CN109773663A - A kind of processing method of engraved glass and stone ceramic mosaic graphic - Google Patents
A kind of processing method of engraved glass and stone ceramic mosaic graphic Download PDFInfo
- Publication number
- CN109773663A CN109773663A CN201910255540.7A CN201910255540A CN109773663A CN 109773663 A CN109773663 A CN 109773663A CN 201910255540 A CN201910255540 A CN 201910255540A CN 109773663 A CN109773663 A CN 109773663A
- Authority
- CN
- China
- Prior art keywords
- glass
- mosaic
- temperature control
- furnace
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the processing methods of a kind of engraved glass and stone ceramic mosaic graphic, the present invention specifically includes the following steps: S1, glass material selection and coloring, S2, modular glass forming, the production of S3, template of stamping, the pressing mold production of S4, glass Mosaic plate, the blasting treatment of S5, glass Mosaic plate, the present invention relates to building material technologies.The processing method of the engraved glass and stone ceramic mosaic graphic, the method that can be achieved to replace engraving machine Carving Machining by using the method that pressing mold is stamped, it is applicable not only to the processing of small lot glass Mosaic, and the processing of high-volume glass Mosaic is generated and is more applicable in, greatly save production and processing time and labour, shorten product term, improve production efficiency, realization improves production method, to realize that inexpensive high-volume processes glass Mosaic, achieve the purpose that not only quick but also easily high-volume glass Mosaic is produced and processed.
Description
Technical field
The present invention relates to building material technology, the processing method of specially a kind of engraved glass and stone ceramic mosaic graphic.
Background technique
Glass Mosaic is a kind of colored finish glass of small dimension, and general requirements is 20 millimeters × 20 millimeters, 30 millimeters
× 30 millimeters, 40 millimeters × 40 millimeters belong to the pieces of glass matter inlaid material of various colors, glass horse with a thickness of 4-6 millimeters
Sai Ke is made of natural mineral matter and glass powder, is safest building materials, its acid and alkali-resistance is corrosion-resistant, colour-fast, is to be most suitable for dress
The building materials on bathroom room wall ground are adornd, it is most small and exquisite finishing material, and it is very more to combine a possibility that changing: having the figure of elephant
Case with the jump of the colour system depth or transition, or is done grain pattern for other ornament materials such as ceramic tiles and is interspersed, the sintering process of glass Mosaic
There are fusion method and sintering process, it is that main production is former that fusion method, which is with quartz sand, lime stone, feldspar, soda ash, colorant and emulsifier,
Material is formed with axis rolling process or plane rolling process after high temperature melt, is finally annealed, sintering process is with cullet and glue
Materials of adhesive is made by techniques such as briquetting, drying, sintering and annealing.
It is the method for directlying adopt engraving machine engraving mostly at present when the pattern to glass Mosaic surface is processed
Pattern processing is carried out, however, such processing method may be only available for the processing to some small lot glass Mosaic, and
For the processing of high-volume glass Mosaic generates, a large amount of production and processing time and labour can be spent using engraving machine engraving
Power, production period limit for length, production efficiency is low, can not achieve and improves to production method, to realize inexpensive high-volume to glass
Mosaic is processed, and mesh that is not only quick but also easily being produced and processed to high-volume glass Mosaic is unable to reach
, so that the processing to the glass Mosaic of production of construction materials enterprise brings great inconvenience.
Summary of the invention
(1) the technical issues of solving
In view of the deficiencies of the prior art, the present invention provides the processing method of a kind of engraved glass and stone ceramic mosaic graphic, solutions
Existing processing method of having determined may be only available for the processing to some small lot glass Mosaic, and for high-volume glass
For mosaic processing generates, a large amount of production and processing time and labour can be spent using engraving machine engraving, production period limit for length,
Production efficiency is low, can not achieve and improves to production method, to realize that inexpensive high-volume processes glass Mosaic
Production is unable to reach not only quickly but also the problem of easily carry out production and processing purpose to high-volume glass Mosaic.
(2) technical solution
In order to achieve the above object, the present invention is achieved by the following technical programs: a kind of engraved glass and stone material Marseille
Gram processing method, specifically includes the following steps:
Selection and the coloring of S1, glass material: the corresponding glass to be processed of selection first, then by the glass-cutting of selection at institute
The glass grain block of specification is needed, then the glass grain block cut is put into smelting furnace and heats the corresponding time under assigned temperature,
So that each glass grain block is quickly melted, backward molten condition under glass in be added needed for color glaze, then lead to
Mixing plant is crossed to carry out being sufficiently mixed stirring, it is achievable to glass coloration；
S2, modular glass forming: the molten glass material that coloring is completed in step S1, which is transported in temperature control furnace, to be reduced
Temperature makes the glass material of molten condition be in the state that melting coexists with solid-state, and keeps glass material under this state equal
Then the even bottom for being laid in temperature control furnace inner wall uses grid rack, squeezes glass material from top to bottom, can make glass material shape
40-60 DEG C is reduced at multimode bulk glass material, while by the temperature of temperature control furnace, glass material is made to maintain multimode block shape:
The production of S3, template of stamping: choosing the high alloy material flitch of fusing point, lays flat and clamps admittedly on engraving machine worktable
It is fixed, engraving program is then inputted into engraving machine according to required engraving pattern, then starts engraving machine and alloy sheets is carved,
Stamp template can be obtained after the completion of engraving；
The pressing mold production of S4, glass Mosaic plate: the stamp template that S3 is obtained is extruded in S2 by the method for pressing mold
On obtained multimode glass material, the temperature of temperature control furnace can control slowly to reduce during pressing mold, until multimode glass
After the complete cooled and solidified of glass material, template of stamping out can be gone, glass Mosaic plate can be obtained；
The blasting treatment of S5, glass Mosaic plate: the glass Mosaic plate that S4 is obtained is taken out out of temperature control furnace, so
The glass Mosaic plate of taking-up is put into sand-blasting machine afterwards, high-pressure sand blast processing is carried out to the surface of glass Mosaic plate, it can
The pattern of glass Mosaic plate surface is set to form stereo concave-convex effect, to can be obtained the glass stone material Marseille completed the process
Gram plate.
Preferably, the dimensions of glass-cutting granulating block can be selected according to duty requirements in the step S1, and
Glass grain block fusion temperature in smelting furnace is 920-990 DEG C, heating time 2-4h.
Preferably, the furnace bottom diameter of temperature control furnace is 0.8-1.5m in the step S2, and furnace depth is 3-6cm, and for the first time
Temperature control furnace is cooled to 500-600 DEG C, and second of temperature control furnace temperature is down to 440-560 DEG C.
Preferably, alloy material flitch is to select vanadium iron in the step S3.
Preferably, the engraving machine selected in the step S3 is digital-controlled carving machine, and the model GF- of digital-controlled carving machine
1325。
It preferably, is to select suction-type dry sand high-pressure sand blast machine, and suction-type dry sand high-pressure sand blast machine in the step S5
Model HJ-6050A.
(3) beneficial effect
The present invention provides the processing methods of a kind of engraved glass and stone ceramic mosaic graphic.Have compared with prior art following
The utility model has the advantages that the processing method of the engraved glass and stone ceramic mosaic graphic, specifically includes the following steps: the selection of S1, glass material
To coloring: the corresponding glass to be processed of selection first, then by the glass-cutting of selection at the glass grain block of required specification, then
The glass grain block cut is put into smelting furnace and is heated under assigned temperature the corresponding time, S2, modular glass forming: by step S1
The middle molten glass material for completing coloring, which is transported in temperature control furnace, reduces temperature, make the glass material of molten condition be in melting with
The state that solid-state coexists, the production of S3, template of stamping: choosing the high alloy material flitch of fusing point, lays flat on engraving machine worktable
It is fixedly clamped, then inputs engraving program, the pressing mold system of S4, glass Mosaic plate into engraving machine according to required engraving pattern
Make: the stamp template that S3 is obtained being extruded on the multimode glass material that S2 is obtained by the method for pressing mold, S5, glass Marseille
The blasting treatment of gram plate: the glass Mosaic plate that S4 is obtained is taken out out of temperature control furnace, then by the glass Marseille of taking-up
Gram plate, which is put into sand-blasting machine, carries out high-pressure sand blast processing, it can be achieved that by using coining to the surface of glass Mosaic plate
The method at quarter is applicable not only to the processing of small lot glass Mosaic come the method for replacing engraving machine Carving Machining, and
The processing of high-volume glass Mosaic is generated and is more applicable in, production and processing time and labour is greatlyd save, shortens production
Time limit improves production efficiency, realizes improve to production method well, to realize inexpensive high-volume to glass horse
Sai Ke is processed, and has been achieved the purpose that not only quick but also has easily been produced and processed to high-volume glass Mosaic, from
And it is highly beneficial to the processing of the glass Mosaic of production of construction materials enterprise.
Detailed description of the invention
Fig. 1 is process flow chart of the invention；
Fig. 2 is the result statistical form figure of present invention comparison case.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
The embodiment of the present invention provides three kinds of technical solutions referring to FIG. 1-2: a kind of engraved glass and stone ceramic mosaic graphic plus
Work method, specifically includes following embodiment:
Embodiment 1
Selection and the coloring of S1, glass material: the corresponding glass to be processed of selection first, then by the glass-cutting of selection at institute
The glass grain block of specification is needed, then the glass grain block cut is put into smelting furnace and heats the corresponding time under assigned temperature,
So that each glass grain block is quickly melted, backward molten condition under glass in be added needed for color glaze, then lead to
It crosses mixing plant to carry out being sufficiently mixed stirring, achievable to glass coloration, the dimensions of glass-cutting granulating block can be according to work
Condition demand is selected, and glass grain block fusion temperature in smelting furnace is 960 DEG C, heating time 3h；
S2, modular glass forming: the molten glass material that coloring is completed in step S1, which is transported in temperature control furnace, to be reduced
Temperature makes the glass material of molten condition be in the state that melting coexists with solid-state, and keeps glass material under this state equal
Then the even bottom for being laid in temperature control furnace inner wall uses grid rack, squeezes glass material from top to bottom, can make glass material shape
50 DEG C are reduced at multimode bulk glass material, while by the temperature of temperature control furnace, glass material is made to maintain multimode block shape, temperature control
The furnace bottom diameter of furnace is 1m, and furnace depth is 5cm, and first time temperature control furnace is cooled to 400 DEG C, and second of temperature control furnace temperature is down to
500 DEG C:
The production of S3, template of stamping: choosing the high alloy material flitch of fusing point, lays flat and clamps admittedly on engraving machine worktable
It is fixed, engraving program is then inputted into engraving machine according to required engraving pattern, then starts engraving machine and alloy sheets is carved,
It can be obtained stamp template after the completion of engraving, alloy material flitch is to select vanadium iron, and engraving machine is digital-controlled carving machine, and numerical control
The model GF-1325 of engraving machine；
The pressing mold production of S4, glass Mosaic plate: the stamp template that S3 is obtained is extruded in S2 by the method for pressing mold
On obtained multimode glass material, the temperature of temperature control furnace can control slowly to reduce during pressing mold, until multimode glass
After the complete cooled and solidified of glass material, template of stamping out can be gone, glass Mosaic plate can be obtained；
The blasting treatment of S5, glass Mosaic plate: the glass Mosaic plate that S4 is obtained is taken out out of temperature control furnace, so
The glass Mosaic plate of taking-up is put into sand-blasting machine afterwards, high-pressure sand blast processing is carried out to the surface of glass Mosaic plate, it can
The pattern of glass Mosaic plate surface is set to form stereo concave-convex effect, to can be obtained the glass stone material Marseille completed the process
Suction-type dry sand high-pressure sand blast machine, and the model HJ-6050A of suction-type dry sand high-pressure sand blast machine can be selected in gram plate.
Embodiment 2
Selection and the coloring of S1, glass material: the corresponding glass to be processed of selection first, then by the glass-cutting of selection at institute
The glass grain block of specification is needed, then the glass grain block cut is put into smelting furnace and heats the corresponding time under assigned temperature,
So that each glass grain block is quickly melted, backward molten condition under glass in be added needed for color glaze, then lead to
It crosses mixing plant to carry out being sufficiently mixed stirring, achievable to glass coloration, the dimensions of glass-cutting granulating block can be according to work
Condition demand is selected, and glass grain block fusion temperature in smelting furnace is 920 DEG C, heating time 2h；
S2, modular glass forming: the molten glass material that coloring is completed in step S1, which is transported in temperature control furnace, to be reduced
Temperature makes the glass material of molten condition be in the state that melting coexists with solid-state, and keeps glass material under this state equal
Then the even bottom for being laid in temperature control furnace inner wall uses grid rack, squeezes glass material from top to bottom, can make glass material shape
40-60 DEG C is reduced at multimode bulk glass material, while by the temperature of temperature control furnace, glass material is made to maintain multimode block shape,
The furnace bottom diameter of temperature control furnace is 0.8m, and furnace depth is 3cm, and first time temperature control furnace is cooled to 500 DEG C, second of temperature control furnace temperature
It is down to 440 DEG C:
The production of S3, template of stamping: choosing the high alloy material flitch of fusing point, lays flat and clamps admittedly on engraving machine worktable
It is fixed, engraving program is then inputted into engraving machine according to required engraving pattern, then starts engraving machine and alloy sheets is carved,
It can be obtained stamp template after the completion of engraving, alloy material flitch is to select vanadium iron, and engraving machine is digital-controlled carving machine, and numerical control
The model GF-1325 of engraving machine；
The pressing mold production of S4, glass Mosaic plate: the stamp template that S3 is obtained is extruded in S2 by the method for pressing mold
On obtained multimode glass material, the temperature of temperature control furnace can control slowly to reduce during pressing mold, until multimode glass
After the complete cooled and solidified of glass material, template of stamping out can be gone, glass Mosaic plate can be obtained；
The blasting treatment of S5, glass Mosaic plate: the glass Mosaic plate that S4 is obtained is taken out out of temperature control furnace, so
The glass Mosaic plate of taking-up is put into sand-blasting machine afterwards, high-pressure sand blast processing is carried out to the surface of glass Mosaic plate, it can
The pattern of glass Mosaic plate surface is set to form stereo concave-convex effect, to can be obtained the glass stone material Marseille completed the process
Suction-type dry sand high-pressure sand blast machine, and the model HJ-6050A of suction-type dry sand high-pressure sand blast machine can be selected in gram plate.
Embodiment 3
Selection and the coloring of S1, glass material: the corresponding glass to be processed of selection first, then by the glass-cutting of selection at institute
The glass grain block of specification is needed, then the glass grain block cut is put into smelting furnace and heats the corresponding time under assigned temperature,
So that each glass grain block is quickly melted, backward molten condition under glass in be added needed for color glaze, then lead to
It crosses mixing plant to carry out being sufficiently mixed stirring, achievable to glass coloration, the dimensions of glass-cutting granulating block can be according to work
Condition demand is selected, and glass grain block fusion temperature in smelting furnace is 990 DEG C, heating time 4h；
S2, modular glass forming: the molten glass material that coloring is completed in step S1, which is transported in temperature control furnace, to be reduced
Temperature makes the glass material of molten condition be in the state that melting coexists with solid-state, and keeps glass material under this state equal
Then the even bottom for being laid in temperature control furnace inner wall uses grid rack, squeezes glass material from top to bottom, can make glass material shape
40-60 DEG C is reduced at multimode bulk glass material, while by the temperature of temperature control furnace, glass material is made to maintain multimode block shape,
The furnace bottom diameter of temperature control furnace is 1.5m, and furnace depth is 6cm, and first time temperature control furnace is cooled to 600 DEG C, second of temperature control furnace temperature
It is down to 560 DEG C:
The production of S3, template of stamping: choosing the high alloy material flitch of fusing point, lays flat and clamps admittedly on engraving machine worktable
It is fixed, engraving program is then inputted into engraving machine according to required engraving pattern, then starts engraving machine and alloy sheets is carved,
It can be obtained stamp template after the completion of engraving, alloy material flitch is to select vanadium iron, and engraving machine is digital-controlled carving machine, and numerical control
The model GF-1325 of engraving machine；
The pressing mold production of S4, glass Mosaic plate: the stamp template that S3 is obtained is extruded in S2 by the method for pressing mold
On obtained multimode glass material, the temperature of temperature control furnace can control slowly to reduce during pressing mold, until multimode glass
After the complete cooled and solidified of glass material, template of stamping out can be gone, glass Mosaic plate can be obtained；
The blasting treatment of S5, glass Mosaic plate: the glass Mosaic plate that S4 is obtained is taken out out of temperature control furnace, so
The glass Mosaic plate of taking-up is put into sand-blasting machine afterwards, high-pressure sand blast processing is carried out to the surface of glass Mosaic plate, it can
The pattern of glass Mosaic plate surface is set to form stereo concave-convex effect, to can be obtained the glass stone material Marseille completed the process
Suction-type dry sand high-pressure sand blast machine, and the model HJ-6050A of suction-type dry sand high-pressure sand blast machine can be selected in gram plate.
Compare case
Certain production of construction materials enterprise is carried out using the glass Mosaic production method of 1-3 of the embodiment of the present invention with batch glass horse
Match gram production and processing, while using conventional production process carry out with batch production, in process of production carry out the production time and
Product quality Qualification is counted.
As shown in table Fig. 2, the time used in the same batch glass Mosaic of the glass Mosaic production method production of embodiment 1
For 5.7 working hours, and producing glass Mosaic quality Qualification is " excellent ", and the glass Marseille of embodiment 2 and embodiment 3
Time used in the same batch glass Mosaic of gram production method production is respectively 7.3 working hours and 6.1 working hours, and produces glass
Glass mosaic quality Qualification is " excellent ", the time used in the same batch glass Mosaic than the production of conventional production process
Short, producing glass Mosaic quality Qualification is " good ", therefore the method stamped by using pressing mold can be achieved in the present invention
Method to replace engraving machine Carving Machining, is applicable not only to the processing of small lot glass Mosaic, and for large quantities of
It measures glass Mosaic processing generation to be more applicable in, greatlys save production and processing time and labour, shorten product term, improve
Production efficiency, realizes improve to production method well, to realize that inexpensive high-volume carries out glass Mosaic
Processing has achieved the purpose that not only quick but also has easily produced and processed to high-volume glass Mosaic, thus to building materials
The processing of the glass Mosaic of manufacturing enterprise is highly beneficial.
It should be noted that, in this document, relational terms such as first and second and the like are used merely to a reality
Body or operation are distinguished with another entity or operation, are deposited without necessarily requiring or implying between these entities or operation
In any actual relationship or order or sequence.Moreover, the terms "include", "comprise" or its any other variant are intended to
Non-exclusive inclusion, so that the process, method, article or equipment including a series of elements is not only wanted including those
Element, but also including other elements that are not explicitly listed, or further include for this process, method, article or equipment
Intrinsic element.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (6)
1. the processing method of a kind of engraved glass and stone ceramic mosaic graphic, it is characterised in that: specifically includes the following steps:
Selection and the coloring of S1, glass material: the corresponding glass to be processed of selection first, then by the glass-cutting of selection at required rule
Then the glass grain block cut is put into smelting furnace and heats the corresponding time under assigned temperature by the glass grain block of lattice size, make each
A glass grain block can quickly melt, backward molten condition under glass in be added needed for color glaze, then by stirring
Mixing equipment carries out being sufficiently mixed stirring, achievable to glass coloration；
S2, modular glass forming: the molten glass material that coloring is completed in step S1, which is transported in temperature control furnace, reduces temperature,
So that the glass material of molten condition is in the state that melting coexists with solid-state, and keeps glass material under this state evenly laid out
In the bottom of temperature control furnace inner wall, grid rack is then used, squeezes glass material from top to bottom, glass material can be made to form multimode
Both bulk glasses material, while the temperature of temperature control furnace is reduced 40-60 DEG C, so that glass material is maintained multimode block shape:
The production of S3, template of stamping: choosing the high alloy material flitch of fusing point, lays flat and is fixedly clamped on engraving machine worktable, so
It inputs engraving program into engraving machine according to required engraving pattern afterwards, then starts engraving machine and alloy sheets are carved, carve
Stamp template can be obtained after the completion；
The pressing mold production of S4, glass Mosaic plate: the stamp template that S3 is obtained is extruded in S2 by the method for pressing mold and is obtained
Multimode glass material on, can control the temperature of temperature control furnace slowly to reduce during pressing mold, until multimode glass material
After expecting complete cooled and solidified, template of stamping out can be gone, glass Mosaic plate can be obtained；
The blasting treatment of S5, glass Mosaic plate: the glass Mosaic plate that S4 is obtained is taken out out of temperature control furnace, then will
The glass Mosaic plate of taking-up is put into sand-blasting machine and carries out high-pressure sand blast processing to the surface of glass Mosaic plate, can make glass
The pattern of glass mosaic plate surface forms stereo concave-convex effect, to can be obtained the glass stone ceramic mosaic plate completed the process
Material.
2. the processing method of a kind of engraved glass and stone ceramic mosaic graphic according to claim 1, it is characterised in that: the step
The dimensions of glass-cutting granulating block can be selected according to duty requirements in rapid S1, and glass grain block melts temperature in smelting furnace
Degree is 920-990 DEG C, heating time 2-4h.
3. the processing method of a kind of engraved glass and stone ceramic mosaic graphic according to claim 1, it is characterised in that: the step
The furnace bottom diameter of temperature control furnace is 0.8-1.5m in rapid S2, and furnace depth is 3-6cm, and first time temperature control furnace is cooled to 500-600 DEG C,
Second of temperature control furnace temperature is down to 440-560 DEG C.
4. the processing method of a kind of engraved glass and stone ceramic mosaic graphic according to claim 1, it is characterised in that: the step
Alloy material flitch is to select vanadium iron in rapid S3.
5. the processing method of a kind of engraved glass and stone ceramic mosaic graphic according to claim 1, it is characterised in that: the step
The engraving machine selected in rapid S3 is digital-controlled carving machine, and the model GF-1325 of digital-controlled carving machine.
6. the processing method of a kind of engraved glass and stone ceramic mosaic graphic according to claim 1, it is characterised in that: the step
It is suction-type dry sand high-pressure sand blast machine of selecting in rapid S5, and the model HJ-6050A of suction-type dry sand high-pressure sand blast machine.