CN109734870A - 一种耐水耐压封堵材料的制备方法 - Google Patents

一种耐水耐压封堵材料的制备方法 Download PDF

Info

Publication number
CN109734870A
CN109734870A CN201811602055.4A CN201811602055A CN109734870A CN 109734870 A CN109734870 A CN 109734870A CN 201811602055 A CN201811602055 A CN 201811602055A CN 109734870 A CN109734870 A CN 109734870A
Authority
CN
China
Prior art keywords
component
parts
dosage
tdi
plugging material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201811602055.4A
Other languages
English (en)
Other versions
CN109734870B (zh
Inventor
魏浩
夏天琦
高闪
欧阳肖
张智嘉
李�瑞
王国军
马宁
张馨月
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Harbin Engineering University
Original Assignee
Harbin Engineering University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Harbin Engineering University filed Critical Harbin Engineering University
Priority to CN201811602055.4A priority Critical patent/CN109734870B/zh
Publication of CN109734870A publication Critical patent/CN109734870A/zh
Application granted granted Critical
Publication of CN109734870B publication Critical patent/CN109734870B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于封堵技术领域，特别涉及一种耐水耐压的聚氨酯封堵材料的制备方法。该方法包括：将A组分搅拌均匀；常温下以A:B为2:1的比例加入B组分，并进行搅拌均匀；将混合料倒于预先准备的塑料膜上，待其反应发热发泡后迅速用手填充于漏水点处。A组分包括聚四氢呋喃二醇、蓖麻油、1,4丁二醇、硫酸盐水泥、氧化钙、氯化钙、聚甲基丙烯酰胺以及二月桂酸二丁基锡、三乙醇胺的一种或两种。B组分包括二苯基甲烷二异氰酸酯MDI、甲苯二异氰酸酯TDI、二苯甲烷‑4,4‑二异氰酸酯IPDI的一种或两种。本发明使用简单、固化速度快，仅几十秒即可固化；粘接强度高，在潮湿水泥板附着力可达2.0MPa；抗压性好且环保无毒，可应用在地铁、高铁、公路隧道漏水的快速封堵中。

Description

一种耐水耐压封堵材料的制备方法
技术领域
本发明属于封堵技术领域，特别涉及一种耐水耐压的聚氨酯封堵材料的制备方法。
背景技术
封堵材料是凝结硬化快，强度大，膨胀系数小的材料，广泛应用于房屋、隧道、地下管道、水坝等工程领域。目前常用的封堵材料有丙烯酸盐、单组分聚氨酯、无机封堵材料等。中国发明专利号为CN20161073623.4的专利公开了一种PU-EP水坝快速堵漏材料及其制备方法。该材料属于聚氨酯与酚醛环氧树脂相结合，具有在水介质中固化快、伸长率高、与潮湿混凝土粘接强度大等特点。但固化时间相对较长，大于十分钟，且无带压施工介绍。目前大部分封堵材料在有水环境中都存在粘接力不好的问题，特别是在有流水及水压力的情况下，难以实现封堵的要求。
发明内容
为了克服上述现有技术取得缺点与不足，本发明的首要目的在于提供一种耐水耐压的封堵材料的制备方法。
本发明的目的通过下述技术方案实现：
一种耐水耐压封堵材料的制备方法，该方法包括以下步骤：
步骤1：准备A组分和B组分，其中A组分包括：聚四氢呋喃二醇、蓖麻油、1,4丁二醇、硫酸盐水泥、氧化钙、氯化钙、聚甲基丙烯酰胺以及二月桂酸二丁基锡、三乙醇胺的一种或两种；B组分包括：二苯基甲烷二异氰酸酯MDI、甲苯二异氰酸酯TDI、二苯甲烷-4,4-二异氰酸酯IPDI的一种或两种；
步骤2：将A组分搅拌均匀；
步骤3：常温下以A:B为2:1的比例加入B组分，并进行搅拌均匀得到混合料；
步骤4：将混合料倒于预先准备的塑料膜上，待其反应发热发泡后迅速用手填充于漏水点处。
所述的A组分中聚四氢呋喃二醇用量0到20份，蓖麻油用量0到30份，丙三醇用量0到5份，1,4丁二醇用量0到5份，硫酸盐水泥用量0到30份，氧化钙用量0到20份，氯化钙用量0到5份，聚甲基丙烯酰胺用量2到5份，二月桂酸二丁基锡、三乙醇胺的一种或两种用量0到2份。
所述的B组分中二苯基甲烷二异氰酸酯MDI、甲苯二异氰酸酯TDI、二苯甲烷-4,4-二异氰酸酯IPDI的一种或两种用量0-50份。
本发明的有益效果在于：
(1)使用简单、固化速度快，仅几十秒即可固化；
(2)粘接强度高，在潮湿水泥板附着力可达2.0MPa；
(3)抗压性好
(4)环保无毒
具体实施方式
下面结合实施案例对本发明做进一步描述，但本发明的实施方式不限于此。
一种耐水耐压的聚氨酯封堵材料，该材料由比例为2:1的A组分和B组分组成：
其中A组分包括：
B组分包括：
二苯基甲烷二异氰酸酯(MDI)、甲苯二异氰酸酯(TDI)、二苯甲烷-4,4-二异氰酸酯(IPDI)的一种或两种 0-50份
上述带水、带压堵漏材料的制备方法,包括以下操作步骤：
将A组分按计量搅拌均匀后，常温下以A:B为2:1的比例加入B组分，并进行搅拌均匀。
将混合料倒于预先准备的塑料膜上，待其反应发热发泡后迅速用手填充于漏水点处，保证物料能够完全将漏点覆盖，按住1min后，可松开。
上述高弹性无溶剂聚氨酯封堵材料可应用在地铁、高铁、公路隧道漏水的快速封堵中。
实施案例1
(1)A组分
(2)B组分
MDI 32.5份
(3)将A组分和B组分按照比例2:1混合均匀,得到新型耐水耐压封堵材料。性能指标见表1。
实施案例2
(1)A组分
(2)B组分
IPDI 31.5份
(3)将A组分和B组分按照比例2:1混合均匀,得到新型耐水耐压封堵材料。性能指标见表1。
实施案例3
(1)A组分
(2)B组分
IPDI、TDI 33
(3)将A组分和B组分按照比例2:1混合均匀,得到新型耐水耐压封堵材料。性能指标见表1。
表1高弹性无溶剂封堵材料性能
上述实施例为本发明较佳的实施方式,但本发明的实施方式并不受上述实施例的限制,其他的任何未背离本发明的精神实质与原理下所作的改变、修饰、替代、组合、简化，均应为等效的置换方式，都包含在本发明的保护范围之内。

Claims (3)

1.一种耐水耐压封堵材料的制备方法，其特征在于，该方法包括以下步骤：
步骤1：准备A组分和B组分，其中A组分包括：聚四氢呋喃二醇、蓖麻油、1,4丁二醇、硫酸盐水泥、氧化钙、氯化钙、聚甲基丙烯酰胺以及二月桂酸二丁基锡、三乙醇胺的一种或两种；B组分包括：二苯基甲烷二异氰酸酯MDI、甲苯二异氰酸酯TDI、二苯甲烷-4,4-二异氰酸酯IPDI的一种或两种；
步骤2：将A组分搅拌均匀；
步骤3：常温下以A:B为2:1的比例加入B组分，并进行搅拌均匀得到混合料；
步骤4：将混合料倒于预先准备的塑料膜上，待其反应发热发泡后迅速用手填充于漏水点处。
2.根据权利要求1所述的一种耐水耐压封堵材料的制备方法，其特征在于：所述的A组分中聚四氢呋喃二醇用量0到20份，蓖麻油用量0到30份，丙三醇用量0到5份，1,4丁二醇用量0到5份，硫酸盐水泥用量0到30份，氧化钙用量0到20份，氯化钙用量0到5份，聚甲基丙烯酰胺用量2到5份，二月桂酸二丁基锡、三乙醇胺的一种或两种用量0到2份。
3.根据权利要求1所述的一种耐水耐压封堵材料的制备方法，其特征在于：所述的B组分中二苯基甲烷二异氰酸酯MDI、甲苯二异氰酸酯TDI、二苯甲烷-4,4-二异氰酸酯IPDI的一种或两种用量0-50份。
CN201811602055.4A 2018-12-26 2018-12-26 一种耐水耐压封堵材料的制备方法 Active CN109734870B (zh)