CN109721962A - A kind of high light transmission car light lampshade - Google Patents
A kind of high light transmission car light lampshade Download PDFInfo
- Publication number
- CN109721962A CN109721962A CN201711031948.3A CN201711031948A CN109721962A CN 109721962 A CN109721962 A CN 109721962A CN 201711031948 A CN201711031948 A CN 201711031948A CN 109721962 A CN109721962 A CN 109721962A
- Authority
- CN
- China
- Prior art keywords
- parts
- car light
- light transmission
- high light
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of high light transmission car light lampshades, the component of the antistatic car light lampshade is as follows according to parts by weight: 30-40 parts of polyethylene terephthalate, 20-25 parts of sodium polydithio-dipropyl sulfonate, 10-15 parts of ethylene-ethyl acrylate copolymer, three (2,4- di-tert-butyl-phenyl) 10-15 parts of phosphite ester, 5-10 parts of dioctyl phthalate, 5-10 parts of sodium isethionate, 1-5 parts of isocyanates, 1-5 parts of ammonium lauryl sulfate, 5-10 parts of crosslinking agent, 5-10 parts of heat stabilizer.Manufacture craft of the present invention is simple, and raw material is easy to buy, and cost of manufacture is cheap, and antistatic effect has broad application prospects.
Description
Technical field
The present invention relates to automobile lamp technical field more particularly to a kind of high light transmission car light lampshades.
Background technique
Automobile lamp is widely used as automobile indispensability component in automotive field.Car light after prolonged use can
Light is influenced because light transmittance is not high, it is therefore desirable to which a kind of high light transmission car light lampshade improves the safety of traveling.
Summary of the invention
To solve the above problems, the present invention provides a kind of high light transmission car light lampshades.
Technical scheme is as follows:
The component of a kind of high light transmission car light lampshade, the antistatic car light lampshade is as follows according to parts by weight: poly- to benzene
30-40 parts of dioctyl phthalate ethylene glycol rouge, 20-25 parts of sodium polydithio-dipropyl sulfonate, 10-15 parts of ethylene-ethyl acrylate copolymer,
Three 10-15 parts of phosphite ester of (2,4- di-tert-butyl-phenyl), 5-10 parts of dioctyl phthalate, sodium isethionate 5-10
Part, 1-5 parts of isocyanates, 1-5 parts of ammonium lauryl sulfate, 5-10 parts of crosslinking agent, 5-10 parts of heat stabilizer.
Further, the crosslinking agent is N, one of N- methylene-bisacrylamide (MBA), divinylbenzene.
Further, the heat stabilizer is Dythal.
Further, a kind of high light transmission car light lampshade preparation method, it is characterised in that:
S1: by polyethylene terephthalate, sodium polydithio-dipropyl sulfonate, ethylene-ethyl acrylate copolymer, three
(2,4- di-tert-butyl-phenyl) phosphite ester, heat stabilizer are put into reaction kettle, are warming up to 130-150 DEG C, moderate-speed mixer reaction
40min；
S2: being added dioctyl phthalate, sodium isethionate, isocyanates, crosslinking agent after being cooled to 60-80 DEG C,
Stir at low speed 1h；
S3: after being cooled to room temperature, ammonium lauryl sulfate is added in a kettle and stirs at low speed reaction 34h, can be obtained
Finished product.
According to the above aspect of the present invention, the present invention at least has the advantages that
Manufacture craft of the present invention is simple, and raw material is easy to buy, and cost of manufacture is cheap, antistatic effect, has wide answer
Use prospect.
Specific embodiment
Technical solution of the present invention is described in detail as follows below with reference to embodiment.
Embodiment 1
The component of a kind of high light transmission car light lampshade, the antistatic car light lampshade is as follows according to parts by weight: poly- to benzene
37 parts of dioctyl phthalate ethylene glycol rouge, 20 parts of sodium polydithio-dipropyl sulfonate, 15 parts of ethylene-ethyl acrylate copolymer, three (2,4- bis-
Tert-butyl-phenyl) 14 parts of phosphite ester, 8 parts of dioctyl phthalate, sodium isethionate 6,2 parts of isocyanates, ethyoxyl
5 parts, 9 parts of divinylbenzene, 8 parts of Dythal of the cruel amine of laurel.
Preparation method are as follows:
S1: by polyethylene terephthalate, sodium polydithio-dipropyl sulfonate, ethylene-ethyl acrylate copolymer, three
(2,4- di-tert-butyl-phenyl) phosphite ester, heat stabilizer are put into reaction kettle, are warming up to 130-150 DEG C, moderate-speed mixer reaction
40min；
S2: being added dioctyl phthalate, sodium isethionate, isocyanates, crosslinking agent after being cooled to 60-80 DEG C,
Stir at low speed 1h；
S3: after being cooled to room temperature, ammonium lauryl sulfate is added in a kettle and stirs at low speed reaction 34h, can be obtained
Finished product.
Embodiment 2
The component of a kind of high light transmission car light lampshade, the antistatic car light lampshade is as follows according to parts by weight: poly- to benzene
37 parts of dioctyl phthalate ethylene glycol rouge, 20 parts of sodium polydithio-dipropyl sulfonate, 13 parts of ethylene-ethyl acrylate copolymer, three (2,4- bis-
Tert-butyl-phenyl) 11 parts of phosphite ester, 8 parts of dioctyl phthalate, 7 parts of sodium isethionate, 5 parts of isocyanates, alkyl
2 parts of sodium sulfonate, 8 parts of divinylbenzene, 5 parts of Dythal.
Preparation method are as follows:
S1: by polyethylene terephthalate, sodium polydithio-dipropyl sulfonate, ethylene-ethyl acrylate copolymer, three
(2,4- di-tert-butyl-phenyl) phosphite ester, heat stabilizer are put into reaction kettle, are warming up to 130-150 DEG C, moderate-speed mixer reaction
40min；
S2: being added dioctyl phthalate, sodium isethionate, isocyanates, crosslinking agent after being cooled to 60-80 DEG C,
Stir at low speed 1h；
S3: after being cooled to room temperature, ammonium lauryl sulfate is added in a kettle and stirs at low speed reaction 34h, can be obtained
Finished product.
Embodiment 3
The component of a kind of high light transmission car light lampshade, the antistatic car light lampshade is as follows according to parts by weight: poly- to benzene
30 parts of dioctyl phthalate ethylene glycol rouge, 25 parts of sodium polydithio-dipropyl sulfonate, 10 parts of ethylene-ethyl acrylate copolymer, three (2,4- bis-
Tert-butyl-phenyl) 15 parts of phosphite ester, 9 parts of dioctyl phthalate, 7 parts of sodium isethionate, 2 parts of isocyanates, alkyl
1 part of sodium sulfonate, N, 5 parts of N- methylene-bisacrylamide (MBA), 8 parts of Dythal.
Preparation method are as follows:
S1: by polyethylene terephthalate, sodium polydithio-dipropyl sulfonate, ethylene-ethyl acrylate copolymer, three
(2,4- di-tert-butyl-phenyl) phosphite ester, heat stabilizer are put into reaction kettle, are warming up to 130-150 DEG C, moderate-speed mixer reaction
40min；
S2: being added dioctyl phthalate, sodium isethionate, isocyanates, crosslinking agent after being cooled to 60-80 DEG C,
Stir at low speed 1h；
S3: after being cooled to room temperature, ammonium lauryl sulfate is added in a kettle and stirs at low speed reaction 34h, can be obtained
Finished product.
The above is only a preferred embodiment of the present invention, it is not intended to restrict the invention, it is noted that for this skill
For the those of ordinary skill in art field, without departing from the technical principles of the invention, can also make it is several improvement and
Modification, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (4)
1. a kind of high light transmission car light lampshade, it is characterised in that: the component of the antistatic car light lampshade is according to the following institute of parts by weight
Show: 30-40 parts of polyethylene terephthalate, 20-25 parts of sodium polydithio-dipropyl sulfonate, ethylene-ethylacrylate copolymerization
10-15 parts of object, three 10-15 parts of phosphite ester of (2,4- di-tert-butyl-phenyl), 5-10 parts of dioctyl phthalate, ethoxy sulphur
Sour sodium 5-10 parts, 1-5 parts of isocyanates, 1-5 parts of ammonium lauryl sulfate, 5-10 parts of crosslinking agent, 5-10 parts of heat stabilizer.
2. a kind of high light transmission car light lampshade according to claim 1, it is characterised in that: the crosslinking agent is N, N- methylene
One of bisacrylamide (MBA), divinylbenzene.
3. a kind of high light transmission car light lampshade according to claim 1, it is characterised in that: the heat stabilizer is that dibasic is adjacent
Phthalic acid lead.
4. a kind of high light transmission car light lampshade preparation method according to claim 1, it is characterised in that:
S1: by polyethylene terephthalate, sodium polydithio-dipropyl sulfonate, ethylene-ethyl acrylate copolymer, three (2,
4- di-tert-butyl-phenyl) phosphite ester, heat stabilizer be put into reaction kettle, it is warming up to 130-150 DEG C, moderate-speed mixer reaction
40min；
S2: dioctyl phthalate, sodium isethionate, isocyanates, crosslinking agent, low speed are added after being cooled to 60-80 DEG C
Stir 1h；
S3: after being cooled to room temperature, ammonium lauryl sulfate is added in a kettle and stirs at low speed reaction 34h, finished product can be obtained.