CN103144489B - Manufacturing method for large azure stone wall - Google Patents
Manufacturing method for large azure stone wall Download PDFInfo
- Publication number
- CN103144489B CN103144489B CN201310035587.5A CN201310035587A CN103144489B CN 103144489 B CN103144489 B CN 103144489B CN 201310035587 A CN201310035587 A CN 201310035587A CN 103144489 B CN103144489 B CN 103144489B
- Authority
- CN
- China
- Prior art keywords
- raw material
- azure
- azure stone
- scale
- stone wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a manufacturing method for azure stone handicrafts, and particularly relates to a manufacturing method for a large azure stone wall. The manufacturing method for the large azure stone wall includes the following steps: 1), paving a flat plate on a flat base plate of a steel structure; 2), carving embossments on the flat plate with greasy filth; 3), making a high-temperature plaster mould from an accomplished greasy filth sample; 4), placing the mould horizontally into a calcinator; 5), placing azure stone materials in various colors into corresponding parts of the high-temperature plaster mould in proportion sequentially; 6), performing calcination; 7), grinding azure stone surfaces manually after azure stones are discharged from the calcinator, performing flat surface grinding with a flat-grinding machine and edging with an edge grinding machine, and cutting the azure stones to be of required sizes with a cutting machine; and 8), processing the whole wall through two abrasive blasting processes including coarse sanding and fine sanding, and accomplishing post stage processing through chemical surface treatment. The azure stone handicrafts manufactured with the manufacturing method have the advantage of being large-sized, attractive, flawless, and the like. The manufacturing method for the large azure stone wall is suitable for manufacturing of decorative walls.
Description
Technical field
The present invention relates to a kind of making method of azure stone handicraft, particularly relate to a kind of making method of large-scale azure stone wall.
Background technology
Prior art, when production azure stone handicraft, needs to adopt resin, wax to be that medium turns over mould to sample, translates into gypsum mold, then produce with gypsum mold.Prior art does not produce the experience of large-scale azure stone handicraft, and coloured glaze product is larger, more easily occurs flaw, such as, and aberration, bubble etc.Adopt prior art to produce large-scale azure stone handicraft cannot avoid producing above-mentioned flaw.If application number is the Chinese invention patent of 201110137296.8, disclose a kind of manufacturing process of azure stone handicraft, comprise the following steps:
according to the profile of coloured glaze, design is applicable to the schema for gemmy metalwork of this coloured glaze;
schema is sprayed mimeograph stencil by forming mill, then mimeograph stencil is processed into silver-colored version by casting reverse mould;
the silver-colored version of further processing, makes itself and coloured glaze mutually coincide;
metalwork work in-process are produced according to silver-colored version;
metalwork work in-process are machined to finished product, and by cameo incrustation on metalwork;
gemmy metalwork is assembled on coloured glaze.Step
be made up of following steps:
utilize mold special purpose rubber to wrap up silver-colored version, and through thermocompression forming, in rubber model, cause the cavity with silver-colored version same shape, thus obtain the rubber moulding that can be used for casting, so that batch production is for the wax sample of casting;
rubber moulding is cut open by certain requirement, takes out silver-colored version, to obtain the special rubber moulding of casting;
again by the rubber moulding made casting repeatedly, to obtain wax part;
repair the surface of wax part, remove the husky gallery on wax sample, steam bubble and other defect of repairing, and make wax part surface smoothing smooth and easy, conform to quality requirements;
wax part is assembled in and rod wax is formed tree-shaped, obtain jewellery bases by once-cast;
perfusion calcium plaster, makes wax tree be enclosed in gypsum, can leaving the model space of wax part, for pouring into a mould silvering solution, casting out product after dewaxing in gypsum;
again by high temperature, the moisture in removing gypsum, melts outflow by the wax part in gypsum simultaneously completely, makes the cavity forming various Jewelry Model in gypsum; Silvering solution is injected in plaster mould to obtain batch jewellery strand, removing gypsum.The prior art that this invented technology is namely previously described, the method is applicable to making small-sized azure stone handicraft, if make large-scale azure stone handicraft, then easily occurs the flaw such as aberration, bubble.
Summary of the invention
The object of the invention is the technical problem for easily producing the flaws such as aberration bubble when solving and adopt prior art to make large-scale azure stone handicraft, a kind of making method of large-scale azure stone wall is provided.
Above-mentioned technical purpose of the present invention is achieved by the following technical programs:
A making method for large-scale azure stone wall, comprises the following steps:
design effect figure on request, makes the flat underside of rigid structural, and spreads flat board by design sketch size;
on flat board, design sketch finishing impression embossment is pressed with greasy filth;
the mud sample completed is translated into high temperature gypsum mold;
this die horizontal is put into calcining furnace;
by design sketch color by assorted coloured glaze raw material, put into the corresponding site of high temperature gypsum mold with order in proportion;
setting temperature control, makes coloured glaze raw material and calcining furnace one at first slowly be preheated to 900-1200 DEG C through the time of 3-5 days, then enters the hot stage constant temperature 1-3 days of 900-1200 DEG C, come out of the stove after being cooled to room temperature;
after coming out of the stove, coloured glaze surface manual grinding, then through flat-grinding machine face machined flat, edge polisher edging, cutting machine cut into and require size;
entirety is processed through coarse sand, fine sand twice blasting craft, and then completes post-production through chemical conversion treatment.
Preferred as technique scheme, step
described raw material is the assorted coloured glaze raw material of square.
Preferred as technique scheme, the assorted coloured glaze raw material of described square is the raw material of size between 1cm × 1cm × 1cm ~ 5cm × 5cm × 5cm.
Usual coloured glaze raw material is the raw material of round pie, diameter about 10cm, thickness about 1cm.Then the weight of the assorted raw material of Size calculation as required, then takes suitable amount by after these round pie raw material crushings.The allotment of concrete color and the calculating of weight belong to the routine techniques means of those skilled in the art, and need the size according to finished product, shape, color to decide.The square raw material size that the present invention adopts is between 1cm × 1cm × 1cm ~ 5cm × 5cm × 5cm, and color is varied, is a kind of pure coloured glaze raw material.As adopted routine techniques to allocate raw material, then easily occur that raw material is not of uniform size, and the problem that feed particles is less than normal, the technical problem brought thus is, the bubble pockety that in large-scale coloured glaze product, as easy as rolling off a log appearance is a large amount of, the size of bubble is at 1mm
3left and right, even larger, impact is greatly produced on the outward appearance of coloured glaze product.Through research, contriver finds that this phenomenon is relevant with the factor such as size, regular degree of raw material, after mainly raw material being put into high temperature gypsum mold, through calcining, raw material becomes liquid from solid, the raw material be deposited in high temperature plaster mould can subside, if raw material is irregular, between raw material, difference is large, then when subsiding, uneven, not only easily occur cavity (i.e. bubble), and colored raw material arrival specified location becomes very uncontrollable, easily produces aberration.When raw material particle size is bigger than normal time, be difficult to the works making the alternate magnificent mansion of color, namely the Color control of the specified location of product will become difficult; If the granularity of raw material is less than normal, then easily there is a large amount of bubbles in interiors of products, and this impact for the coloured glaze product of exquisite ornamental value will be fatal.The present inventor is through studying for a long period of time, find that raw material being replaced to the square raw material of size between 1cm*1cm*1cm ~ 5cm*5cm*5cm can solve the problems of the technologies described above, replace to the square raw material of size between 1cm*1cm*1cm ~ 5cm*5cm*5cm by raw material and more easily control raw material arrival specified location, avoid the generation of aberration, more easily control not producing of bubble.Why prior art is not furtherd investigate mainly because prior art is not seen the developing direction of this industry on maximization future development to this technology, and azure stone handicraft does the larger accuracy requirement for controlling is higher.Trace it to its cause, applicant thinks to adopt the gypsum mold of miniaturization to calcine, and the phenomenon of subsiding comparatively speaking can be little many, and namely the contraction ratio of raw material is less.In the manufacturing processed of the azure stone handicraft maximized, the contraction ratio of raw material is obviously so great that many.Obviously this has higher requirement to the control of technique.
Preferred as technique scheme, adds in described high temperature gypsum mold to have and reinforces steel construction and high-temperature-resistant structure material to ensure the thermally-stabilised of high temperature gypsum mold.
Because high temperature plaster mould build of the present invention is large, and gypsum is more crisp, and therefore contriver adds reinforcing steel construction in high temperature gypsum mold.Described reinforcing steel construction works just as the reinforcing bar in concrete, and the intensity of high temperature gypsum mold is increased.
Preferred as technique scheme, step
in, be preheated to 950-1100 DEG C, hot stage is 950-1100 DEG C.
Preferred as technique scheme, step
in, be preheated to 980-1080 DEG C, hot stage is 980-1080 DEG C.
Preferred as technique scheme, step
in, be preheated to 1000 DEG C, hot stage is 1000 DEG C.
Preferred as technique scheme, step
in, the flat underside of described rigid structural is steel construction base plate.
The present invention has following beneficial effect:
1, the present invention adopts the square raw material of size between 1cm × 1cm × 1cm ~ 5cm × 5cm × 5cm can solve the bubble pockety that in large-scale coloured glaze product, easily appearance is a large amount of, easily produces the technical problem of aberration;
2, utilize the azure stone handicraft that the inventive method is obtained, there is maximization, the advantage such as attractive in appearance, indefectible, be suitable for the making of decorative wall;
3, production method of the present invention, directly on greasy filth, carry out finishing impression embossment, can direct reverse mould, do not need to adopt conventional method: adopt silica gel to smear master, after waiting silica gel shaping, scratch silica gel with blade again, take out master, obtain Silicon moulds, then casting in Silicon moulds, obtains cere, carry out reverse mould with cere again, make plaster mould; Therefore, production method of the present invention saves the step producing Silicon moulds, saves the step producing cere, operates more simple and convenient, remarkable improving production efficiency, reduces production cost.
Embodiment
This specific embodiment is only explanation of the invention, is not limitation of the present invention.Any change that those skilled in the art make after the specification sheets reading the application, as long as within the limited range of claims of the application, all will be subject to the protection of patent law.
Embodiment one
A making method for large-scale azure stone wall, comprises the following steps:
design effect figure on request, makes steel construction base plate by design sketch size, and spreads flat board;
Design sketch is of a size of 4.5m × 1.5m, and steel construction base plate size is also 4.5m × 1.5m;
on flat board, design sketch finishing impression embossment is pressed with greasy filth;
Greasy filth is laid on flat board, then presses design sketch finishing impression embossment;
the mud sample completed is translated into high temperature gypsum mold, adds in high temperature gypsum mold and reinforce steel construction and high-temperature-resistant structure material to ensure the thermally-stabilised of high temperature gypsum mold;
Mud sample refers to the mud sample that greasy filth finishing impression becomes, and turn over the routine techniques means that mould belongs to those skilled in the art, therefore not to repeat here;
this die horizontal is put into calcining furnace;
by design sketch color by assorted coloured glaze raw material, put into the corresponding site of high temperature gypsum mold with order in proportion;
setting temperature control, makes coloured glaze raw material and calcining furnace one at first through the preheating of 3 days, then enters the hot stage constant temperature 1 day of 900 DEG C, comes out of the stove after being cooled to room temperature;
after coming out of the stove, coloured glaze surface manual grinding, then cuts into require size through large-scale flat-grinding machine face machined flat, edge polisher edging, cutting machine;
entirety is processed through coarse sand, fine sand twice blasting craft, and then completes post-production through chemical conversion treatment.
Step
described raw material is the assorted coloured glaze raw material of square.Raw material size is between 1cm × 1cm × 1cm ~ 5cm × 5cm × 5cm, and color is varied, is a kind of pure coloured glaze raw material.
Through the process of above-mentioned 8 steps, can obtain attractive in appearance, flawless large-scale azure stone wall, this wall can be used for the places such as temple pagoda as decorative constructional materials.The number of bubbles of described large-scale azure stone wall is no more than 15, and size is no more than 1 mm
3.
Embodiment two
A making method for large-scale azure stone wall, comprises the following steps:
design effect figure on request, makes steel construction base plate by design sketch size, and spreads flat board;
Design sketch is of a size of 4.5m × 1.5m, and steel construction base plate size is also 4.5m × 1.5m;
on flat board, design sketch finishing impression embossment is pressed with greasy filth;
Greasy filth is laid on flat board, then presses design sketch finishing impression embossment;
the mud sample completed is translated into high temperature gypsum mold, adds in high temperature gypsum mold and reinforce steel construction and high-temperature-resistant structure material to ensure the thermally-stabilised of high temperature gypsum mold;
Mud sample refers to the mud sample that greasy filth finishing impression becomes, and turn over the routine techniques means that mould belongs to those skilled in the art, therefore not to repeat here;
this die horizontal is put into calcining furnace;
by design sketch color by assorted coloured glaze raw material, put into the corresponding site of high temperature gypsum mold with order in proportion;
setting temperature control, makes coloured glaze raw material and calcining furnace one at first through the preheating of 3 days, then enters the hot stage constant temperature 2 days of 950 DEG C, comes out of the stove after being cooled to room temperature;
after coming out of the stove, coloured glaze surface manual grinding, then cuts into require size through large-scale flat-grinding machine face machined flat, edge polisher edging, cutting machine;
entirety is processed through coarse sand, fine sand twice blasting craft, and then completes post-production through chemical conversion treatment.
Step
described raw material is the assorted coloured glaze raw material of square.Raw material size is between 1cm × 1cm × 1cm ~ 5cm × 5cm × 5cm, and color is varied, is a kind of pure coloured glaze raw material.
Through the process of above-mentioned 8 steps, can obtain attractive in appearance, flawless large-scale azure stone wall, this wall can be used for the places such as temple pagoda as decorative constructional materials.The number of bubbles of described large-scale azure stone wall is no more than 8, and size is no more than 0.6 mm
3.
Embodiment three
A making method for large-scale azure stone wall, comprises the following steps:
design effect figure on request, makes steel construction base plate by design sketch size, and spreads flat board;
Design sketch is of a size of 4.5m × 1.5m, and steel construction base plate size is also 4.5m × 1.5m;
on flat board, design sketch finishing impression embossment is pressed with greasy filth;
Greasy filth is laid on flat board, then presses design sketch finishing impression embossment;
the mud sample completed is translated into high temperature gypsum mold, adds in high temperature gypsum mold and reinforce steel construction and high-temperature-resistant structure material to ensure the thermally-stabilised of high temperature gypsum mold;
Mud sample refers to the mud sample that greasy filth finishing impression becomes, and turn over the routine techniques means that mould belongs to those skilled in the art, therefore not to repeat here;
this die horizontal is put into calcining furnace;
by design sketch color by assorted coloured glaze raw material, put into the corresponding site of high temperature gypsum mold with order in proportion;
setting temperature control, makes coloured glaze raw material and calcining furnace one at first through the preheating of 3 days, then enters the hot stage constant temperature 3 days of 1000 DEG C, comes out of the stove after being cooled to room temperature;
after coming out of the stove, coloured glaze surface manual grinding, then cuts into require size through large-scale flat-grinding machine face machined flat, edge polisher edging, cutting machine;
entirety is processed through coarse sand, fine sand twice blasting craft, and then completes post-production through chemical conversion treatment.
Step
described raw material is the assorted coloured glaze raw material of square.Raw material size is between 1cm × 1cm × 1cm ~ 5cm × 5cm × 5cm, and color is varied, is a kind of pure coloured glaze raw material.
Through the process of above-mentioned 8 steps, can obtain attractive in appearance, flawless large-scale azure stone wall, this wall can be used for the places such as temple pagoda as decorative constructional materials.The number of bubbles of described large-scale azure stone wall is no more than 6, and size is no more than 0.5 mm
3.
Embodiment four
A making method for large-scale azure stone wall, comprises the following steps:
design effect figure on request, makes steel construction base plate by design sketch size, and spreads flat board;
Design sketch is of a size of 4.5m × 1.5m, and steel construction base plate size is also 4.5m × 1.5m;
on flat board, design sketch finishing impression embossment is pressed with greasy filth;
Greasy filth is laid on flat board, then presses design sketch finishing impression embossment;
the mud sample completed is translated into high temperature gypsum mold, adds in high temperature gypsum mold and reinforce steel construction and high-temperature-resistant structure material to ensure the thermally-stabilised of high temperature gypsum mold;
Mud sample refers to the mud sample that greasy filth finishing impression becomes, and turn over the routine techniques means that mould belongs to those skilled in the art, therefore not to repeat here;
this die horizontal is put into calcining furnace;
by design sketch color by assorted coloured glaze raw material, put into the corresponding site of high temperature gypsum mold with order in proportion;
setting temperature control, makes coloured glaze raw material and calcining furnace one at first through the preheating of 4 days, then enters the hot stage constant temperature 3 days of 1000 DEG C, comes out of the stove after being cooled to room temperature;
after coming out of the stove, coloured glaze surface manual grinding, then cuts into require size through large-scale flat-grinding machine face machined flat, edge polisher edging, cutting machine;
entirety is processed through coarse sand, fine sand twice blasting craft, and then completes post-production through chemical conversion treatment.
Step
described raw material is the assorted coloured glaze raw material of square.Raw material size is between 1cm × 1cm × 1cm ~ 5cm × 5cm × 5cm, and color is varied, is a kind of pure coloured glaze raw material.
Through the process of above-mentioned 8 steps, can obtain attractive in appearance, flawless large-scale azure stone wall, this wall can be used for the places such as temple pagoda as decorative constructional materials.The number of bubbles of described large-scale azure stone wall is no more than 5, and size is no more than 1 mm
3.
Embodiment five
A making method for large-scale azure stone wall, comprises the following steps:
design effect figure on request, makes steel construction base plate by design sketch size, and spreads flat board;
Design sketch is of a size of 4.5m × 1.5m, and steel construction base plate size is also 4.5m × 1.5m;
on flat board, design sketch finishing impression embossment is pressed with greasy filth;
Greasy filth is laid on flat board, then presses design sketch finishing impression embossment;
the mud sample completed is translated into high temperature gypsum mold, adds in high temperature gypsum mold and reinforce steel construction and high-temperature-resistant structure material to ensure the thermally-stabilised of high temperature gypsum mold;
Mud sample refers to the mud sample that greasy filth finishing impression becomes, and turn over the routine techniques means that mould belongs to those skilled in the art, therefore not to repeat here;
this die horizontal is put into calcining furnace;
by design sketch color by assorted coloured glaze raw material, put into the corresponding site of high temperature gypsum mold with order in proportion;
setting temperature control, makes coloured glaze raw material and calcining furnace one at first through the preheating of 4 days, then enters the hot stage constant temperature 3 days of 1100 DEG C, comes out of the stove after being cooled to room temperature;
after coming out of the stove, coloured glaze surface manual grinding, then cuts into require size through large-scale flat-grinding machine face machined flat, edge polisher edging, cutting machine;
entirety is processed through coarse sand, fine sand twice blasting craft, and then completes post-production through chemical conversion treatment.
Step
described raw material is the assorted coloured glaze raw material of square.Raw material size is between 1cm × 1cm × 1cm ~ 5cm × 5cm × 5cm, and color is varied, is a kind of pure coloured glaze raw material.
Through the process of above-mentioned 8 steps, can obtain attractive in appearance, flawless large-scale azure stone wall, this wall can be used for the places such as temple pagoda as decorative constructional materials.The number of bubbles of described large-scale azure stone wall is no more than 6, and size is no more than 1 mm
3.
Embodiment six
A making method for large-scale azure stone wall, comprises the following steps:
design effect figure on request, makes steel construction base plate by design sketch size, and spreads flat board;
Design sketch is of a size of 4.5m × 1.5m, and steel construction base plate size is also 4.5m × 1.5m;
on flat board, design sketch finishing impression embossment is pressed with greasy filth;
Greasy filth is laid on flat board, then presses design sketch finishing impression embossment;
the mud sample completed is translated into high temperature gypsum mold, adds in high temperature gypsum mold and reinforce steel construction and high-temperature-resistant structure material to ensure the thermally-stabilised of high temperature gypsum mold;
Mud sample refers to the mud sample that greasy filth finishing impression becomes, and turn over the routine techniques means that mould belongs to those skilled in the art, therefore not to repeat here;
this die horizontal is put into calcining furnace;
by design sketch color by assorted coloured glaze raw material, put into the corresponding site of high temperature gypsum mold with order in proportion;
setting temperature control, makes coloured glaze raw material and calcining furnace one at first through the preheating of 5 days, then enters the hot stage constant temperature 3 days of 1200 DEG C, comes out of the stove after being cooled to room temperature;
after coming out of the stove, coloured glaze surface manual grinding, then cuts into require size through large-scale flat-grinding machine face machined flat, edge polisher edging, cutting machine;
entirety is processed through coarse sand, fine sand twice blasting craft, and then completes post-production through chemical conversion treatment.
Step
described raw material is the assorted coloured glaze raw material of square.Raw material size is between 1cm × 1cm × 1cm ~ 5cm × 5cm × 5cm, and color is varied, is a kind of pure coloured glaze raw material.
Through the process of above-mentioned 8 steps, can obtain attractive in appearance, flawless large-scale azure stone wall, this wall can be used for the places such as temple pagoda as decorative constructional materials.The number of bubbles of described large-scale azure stone wall is no more than 8, and size is no more than 1 mm
3.
Embodiment seven
A making method for large-scale azure stone wall, comprises the following steps:
design effect figure on request, makes steel construction base plate by design sketch size, and spreads flat board;
Design sketch is of a size of 4.5m × 1.5m, and steel construction base plate size is also 4.5m × 1.5m;
on flat board, design sketch finishing impression embossment is pressed with greasy filth;
Greasy filth is laid on flat board, then presses design sketch finishing impression embossment;
the mud sample completed is translated into high temperature gypsum mold, adds in high temperature gypsum mold and reinforce steel construction and high-temperature-resistant structure material to ensure the thermally-stabilised of high temperature gypsum mold;
Mud sample refers to the mud sample that greasy filth finishing impression becomes, and turn over the routine techniques means that mould belongs to those skilled in the art, therefore not to repeat here;
this die horizontal is put into calcining furnace;
by design sketch color by assorted coloured glaze raw material, put into the corresponding site of high temperature gypsum mold with order in proportion;
setting temperature control, makes coloured glaze raw material and calcining furnace one at first through the preheating of 5 days, then enters the hot stage constant temperature 3 days of 1200 DEG C, comes out of the stove after being cooled to room temperature;
after coming out of the stove, coloured glaze surface manual grinding, then cuts into require size through large-scale flat-grinding machine face machined flat, edge polisher edging, cutting machine;
entirety is processed through coarse sand, fine sand twice blasting craft, and then completes post-production through chemical conversion treatment.
Step
described raw material is the assorted coloured glaze raw material of square.Raw material size is between 1cm × 1cm × 1cm ~ 5cm × 5cm × 5cm, and color is varied, is a kind of pure coloured glaze raw material.
Through the process of above-mentioned 8 steps, can obtain attractive in appearance, flawless large-scale azure stone wall, this wall can be used for the places such as temple pagoda as decorative constructional materials.The number of bubbles of described large-scale azure stone wall is no more than 5, and size is no more than 1 mm
3.
Claims (6)
1. a making method for large-scale azure stone wall, comprises the following steps:
1. design effect figure on request, makes the flat underside of rigid structural, and spreads flat board by design sketch size;
2. on flat board, design sketch finishing impression embossment is pressed with greasy filth;
3. the mud sample completed is translated into high temperature gypsum mold;
4. this die horizontal is put into calcining furnace;
5. press design sketch color by assorted coloured glaze raw material, put into the corresponding site of high temperature gypsum mold with order in proportion;
6. set temperature control, make coloured glaze raw material and calcining furnace one at first slowly be preheated to 900-1200 DEG C through the time of 3-5 days, then enter the hot stage constant temperature 1-3 days of 900-1200 DEG C, come out of the stove after being cooled to room temperature;
7. after coming out of the stove, coloured glaze surface manual grinding, then through flat-grinding machine face machined flat, edge polisher edging, cutting machine cut into and require size;
8. entirety is processed through coarse sand, fine sand twice blasting craft, and then completes post-production through chemical conversion treatment;
Step 5. described raw material is the assorted coloured glaze raw material of square, and size is between 1cm × 1cm × 1cm ~ 5cm × 5cm × 5cm.
2. the making method of a kind of large-scale azure stone wall according to claim 1, is characterized in that: add in described high temperature gypsum mold and have reinforcing steel construction and high-temperature-resistant structure material to ensure the thermally-stabilised of high temperature gypsum mold.
3. the making method of a kind of large-scale azure stone wall according to claim 1, is characterized in that: step 6. in, be preheated to 950-1100 DEG C, hot stage is 950-1100 DEG C.
4. the making method of a kind of large-scale azure stone wall according to claim 1, is characterized in that: step 6. in, be preheated to 980-1080 DEG C, hot stage is 980-1080 DEG C.
5. the making method of a kind of large-scale azure stone wall according to claim 1, is characterized in that: step 6. in, be preheated to 1000 DEG C, hot stage is 1000 DEG C.
6. the making method of a kind of large-scale azure stone wall according to claim 1, is characterized in that: step 1. in, the flat underside of described rigid structural is steel construction base plate.