CN109836683A - 一种抗静电塑料膜 - Google Patents
一种抗静电塑料膜 Download PDFInfo
- Publication number
- CN109836683A CN109836683A CN201711212800.XA CN201711212800A CN109836683A CN 109836683 A CN109836683 A CN 109836683A CN 201711212800 A CN201711212800 A CN 201711212800A CN 109836683 A CN109836683 A CN 109836683A
- Authority
- CN
- China
- Prior art keywords
- parts
- plastic film
- antistatic
- antistatic plastic
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种抗静电塑料膜，其特征在于，所述抗静电塑料膜的组分按照重量份如下所示：二羟甲基二羟基环乙烯脲30‑40份、乙烯醋酸乙烯酯共聚物20‑30份、丙烯腈‑乙烯‑苯乙烯共聚物10‑15份、十溴联苯醚5‑10份、聚乙烯蜡5‑10份、硬脂酸钡4‑6份、氢化聚丁二烯1‑2份、高硅氧纤维1‑2份、仲烷基磺酸盐0.2‑0.6份、抗老化剂0.5‑1份、固化剂0.2‑0.4份、分散剂0.2‑0.5份和抗静电剂0.5‑1份。本发明抗静电塑料膜具有良好的物理性能以及抗静电性，可以在应用的过程中很好的克服静电吸附问题。
Description
技术领域
本发明涉及塑料制品技术领域，尤其涉及一种抗静电塑料膜。
背景技术
塑料膜用于包装,以及用作覆膜层。塑料包装及塑料包装产品在市场上所占的份额越来越大，特别是复合塑料软包装，已经广泛地应用于食品、医药、化工等领域，其中又以食品包装所占比例最大，比如饮料包装、速冻食品包装、蒸煮食品包装、快餐食品包装等，这些产品都给人们生活带来了极大的便利。
但是目前的塑料膜普遍存在静电的问题，在使用过程中经常会产生静电吸附，给使用过程中带来麻烦。
发明内容
为解决上述问题，本发明提供了一种抗静电塑料膜。
本发明的技术方案如下：
一种抗静电塑料膜，其特征在于：所述抗静电塑料膜的组分按照重量份如下所示：二羟甲基二羟基环乙烯脲30-40份、乙烯醋酸乙烯酯共聚物20-30份、丙烯腈-乙烯-苯乙烯共聚物10-15份、十溴联苯醚5-10份、聚乙烯蜡5-10份、硬脂酸钡4-6份、氢化聚丁二烯1-2份、高硅氧纤维1-2份、仲烷基磺酸盐0.2-0.6份、抗老化剂0.5-1份、固化剂0.2-0.4份、分散剂0.2-0.5份和抗静电剂0.5-1份。
进一步的，所述抗老化剂为硫代双甲基苯酚、硫代二丙酸双十八醇酯中的一种。
进一步的，所述固化剂为氨乙基哌嗪。
进一步的，所述分散剂为1,6－己二醇双丙烯酸酯、乙撑基双硬脂酰胺中的一种。
进一步的，所述抗静电剂为十八烷基二羟乙基甲基溴化铵。
借由上述方案，本发明至少具有如下优点：
本发明抗静电塑料膜具有良好的物理性能以及抗静电性，可以在应用的过程中很好的克服静电吸附问题。。
具体实施方式
下面结合实施例对本发明的技术方案作如下详细说明。
实施例1
一种抗静电塑料膜，其特征在于：所述抗静电塑料膜的组分按照重量份如下所示：二羟甲基二羟基环乙烯脲35份、乙烯醋酸乙烯酯共聚物24份、丙烯腈-乙烯-苯乙烯共聚物12份、十溴联苯醚7份、聚乙烯蜡6份、硬脂酸钡4份、氢化聚丁二烯1份、高硅氧纤维2份、仲烷基磺酸盐0.4份、抗老化剂0.8份、固化剂0.3份、分散剂0.5份和抗静电剂0.8份。
实施例2
一种抗静电塑料膜，其特征在于：所述抗静电塑料膜的组分按照重量份如下所示：二羟甲基二羟基环乙烯脲36份、乙烯醋酸乙烯酯共聚物30份、丙烯腈-乙烯-苯乙烯共聚物13份、十溴联苯醚8份、聚乙烯蜡10份、硬脂酸钡4份、氢化聚丁二烯2份、高硅氧纤维1份、仲烷基磺酸盐0.6份、抗老化剂0.5份、固化剂0.4份、分散剂0.2份和抗静电剂0.6份。
以上所述仅是本发明的优选实施方式，并不用于限制本发明，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和变型，这些改进和变型也应视为本发明的保护范围。
Claims (5)
1.一种抗静电塑料膜，其特征在于：所述抗静电塑料膜的组分按照重量份如下所示：二羟甲基二羟基环乙烯脲30-40份、乙烯醋酸乙烯酯共聚物20-30份、丙烯腈-乙烯-苯乙烯共聚物10-15份、十溴联苯醚5-10份、聚乙烯蜡5-10份、硬脂酸钡4-6份、氢化聚丁二烯1-2份、高硅氧纤维1-2份、仲烷基磺酸盐0.2-0.6份、抗老化剂0.5-1份、固化剂0.2-0.4份、分散剂0.2-0.5份和抗静电剂0.5-1份。
2.根据权利要求1所述的一种抗静电塑料膜，其特征在于：所述抗老化剂为硫代双甲基苯酚、硫代二丙酸双十八醇酯中的一种。
3.根据权利要求1所述的一种抗静电塑料膜，其特征在于：所述固化剂为氨乙基哌嗪。
4.根据权利要求1所述的一种抗静电塑料膜，其特征在于：所述分散剂为1,6－己二醇双丙烯酸酯、乙撑基双硬脂酰胺中的一种。
5.根据权利要求1所述的一种抗静电塑料膜，其特征在于：所述抗静电剂为十八烷基二羟乙基甲基溴化铵。