察信号干扰强度。 | 信号干扰强度100% |
| 4 | 将普通室内用涂料涂至会议室墙面，拨打会议室内电话，观察信号干扰强度。 | 信号干扰强度0 |
实验结果分析：信号屏蔽涂料利用导电金属氧化物配合石墨烯、以及涂料在会议室内部涂覆，利用静电屏蔽的原理使其内部形成封闭的信号屏蔽腔室，模拟金属密闭室形成连续的信号屏蔽腔室，可有效的降低开会期间、电话干扰的情况，保证会议的有序进行。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (9)
1.一种会议室用信号干扰涂料，其特征在于，由以下重量份数的各原料制备而成：丙烯酸合成树脂35～40份、水18～22份、偶联剂0.4～0.5份、分散剂0.6～0.8份、乙二醇2～2.5份、十六碳双酯2.5～3份、十二碳醇酯10～15份、二氧化钛粉体12～15份、氧化铝粉体8～12份、导电金属氧化物粉体10～13份、石墨烯粉体4～6份、闭合性增稠剂0.3～0.4份、有机硅消泡剂0.4～0.6份、乙基纤维素0.3～0.4份、PH调节剂0.1～0.15份、卡松杀菌剂0.15～0.2份、闭合性增稠剂0.2～0.25份。
2.根据权利要求1所述的一种会议室用信号干扰涂料，其特征在于，由以下重量份数的各原料制备而成：丙烯酸合成树脂38份、水20份、偶联剂0.5份、分散剂0.7份、乙二醇2份、十六碳双酯3份、十二碳醇酯12份、二氧化钛粉体13份、氧化铝粉体10份、导电金属氧化物粉体12份、石墨烯粉体6份、闭合性增稠剂0.4份、有机硅消泡剂0.5份、乙基纤维素0.4份、PH调节剂0.15份、卡松杀菌剂0.15份、闭合性增稠剂0.2份。
3.根据权利要求1或2所述的一种会议室用信号干扰涂料，其特征在于：所述偶联剂采用钛酸酯偶联剂、铝酸酯偶联剂、锆酸酯偶联剂中的一种或者至少两种的混合物。
4.根据权利要求1或2所述的一种会议室用信号干扰涂料，其特征在于：所述分散剂采用导电炭黑分散剂。
5.根据权利要求1或2所述的一种会议室用信号干扰涂料，其特征在于：所述二氧化钛采用改性包裹处理后的导电二氧化钛。
6.根据权利要求1或2所述的一种会议室用信号干扰涂料，其特征在于：所述导电金属氧化物粉体采用掺锑二氧化锡粉体、掺铝氧化锌粉体、掺铟氧化锡粉体中的一种。
7.根据权利要求6所述的一种会议室用信号干扰涂料，其特征在于：所述导电金属氧化物粉体采用掺锑二氧化锡粉体。
8.根据权利要求1所述的一种会议室用信号干扰涂料，其特征在于：所述闭合性增稠剂采用纤维素增稠剂、聚氨酯增稠剂、聚丙烯酸酯增稠剂中的一种或者至少两种的混合物。
9.一种制备如权利要求1所述的一种会议室用信号干扰涂料的方法，其特征在于：包括以下步骤：
步骤一：在高速分散机中依次加入水、偶联剂、分散剂、乙二醇、十六碳双酯在转速为500r/min的条件下，搅拌2～5分钟；
步骤二：在步骤一中制得的原料中依次加入十二碳醇酯、二氧化钛粉体、氧化铝粉体、掺锑二氧化锡、石墨烯粉体、闭合性增稠剂、有机硅消泡剂，提高高速分散机转速至700r/min的条件下，搅拌3～6分钟；
步骤三：在步骤二中制得的原料中依次加入乙基纤维素、PH调节剂，提高高速分散机转速至1500r/min的条件下，分散10～25分钟，直至涂料粒径达到50um以下；
步骤四：在步骤三中制得的原料中加入丙烯酸合成树脂，保持高速分散机转速在1500r/min的条件下，分散直至涂料粒径达到40～50um；
步骤五：在步骤四中制得的原料降温至50℃以下后中加入卡松杀菌剂、闭合性增稠剂制成成品涂料，灌装存储。