CN109928775A - 一种防裂性强的混凝土养护剂及其制备方法 - Google Patents

一种防裂性强的混凝土养护剂及其制备方法 Download PDF

Info

Publication number
CN109928775A
CN109928775A CN201910247393.9A CN201910247393A CN109928775A CN 109928775 A CN109928775 A CN 109928775A CN 201910247393 A CN201910247393 A CN 201910247393A CN 109928775 A CN109928775 A CN 109928775A
Authority
CN
China
Prior art keywords
parts
cracking resistance
powder
curing compound
strong
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910247393.9A
Other languages
English (en)
Inventor
肖国强
林晓珺
胡晓轶
尹小琴
王辉
殷潇锡
陈玲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kao Ecological Engineering Ltd By Share Ltd
Original Assignee
Kao Ecological Engineering Ltd By Share Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kao Ecological Engineering Ltd By Share Ltd filed Critical Kao Ecological Engineering Ltd By Share Ltd
Priority to CN201910247393.9A priority Critical patent/CN109928775A/zh
Publication of CN109928775A publication Critical patent/CN109928775A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种防裂性强的混凝土养护剂及其制备方法,由以下重量份的原料制成:硅酸钠22‑27份,硫酸铝22‑28份,羧甲基纤维素4.5‑7份,碳酸钙20‑25份,氧化镁8‑10份,七水硫酸镁:4‑6份,滑石粉:21‑24.5份,乳胶粉:6‑8份,二氧化钛4‑5份;通过以上各成分的不同作用,大大降低混凝土表面水份的挥发,减少混凝土的开裂,增强混凝土的强度,同时还具有净化环境和空气的目的。

Description

一种防裂性强的混凝土养护剂及其制备方法
技术领域
本发明属于土建领域,具体涉及一种防裂性强的混凝土养护剂及其制备方法。
背景技术
在房屋建设或生产过程中,因水泥凝固硬化过程中需要大量的水来进行其本身的水化反应,所以,水泥胶凝结构体的保水养护直接影响到工程或工程预制产品的质量。
目前混凝土养护以表面喷水,覆膜等为主,这种常规的混凝土养护方法,费时费力,对于施工人员要求较高,尤其是对于异型混凝土结构养护难以操作。近年有采用混凝土养护剂对混凝土进行养护,养护剂主要作用机理是通过对混凝土堵孔或者保水达到养护混凝土的目的。因养护剂可以采用喷涂的方法施工,可节省大量的人力物力,能够降低混凝土的后期养护成本,避免因工人的操作失误而造成的混凝土养护不足,且对于提高混凝土构造物的耐久性具有一定的作用,但还是存在保水性差、抗裂性能低的缺点。
发明内容
发明目的:本发明的目的是为了解决以上现有技术的不足,提供一种防裂性强的混凝土养护剂,适用于房屋、道路等建筑工程的养护。
技术方案:本发明所述的一种防裂性强的混凝土养护剂,由以下重量份的原料制成:硅酸钠22-27份,硫酸铝22-28份,羧甲基纤维素4.5-7份,碳酸钙20-25份,氧化镁8-10份,七水硫酸镁:4-6份,滑石粉:21-24.5份,乳胶粉:6-8份,二氧化钛4-5份。
优选地方案一,所述的防裂性强的混凝土养护剂,由以下重量份的原料制成:硅酸钠22.5份,硫酸铝24份,羧甲基纤维素5.4份,碳酸钙22份,氧化镁8份,七水硫酸镁6份,滑石粉22.5份,乳胶粉8份,二氧化钛5份。
优选地方案二,所述的防裂性强的混凝土养护剂,由以下重量份的原料制成:硅酸钠25份,硫酸铝22.5份,羧甲基纤维素6份,碳酸钙22份,氧化镁9.4份,七水硫酸镁:5.6份,滑石粉:23.5份,乳胶粉:7份,二氧化钛5份。
优选地方案三,所述的防裂性强的混凝土养护剂,由以下重量份的原料制成:硅酸钠27份,硫酸铝23份,羧甲基纤维素6份,碳酸钙24份,氧化镁9.5份,七水硫酸镁6份,滑石粉22份,乳胶粉6份,二氧化钛5份。
优选地,所述的二氧化钛为纳米级。
本发明还提供一种上防裂性强的混凝土养护剂的制备方法,将上述比例的原料在粉末混合机进行混合均匀,然后通过皮带输送机输送至球磨机中研磨成规定50-120目,然后输送至粉末均化机中均化,即可得粉末状成品。
有益效果:本发明通过碳酸钙,氧化镁,七水硫酸镁,滑石粉和乳胶粉的微膨胀作用,可补偿混凝土干燥时的收缩,以减少混凝土的自收缩变形,从而防止混凝土产生裂缝,通过硅酸钠和硫酸铝的保水作用,硅酸钠由混凝土表面的微孔渗透入混凝土内,与水泥水化产物Ca(OH)2反应生产硅酸钙胶体从而形成致密薄膜,同时硫酸盐与水泥水化产物Ca(OH)2反应生成钙矾石针状晶体,从而阻塞表面微孔,防止水分蒸发,通过羧甲基纤维素的增稠作用,进一步减少混凝土的泌水和表面水分的蒸发,并促进水泥的持续水化以减少混凝土的干缩开裂,另外,二氧化钛在光催化的作用下,将空气中氧气和水分子激发,形成氧化能力极强的氢氧自由基和活性基,其可捕杀空气中的浮游细菌,去除臭味,并把有机污染物不断降解成无污染的水和二氧化碳等,从而达到净化环境和空气;通过以上各成分的不同作用,大大降低混凝土表面水份的挥发,减少混凝土的开裂,增强混凝土的强度,同时还具有净化环境和空气的目的。
具体实施方式
为了加深对本发明的理解,下面将结合实施例对本发明作进一步详述,该实施例仅用于解释本发明,并不构成对本发明保护范围的限定。
实施例1
所述的防裂性强的混凝土养护剂,由以下重量份的原料制成:硅酸钠22.5份,硫酸铝24份,羧甲基纤维素5.4份,碳酸钙22份,氧化镁8份,七水硫酸镁6份,滑石粉22.5份,乳胶粉8份,二氧化钛5份,将上述比例的原料在粉末混合机进行混合均匀,然后通过皮带输送机输送至球磨机中研磨成规定50-120目,然后输送至粉末均化机中均化,即可得粉末状成品。
实施例2
所述的防裂性强的混凝土养护剂,由以下重量份的原料制成:硅酸钠25份,硫酸铝22.5份,羧甲基纤维素6份,丙烯酸乳液33份,碳酸钙22份,氧化镁9.4份,七水硫酸镁5.6份,滑石粉23.5份,乳胶粉7份,二氧化钛5份,将上述比例的原料在粉末混合机进行混合均匀,然后通过皮带输送机输送至球磨机中研磨成规定50-120目,然后输送至粉末均化机中均化,即可得粉末状成品。
实施例3
所述的防裂性强的混凝土养护剂,由以下重量份的原料制成:硅酸钠27份,硫酸铝23份,羧甲基纤维素6份,丙烯酸乳液34份,碳酸钙24份,氧化镁9.5份,七水硫酸镁6份,滑石粉22份,乳胶粉6份,二氧化钛5份,将上述比例的原料在粉末混合机进行混合均匀,然后通过皮带输送机输送至球磨机中研磨成规定50-120目,然后输送至粉末均化机中均化,即可得粉末状成品。
在1L水中加入实施例1-3制备的混凝土养护剂80-100g,搅拌均匀后通过喷雾设备直接喷洒到初浇筑的混凝土表面,将喷雾有实施例1-3制备的混凝土养护剂置于室温下养护24h后,与未喷洒混凝土养护剂的混凝土置于35-40度环境中,记录混凝土6面的裂纹情况。
性能测试如下表1所示:
以上所述仅为本发明的较佳实施例而已,并不用以限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。

Claims (6)

1.一种防裂性强的混凝土养护剂,其特征在于,由以下重量份的原料制成:硅酸钠22-27份,硫酸铝22-28份,羧甲基纤维素4.5-7份,碳酸钙20-25份,氧化镁8-10份,七水硫酸镁4-6份,滑石粉21-24.5份,乳胶粉6-8份,二氧化钛4-5份。
2.根据权利要求1所述的一种防裂性强的混凝土养护剂,其特征在于,由以下重量份的原料制成:硅酸钠22.5份,硫酸铝24份,羧甲基纤维素5.4份,碳酸钙22份,氧化镁8份,七水硫酸镁6份,滑石粉22.5份,乳胶粉8份,二氧化钛5份。
3.根据权利要求1所述的一种防裂性强的混凝土养护剂,其特征在于,由以下重量份的原料制成:硅酸钠25份,硫酸铝22.5份,羧甲基纤维素6份,碳酸钙22份,氧化镁9.4份,七水硫酸镁5.6份,滑石粉23.5份,乳胶粉7份,二氧化钛5份。
4.根据权利要求1所述的一种防裂性强的混凝土养护剂,其特征在于,由以下重量份的原料制成:硅酸钠27份,硫酸铝23份,羧甲基纤维素6份,碳酸钙24份,氧化镁9.5份,七水硫酸镁6份,滑石粉22份,乳胶粉6份,二氧化钛5份。
5.根据权利要求1所述的一种防裂性强的混凝土养护剂,其特征在于,所述的二氧化钛为纳米级。
6.权利要求1-5任一权利要求所述的防裂性强的混凝土养护剂的制备方法,其特征在于,将上述比例的原料在粉末混合机进行混合均匀,然后通过皮带输送机输送至球磨机中研磨成规定50-120目,然后输送至粉末均化机中均化,即可得粉末状成品。
CN201910247393.9A 2019-03-29 2019-03-29 一种防裂性强的混凝土养护剂及其制备方法 Pending CN109928775A (zh)