CN109837780A - A kind of colouring method of high fire-retardance tooling fabric - Google Patents
A kind of colouring method of high fire-retardance tooling fabric Download PDFInfo
- Publication number
- CN109837780A CN109837780A CN201910153419.3A CN201910153419A CN109837780A CN 109837780 A CN109837780 A CN 109837780A CN 201910153419 A CN201910153419 A CN 201910153419A CN 109837780 A CN109837780 A CN 109837780A
- Authority
- CN
- China
- Prior art keywords
- follows
- retardance
- fabric
- high fire
- time
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of colouring method of high fire-retardance tooling fabric, including the following steps: that fabric → pre-treatment → front dyeing → is dried for the first time → baked, → finished product packing → detection is dried for the second time → baked to → back side dyeing →.The present invention uses warp thread 14.5tex* weft yarn 14.5tex, 100% polyimides yarn, weaving is through 90 per inch of close 120 per inch * filling density, breadth is 152-154 centimetres, the tooling fabric of plain weave, fabric is padded into hydrophily and bibulous pretreatment liquid, nano paint ink completely digital spray printing is carried out to tow sides again, drying, bake sizing, produce high fire-retardance, the tooling fabric of polychrome kind, igniting can not also burn for 6 minutes, flame retardant effect reaches aphlogistic rank, it is suitble to fire-fighting, steel-making, the Functional Requirement of the special type protections industry clothes such as Fight Fire in Forest.
Description
Technical field
The invention belongs to textile industry fabric fields, and in particular to a kind of colouring method of high fire-retardance tooling fabric.
Background technique
Polyimide fiber has high-strength, Gao Mo and high-temperature stability, is a kind of important high-performance fiber, molecule master
Contain imide ring group, referred to as PI fiber on chain.The country is able to carry out polyimide fiber scale, industry metaplasia at present
The refreshing new material share of Austria of the Gao Qi polyimide material Co., Ltd for mainly having Jilin Changchun and Lianyungang of Jiangsu that produce is limited
Company.Based on polyimide fiber have the performances such as excellent high temperature resistant, fire-retardant, mechanics, chemically-resistant, it has also become produce it is heat-insulated,
One of the hot spot material of the security protections product such as fire-fighting, the favor by market.But polyimide fiber itself carry it is golden yellow
Color, original liquid coloring produces limited several colors in spinning process at present, greatly constrains the application of fiber.
Summary of the invention
Goal of the invention: in order to solve the deficiencies in the prior art, the present invention provides a kind of dyeing of high fire-retardance tooling fabric
Method.
A kind of technical solution: colouring method of high fire-retardance tooling fabric, characterized by the following steps: fabric →
Pre-treatment → front dyeing → is dried for the first time → baked, and → finished product packing → inspection is dried for the second time → baked to → back side dyeing →
It surveys；Wherein:
The fabric pretreatment: technology preparation and condition are as follows:
The front dyeing is as follows: using spray printing coating ink, using Du Pont's coating ink, starlight spray head, flower pattern is (full
Ground), spray printing speed is 50-60m/min.
As optimization: the fabric specification is as follows: warp thread 14.5tex* weft yarn 14.5tex, 100% polyimides, warp
90 per inch of close 120 per inch * filling density, breadth 152-154cm, using plain weave.
As optimization: the first time drying: drying temperature: 100 DEG C -110 DEG C；Drying time: 6-8min.
As optimization: described to bake, baking temperature: 150 DEG C -160 DEG C；Bake the time: 3-5min.
As optimization: the back side dyeing is as follows: using spray printing coating ink, uses Du Pont's coating ink, starlight spray
Head, flower pattern (completely), spray printing speed are 50-60m/min.
As optimization: second of drying: drying temperature: 100 DEG C -110 DEG C；Drying time: 6-8min.
As optimization: described bakes are as follows: baking temperature are as follows: 150 DEG C -160 DEG C；Bake the time are as follows: 3-5min；Width is
150-152cm。
The utility model has the advantages that specific advantage of the invention is as follows:
1, the present invention uses warp thread 14.5tex* weft yarn 14.5tex, and 100% polyimides yarn is weaved through close 120 every English
90 per inch of very little * filling density, 152-154 centimetres of breadth, the tooling fabric of plain weave.
2, polyimides fabric second dipping and rolling hydrophily, bibulous pretreatment liquid are overcome polyimides by the present invention
The disadvantage of hygroscopicity difference convenient for absorption, while controlling pretreatment liquid liquid carrying rate.
3, the present invention uses Du Pont's digit printing nano-level coating ink, prevents granules of pigments in ink big, friction jail
It is poor to spend.
4, the present invention expires bottom spray printing using digital decorating machine, obtains unified color, substitution dyeing, while inkless water wave
Take, no discharge is pollution-free.
5, tow sides of the invention spray printing twice, prevents from showing money or valuables one carries unintentionally.
6, the present invention uses infrared baking, keeps ink full cross-linked with yarn.
7, the present invention can produce green on the basis of polyimides golden yellow itself, coffee, grey, the colour of loess, black,
The dark blue equal several hundred a color kinds of colour systems.
8, flame retardant effect of the invention reaches aphlogistic rank, is suitble to the special type protections such as fire-fighting, steel-making, Fight Fire in Forest
The Functional Requirement of industry clothes.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, so that the technology of this field
Personnel can better understand advantages and features of the invention, to make apparent boundary to protection scope of the present invention
It is fixed.Embodiment described in the invention is only a part of the embodiment of the present invention, instead of all the embodiments, based on the present invention
In embodiment, those of ordinary skill in the art's every other implementation obtained without making creative work
Example, shall fall within the protection scope of the present invention.
Embodiment
The present invention uses warp thread 14.5tex* weft yarn 14.5tex, and 100% polyimides yarn is weaved through close 120 every English
90 per inch of very little * filling density, 152-154 centimetres of breadth, fabric is padded hydrophily and hygroscopicity by the tooling fabric of plain weave
Strong pretreatment liquid, then nano paint ink completely digital spray printing is carried out to tow sides, drying bakes sizing, produces height
Fire-retardant, the tooling fabric of polychrome kind, igniting can not also burn for 6 minutes, and flame retardant effect reaches aphlogistic rank, is suitble to disappear
The Functional Requirement of the special type protections industry clothes such as anti-, steel-making, Fight Fire in Forest.
Process flow of the invention is substantially as follows: fabric → pre-treatment → front dyeing → is dried → baking → for the first time and is carried on the back
Face dyeing → drying for the second time → bakes → finished product packing → detection.
1, fabric specification
Warp thread 14.5tex* weft yarn 14.5tex, 100% polyimides
Through 90 per inch of close 120 per inch * filling density
152-154 centimetres of breadth
Using plain weave.
2, fabric pretreatment
Technology preparation and condition:
3, front dyeing
Using spray printing coating ink, using Du Pont's coating ink, starlight spray head, flower pattern (completely), spray printing speed is 50-
60m/min；
4, it dries for the first time
Drying temperature: 100-110 DEG C；
Drying time: 6-8min；
5, it bakes
Baking temperature: 150-160 DEG C；
Bake the time: 3-5min；
6, the back side is dyed
Using spray printing coating ink, using Du Pont's coating ink, starlight spray head, flower pattern (completely), spray printing speed is 50-
60m/min；
7, it dries for second
Drying temperature: 100-110 DEG C；
Drying time: 6-8min；
8, it bakes
Baking temperature: 150 DEG C -160 DEG C；
Bake the time: 3-5min；
Width (centimetre) 150-152cm；
9, it packs
Clot packaging
10, fabrics flame resistance performance test
Polyimides fabrics flame resistance performance
Data show that polyimide fiber broadwise burning time is both greater than 6min in table, and burning rank is level-one, show
Polyimide fiber is difficult to light, and the flame retardant property of polyimide fiber is good.
Claims (7)
1. a kind of colouring method of high fire-retardance tooling fabric, characterized by the following steps: fabric → pre-treatment → front
Dyeing → drying for the first time → bakes, and → finished product packing → detection is dried for the second time → baked to → back side dyeing →；Wherein:
The fabric pretreatment: technology preparation and condition are as follows:
The described front dyeing is as follows: using spray printing coating ink, using Du Pont's coating ink, and starlight spray head, flower pattern (completely),
Spray printing speed is 50-60m/min.
2. the colouring method of high fire-retardance tooling fabric according to claim 1, it is characterised in that: the fabric specification is such as
Under: warp thread 14.5tex* weft yarn 14.5tex, 100% polyimides, through 90 per inch of close 120 per inch * filling density, breadth
152-154cm, using plain weave.
3. the colouring method of high fire-retardance tooling fabric according to claim 1, it is characterised in that: the first time dries
It is dry: drying temperature are as follows: 100 DEG C -110 DEG C；Drying time are as follows: 6-8min.
4. the colouring method of high fire-retardance tooling fabric according to claim 1, it is characterised in that: described to bake, roasting
Dry temperature are as follows: 150 DEG C -160 DEG C；Bake the time are as follows: 3-5min.
5. the colouring method of high fire-retardance tooling fabric according to claim 1, it is characterised in that: the back side dyeing is such as
Under: spray printing coating ink is used, using Du Pont's coating ink, starlight spray head, flower pattern (completely), spray printing speed is 50-60m/
min。
6. the colouring method of high fire-retardance tooling fabric according to claim 1, it is characterised in that: second of baking
It is dry: drying temperature are as follows: 100 DEG C -110 DEG C；Drying time are as follows: 6-8min.
7. the colouring method of high fire-retardance tooling fabric according to claim 1, it is characterised in that: described bakes are as follows: roasting
Dry temperature are as follows: 150 DEG C -160 DEG C；Bake the time are as follows: 3-5min；Width is 150-152cm.