CN108570863A - A kind of colouring method of high-strength polyethylene tooling fabric - Google Patents
A kind of colouring method of high-strength polyethylene tooling fabric Download PDFInfo
- Publication number
- CN108570863A CN108570863A CN201810379178.XA CN201810379178A CN108570863A CN 108570863 A CN108570863 A CN 108570863A CN 201810379178 A CN201810379178 A CN 201810379178A CN 108570863 A CN108570863 A CN 108570863A
- Authority
- CN
- China
- Prior art keywords
- temperature
- molecular weight
- minutes
- weight polyethylene
- time
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of colouring methods of high-strength polyethylene tooling fabric:Include the following steps:Raw material → weaving → pre-setting → dyes → soap, wash, be dehydrated → and bakes → finished product.The present invention is the high-grade tooling fabric of exploitation, it gives full play to ultra-high molecular weight polyethylene and viscose rayon and respectively performance advantage and has complementary functions, select 30/ viscose glue of ultra-high molecular weight polyethylene, 70 18.5tex doublet cords as warp, weft yarn raw material, select rational fabric specification and technological design, make that product cloth cover is smooth, moisture absorption is ventilative, quality is flexible, cool and comfortable and easy to clean, becomes a kind of high-grade tooling fabric.
Description
Technical field
The invention belongs to textile industry fabric fields, and in particular to a kind of colouring method of high-strength polyethylene tooling fabric.
Background technology
Ultra-high molecular weight polyethylene (UHMWPE) fiber is the high-performance fiber for realizing industrialized production the 1980s,
Also known as high-strength and high-modulus weight northylen (PE) fiber.The high relative molecular mass of UHMWPE fibers, height-oriented, strand height
Tangle and the performance characteristics such as high-crystallinity give material fabulous comprehensive performance, have density is low, modulus is high, UV resistant,
The performances such as wear-resisting, shock resistance, intensity height have best cost performance super high molecular weights poly- in existing three big fibrous materials
Ethylene (UHMWPE) fiber, UHMWPE fibre crystallinities are high, lack dye radical, it is difficult to dye, current main research aircraft
Structure, using the methods of original liquid coloring method, Conventional dye decoration method, particular dye mechanical development, specific stain technique, but color is firm
Degree is not up to standard, and chromatography is not complete, cannot meet big production requirement.And superhigh molecular weight polyethylene fibers are oozed to weaving downstream field
Thoroughly, dyeing is the project that can't steer clear of.
Invention content
Goal of the invention:In order to solve the deficiencies in the prior art, the present invention provides a kind of high-strength polyethylene tooling fabrics
Colouring method.
Technical solution:A kind of colouring method of high-strength polyethylene tooling fabric, includes the following steps:Raw material → weaving → pre-
Sizing → dyeing → is soaped, washes, being dehydrated → baking → finished product, wherein:The dyeing:
A. cold dyeing viscose:
(1) technical recipe:Low form reactive dye:Activated red X-3B is 2%;Anhydrous sodium sulphate is 20-30g/L;Soda ash is 10-
15g/L;
(2) process conditions:The fabric for padding dyestuff is wound up on plastic tube, outsourcing plastic film, is banked up 20-24 hours,
Dyestuff is upper at normal temperatures to contaminate viscose fiber;
It soaps:Soaping agent is 2-3g/L;Temperature is 90-95 DEG C, and the time is 15-20 minutes;
Washing:Use temperature for 60-70 DEG C of hot water wash 10-15 minutes;Cold water is washed 20 minutes;It is pH=7-8 that acid, which neutralizes,;
B. ultra-high molecular weight polyethylene graft modification is handled:
(1) technology preparation:Cation graft agents:2~5g/L;Sodium hydroxide (30%):3~5g/L;Bath raio:1:40;
(2) process conditions:Grafting temperature is:65℃;Grafting time is:35min;Washing temperature is:50 DEG C, washing two
Time;
C. ultra-high molecular weight polyethylene pigment dyeing:
(1) technology preparation:Coating G-18 red is 0.5%;Coating G-22 Huangs are 0.9%;Bath raio is 1:40;
(2) process conditions:Dyeing temperature is 65 DEG C;Dyeing time is 35min;Heating rate is 2~3 DEG C/min
D. ultra-high molecular weight polyethylene bonds fixation:
(1) technology preparation:Adhesive is 3mL/L;
(2) process conditions:Tack temperature is 65 DEG C, the bonding time is 25min.
As an optimization:The raw material is:Warp thread weft yarn is the 18.5tex of 30/ viscose glue 70 of ultra-high molecular weight polyethylene bis-
Strand.
As an optimization:The weaving:Using wealthy width air-jet loom weaving, 1/3 twill-weave, it is 600-650m/ to knit speed
Min, warp tension 1500-1600N.
As an optimization:The pre-setting:Temperature is:100-110 DEG C, the time be:5-8 minutes.
As an optimization:It is described to soap, wash, being dehydrated:
It soaps:Soaping agent 2-3g/L, temperature are 90-95 DEG C, the time is 15-20 minutes;
Washing:Temperature is 60-70 DEG C, hot water wash 10-15 minutes, cold water is washed 20 minutes, acid neutralizes is pH=7-8;
Dehydration:Dewaterer rotating speed:800-900r/min, dewatering time:8-10min.
As an optimization:It is described to bake:Baking temperature:100-110 DEG C, bake the time:8-10 minutes.
Advantageous effect:Superhigh molecular weight polyethylene fibers in the present invention have good mechanical property and chemical property,
Its surface is smooth nice and cool, and friction factor is small, and curling stability is poor, and spinning performance is poor, and yarn feel is hardened, comfort, water imbibition,
Dyeability, poor flexibility, fusing point are low.And viscose fiber has good hygroscopicity, it is high dyeability, the features such as intensity is low, high-grade for exploitation
Tooling fabric gives full play to ultra-high molecular weight polyethylene and viscose rayon and respectively performance advantage and has complementary functions, selects superelevation point
The 18.5tex doublet cords of 30/ viscose glue 70 of sub- weight northylen are weaved as warp, weft yarn raw material using twill-weave, and using activity
Dyestuff cold dyeing process, makes viscose fiber paint, and 30% ultra-high molecular weight polyethylene is contaminated on coating, it is flat to produce product cloth cover
Whole, moisture absorption is ventilative, quality is flexible, cool and comfortable and dyeing top grade tooling fabric easy to clean.
Dyeing in the present invention is gathered using 70% viscose fiber, the super high molecular weight that 30% is contaminated on coating is contaminated on reactive dye
Ethylene carries out cation graft modification to superhigh molecular weight polyethylene fibers, makes superhigh molecular weight polyethylene fibers in sun
It is charge, improve the absorption property of coating.
The present invention uses cold and hot technique, and dyeing need not heat, energy saving, reduce cost, production process clean environment firendly.
Specific implementation mode
The technical scheme in the embodiments of the invention will be clearly and completely described below, so that the technology of this field
Personnel can be better understood from advantages and features of the invention, to make apparent boundary to protection scope of the present invention
It is fixed.Embodiment described in the invention is only a part of the embodiment of the present invention, instead of all the embodiments, based on the present invention
In embodiment, the every other implementation that those of ordinary skill in the art are obtained without making creative work
Example, shall fall within the protection scope of the present invention.
Specific embodiment 1
A kind of colouring method of high-strength polyethylene tooling fabric, includes the following steps:Raw material → weaving → pre-setting → dye
Color → soap, wash, be dehydrated → bakes → finished product.
A, the raw material is:Warp thread weft yarn is the 18.5tex doublet cords of 30/ viscose glue 70 of ultra-high molecular weight polyethylene.
B, the weaving:Using wealthy width air-jet loom weaving, 1/3 twill-weave, it is 600m/min to knit speed, and warp tension is
1500N。
C, the pre-setting:Temperature is:100 DEG C, the time be:5 minutes.
D, the dyeing:
A. cold dyeing viscose:
(1) technical recipe:Low form reactive dye:Activated red X-3B is 2%;Anhydrous sodium sulphate is 20g/L;Soda ash is 10g/L;
(2) process conditions:The fabric for padding dyestuff is wound up on plastic tube, and outsourcing plastic film banks up 20 hours, dyestuff
It is upper at normal temperatures to contaminate viscose fiber;
It soaps:Soaping agent is 2g/L;Temperature is 90 DEG C, and the time is 15 minutes;
Washing:Use temperature for 60 DEG C of hot water wash 10 minutes;Cold water is washed 20 minutes;It is pH=7 that acid, which neutralizes,;
B. ultra-high molecular weight polyethylene graft modification is handled:
(1) technological principle:Coating is a kind of pigment, without substantivity, will not react to form covalent bond with fiber, institute
It is that cation graft modification is carried out again to superhigh molecular weight polyethylene fibers with the most basic absorption principle of coating, makes superelevation
Molecular weight polyethylene fiber is in positive electricity, and superhigh molecular weight polyethylene fibers is on the one hand made firmly to be bonded with coating, another
Aspect addition alkali can improve grafting agent and be combined with the acrylic acid on superhigh molecular weight polyethylene fibers, can improve the suction of coating
Attached performance;
(2) technology preparation:Cation graft agents:2g/L;Sodium hydroxide (30%):3g/L;Bath raio:1:40;
(3) process conditions:Grafting temperature is:65℃;Grafting time is:35min;Washing temperature is:50 DEG C, washing two
Time;
C. ultra-high molecular weight polyethylene pigment dyeing:
(1) technological principle:After carrying out grafting processing to superhigh molecular weight polyethylene fibers, ultra-high molecular weight polyethylene
Fiber is just in positive electricity, so that it is enhanced the adsorption capacity of coating, improves coating to superhigh molecular weight polyethylene fibers
Dye-uptake and dyefastness;
(2) technology preparation:Coating G-18 red is 0.5%;Coating G-22 Huangs are 0.9%;Bath raio is 1:40;
(3) process conditions:Dyeing temperature is 65 DEG C;Dyeing time is 35min;Heating rate is 2 DEG C/min
D. ultra-high molecular weight polyethylene bonds fixation:
(1) technological principle:After grafting, coating is only capable of being adsorbed on the surface of fiber superhigh molecular weight polyethylene fibers,
Only pass through fixation, i.e. crosslinking between the self-crosslinking and fiber of adhesive can be only achieved certain depth, improve color fastness;
(2) technology preparation:Adhesive is 3mL/L;
(3) process conditions:Tack temperature is 65 DEG C, the bonding time is 25min.
E, described to soap, wash, being dehydrated:
It soaps:Soaping agent 2g/L, temperature are 90 DEG C, the time is 15 minutes;
Washing:Temperature is 60 DEG C, hot water wash 10 minutes, cold water is washed 20 minutes, acid neutralizes is pH=7;
Dehydration:Dewaterer rotating speed:800r/min, dewatering time:8min.
F, described to bake:Baking temperature:100 DEG C, bake the time:8 minutes.
Specific embodiment 2
A kind of colouring method of high-strength polyethylene tooling fabric, includes the following steps:Raw material → weaving → pre-setting → dye
Color → soap, wash, be dehydrated → bakes → finished product.
A, the raw material is:Warp thread weft yarn is the 18.5tex doublet cords of 30/ viscose glue 70 of ultra-high molecular weight polyethylene.
B, the weaving:Using wealthy width air-jet loom weaving, 1/3 twill-weave, it is 650m/min to knit speed, and warp tension is
1600N。
C, the pre-setting:Temperature is:110 DEG C, the time be:8 minutes.
D, the dyeing:
A. cold dyeing viscose:
(1) technical recipe:Low form reactive dye:Activated red X-3B is 2%;Anhydrous sodium sulphate is 30g/L;Soda ash is 15g/L;
(2) process conditions:The fabric for padding dyestuff is wound up on plastic tube, and outsourcing plastic film banks up 24 hours, dyestuff
It is upper at normal temperatures to contaminate viscose fiber;
It soaps:Soaping agent is 3g/L;Temperature is 95 DEG C, and the time is 20 minutes;
Washing:Use temperature for 70 DEG C of hot water wash 15 minutes;Cold water is washed 20 minutes;It is pH=8 that acid, which neutralizes,;
B. ultra-high molecular weight polyethylene graft modification is handled:
(1) technological principle:Coating is a kind of pigment, without substantivity, will not react to form covalent bond with fiber, institute
It is that cation graft modification is carried out again to superhigh molecular weight polyethylene fibers with the most basic absorption principle of coating, makes superelevation
Molecular weight polyethylene fiber is in positive electricity, and superhigh molecular weight polyethylene fibers is on the one hand made firmly to be bonded with coating, another
Aspect addition alkali can improve grafting agent and be combined with the acrylic acid on superhigh molecular weight polyethylene fibers, can improve the suction of coating
Attached performance;
(2) technology preparation:Cation graft agents:5g/L;Sodium hydroxide (30%):5g/L;Bath raio:1:40;
(3) process conditions:Grafting temperature is:65℃;Grafting time is:35min;Washing temperature is:50 DEG C, washing two
Time;
C. ultra-high molecular weight polyethylene pigment dyeing:
(1) technological principle:After carrying out grafting processing to superhigh molecular weight polyethylene fibers, ultra-high molecular weight polyethylene
Fiber is just in positive electricity, so that it is enhanced the adsorption capacity of coating, improves coating to superhigh molecular weight polyethylene fibers
Dye-uptake and dyefastness;
(2) technology preparation:Coating G-18 red is 0.5%;Coating G-22 Huangs are 0.9%;Bath raio is 1:40;
(3) process conditions:Dyeing temperature is 65 DEG C;Dyeing time is 35min;Heating rate is 3 DEG C/min
D. ultra-high molecular weight polyethylene bonds fixation:
(1) technological principle:After grafting, coating is only capable of being adsorbed on the surface of fiber superhigh molecular weight polyethylene fibers,
Only pass through fixation, i.e. crosslinking between the self-crosslinking and fiber of adhesive can be only achieved certain depth, improve color fastness;
(2) technology preparation:Adhesive is 3mL/L;
(3) process conditions:Tack temperature is 65 DEG C, the bonding time is 25min.
E, described to soap, wash, being dehydrated:
It soaps:Soaping agent 3g/L, temperature are 95 DEG C, the time is 20 minutes;
Washing:Temperature is 70 DEG C, hot water wash 15 minutes, cold water is washed 20 minutes, acid neutralizes is pH=8;
Dehydration:Dewaterer rotating speed:900r/min, dewatering time:10min.
F, described to bake:Baking temperature:110 DEG C, bake the time:10 minutes.
Specific embodiment 3
A kind of colouring method of high-strength polyethylene tooling fabric, includes the following steps:Raw material → weaving → pre-setting → dye
Color → soap, wash, be dehydrated → bakes → finished product.
A, the raw material is:Warp thread weft yarn is the 18.5tex doublet cords of 30/ viscose glue 70 of ultra-high molecular weight polyethylene.
B, the weaving:Using wealthy width air-jet loom weaving, 1/3 twill-weave, it is 630m/min to knit speed, and warp tension is
1540N。
C, the pre-setting:Temperature is:103 DEG C, the time be:6 minutes.
D, the dyeing:
A. cold dyeing viscose:
(1) technical recipe:Low form reactive dye:Activated red X-3B is 2%;Anhydrous sodium sulphate is 24g/L;Soda ash is 11g/L;
(2) process conditions:The fabric for padding dyestuff is wound up on plastic tube, and outsourcing plastic film banks up 23 hours, dyestuff
It is upper at normal temperatures to contaminate viscose fiber;
It soaps:Soaping agent is 2.5g/L;Temperature is 92 DEG C, and the time is 17 minutes;
Washing:Use temperature for 64 DEG C of hot water wash 13 minutes;Cold water is washed 20 minutes;It is pH=7 that acid, which neutralizes,;
B. ultra-high molecular weight polyethylene graft modification is handled:
(1) technological principle:Coating is a kind of pigment, without substantivity, will not react to form covalent bond with fiber, institute
It is that cation graft modification is carried out again to superhigh molecular weight polyethylene fibers with the most basic absorption principle of coating, makes superelevation
Molecular weight polyethylene fiber is in positive electricity, and superhigh molecular weight polyethylene fibers is on the one hand made firmly to be bonded with coating, another
Aspect addition alkali can improve grafting agent and be combined with the acrylic acid on superhigh molecular weight polyethylene fibers, can improve the suction of coating
Attached performance;
(2) technology preparation:Cation graft agents:4g/L;Sodium hydroxide (30%):4g/L;Bath raio:1:40;
(3) process conditions:Grafting temperature is:65℃;Grafting time is:35min;Washing temperature is:50 DEG C, washing two
Time;
C. ultra-high molecular weight polyethylene pigment dyeing:
(1) technological principle:After carrying out grafting processing to superhigh molecular weight polyethylene fibers, ultra-high molecular weight polyethylene
Fiber is just in positive electricity, so that it is enhanced the adsorption capacity of coating, improves coating to superhigh molecular weight polyethylene fibers
Dye-uptake and dyefastness;
(2) technology preparation:Coating G-18 red is 0.5%;Coating G-22 Huangs are 0.9%;Bath raio is 1:40;
(3) process conditions:Dyeing temperature is 65 DEG C;Dyeing time is 35min;Heating rate is 2.5 DEG C/min
D. ultra-high molecular weight polyethylene bonds fixation:
(1) technological principle:After grafting, coating is only capable of being adsorbed on the surface of fiber superhigh molecular weight polyethylene fibers,
Only pass through fixation, i.e. crosslinking between the self-crosslinking and fiber of adhesive can be only achieved certain depth, improve color fastness;
(2) technology preparation:Adhesive is 3mL/L;
(3) process conditions:Tack temperature is 65 DEG C, the bonding time is 25min.
E, described to soap, wash, being dehydrated:
It soaps:Soaping agent 2.4g/L, temperature are 93 DEG C, the time is 18 minutes;
Washing:Temperature is 63 DEG C, hot water wash 12 minutes, cold water is washed 20 minutes, acid neutralizes is pH=8;
Dehydration:Dewaterer rotating speed:840r/min, dewatering time:9min.
F, described to bake:Baking temperature:103 DEG C, bake the time:9 minutes.
Superhigh molecular weight polyethylene fibers in the present invention have good mechanical property and chemical property, surface smooth
Nice and cool, friction factor is small, and curling stability is poor, and spinning performance is poor, and yarn feel is hardened, comfort, water imbibition, dyeability, bullet
Property is poor, fusing point is low.And viscose fiber has a good hygroscopicity, high dyeability, the features such as intensity is low, for the high-grade tooling fabric of exploitation,
It gives full play to ultra-high molecular weight polyethylene and viscose rayon and respectively performance advantage and has complementary functions, select ultra-high molecular weight polyethylene
The 18.5tex doublet cords of 30/ viscose glue 70 are weaved as warp, weft yarn raw material using twill-weave, and use reactive dye cold dyeing work
Skill makes viscose fiber paint, and 30% ultra-high molecular weight polyethylene is contaminated on coating, produce product cloth cover is smooth, moisture absorption is ventilative,
Flexible, the easy to clean dyeing top grade tooling fabric of quality.
Dyeing in the present invention is gathered using 70% viscose fiber, the super high molecular weight that 30% is contaminated on coating is contaminated on reactive dye
Ethylene carries out cation graft modification to superhigh molecular weight polyethylene fibers, makes superhigh molecular weight polyethylene fibers in sun
It is charge, improve the absorption property of coating.
The present invention uses cold and hot technique, and dyeing need not heat, energy saving, reduce cost, production process clean environment firendly.
Claims (6)
1. a kind of colouring method of high-strength polyethylene tooling fabric, it is characterised in that:Include the following steps:Raw material → weaving → pre-
Sizing → dyeing → is soaped, washes, being dehydrated → baking → finished product, wherein:The dyeing:
A. cold dyeing viscose:
(1) technical recipe:Low form reactive dye:Activated red X-3B is 2%;Anhydrous sodium sulphate is 20-30g/L;Soda ash is 10-15g/
L;
(2) process conditions:The fabric for padding dyestuff is wound up on plastic tube, and outsourcing plastic film banks up 20-24 hours, dyestuff
It is upper at normal temperatures to contaminate viscose fiber;
It soaps:Soaping agent is 2-3g/L;Temperature is 90-95 DEG C, and the time is 15-20 minutes;
Washing:Use temperature for 60-70 DEG C of hot water wash 10-15 minutes;Cold water is washed 20 minutes;It is pH=7-8 that acid, which neutralizes,;
B. ultra-high molecular weight polyethylene graft modification is handled:
(1) technology preparation:Cation graft agents:2~5g/L;Sodium hydroxide (30%):3~5g/L;Bath raio:1:40;
(2) process conditions:Grafting temperature is:65℃;Grafting time is:35min;Washing temperature is:50 DEG C, washing twice;
C. ultra-high molecular weight polyethylene pigment dyeing:
(1) technology preparation:Coating G-18 red is 0.5%;Coating G-22 Huangs are 0.9%;Bath raio is 1:40;
(2) process conditions:Dyeing temperature is 65 DEG C;Dyeing time is 35min;Heating rate is 2~3 DEG C/min
D. ultra-high molecular weight polyethylene bonds fixation:
(1) technology preparation:Adhesive is 3mL/L;
(2) process conditions:Tack temperature is 65 DEG C, the bonding time is 25min.
2. the colouring method of high-strength polyethylene tooling fabric according to claim 1, it is characterised in that:The raw material is:
Warp thread weft yarn is the 18.5tex doublet cords of 30/ viscose glue 70 of ultra-high molecular weight polyethylene.
3. the colouring method of high-strength polyethylene tooling fabric according to claim 1, it is characterised in that:The weaving:It adopts
With wealthy width air-jet loom weaving, 1/3 twill-weave, it is 600-650m/min, warp tension 1500-1600N to knit speed.
4. the colouring method of high-strength polyethylene tooling fabric according to claim 1, it is characterised in that:The pre-setting:
Temperature is:100-110 DEG C, the time be:5-8 minutes.
5. the colouring method of high-strength polyethylene tooling fabric according to claim 1, it is characterised in that:It is described soap, water
It washes, be dehydrated:
It soaps:Soaping agent 2-3g/L, temperature are 90-95 DEG C, the time is 15-20 minutes;
Washing:Temperature is 60-70 DEG C, hot water wash 10-15 minutes, cold water is washed 20 minutes, acid neutralizes is pH=7-8;
Dehydration:Dewaterer rotating speed:800-900r/min, dewatering time:8-10min.
6. the colouring method of high-strength polyethylene tooling fabric according to claim 1, it is characterised in that:It is described to bake:Roasting
Dry temperature:100-110 DEG C, bake the time:8-10 minutes.