CN105965654A - Flat recombined bamboo floor with natural color and paint production technology of flat recombined bamboo floor - Google Patents
Flat recombined bamboo floor with natural color and paint production technology of flat recombined bamboo floor Download PDFInfo
- Publication number
- CN105965654A CN105965654A CN201610442044.9A CN201610442044A CN105965654A CN 105965654 A CN105965654 A CN 105965654A CN 201610442044 A CN201610442044 A CN 201610442044A CN 105965654 A CN105965654 A CN 105965654A
- Authority
- CN
- China
- Prior art keywords
- coating
- coated
- coating weight
- weight
- bamboo floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a flat recombined bamboo floor with a natural color and a paint production technology of the flat recombined bamboo floor. The flat recombined bamboo floor with the natural color comprises a recombined bamboo floor body subjected to thickness determination and fine sanding, wherein tenoning is performed on the periphery of the recombined bamboo floor body, and mortise joint parts are formed; the surface of the recombined bamboo floor body is sequentially coated with a water-based primer coating, an anti-cracking oil coating, a heavy putty coating, a hardened primer coating, a first transparent primer coating, a wear-resistant primer coating, a second transparent primer coating, a sanding primer coating and a finish paint coating. Besides, the back surface of the recombined bamboo floor body is coated with a back paint coating. The flat recombined bamboo floor with the natural color is good in paint film brightness, high in adhesive force and good in permeability, is free of pinholes, obvious raised grains and bright lines, avoids paint attachment, has flat and smooth paint surface and natural, fine and exquisite texture and has the characteristics of large density, high strength, impact resistance and wear resistance, the feet feel is comfortable, and sound absorption and insulation effects are good; the flat recombined bamboo floor can be wear-resistant for a long term, can be dampproof, and is suitable for being used in damp places.
Description
Technical field
The present invention relates to a kind of heavy bamboo floor and paint production technique thereof, be a kind of heavy bamboo plane true qualities ground in particular
Plate and paint production technique thereof.
Background technology
Solid wooden floor board presents various form due to various wooden color and veins differences, is well received by consumers.But
Solid wooden floor board needs to consume substantial amounts of timber, timber resource shortage, becomes wood growth cycle long, falls trees the most in a large number, to ring
Bigger destruction is caused in border.And Phyllostachys pubescens Mazei ex H.de Lebaie is because its growth cycle is short, aboundresources, recyclability is high, and Phyllostachys pubescens Mazei ex H.de Lebaie applies to field, floor
More and more universal, the most generally praise highly wood substituted by bamboo, the most even with bamboo victory wood.
The heavy bamboo floor of main flow is still with heavy bamboo plane true qualities floor as classics the most on the market, heavy bamboo plane true qualities floor
Praised highly by consumer, yet with the paint production technique also imperfection on existing heavy bamboo plane true qualities floor, cause existing
Heavy bamboo plane true qualities floor lacquer painting coarse, paint film luminance difference, permeability are poor, pin hole, obvious ripple glaze, bright line, oil easily occur
Paint slips extension etc., and texture is the finest and the smoothest, poor adhesive force, and tolerance wear resistance is poor, and it is uneven that use a period of time occurs as soon as tone, and
And moisture protection is poor, be not suitable for being applied to moist place.
Summary of the invention
Based on above-mentioned the deficiencies in the prior art, it is an object of the invention to provide a kind of heavy bamboo plane true qualities floor and oil thereof
Paint production technology.The heavy bamboo plane true qualities floor paint film good brightness of the present invention, adhesive force is strong, permeability good, free of pinholes, without substantially
Ripple glaze, without bright line, slip extension, lacquer painting flat smooth without paint, texture is natural, fine and smooth, exquisite, has that density is big, intensity is high, resistance to
Impact, anti abrasive feature, comfortable foot feeling, sound-absorbing soundproof effect is good；Can be long-term resistance to frayed, and can be moistureproof, also it is applicable to tide
Wet place.
Technical program of the present invention lies in: a kind of heavy bamboo plane true qualities floor.This heavy bamboo plane true qualities floor include through
The heavy bamboo floor body of fixed thick washed ore.The perimembranous mortise of described heavy bamboo floor body forms dovetail.Described heavy bamboo floor body
Surface be coated with aqueous priming paint coating, anticracking oil coating, heavy putty coating, hardening primer coating, the first clear bottom successively
Lacquer coat, wear-resistant primer coating, the second transparent priming coating, sanding primer coating and topcoat.Described heavy bamboo floor body
Backsize have back of the body lacquer coat.
The coating weight of described aqueous priming paint coating is 6-10g/；The coating weight of described anticracking oil coating is 15-25g/；
Described heavy putty coating is coated with at twice, and the coating weight being coated with first is 30-40g/, and the coating weight being again coated with is 20-
30g/㎡；The coating weight of described hardening primer coating is 20-30g/；The coating weight of described first transparent priming coating is 20-
30g/㎡；The coating weight of described wear-resistant primer coating is 15-25 g/；Described second transparent priming coating is coated with at twice, first
The coating weight of secondary coating is 15-25g/, and the coating weight being again coated with is 10-20g/；The coating of described sanding primer coating
Amount is 5-10 g/；Described topcoat is coated with at twice, and the coating weight being coated with first is 5-9g/, the coating being again coated with
Amount is 4-8g/；The coating weight of described back of the body lacquer coat is 10-18g/.
In a preferred approach, the coating weight of described aqueous priming paint coating is 8g/；The coating weight of described anticracking oil coating is
20g/㎡；Described heavy putty coating is coated with at twice, and the coating weight being coated with first is 35g/, and the coating weight being again coated with is
25g/㎡；The coating weight of described hardening primer coating is 20g/；The coating weight of described first transparent priming coating is 25g/；
The coating weight of described wear-resistant primer coating is 20g/；Described second transparent priming coating is coated with at twice, the painting being coated with first
Cloth amount is 20g/, and the coating weight being again coated with is 15g/；The coating weight of described sanding primer coating is 10g/；Described
Lacquer coat is coated with at twice, and the coating weight being coated with first is 7g/, and the coating weight being again coated with is 6g/；Described back of the body lacquer coat
Coating weight be 14g/.
Technical program of the present invention lies in: the paint production technique on a kind of heavy bamboo plane true qualities floor.This paint production work
Skill includes heavy bamboo floor body, sequentially includes the following steps:
Step 1, the surface of heavy bamboo floor body be coated with aqueous priming paint, coating weight is 6-10g/, then use 80 degree infrared
Line is dried, and forms aqueous priming paint coating；
Step 2, add in anticracking oil its parts by weight 1/8 cross-linking agent, the surface of heavy bamboo floor body be coated with anticracking
Oil, coating weight is 15-25g/, and is dried to half-dried, forms anticracking oil coating；
Step 3, at the heavy putty of the surface of heavy bamboo floor body coating, be coated with at twice, the coating weight being coated with first is 30-
40g/, is dried after 70% employing abrasive band sanding；The coating weight being again coated with is 20-30g/, and reach 70% be dried, formed
Heavy putty coating；
Step 4, the surface of heavy bamboo floor body be coated with hardening primer, coating weight is 20-30g/, and reach 70% be dried, shape
Become hardening primer coating；
Step 5, the surface of heavy bamboo floor body be coated with transparent priming, coating weight is 20-30g/, and reach 70% be dried, adopt
Use abrasive band sanding, form the first transparent priming coating；
Step 6, the surface of heavy bamboo floor body be coated with wear-resistant primer, coating weight is 15-25 g/, and is dried to half-dried, shape
Become wear-resistant primer coating；
Step 7, the surface of heavy bamboo floor body be coated with transparent priming, be coated with at twice, the coating weight being coated with first is 15-
25g/, and it is dry to reach 70%；The coating weight being again coated with is 10-20g/, and reach 70% be dried, form the second clear bottom
Lacquer coat；
Step 8, the surface of heavy bamboo floor body be coated with sanding priming paint, coating weight is 5-10 g/, and reach 70% be dried, adopt
Use abrasive band sanding, form sanding primer coating；
Step 9, the surface of heavy bamboo floor body be coated with finish paint, be coated with at twice, the coating weight being coated with first is 5-9g/,
And be dried to half-dried；The coating weight being again coated with is 4-8g/, and reach 100% be dried, formed topcoat；
Step 10, heavy bamboo floor body backsize carry on the back paint, coating weight is 14g/, and reach 100% be dried, formed the back of the body
Lacquer coat.
In a preferred approach, the coating weight of described aqueous priming paint coating is 8g/；The coating weight of described anticracking oil coating is
20g/㎡；Described heavy putty coating is coated with at twice, and the coating weight being coated with first is 35g/, and the coating weight being again coated with is
25g/㎡；The coating weight of described hardening primer coating is 20g/；The coating weight of described first transparent priming coating is 25g/；
The coating weight of described wear-resistant primer coating is 20g/；Described second transparent priming coating is coated with at twice, the painting being coated with first
Cloth amount is 20g/, and the coating weight being again coated with is 15g/；The coating weight of described sanding primer coating is 10g/；Described
Lacquer coat is coated with at twice, and the coating weight being coated with first is 7g/, and the coating weight being again coated with is 6g/；Described back of the body lacquer coat
Coating weight be 14g/.
In a preferred approach, before step 1, described heavy bamboo floor body also have passed through fixed thick washed ore processing, and carries out
Except silk is processed.
In a preferred approach, between step 4 and step 5, mortise processing has also been carried out, in order at heavy bamboo floor body
Perimembranous forms dovetail.
The beneficial effects of the present invention is: the heavy bamboo plane true qualities floor paint film good brightness of the present invention, adhesive force are strong, penetrating
Property good, free of pinholes, slip extensions, lacquer painting flat smooth without obvious ripple glaze, without bright line, without paint, texture is natural, fine and smooth, exquisite, has
Have that density is big, intensity is high, impact resistance, anti abrasive feature, comfortable foot feeling, sound-absorbing soundproof effect is good；Can be long-term resistance to frayed, and
Can be moistureproof, also it is applicable to moist place.
Accompanying drawing explanation
Fig. 1 is the structural representation on heavy bamboo plane true qualities floor.
Fig. 2 is the paint production process chart on heavy bamboo plane true qualities floor.
Label declaration: 1-heavy bamboo floor body 2-dovetail 3-aqueous priming paint coating 4-anticracking oil coating 5-
Heavy putty coating 6-hardening primer coating 7-the first transparent priming coating 8-wear-resistant primer coating 9-second is transparent
Primer coating 10-sanding primer coating 11-topcoat 12-carries on the back lacquer coat.
Detailed description of the invention
By describing the technology contents of the present invention, structural feature in detail, being realized purpose and effect, below in conjunction with embodiment
And coordinate accompanying drawing to be explained in detail.
As it is shown in figure 1, the structural representation that Fig. 1 is heavy bamboo plane true qualities floor.It should be understood that Fig. 1 is only
Explanation technical scheme and the schematic diagram that shows, the most therefore limit true form and the thickness of the present invention.
The heavy bamboo plane true qualities floor of the present invention includes the heavy bamboo floor body 1 through fixed thick washed ore.Described heavy bamboo floor
The perimembranous mortise of body forms dovetail 2.The surface of described heavy bamboo floor body is coated with aqueous priming paint coating 3, anticracking successively
Oil coating 4, heavy putty coating 5, hardening primer coating the 6, first transparent priming coating 7, wear-resistant primer coating 8, second are transparent
Primer coating 9, sanding primer coating 10 and topcoat 11.The backsize of described heavy bamboo floor body has back of the body lacquer coat 12.
The coating weight of above-mentioned aqueous priming paint coating is 6-10g/；The coating weight of described anticracking oil coating is 15-25g/；
Described heavy putty coating is coated with at twice, and the coating weight being coated with first is 30-40g/, and the coating weight being again coated with is 20-
30g/㎡；The coating weight of described hardening primer coating is 20-30g/；The coating weight of described first transparent priming coating is 20-
30g/㎡；The coating weight of described wear-resistant primer coating is 15-25 g/；Described second transparent priming coating is coated with at twice, first
The coating weight of secondary coating is 15-25g/, and the coating weight being again coated with is 10-20g/；The coating of described sanding primer coating
Amount is 5-10 g/；Described topcoat is coated with at twice, and the coating weight being coated with first is 5-9g/, the coating being again coated with
Amount is 4-8g/；The coating weight of described back of the body lacquer coat is 10-18g/.
In the present embodiment, the coating weight of described aqueous priming paint coating is 8g/；The coating weight of described anticracking oil coating is
20g/㎡；Described heavy putty coating is coated with at twice, and the coating weight being coated with first is 35g/, and the coating weight being again coated with is
25g/㎡；The coating weight of described hardening primer coating is 20g/；The coating weight of described first transparent priming coating is 25g/；
The coating weight of described wear-resistant primer coating is 20g/；Described second transparent priming coating is coated with at twice, the painting being coated with first
Cloth amount is 20g/, and the coating weight being again coated with is 15g/；The coating weight of described sanding primer coating is 10g/；Described
Lacquer coat is coated with at twice, and the coating weight being coated with first is 7g/, and the coating weight being again coated with is 6g/；Described back of the body lacquer coat
Coating weight be 14g/.
As in figure 2 it is shown, the paint production technique on above-mentioned heavy bamboo plane true qualities floor.Sequentially include the following steps:
Step 1, the surface of heavy bamboo floor body be coated with aqueous priming paint, coating weight is 6-10g/, then use 80 degree infrared
Line is dried, and forms aqueous priming paint coating；
Step 2, add in anticracking oil its parts by weight 1/8 cross-linking agent, the surface of heavy bamboo floor body be coated with anticracking
Oil, coating weight is 15-25g/, and is dried to half-dried, forms anticracking oil coating；
Step 3, at the heavy putty of the surface of heavy bamboo floor body coating, be coated with at twice, the coating weight being coated with first is 30-
40g/, is dried after 70% employing abrasive band sanding；The coating weight being again coated with is 20-30g/, and reach 70% be dried, formed
Heavy putty coating；
Step 4, the surface of heavy bamboo floor body be coated with hardening primer, coating weight is 20-30g/, and reach 70% be dried, shape
Become hardening primer coating；
Step 5, the surface of heavy bamboo floor body be coated with transparent priming, coating weight is 20-30g/, and reach 70% be dried, adopt
Use abrasive band sanding, form the first transparent priming coating；
Step 6, the surface of heavy bamboo floor body be coated with wear-resistant primer, coating weight is 15-25 g/, and is dried to half-dried, shape
Become wear-resistant primer coating；
Step 7, the surface of heavy bamboo floor body be coated with transparent priming, be coated with at twice, the coating weight being coated with first is 15-
25g/, and it is dry to reach 70%；The coating weight being again coated with is 10-20g/, and reach 70% be dried, form the second clear bottom
Lacquer coat；
Step 8, the surface of heavy bamboo floor body be coated with sanding priming paint, coating weight is 5-10 g/, and reach 70% be dried, adopt
Use abrasive band sanding, form sanding primer coating；
Step 9, the surface of heavy bamboo floor body be coated with finish paint, be coated with at twice, the coating weight being coated with first is 5-9g/,
And be dried to half-dried；The coating weight being again coated with is 4-8g/, and reach 100% be dried, formed topcoat；
Step 10, heavy bamboo floor body backsize carry on the back paint, coating weight is 14g/, and reach 100% be dried, formed the back of the body
Lacquer coat.
In a preferred approach, the coating weight of described aqueous priming paint coating is 8g/；The coating weight of described anticracking oil coating is
20g/㎡；Described heavy putty coating is coated with at twice, and the coating weight being coated with first is 35g/, and the coating weight being again coated with is
25g/㎡；The coating weight of described hardening primer coating is 20g/；The coating weight of described first transparent priming coating is 25g/；
The coating weight of described wear-resistant primer coating is 20g/；Described second transparent priming coating is coated with at twice, the painting being coated with first
Cloth amount is 20g/, and the coating weight being again coated with is 15g/；The coating weight of described sanding primer coating is 10g/；Described
Lacquer coat is coated with at twice, and the coating weight being coated with first is 7g/, and the coating weight being again coated with is 6g/；Described back of the body lacquer coat
Coating weight be 14g/.
In the present embodiment, before step 1, described heavy bamboo floor body also have passed through fixed thick washed ore processing, and carries out
Except silk is processed.
In the present embodiment, between step 4 and step 5, mortise processing has also been carried out, in order at heavy bamboo floor body
Perimembranous forms dovetail.
The foregoing is only embodiments of the invention, not thereby limit the scope of the claims of the present invention, every utilize this
Equivalent structure or equivalence flow process that bright description and accompanying drawing content are made convert, or are directly or indirectly used in other relevant skills
Art field, is included in the scope of patent protection of the present invention.
Claims (7)
1. a heavy bamboo plane true qualities floor, including the heavy bamboo floor body through fixed thick washed ore, it is characterised in that: described heavy bamboo
The perimembranous mortise of floor body forms dovetail；The surface of described heavy bamboo floor body is coated with aqueous priming paint coating successively, prevents
Split oil coating, heavy putty coating, hardening primer coating, the first transparent priming coating, wear-resistant primer coating, the second transparent priming
Coating, sanding primer coating and topcoat；The backsize of described heavy bamboo floor body has back of the body lacquer coat.
Heavy bamboo plane true qualities floor the most according to claim 1, it is characterised in that the coating weight of described aqueous priming paint coating
For 6-10g/；The coating weight of described anticracking oil coating is 15-25g/；Described heavy putty coating is coated with, first at twice
The coating weight of coating is 30-40g/, and the coating weight being again coated with is 20-30g/；The coating weight of described hardening primer coating
For 20-30g/；The coating weight of described first transparent priming coating is 20-30g/；The coating weight of described wear-resistant primer coating
For 15-25 g/；Described second transparent priming coating is coated with at twice, and the coating weight being coated with first is 15-25g/, again
The coating weight of coating is 10-20g/；The coating weight of described sanding primer coating is 5-10 g/；Described topcoat divides two
Secondary coating, the coating weight being coated with first is 5-9g/, and the coating weight being again coated with is 4-8g/；The coating of described back of the body lacquer coat
Amount is 10-18g/.
Heavy bamboo plane true qualities floor the most according to claim 1, it is characterised in that the coating weight of described aqueous priming paint coating
For 8g/；The coating weight of described anticracking oil coating is 20g/；Described heavy putty coating is coated with at twice, is coated with first
Coating weight is 35g/, and the coating weight being again coated with is 25g/；The coating weight of described hardening primer coating is 20g/；Described
The coating weight of the first transparent priming coating is 25g/；The coating weight of described wear-resistant primer coating is 20g/；Described second saturating
Bright primer coating is coated with at twice, and the coating weight being coated with first is 20g/, and the coating weight being again coated with is 15g/；Described sand
The coating weight of light primer coating is 10g/；Described topcoat is coated with at twice, and the coating weight being coated with first is 7g/, then
The coating weight of secondary coating is 6g/；The coating weight of described back of the body lacquer coat is 14g/.
4. the paint production technique on heavy bamboo plane true qualities floor, including heavy bamboo floor body, it is characterised in that by following step
Suddenly carry out:
Step 1, the surface of heavy bamboo floor body be coated with aqueous priming paint, coating weight is 6-10g/, then use 80 degree infrared
Line is dried, and forms aqueous priming paint coating；
Step 2, add in anticracking oil its parts by weight 1/8 cross-linking agent, the surface of heavy bamboo floor body be coated with anticracking
Oil, coating weight is 15-25g/, and is dried to half-dried, forms anticracking oil coating；
Step 3, at the heavy putty of the surface of heavy bamboo floor body coating, be coated with at twice, the coating weight being coated with first is 30-
40g/, is dried after 70% employing abrasive band sanding；The coating weight being again coated with is 20-30g/, and reach 70% be dried, formed
Heavy putty coating；
Step 4, the surface of heavy bamboo floor body be coated with hardening primer, coating weight is 20-30g/, and reach 70% be dried, shape
Become hardening primer coating；
Step 5, the surface of heavy bamboo floor body be coated with transparent priming, coating weight is 20-30g/, and reach 70% be dried, adopt
Use abrasive band sanding, form the first transparent priming coating；
Step 6, the surface of heavy bamboo floor body be coated with wear-resistant primer, coating weight is 15-25 g/, and is dried to half-dried, shape
Become wear-resistant primer coating；
Step 7, the surface of heavy bamboo floor body be coated with transparent priming, be coated with at twice, the coating weight being coated with first is 15-
25g/, and it is dry to reach 70%；The coating weight being again coated with is 10-20g/, and reach 70% be dried, form the second clear bottom
Lacquer coat；
Step 8, the surface of heavy bamboo floor body be coated with sanding priming paint, coating weight is 5-10 g/, and reach 70% be dried, adopt
Use abrasive band sanding, form sanding primer coating；
Step 9, the surface of heavy bamboo floor body be coated with finish paint, be coated with at twice, the coating weight being coated with first is 5-9g/,
And be dried to half-dried；The coating weight being again coated with is 4-8g/, and reach 100% be dried, formed topcoat；
Step 10, heavy bamboo floor body backsize carry on the back paint, coating weight is 14g/, and reach 100% be dried, formed the back of the body
Lacquer coat.
The paint production technique on heavy bamboo plane true qualities floor the most according to claim 4, it is characterised in that at the bottom of described aqueous
The coating weight of lacquer coat is 8g/；The coating weight of described anticracking oil coating is 20g/；Described heavy putty coating is coated with at twice
Cloth, the coating weight being coated with first is 35g/, and the coating weight being again coated with is 25g/；The coating weight of described hardening primer coating
For 20g/；The coating weight of described first transparent priming coating is 25g/；The coating weight of described wear-resistant primer coating is 20g/
㎡；Described second transparent priming coating is coated with at twice, and the coating weight being coated with first is 20g/, and the coating weight being again coated with is
15g/㎡；The coating weight of described sanding primer coating is 10g/；Described topcoat is coated with at twice, the coating being coated with first
Amount is 7g/, and the coating weight being again coated with is 6g/；The coating weight of described back of the body lacquer coat is 14g/.
The paint production technique on heavy bamboo plane true qualities floor the most according to claim 4, it is characterised in that step 1 it
Before, described heavy bamboo floor body also have passed through fixed thick washed ore processing, and has carried out except silk is processed.
The paint production technique on heavy bamboo plane true qualities floor the most according to claim 4, it is characterised in that in step 4 and
Mortise processing has also been carried out, in order to the perimembranous at heavy bamboo floor body forms dovetail between step 5.