CN109732724A - A kind of oiling process of jade santal - Google Patents
A kind of oiling process of jade santal Download PDFInfo
- Publication number
- CN109732724A CN109732724A CN201811649838.8A CN201811649838A CN109732724A CN 109732724 A CN109732724 A CN 109732724A CN 201811649838 A CN201811649838 A CN 201811649838A CN 109732724 A CN109732724 A CN 109732724A
- Authority
- CN
- China
- Prior art keywords
- santal
- layer
- beautiful
- oiling process
- acrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of oiling process of beautiful santal comprising following steps: the wooden embryo material that puts one's child in a boarding nursery is put into constant temperature and humidity room, and keeping room temperature section is 30-70 degrees Celsius, and humidity section is 45%-60%, and liposuction processing is dried；The wooden embryo material that puts one's child in a boarding nursery of dry liposuction is placed into 60 days formation planks in room temperature and 60% humidity environment；Polychlorostyrene rouge acrylate, tripropylene glycol diacrylate rouge, six acrylate of diamyl tetrol is added and mixes, is coated uniformly in wood plate surface, then spontaneously dries maintenance at least 48 hours.The present invention is handled by drying liposuction for the first time, internal a large amount of greases and moisture are drained, polychlorostyrene rouge acrylate, tripropylene glycol diacrylate rouge, six acrylate of diamyl tetrol are added simultaneously, the mixing of the three can enable this wooden and form affinity with this layer, simultaneously, the mixing of three after drying, can reach with grease it is close merge, wooden effective be bonded to reach outer layer grease with this.
Description
Technical field
The invention belongs to wood working process fields, and in particular to a kind of oiling process of jade santal.
Background technique
Beautiful santal is also known as green wingceltis, sets water then heavy included fragrance, is always the first-class of rare engraving, decoration and furniture
Timber, wooden to give out unique santal taste, because natural growing pullets are slow, thus natural storage is extremely limited, decorative pattern it is clear it is lively,
Varying color is obvious.In the existing technique for being applied to beautiful santal, there has been no the technologies for carrying out the direct oiling in surface, this is because it contains
Have more rich organic substance, under closed film its organic substance can not evaporate will be formed in wood surface it is sparkling and crystal-clear
Exquisitely carved cotton-shaped crystal, this is caused by organic matter abundant contained by characteristic in green wingceltis.It is rich in grease, so can be with light
Power is variable to dissolve yellow, green, the blue multiple color for keynote, but also in that this problem, causes to have been scalded rear oil by boiled water
Rouge is easy to emerge to form particle.
Summary of the invention
Can oil the technique of effect on the jade santal surface the technical problem to be solved in the present invention is to provide a kind of.
A kind of oiling process of beautiful santal of the present invention comprising following steps:
A. the wooden embryo material that puts one's child in a boarding nursery is put into constant temperature and humidity room, and keeping room temperature section is 30-70 degrees Celsius, and humidity section is
Liposuction processing is dried in 45%-60%；
B. the wooden embryo material that puts one's child in a boarding nursery by dry liposuction places 60 days formation planks in room temperature and 60% humidity environment；
C. polychlorostyrene rouge acrylate, tripropylene glycol diacrylate rouge, six acrylate of diamyl tetrol is added and mixes, uniformly
Coated in wood plate surface, maintenance at least 48 hours is then spontaneously dried.
As further describing to a kind of above-mentioned oiling process of beautiful santal, the wooden embryo material that puts one's child in a boarding nursery uniformly is stacked.
As further describing to a kind of above-mentioned oiling process of beautiful santal, the drying care environments in step C are temperature
15-20 degrees Celsius of degree, humidity 45%-60%.
It further include step D: in wood plate surface successively as further describing to a kind of above-mentioned oiling process of beautiful santal
It coats UV prime coat, prevent spitting oil reservoir, hardening primer layer, stiffened putty layer and wear-resistant primer layer, every layer of coating need to wait respectively
Next layer is coated after drying.
As further describing to a kind of above-mentioned oiling process of beautiful santal, the UV prime coat drying temperature in step D
It is 85 degrees Celsius, prevents that spitting oil reservoir, hardening primer layer, stiffened putty layer and wear-resistant primer layer drying temperature is 150 degrees Celsius.
It further include step E: coated sand after step D as further describing to a kind of above-mentioned oiling process of beautiful santal
Light prime coat, clear primer layer and top coat layer, the drying temperature of sanding prime coat are 150 degrees Celsius.
The beneficial effects of the present invention are: by drying liposuction for the first time processing, by internal a large amount of greases and moisture into
Row is drained, while polychlorostyrene rouge acrylate, tripropylene glycol diacrylate rouge, six acrylate of diamyl tetrol is added, the three's
Mixing can enable this wooden and form affinity with this layer, meanwhile, the mixing of three can reach closely after drying with grease
Fusion, wooden effective be bonded to reach outer layer grease with this.
Specific embodiment
A kind of oiling process of beautiful santal of the present invention comprising following steps:
A. the wooden embryo material that puts one's child in a boarding nursery is put into constant temperature and humidity room, and keeping room temperature section is 30-70 degrees Celsius, and humidity section is
Liposuction processing is dried in 45%-60%；
B. the wooden embryo material that puts one's child in a boarding nursery by dry liposuction places 60 days formation planks in room temperature and 60% humidity environment；
C. polychlorostyrene rouge acrylate, tripropylene glycol diacrylate rouge, six acrylate of diamyl tetrol is added and mixes, uniformly
Coated in wood plate surface, maintenance at least 48 hours is then spontaneously dried.
During above-mentioned, polychlorostyrene rouge acrylate, tripropylene glycol diacrylate rouge, diamyl tetrol six acrylate
Mixing can enable this wooden and form affinity with this layer, meanwhile, the mixing of three can reach closely after drying with grease
Fusion, wooden effective be bonded to reach outer layer grease with this.
As further describing to a kind of above-mentioned oiling process of beautiful santal, the wooden embryo material that puts one's child in a boarding nursery uniformly is stacked.
As further describing to a kind of above-mentioned oiling process of beautiful santal, the drying care environments in step C are temperature
15-20 degrees Celsius of degree, humidity 45%-60%.
It further include step D: in wood plate surface successively as further describing to a kind of above-mentioned oiling process of beautiful santal
It coats UV prime coat, prevent spitting oil reservoir, hardening primer layer, stiffened putty layer and wear-resistant primer layer, every layer of coating need to wait respectively
Next layer is coated after drying.And effect is coated in order to reach preferably to oil, it is applied in wood plate surface by above-mentioned multilayer
It covers, can protect timber, and since bottom coating bonding force is close, thus every layer oil can effectively ensure that its stability,
It avoids falling off.
As further describing to a kind of above-mentioned oiling process of beautiful santal, the UV prime coat drying temperature in step D
It is 85 degrees Celsius, prevents that spitting oil reservoir, hardening primer layer, stiffened putty layer and wear-resistant primer layer drying temperature is 150 degrees Celsius.
It further include step E: coated sand after step D as further describing to a kind of above-mentioned oiling process of beautiful santal
Light prime coat, clear primer layer and top coat layer, the drying temperature of sanding prime coat are 150 degrees Celsius.The painting of a variety of paint layers
It covers, while can playing a protective role, also appearance can be made more aesthetically pleasing.
The above is not intended to limit the scope of the present invention, and all technical spirits according to the present invention are to above
Any modification, equivalent variations and modification made by embodiment, all of which are still within the scope of the technical scheme of the invention.
Claims (6)
1. a kind of oiling process of jade santal, which comprises the steps of:
A. the wooden embryo material that puts one's child in a boarding nursery is put into constant temperature and humidity room, and keeping room temperature section is 30-70 degrees Celsius, and humidity section is
Liposuction processing is dried in 45%-60%；
B. the wooden embryo material that puts one's child in a boarding nursery by dry liposuction places 60 days formation planks in room temperature and 60% humidity environment；
C. polychlorostyrene rouge acrylate, tripropylene glycol diacrylate rouge, six acrylate of diamyl tetrol is added and mixes, uniformly coats
In wood plate surface, maintenance at least 48 hours is then spontaneously dried.
2. a kind of oiling process of beautiful santal according to claim 1, it is characterised in that: the wooden embryo material that puts one's child in a boarding nursery is uniform
It stacks.
3. a kind of oiling process of beautiful santal according to claim 1, it is characterised in that: the dry maintenance ring in step C
Border is 15-20 degrees Celsius of temperature, humidity 45%-60%.
4. a kind of oiling process of beautiful santal according to claim 1, which is characterized in that further include step D: in wood plate surface
On successively coat UV prime coat, it is anti-spit oil reservoir, hardening primer layer, stiffened putty layer and wear-resistant primer layer, coat every layer of need point
Next layer is coated after not etc. not to be dried.
5. a kind of oiling process of beautiful santal according to claim 4, it is characterised in that: the UV prime coat in step D is dry
Dry temperature is 85 degrees Celsius, prevents that spitting oil reservoir, hardening primer layer, stiffened putty layer and wear-resistant primer layer drying temperature is 150
Degree Celsius.
6. a kind of oiling process of beautiful santal according to claim 1, which is characterized in that further include step E after step D:
Sanding prime coat, clear primer layer and top coat layer are coated, the drying temperature of sanding prime coat is 150 degrees Celsius.