CN109057233A - A kind of moisture-proof floor and its manufacturing method - Google Patents
A kind of moisture-proof floor and its manufacturing method Download PDFInfo
- Publication number
- CN109057233A CN109057233A CN201810946337.XA CN201810946337A CN109057233A CN 109057233 A CN109057233 A CN 109057233A CN 201810946337 A CN201810946337 A CN 201810946337A CN 109057233 A CN109057233 A CN 109057233A
- Authority
- CN
- China
- Prior art keywords
- layer
- moisture
- proof floor
- adhesive
- substrate layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of moisture-proof floor and its manufacturing methods; the moisture-proof floor from top to bottom successively includes the wearing layer with protective effect, the decorative layer with beauty function, the substrate layer with supporting role and the balance layer with Moistureproof anti-deformation effect, and wearing layer is the clean oil paint layer containing mass fraction for 1~5% nano-aluminium oxide；Decorative layer is made of PVC coloured silk film paper；Gluing is carried out using hypergolic polyurethane resin adhesive between decorative layer and substrate layer, one layer of waterproof layer formed by thermoplastic adhesive is additionally provided between substrate layer and balance layer.Moisture-proof floor of the invention is compared with existing moisture-proof floor, with excellent wear-resisting property, waterproof and dampproof performance, and manufacturing method is simple, economical and practical, planarization is good, it is environmentally friendly, in addition, according to the difference that auxiliary agent type is added, it realizes that moisture-proof floor of the invention has the additional functions such as antimycotic antiseptic, anti-oxidant and taste removal, there is practical value very much.
Description
Technical field
The present invention relates to the composite floor fields of building decoration, and in particular to a kind of moisture-proof floor and its manufacturing method.
Technical background
Traditional solid sawn composite floor board is formed by the plate crosswise lamination of different tree species, because of the anisotropic of timber itself, when
When external environment (temperature, humidity etc.) changes, the variation of moisture content can be caused, cause wood shrinkage bulking, warpage
Deformation etc., and through Water Damage after unrepairable, comfortable foot feeling degree reduce, seriously affect the comfort and aesthetic effect on floor；
In addition, solid wooden compound floor wears no resistance, structure is complex, the poor dimensional stability on floor.Currently, general anti-in the market
Damp floor is also only laid with damp-proof layer in floor surface, completely cuts off the moisture above floor, and has ignored floor bottoms water-cut variation
Problem, so that still resulting in the buckling deformation on floor after timber floor dampness.
Publication date on 01 22nd, 2014, the Chinese invention patent of publication number CN103526910A disclosed a kind of compound
Floor is followed successively by superficial layer, decorative layer, substrate layer and bottom from top to bottom, and the bottom has additional waterproof layer, although can reach
Moisture-proof role, but technique is cumbersome, and material cost increases.For this purpose, the present invention provides a kind of moisture-proof floor and its manufacturing method.
Summary of the invention
It is an object of the present invention to solving the deficiencies in the prior art, provide a kind of good decorating effect, humidity resistance it is high,
In addition simple process, economical and practical moisture-proof floor also have good antibacterial and anti-mildew performance.
The second object of the present invention is to provide a kind of manufacturing method of moisture-proof floor.
The technical solution adopted by the present invention to solve the technical problems is:
A kind of moisture-proof floor from top to bottom successively includes the wearing layer with protective effect, the decoration with beauty function
Layer, the substrate layer with supporting role and the balance layer with Moistureproof anti-deformation effect, it is 1 that the wearing layer, which is containing mass fraction,
The clean oil paint layer of~5% nano-aluminium oxide, with a thickness of 0.05~2.00mm；The decorative layer (2) is by PVC coloured silk film paper structure
At the substrate layer (3) is Eucalyptus glued board or poplar plywood, and the balance layer (4) is veneer；The decorative layer (2) with
Gluing is carried out using hypergolic polyurethane resin adhesive between substrate layer (3), between the substrate layer (3) and balance layer (4)
It is additionally provided with one layer of waterproof layer formed by thermoplastic adhesive (5).
Preferably, the hypergolic polyurethane resin adhesive the preparation method is as follows: by 90~100 mass parts isocyanide
The rosin conduct of 1~10 mass parts is added as two-component ingredient in acid esters and the polyvinyl acetate emulsion of 10~70 mass parts
Tackifier, 1~10 phthalic acid ester add the natto gum of 1~5 mass parts as defoaming agent, the auxiliary agent of 1~3 mass parts,
It is uniformly mixed, is made.
Preferably, the auxiliary agent is at least one of antimildew disinfectant, antioxidant and eliminating smell agent.
Preferably, the thermoplastic resin is polyethylene, polypropylene or polyvinyl chloride.
A kind of manufacturing method of moisture-proof floor, specific preparation process is as follows:
S1: thermoplastic resin is imposed between balance layer (4) and substrate layer (3) as adhesive, forms one layer by thermoplastic
Property resin adhesive constitute waterproof layer (5), resin added be 105~135g/m2, the cold moudling after hot pressing is spare；
S2: substrate layer (3) another side in step sl imposes hypergolic polyurethane resin adhesive as adhesive, applies
Glue amount is 105~135g/m2, it is compound with decorative layer (2), through cold moudling, semi-finished product are made；
S3: it is 1~5% nano-aluminium oxide that decorative layer (2) surface in step s 2, which sprays one layer containing mass fraction,
Clean oil paint layer, be prepared into moisture-proof floor.
Preferably, in the step S1,70~95 DEG C of hot pressing temperature, 5~20min of time, 0.5~1.5MPa of pressure；It is cold
Press 0.5~1h of time, 0.5~1MPa of pressure.
Preferably, in the step S2,2~5h of time, 0.6~1.4MPa of pressure are cold-pressed.
Preferably, it in the step S3, is handled using one finishing coat of a priming paint when spraying, paint dosage is 7~15g/m2。
Hypergolic polyurethane resin adhesive has been used in technical solution of the present invention, in its preparation process, be joined and is received
Bean gum and auxiliary agent, wherein natto gum itself have certain skeleton structure in conjunction with different auxiliary agents after, skeleton space can accommodate
Wrapping portion auxiliary molecules play slow releasing function to the release of auxiliary agent, are conducive to antimildew disinfectant, antioxidant and eliminating smell agent etc.
The effect of auxiliary agent, slowly persistently generates for a long time, to impart hypergolic polyurethane resin adhesive antimycotic antiseptic, antioxygen
The functions such as change and taste removal, serve as the adhesive between moisture-proof floor decorative layer and substrate layer herein, equally impart moisture-proofly
Plate antimycotic antiseptic, anti-oxidant and taste removal additional benefit have very big practical value.In addition, natto gum also have it is superpower
Adsorptivity and biodegradability can adsorb metal ion, poisonous and harmful smell etc. in environment, further promote living space
Environmental quality, and generate non-harmful glutamic acid after biodegrade, be a kind of environmentally friendly high molecular material.
Technical solution of the present invention is provided with one layer also between substrate layer and balance layer and is formed by thermoplastic adhesive
Waterproof layer, for completely cut off floor bottoms dampness after infringement of the moisture to floor, thermoplastic resin has not only acted as glue herein
The effect of stick, and the effect of waterproof is also acted, multiple and different effects is realized, to simplify the production of moist-proof board
Technique.In addition, one layer of celluloid paint containing nano-aluminium oxide is sprayed in the decor surface being made of PVC coloured silk film paper,
One layer of compactness height is formed, and has the skin of paint of anti-wear energy, the PVC coloured silk film paper for protecting it internal well.PVC coloured silk film
Paper is mainly used for completely cutting off the infringement of moisture plate surface over the ground, the waterproof formed in substrate and balance layer by thermoplastic adhesive
Layer is mainly used for completely cutting off the infringement in moisture board bottom face over the ground, by thermoplastic resin shape between PVC coloured silk film paper and substrate and balance layer
At waterproof layer synergistic effect, completely cut off infringement of the moisture to floor well.
Wearing layer in the technical program is the clean oil paint layer containing mass fraction for 1~5% nano-aluminium oxide, institute
The celluloid paint stated is that UV is painted, and UV paint tool is one of paint most environmentally friendly at present, not only has transparency height, yellowing resistance excellent
Good, the advantages that solid content is high, and itself also has certain wearability, can play wear-resisting effect.Nanometer three aoxidizes
Two aluminium large specific surface areas, pore structure are good, and have excellent dispersion performance, can improve UV in being uniformly dispersed in paint
While painting anti-wear energy, the coating weight of the UV paint of also opposite reduction, environmental protection and economy, and accelerate the production cycle.
In conclusion the beneficial effects of the present invention are: moisture-proof floor of the invention has compared with existing moisture-proof floor
Excellent wear-resisting property, waterproof and dampproof performance, and manufacturing method is simple, economical and practical, planarization is good, and it is environmentally friendly, this
Outside, according to the difference that auxiliary agent type is added, realize that moisture-proof floor of the invention has antimycotic antiseptic, anti-oxidant and taste removal etc. a variety of
Additional function has practical value very much.
Detailed description of the invention
Fig. 1 is the structural schematic diagram of moisture-proof floor of the present invention.
In figure: 1, wearing layer；2, decorative layer；3, substrate layer；4, balance layer；5, waterproof layer
Specific embodiment
Below by specific embodiment, technical scheme of the present invention will be further explained in detail.
Embodiment 1:
A kind of moisture-proof floor from top to bottom successively includes the wearing layer 1 with protective effect, the decoration with beauty function
Layer 2, the substrate layer 3 with supporting role and the balance layer 4 with Moistureproof anti-deformation effect, the wearing layer 1 are containing quality point
Number is the clean oil paint layer of 3% nano-aluminium oxide, with a thickness of 0.05~2.00mm；The decorative layer 2 is by PVC coloured silk film paper structure
At the substrate layer 3 is Eucalyptus glued board, and the balance layer 4 is veneer；Using double groups between the decorative layer 2 and substrate layer 3
Divide polyurethane resin adhesive to carry out glued, one layer is additionally provided between the substrate layer 3 and balance layer 4 by thermoplastic resin adhesive
The waterproof layer 5 that stick is formed.
The hypergolic polyurethane resin adhesive the preparation method is as follows: by 90 mass parts isocyanates and 70 mass
The rosin of 10 mass parts is added as tackifier, 8 phthalic acid esters as two-component ingredient in the polyvinyl acetate emulsion of part
As defoaming agent, the natto gum of 5 mass parts is added, the auxiliary agent of 3 mass parts is uniformly mixed, and is made.
The auxiliary agent is antimildew disinfectant, antioxidant and eliminating smell agent；The thermoplastic resin is polyethylene.
A kind of manufacturing method of moisture-proof floor is as follows:
S1: thermoplastic resin is imposed between balance layer 4 and substrate layer 3 as adhesive, forms one layer by thermoplastic resin
The waterproof layer 5 that rouge adhesive is constituted, resin added 135g/m2, the cold moudling after hot pressing is spare；
S2: 3 another side of substrate layer in step sl imposes hypergolic polyurethane resin adhesive as adhesive, sizing
Amount is 125g/m2, it is compound with decorative layer 2, through cold moudling, semi-finished product are made；
S3: it is the transparent of 3% nano-aluminium oxide that 2 surface of decorative layer in step s 2, which sprays one layer containing mass fraction,
Skin of paint is prepared into moisture-proof floor.
In the step S1,70 DEG C of hot pressing temperature, time 20min, pressure 1.5MPa；It is cold-pressed time 0.5h, pressure 1MPa.
In the step S2, it is cold-pressed time 5h, pressure 0.6MPa.
It in the step S3, is handled using one finishing coat of a priming paint when spraying, paint dosage is 15g/m2。
Embodiment 2
A kind of moisture-proof floor from top to bottom successively includes the wearing layer 1 with protective effect, the decoration with beauty function
Layer 2, the substrate layer 3 with supporting role and the balance layer 4 with Moistureproof anti-deformation effect, the wearing layer 1 are containing quality point
Number is the clean oil paint layer of 5% nano-aluminium oxide, with a thickness of 0.05~2.00mm；The decorative layer 2 is by PVC coloured silk film paper structure
At the substrate layer 3 is poplar plywood, and the balance layer 4 is veneer；Using double groups between the decorative layer 2 and substrate layer 3
Divide polyurethane resin adhesive to carry out glued, one layer is additionally provided between the substrate layer 3 and balance layer 4 by thermoplastic resin adhesive
The waterproof layer 5 that stick is formed.
The manufacturing method of the hypergolic polyurethane resin adhesive is as follows: by the isocyanates and 70 mass of 90 mass parts
The rosin of 10 mass parts is added as tackifier, 5 phthalic acid esters as two-component ingredient in the polyvinyl acetate emulsion of part
As defoaming agent, the natto gum of 5 mass parts is added, the auxiliary agent of 3 mass parts is uniformly mixed, and is made.
The auxiliary agent is antimildew disinfectant；The thermoplastic resin is polypropylene.
A kind of manufacturing method of moisture-proof floor is as follows:
S1: thermoplastic resin is imposed between balance layer 4 and substrate layer 3 as adhesive, forms one layer by thermoplastic resin
The waterproof layer 5 that rouge adhesive is constituted, resin added 105g/m2, the cold moudling after hot pressing is spare；
S2: 3 another side of substrate layer in step sl imposes hypergolic polyurethane resin adhesive as adhesive, sizing
Amount is 135g/m2, it is compound with decorative layer 2, through cold moudling, semi-finished product are made；
S3: it is the transparent of 5% nano-aluminium oxide that 2 surface of decorative layer in step s 2, which sprays one layer containing mass fraction,
Skin of paint is prepared into moisture-proof floor.
In the step S1,90 DEG C of hot pressing temperature, time 15min, pressure 1.0MPa；It is cold-pressed time 1h, pressure 0.8MPa；
In the step S2, it is cold-pressed time 3h, pressure 0.8MPa.
It in the step S3, is handled using one finishing coat of a priming paint when spraying, paint dosage is 12g/m2。
Embodiment 3
A kind of moisture-proof floor from top to bottom successively includes the wearing layer 1 with protective effect, the decoration with beauty function
Layer 2, the substrate layer 3 with supporting role and the balance layer 4 with Moistureproof anti-deformation effect, the wearing layer 1 are containing quality point
Number is the clean oil paint layer of 2% nano-aluminium oxide, with a thickness of 0.05~2.00mm；The decorative layer 2 is by PVC coloured silk film paper structure
At the substrate layer 3 is poplar plywood, and the balance layer 4 is veneer；Using double groups between the decorative layer 2 and substrate layer 3
Divide polyurethane resin adhesive to carry out glued, one layer is additionally provided between the substrate layer 3 and balance layer 4 by thermoplastic resin adhesive
The waterproof layer 5 that stick is formed.
The manufacturing method of the hypergolic polyurethane resin adhesive is as follows: by the isocyanates and 50 mass of 95 mass parts
The rosin of 8 mass parts is added as tackifier, 10 phthalic acid esters as two-component ingredient in the polyvinyl acetate emulsion of part
As defoaming agent, the natto gum of 4 mass parts is added, the auxiliary agent of 2 mass parts is uniformly mixed, and is made.
The auxiliary agent is antimildew disinfectant and eliminating smell agent；The thermoplastic resin is polyvinyl chloride.
A kind of manufacturing method of moisture-proof floor is as follows:
S1: thermoplastic resin is imposed between balance layer 4 and substrate layer 3 as adhesive, forms one layer by thermoplastic resin
The waterproof layer 5 that rouge adhesive is constituted, resin added 110g/m2, the cold moudling after hot pressing is spare；
S2: 3 another side of substrate layer in step sl imposes hypergolic polyurethane resin adhesive as adhesive, sizing
Amount is 120g/m2, it is compound with decorative layer 2, through cold moudling, semi-finished product are made；
S3: it is the transparent of 2% nano-aluminium oxide that 2 surface of decorative layer in step s 2, which sprays one layer containing mass fraction,
Skin of paint is prepared into moisture-proof floor.
In the step S1,85 DEG C of hot pressing temperature, time 15min, pressure 1.2MPa；It is cold-pressed time 1h, pressure 0.8MPa.
In the step S2, it is cold-pressed time 2.5h, pressure 1.4MPa.
It in the step S3, is handled using one finishing coat of a priming paint when spraying, paint dosage is 12g/m2。
Above-mentioned embodiment is only a preferred solution of the present invention, not the present invention is made in any form
Limitation, there are also other variations and modifications on the premise of not exceeding the technical scheme recorded in the claims.
Claims (8)
- It from top to bottom successively include wearing layer (1), decorative layer (2), substrate layer (3) and balance layer (4) 1. a kind of moisture-proof floor, It is characterized in that, the wearing layer (1) is the clean oil paint layer containing mass fraction for 1~5% nano-aluminium oxide, with a thickness of 0.05~2.00mm；The decorative layer (2) is made of PVC coloured silk film paper, and the substrate layer (3) is that Eucalyptus glued board or poplar are glued Plate, the balance layer (4) are veneer；Hypergolic polyurethane resin adhesive is used between the decorative layer (2) and substrate layer (3) Gluing is carried out, is additionally provided with one layer of waterproof formed by thermoplastic adhesive between the substrate layer (3) and balance layer (4) Layer (5).
- 2. moisture-proof floor according to claim 1, which is characterized in that the preparation side of the hypergolic polyurethane resin adhesive Method is as follows: by 90~100 mass parts isocyanates and 10~70 mass parts polyvinyl acetate emulsion as two-component at Point, the rosin of 1~10 mass parts is added as tackifier, 1~10 phthalic acid ester adds 1~5 mass as defoaming agent The natto gum of part, the auxiliary agent of 1~3 mass parts are uniformly mixed, and are made.
- 3. moisture-proof floor according to claim 2, which is characterized in that the auxiliary agent is antimildew disinfectant, antioxidant and removes At least one of taste agent.
- 4. moisture-proof floor according to claim 1, which is characterized in that the thermoplastic resin is polyethylene, polypropylene or poly- Vinyl chloride.
- 5. the manufacturing method of moisture-proof floor described in a kind of any one of Claims 1 to 4, which is characterized in that specific preparation step It is rapid as follows:S1: thermoplastic resin is imposed between balance layer (4) and substrate layer (3) as adhesive, forms one layer by thermoplastic resin The waterproof layer (5) that rouge adhesive is constituted, resin added are 105~135g/m2, the cold moudling after hot pressing is spare；S2: substrate layer (3) another side in step sl imposes hypergolic polyurethane resin adhesive as adhesive, resin added For 105~135g/m2, it is compound with decorative layer (2), through cold moudling, semi-finished product are made；S3: it is the saturating of 1~5% nano-aluminium oxide that decorative layer (2) surface in step s 2, which sprays one layer containing mass fraction, Bright skin of paint, is prepared into moisture-proof floor.
- 6. the manufacturing method of moisture-proof floor according to claim 5, which is characterized in that in the step S1, hot pressing temperature 70 ~95 DEG C, 5~20min of time, 0.5~1.5MPa of pressure；It is cold-pressed 0.5~1h of time, 0.5~1MPa of pressure.
- 7. the manufacturing method of moisture-proof floor according to claim 5, which is characterized in that in the step S2, pressure 0.6~ 1.4MPa；It is cold-pressed 2~5h of time.
- 8. the manufacturing method of moisture-proof floor according to claim 5, which is characterized in that in the step S3, when spraying is used The processing of one priming paint, one finishing coat, paint dosage are 7~15g/m2。