CN109721955A - A kind of antistatic car light lampshade - Google Patents
A kind of antistatic car light lampshade Download PDFInfo
- Publication number
- CN109721955A CN109721955A CN201711026280.3A CN201711026280A CN109721955A CN 109721955 A CN109721955 A CN 109721955A CN 201711026280 A CN201711026280 A CN 201711026280A CN 109721955 A CN109721955 A CN 109721955A
- Authority
- CN
- China
- Prior art keywords
- parts
- antistatic
- car light
- light lampshade
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of antistatic car light lampshades, the component of the antistatic car light lampshade is as follows according to parts by weight: 30-40 parts of polyethylene terephthalate, 20-25 parts of haloflex, 10-15 parts of ethylene-ethyl acrylate copolymer, three (2,4- di-tert-butyl-phenyl) 10-15 parts of phosphite ester, 5-10 parts of dioctyl phthalate, 5-10 parts of water methyl methacrylate, 1-5 parts of isocyanates, 1-5 parts of antistatic agent, 5-10 parts of crosslinking agent, 5-10 parts of heat stabilizer.Manufacture craft of the present invention is simple, and raw material is easy to buy, and cost of manufacture is cheap, and antistatic effect has broad application prospects.
Description
Technical field
The present invention relates to automobile lamp technical field more particularly to a kind of antistatic car light lampshades.
Background technique
Automobile lamp is widely used as automobile indispensability component in automotive field.Car light after prolonged use can
Because of a large amount of dusts of Electrostatic Absorption, vehicle lamp brightness is influenced, brings risk to user's driving at night, it is therefore desirable to a kind of antistatic vehicle
Lamp lampshade improves the safety of traveling.
Summary of the invention
To solve the above problems, the present invention provides a kind of antistatic car light lampshades.
Technical scheme is as follows:
The component of a kind of antistatic car light lampshade, the antistatic car light lampshade is as follows according to parts by weight: poly- to benzene
30-40 parts of dioctyl phthalate ethylene glycol rouge, 20-25 parts of haloflex, 10-15 parts of ethylene-ethyl acrylate copolymer, three (2,4-
Di-tert-butyl-phenyl) 10-15 parts of phosphite ester, it is 5-10 parts of dioctyl phthalate, 5-10 parts of water methyl methacrylate, different
1-5 parts of cyanate, 1-5 parts of antistatic agent, 5-10 parts of crosslinking agent, 5-10 parts of heat stabilizer.
Further, the antistatic agent is one of the cruel amine of ethyoxyl laurel, sodium alkyl sulfonate.
Further, the crosslinking agent is N, one of N- methylene-bisacrylamide (MBA), divinylbenzene.
Further, the heat stabilizer is Dythal.
Further, a kind of antistatic car light lampshade preparation method, it is characterised in that:
S1: by polyethylene terephthalate, haloflex, ethylene-ethyl acrylate copolymer, three (2,4- bis-
Tert-butyl-phenyl) phosphite ester, heat stabilizer be put into reaction kettle, it is warming up to 130-150 DEG C, moderate-speed mixer reacts 40min；
S2: dioctyl phthalate, water methyl methacrylate, isocyanates, crosslinking are added after being cooled to 60-80 DEG C
Agent stirs at low speed 1h；
S3: after being cooled to room temperature, antistatic agent is added in a kettle and stirs at low speed reaction 34h, finished product can be obtained.
According to the above aspect of the present invention, the present invention at least has the advantages that
Manufacture craft of the present invention is simple, and raw material is easy to buy, and cost of manufacture is cheap, antistatic effect, has wide answer
Use prospect.
Specific embodiment
Technical solution of the present invention is described in detail as follows below with reference to embodiment.
Embodiment 1
The component of a kind of antistatic car light lampshade, the antistatic car light lampshade is as follows according to parts by weight: poly- to benzene
37 parts of dioctyl phthalate ethylene glycol rouge, 20 parts of haloflex, 15 parts of ethylene-ethyl acrylate copolymer, three (2,4- di-tert-butyls
Base) 14 parts of phosphite ester, 8 parts of dioctyl phthalate, water methyl methacrylate 6,2 parts of isocyanates, ethyoxyl laurel
Cruel 5 parts of amine, 9 parts of divinylbenzene, 8 parts of Dythal.
Preparation method are as follows:
S1: by polyethylene terephthalate, haloflex, ethylene-ethyl acrylate copolymer, three (2,4- bis-
Tert-butyl-phenyl) phosphite ester, heat stabilizer be put into reaction kettle, it is warming up to 130-150 DEG C, moderate-speed mixer reacts 40min；
S2: dioctyl phthalate, water methyl methacrylate, isocyanates, crosslinking are added after being cooled to 60-80 DEG C
Agent stirs at low speed 1h；
S3: after being cooled to room temperature, antistatic agent is added in a kettle and stirs at low speed reaction 34h, finished product can be obtained.
Embodiment 2
The component of a kind of antistatic car light lampshade, the antistatic car light lampshade is as follows according to parts by weight: poly- to benzene
37 parts of dioctyl phthalate ethylene glycol rouge, 20 parts of haloflex, 13 parts of ethylene-ethyl acrylate copolymer, three (2,4- di-tert-butyls
Base) 11 parts of phosphite ester, 8 parts of dioctyl phthalate, 7 parts of water methyl methacrylate, 5 parts of isocyanates, alkyl sulfonic acid
2 parts of sodium, 8 parts of divinylbenzene, 5 parts of Dythal.
Preparation method are as follows:
S1: by polyethylene terephthalate, haloflex, ethylene-ethyl acrylate copolymer, three (2,4- bis-
Tert-butyl-phenyl) phosphite ester, heat stabilizer be put into reaction kettle, it is warming up to 130-150 DEG C, moderate-speed mixer reacts 40min；
S2: dioctyl phthalate, water methyl methacrylate, isocyanates, crosslinking are added after being cooled to 60-80 DEG C
Agent stirs at low speed 1h；
S3: after being cooled to room temperature, antistatic agent is added in a kettle and stirs at low speed reaction 34h, finished product can be obtained.
Embodiment 3
The component of a kind of antistatic car light lampshade, the antistatic car light lampshade is as follows according to parts by weight: poly- to benzene
30 parts of dioctyl phthalate ethylene glycol rouge, 25 parts of haloflex, 10 parts of ethylene-ethyl acrylate copolymer, three (2,4- di-tert-butyls
Base) 15 parts of phosphite ester, 9 parts of dioctyl phthalate, 7 parts of water methyl methacrylate, 2 parts of isocyanates, alkyl sulfonic acid
1 part of sodium, N, 5 parts of N- methylene-bisacrylamide (MBA), 8 parts of Dythal.
Preparation method are as follows:
S1: by polyethylene terephthalate, haloflex, ethylene-ethyl acrylate copolymer, three (2,4- bis-
Tert-butyl-phenyl) phosphite ester, heat stabilizer be put into reaction kettle, it is warming up to 130-150 DEG C, moderate-speed mixer reacts 40min；
S2: dioctyl phthalate, water methyl methacrylate, isocyanates, crosslinking are added after being cooled to 60-80 DEG C
Agent stirs at low speed 1h；
S3: after being cooled to room temperature, antistatic agent is added in a kettle and stirs at low speed reaction 34h, finished product can be obtained.
The above is only a preferred embodiment of the present invention, it is not intended to restrict the invention, it is noted that for this skill
For the those of ordinary skill in art field, without departing from the technical principles of the invention, can also make it is several improvement and
Modification, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (5)
1. a kind of antistatic car light lampshade, it is characterised in that: the component of the antistatic car light lampshade is according to the following institute of parts by weight
Show: 30-40 parts of polyethylene terephthalate, 20-25 parts of haloflex, ethylene-ethyl acrylate copolymer 10-15
Part, three 10-15 parts of phosphite ester of (2,4- di-tert-butyl-phenyl), 5-10 parts of dioctyl phthalate, water methyl methacrylate
5-10 parts of ester, 1-5 parts of isocyanates, 1-5 parts of antistatic agent, 5-10 parts of crosslinking agent, 5-10 parts of heat stabilizer.
2. a kind of antistatic car light lampshade according to claim 1, it is characterised in that: the antistatic agent is the ethyoxyl moon
One of the cruel amine in osmanthus, sodium alkyl sulfonate.
3. a kind of antistatic car light lampshade according to claim 1, it is characterised in that: the crosslinking agent is N, N- methylene
One of bisacrylamide (MBA), divinylbenzene.
4. a kind of antistatic car light lampshade according to claim 1, it is characterised in that: the heat stabilizer is that dibasic is adjacent
Phthalic acid lead.
5. a kind of antistatic car light lampshade preparation method according to claim 1, it is characterised in that:
S1: by polyethylene terephthalate, haloflex, ethylene-ethyl acrylate copolymer, three (the tertiary fourths of 2,4- bis-
Base phenyl) phosphite ester, heat stabilizer be put into reaction kettle, it is warming up to 130-150 DEG C, moderate-speed mixer reacts 40min；
S2: being added dioctyl phthalate, water methyl methacrylate, isocyanates, crosslinking agent after being cooled to 60-80 DEG C,
Stir at low speed 1h；
S3: after being cooled to room temperature, antistatic agent is added in a kettle and stirs at low speed reaction 34h, finished product can be obtained.