CN109722126A - A kind of car light antistatic coating - Google Patents
A kind of car light antistatic coating Download PDFInfo
- Publication number
- CN109722126A CN109722126A CN201711019583.2A CN201711019583A CN109722126A CN 109722126 A CN109722126 A CN 109722126A CN 201711019583 A CN201711019583 A CN 201711019583A CN 109722126 A CN109722126 A CN 109722126A
- Authority
- CN
- China
- Prior art keywords
- parts
- car light
- antistatic coating
- water
- reaction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of car light antistatic coatings, the component of the car light antistatic coating is as follows according to parts by weight: 30-40 parts of polyester light-cured resin of water-based isocyanate modified ultra-branching, 20-25 parts of kaolin, 10-15 parts of antistatic agent, 10-15 parts of acrylonitrile, 5-10 parts of water methyl methacrylate, 5-10 parts of titanium dioxide, 5-10 parts of organobentonite, 4-6 parts of cosolvent, 35-45 parts of diluent.Manufacture craft of the present invention is simple, and raw material is easy to buy, and cost of manufacture is cheap, and antistatic effect has broad application prospects.
Description
Technical field
The present invention relates to automobile lamp technical field more particularly to a kind of car light antistatic coatings.
Background technique
Automobile lamp is widely used as automobile indispensability component in automotive field.Car light after prolonged use can
Because of a large amount of dusts of Electrostatic Absorption, vehicle lamp brightness is influenced, brings risk to user's driving at night, it is therefore desirable to which a kind of car light use is anti-
Electrostatic coating improves the safety of traveling.
Summary of the invention
To solve the above problems, the present invention provides a kind of car light antistatic coatings.
Technical scheme is as follows:
The component of a kind of car light antistatic coating, the car light antistatic coating is as follows according to parts by weight: water
Property is 30-40 parts of hyper-branched polyester light-cured resin isocyanate-modified, and 20-25 parts of kaolin, 10-15 parts of antistatic agent, propylene
It is 10-15 parts of nitrile, 5-10 parts of water methyl methacrylate, 5-10 parts of titanium dioxide, 5-10 parts of organobentonite, 4-6 parts of cosolvent, dilute
Release 35-45 parts of agent.
Further, the antistatic agent is one of the cruel amine of ethyoxyl laurel, glycerol-stearate (GMS).
Further, the cosolvent is one of sodium benzoate, sodium salicylate, p-aminobenzoic acid
Further, the diluent is one of n-butyl acetate and styrene.
Further, a kind of car light antistatic coating preparation method, it is characterised in that: the following steps are included:
S1: water-based isocyanate modified ultra-branching polyester light-cured resin, acrylonitrile, water methyl methacrylate are put into
In reaction kettle, 15min is stirred at low speed.
S2:, by 80 mesh screens, then mixed-powder will be added anti-after kaolin, titanium dioxide, organobentonite grinding
Answer kettle, moderate-speed mixer 30-50min；
S3: reaction kettle is warming up to 40-60 DEG C, after addition antistatic agent, cosolvent and diluent stir at low speed reaction 2h
It is cooled to room temperature, finished product can be obtained in the reaction was continued 35h.
According to the above aspect of the present invention, the present invention at least has the advantages that
Manufacture craft of the present invention is simple, and raw material is easy to buy, and cost of manufacture is cheap, antistatic effect, has wide answer
Use prospect.
Specific embodiment
Technical solution of the present invention is described in detail as follows below with reference to embodiment.
Embodiment 1
A kind of car light antistatic coating, it is characterised in that: the component of the car light antistatic coating is according to parts by weight
It is as follows: 30-40 parts of polyester light-cured resin of water-based isocyanate modified ultra-branching, 20-25 parts of kaolin, glycerol-tristearin
10 parts of acid esters (GMS), 5 parts of acrylonitrile, 8 parts of water methyl methacrylate, 7 parts of titanium dioxide, 6 parts of organobentonite, sodium benzoate 4
Part, 35 parts of n-butyl acetate.
Preparation method includes the following steps:
S1: water-based isocyanate modified ultra-branching polyester light-cured resin, acrylonitrile, water methyl methacrylate are put into
In reaction kettle, 15min is stirred at low speed.
S2:, by 80 mesh screens, then mixed-powder will be added anti-after kaolin, titanium dioxide, organobentonite grinding
Answer kettle, moderate-speed mixer 30-50min；
S3: reaction kettle is warming up to 40-60 DEG C, after addition antistatic agent, cosolvent and diluent stir at low speed reaction 2h
It is cooled to room temperature, finished product can be obtained in the reaction was continued 35h.
Embodiment 2
A kind of car light antistatic coating, it is characterised in that: the component of the car light antistatic coating is according to parts by weight
It is as follows: 38 parts of light-cured resin of water-based isocyanate modified ultra-branching polyester, 20 parts of kaolin, the cruel amine 15 of ethyoxyl laurel
Part, 12 parts of acrylonitrile, 6 parts of water methyl methacrylate, 8 parts of titanium dioxide, 9 parts of organobentonite, 4 parts of p-aminobenzoic acid, benzene
37 parts of ethylene.
Preparation method includes the following steps:
S1: water-based isocyanate modified ultra-branching polyester light-cured resin, acrylonitrile, water methyl methacrylate are put into
In reaction kettle, 15min is stirred at low speed.
S2:, by 80 mesh screens, then mixed-powder will be added anti-after kaolin, titanium dioxide, organobentonite grinding
Answer kettle, moderate-speed mixer 30-50min；
S3: reaction kettle is warming up to 40-60 DEG C, after addition antistatic agent, cosolvent and diluent stir at low speed reaction 2h
It is cooled to room temperature, finished product can be obtained in the reaction was continued 35h.
Embodiment 3
A kind of car light antistatic coating, it is characterised in that: the component of the car light antistatic coating is according to parts by weight
It is as follows: 34 parts of light-cured resin of water-based isocyanate modified ultra-branching polyester, 22 parts of kaolin, glycerol-stearate
(GMS) 12 parts, 13 parts of acrylonitrile, 9 parts of water methyl methacrylate, 7 parts of titanium dioxide, 8 parts of organobentonite, 4 parts of sodium salicylate,
35 parts of n-butyl acetate.
Preparation method includes the following steps:
S1: water-based isocyanate modified ultra-branching polyester light-cured resin, acrylonitrile, water methyl methacrylate are put into
In reaction kettle, 15min is stirred at low speed.
S2:, by 80 mesh screens, then mixed-powder will be added anti-after kaolin, titanium dioxide, organobentonite grinding
Answer kettle, moderate-speed mixer 30-50min；
S3: reaction kettle is warming up to 40-60 DEG C, after addition antistatic agent, cosolvent and diluent stir at low speed reaction 2h
It is cooled to room temperature, finished product can be obtained in the reaction was continued 35h.
The above is only a preferred embodiment of the present invention, it is not intended to restrict the invention, it is noted that for this skill
For the those of ordinary skill in art field, without departing from the technical principles of the invention, can also make it is several improvement and
Modification, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (5)
1. a kind of car light antistatic coating, it is characterised in that: the component of the car light antistatic coating according to parts by weight such as
Shown in lower: 30-40 parts of polyester light-cured resin of water-based isocyanate modified ultra-branching, 20-25 parts of kaolin, antistatic agent 10-
15 parts, 10-15 parts of acrylonitrile, 5-10 parts of water methyl methacrylate, 5-10 parts of titanium dioxide, 5-10 parts of organobentonite, hydrotropy
4-6 parts of agent, 35-45 parts of diluent.
2. a kind of car light antistatic coating according to claim 1, it is characterised in that: the antistatic agent is ethyoxyl
One of the cruel amine of laurel, glycerol-stearate (GMS).
3. a kind of car light antistatic coating according to claim 1, it is characterised in that: the cosolvent is benzoic acid
One of sodium, sodium salicylate, p-aminobenzoic acid.
4. a kind of car light antistatic coating according to claim 1, it is characterised in that: the diluent is the positive fourth of acetic acid
One of ester and styrene.
5. a kind of car light antistatic coating preparation method according to claim 1, it is characterised in that:
S1: water-based isocyanate modified ultra-branching polyester light-cured resin, acrylonitrile, water methyl methacrylate are put into reaction
In kettle, 15min is stirred at low speed.
S2:, by 80 mesh screens, then will be added reaction kettle for mixed-powder after kaolin, titanium dioxide, organobentonite grinding,
Moderate-speed mixer 30-50min；
S3: being warming up to 40-60 DEG C for reaction kettle, and antistatic agent, cosolvent and diluent is added and stirs at low speed cooling after reaction 2h
To room temperature, finished product is can be obtained in the reaction was continued 35h.