CN109880549A - 一种单向透视胶片的生产工艺 - Google Patents
一种单向透视胶片的生产工艺 Download PDFInfo
- Publication number
- CN109880549A CN109880549A CN201910107691.8A CN201910107691A CN109880549A CN 109880549 A CN109880549 A CN 109880549A CN 201910107691 A CN201910107691 A CN 201910107691A CN 109880549 A CN109880549 A CN 109880549A
- Authority
- CN
- China
- Prior art keywords
- film
- single plane
- extruder
- master batch
- plane fluoroscopy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种单向透视胶片的生产工艺。包括以下步骤，(1)制备母粒的步骤，母粒基材采用190℃时熔融指数在3‑5g/10min的EVA树脂，采用高分子蜡作分散剂；(2)将母粒与EVA树脂和偶联剂混合均匀的步骤，EVA树脂的VA含量为30‑33％，在190℃时熔融指数小于1g/10min；(3)采用流延成膜工艺生成单向透视胶片的步骤，此步骤时挤出机的挤出量控制在100‑120kg/h，挤出机的螺杆温度控制在115℃‑130℃，套筒温度控制在130℃以下，模头温度控制在130℃‑145℃。
Description
技术领域
本发明涉及一种单向透视胶片的生产工艺。
背景技术
在建筑装饰等领域，夹胶玻璃以其美观、坚固等优良特性得到了越来越广泛的应用，夹胶玻璃包括位于中心的玻璃胶片层和位于两侧的玻璃。单向透视玻璃是一款将液晶膜复合进两层玻璃中间，经高温高压胶合后，一体成型的夹层结构的新型特种光电玻璃产品，具有单向透视的特性。单向透视胶片在现有加工工艺下不利于生产。
发明内容
本发明为解决公知技术中存在的技术问题而提供一种单向透视胶片的生产工艺，解决背景技术中存在的问题。
本发明为解决公知技术中存在的技术问题所采取的技术方案是：一种单向透视胶片的生产工艺包括以下步骤，(1)制备母粒的步骤，母粒基材采用190℃时熔融指数在3-5g/10min的EVA树脂，采用高分子蜡作分散剂；(2)将母粒与EVA树脂和偶联剂混合均匀的步骤，EVA树脂的VA含量为30-33％，在190℃时熔融指数小于1g/10min；(3)采用流延成膜工艺生成单向透视胶片的步骤，此步骤时挤出机的挤出量控制在100-120kg/h，挤出机的螺杆温度控制在115℃-130℃，套筒温度控制在130℃以下，模头温度控制在130℃-145℃
本发明的优点和积极效果是：本发明提供了一种单向透视胶片的生产工艺，通过采用EVA材料代替传统的PVB材料，在生产过程中采用了低温成型工艺，得到的胶片具有单向透光的特性。
优选地：步骤(2)中所述的偶联剂选取为氨丙基三甲氧基硅烷或者氨乙基氨丙基三乙氧基硅烷。
优选地：步骤(3)中流延成膜工艺采用单螺杆挤出机，挤出温度为90℃-130℃。
具体实施方式
为能进一步了解本发明的发明内容、特点及功效，兹举以下实施例详细说明如下：
实施例1
(1)制备母粒，母粒基材采用190℃时熔融指数在3g/10min的EVA树脂，采用高分子蜡作分散剂；(2)将母粒与EVA树脂和偶联剂混合均匀，EVA树脂的VA含量为30％，在190℃时熔融指数0.5g/10min；(3)采用流延成膜工艺生成单向透视胶片，此步骤时挤出机的挤出量控制在100kg/h，挤出机的螺杆温度控制在128℃，套筒温度控制在120℃，模头温度控制在130℃。
其中，步骤(2)中所述的偶联剂选取为氨丙基三甲氧基硅烷；步骤(3)中流延成膜工艺采用单螺杆挤出机，挤出温度为90℃；挤出机选用敞开式网板。
实施例2
(1)制备母粒，母粒基材采用190℃时熔融指数在4.5g/10min的EVA树脂，采用高分子蜡作分散剂；(2)将母粒与EVA树脂和偶联剂混合均匀，EVA树脂的VA含量为31％，在190℃时熔融指数0.6g/10min；(3)采用流延成膜工艺生成单向透视胶片，此步骤时挤出机的挤出量控制在100kg/h，挤出机的螺杆温度控制在129℃，套筒温度控制在125℃，模头温度控制在143℃。
其中，步骤(2)中所述的偶联剂选取为氨乙基氨丙基三乙氧基硅烷；步骤(3)中流延成膜工艺采用单螺杆挤出机，挤出温度为100℃。
实施例3
(1)制备母粒，母粒基材采用190℃时熔融指数在5g/10min的EVA树脂，采用高分子蜡作分散剂；(2)将母粒与EVA树脂和偶联剂混合均匀，EVA树脂的VA含量为32％，在190℃时熔融指数0.7g/10min；(3)采用流延成膜工艺生成单向透视胶片，此步骤时挤出机的挤出量控制在120kg/h，挤出机的螺杆温度控制在130℃，套筒温度控制在110℃，模头温度控制在144℃。
其中，步骤(2)中所述的偶联剂选取为氨乙基氨丙基三乙氧基硅烷；步骤(3)中流延成膜工艺采用单螺杆挤出机，挤出温度为125℃。
Claims (3)
1.一种单向透视胶片的生产工艺，其特征是：包括以下步骤，
(1)制备母粒的步骤，母粒基材采用190℃时熔融指数在3-5g/10min的EVA树脂，采用高分子蜡作分散剂；
(2)将母粒与EVA树脂和偶联剂混合均匀的步骤，EVA树脂的VA含量为30-33％，在190℃时熔融指数小于1g/10min；
(3)采用流延成膜工艺生成单向透视胶片的步骤，此步骤时挤出机的挤出量控制在100-120kg/h，挤出机的螺杆温度控制在115℃-130℃，套筒温度控制在130℃以下，模头温度控制在130℃-145℃。
2.如权利要求1所述的单向透视胶片的生产工艺，其特征在于：步骤(2)中所述的偶联剂选取为氨丙基三甲氧基硅烷或者氨乙基氨丙基三乙氧基硅烷。
3.如权利要求1所述的单向透视胶片的生产工艺，其特征在于：步骤(3)中流延成膜工艺采用单螺杆挤出机，挤出温度为90℃-130℃。