CN109719016A - A kind of technique using color powder preparation surface flash of light frosted Environmental protection floor - Google Patents
A kind of technique using color powder preparation surface flash of light frosted Environmental protection floor Download PDFInfo
- Publication number
- CN109719016A CN109719016A CN201811538389.XA CN201811538389A CN109719016A CN 109719016 A CN109719016 A CN 109719016A CN 201811538389 A CN201811538389 A CN 201811538389A CN 109719016 A CN109719016 A CN 109719016A
- Authority
- CN
- China
- Prior art keywords
- floor
- paint
- color
- proportion
- technique
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of technique using color powder preparation surface flash of light frosted Environmental protection floor, and chromatic metallic powder is compound as a kind of progress of ingredient of floor surface, obtains surface flash of light, appearance is beautiful, more wear-resisting floor；The technical solution of use are as follows: a kind of technique using color powder preparation surface flash of light frosted Environmental protection floor first processes floor base body, spare；Then water-based paint and metal powder configuration paint body are mixed in proportion according to the depth of required color, the basis proportion of paint body is water-based paint and metal powder mixed proportion is 5:1, and the color needed is deep, increases the adding proportion of metal powder, conversely, reducing the adding proportion of metal powder；And the paint body modulated is sprayed on building site plate matrix surface；It is then allowed to stand 24 hours, makes its natural drying；Curing process is done after painting body drying, forms finished product；It the composite can be widely applied to floor and manufacture field.
Description
Technical field
A kind of technique using color powder preparation surface flash of light frosted Environmental protection floor of the present invention, belongs to the floor manufacturing
Technical field.
Background technique
Currently, wood floors are recovered one's original simplicity with it, the natural decorated style of texture, floor decorative material huge legendary turtle is monopolized always
Head, but since the problems such as product price is high, burst size of methanal is high and flame retardant property is not high constrains the development of Floor Industry,
And its surface color of existing wood floors is relatively simple.
Summary of the invention
The flash of light frosted of color powder preparation surface is utilized the invention overcomes the deficiencies of the prior art, and provides a kind of
The technique of Environmental protection floor, chromatic metallic powder is compound as a kind of progress of ingredient of floor surface, obtain surface flash of light, appearance drift
Bright, more wear-resisting floor.
In order to solve the above-mentioned technical problem, the technical solution adopted by the present invention are as follows: a kind of to prepare surface using color powder
The technique of flash of light frosted Environmental protection floor, comprising the following steps:
Step 1: processing floor base body, spare；
Step 2: modulation paint body；Mix water-based paint and metal powder, basis proportion in proportion according to the depth of required color
It is 5:1 for water-based paint and metal powder mixed proportion, the color needed is deep, increases the adding proportion of metal powder, conversely, subtracting
The adding proportion of few metal powder；
Step 3: the paint body modulated in second step is sprayed on building site plate matrix surface；It is then allowed to stand 24 hours, keeps it naturally dry
It is dry；
Step 4: doing curing process after painting body drying, finished product is formed.
Do frosted processing in the floor base body surface.
Array distribution has multiple grooves on the floor base body surface, and the groove is for filling paint body.
In paint body roller coating before floor base body surface, first floor base body is heated, so that the floor when painting body roller coating
Matrix is maintained at 70-80 DEG C.
Compared with the prior art, the invention has the beneficial effects that: the present invention is sprayed on floor base body surface will paint body
Afterwards, it is spontaneously dried after standing 24 hours, curing process is done after dry, form finished product, there is unique two dimension using metal powder
The functions such as sheet barrier, shielding ultraviolet light, steady chemical structure, effectively improve permeability resistance, the weatherability, wearability of film
And corrosion resistance, meanwhile, any radioactive element is free of, the trend for leading paint field environmentally protective is played.
Specific embodiment
A kind of technique using color powder preparation surface flash of light frosted Environmental protection floor of the present invention, comprising the following steps:
Step 1: processing floor base body, spare；
Step 2: modulation paint body；Mix water-based paint and metal powder, basis proportion in proportion according to the depth of required color
It is 5:1 for water-based paint and metal powder mixed proportion, the color needed is deep, increases the adding proportion of metal powder, conversely, subtracting
The adding proportion of few metal powder；
Step 3: the paint body modulated in second step is sprayed on building site plate matrix surface；It is then allowed to stand 24 hours, keeps it naturally dry
It is dry；
Step 4: doing curing process after painting body drying, finished product is formed.
Do frosted processing in the floor base body surface.
Array distribution has multiple grooves on the floor base body surface, and the groove is for filling paint body.
In paint body roller coating before floor base body surface, first floor base body is heated, so that the floor when painting body roller coating
Matrix is maintained at 70-80 DEG C.
Chromatic metallic powder of the present invention is a kind of environmentally protective filler of new type functional, with unique two-dimensional slice
Shape barrier, shielding ultraviolet light, the functions such as steady chemical structure, effectively improve the permeability resistance of film, weatherability, wearability and
Corrosion resistance, meanwhile, any radioactive element is free of, the trend for leading paint field environmentally protective is played.
Chromatic metallic powder of the present invention is widely used in building external paint, anticorrosive paint, powdery paints, resistance to height
Thermo-paint, coatings, water-repellent paint, marking paint, radiation shielding coating and some special coatings, such as marine paint, space flight
Device thermal control coating and food container coating etc..
Chromatic metallic powder of the present invention is a kind of silicate of layer structure, and structure is clipped by two layers of oxygen-octahedron
The compound silica layer that one layer of alumina octahedral is constituted.
Chromatic metallic powder of the present invention can be split into very thin sheet, piece thickness is up to 1 μm or less when dissociating complete
(can theoretically be whittled into 0.001 μm), radius-thickness ratio is big.
The present invention substantially belongs to a kind of mica powder crystal, chemical formula are as follows:
Mica powder crystal: K0.5-1 (Al, Fe, Mg) 2 (SiAl) 4O10 (OH) 2 nH2O, general chemical component: SiO2:
43.13-49.04%, Al2O3:27.93-37.44%, K2O+Na2O:9-11%.
Chromatic metallic powder of the present invention is a kind of nonmetallic mineral, containing Multiple components, wherein mainly there is SiO2, is contained
Amount is generally in 49% or so, Al2O3 content 30% or so.
The above are the characteristics of chromatic metallic powder, and the chromatic metallic powder is compound as a kind of progress of ingredient of floor surface,
The floor of manufacture can glisten, and appearance is beautiful, and floor is more wear resistant.It is usually used in child room and compares the space use of trend.
Production method: water-based paint and this ingredient of metal powder about 5:1(be according to the depth of color come, do not have
Standard) mixed, roller coating is carried out after mixing, is then spontaneously dried after 24 hours, curing process is done after dry, formed at
Product.
The present invention is explained in detail above in conjunction with embodiment, but the present invention is not limited to above-described embodiments, at this
Field those of ordinary skill within the scope of knowledge, can also make various changes without departing from the purpose of the present invention
Change.
Claims (4)
1. a kind of technique using color powder preparation surface flash of light frosted Environmental protection floor, which comprises the following steps:
Step 1: processing floor base body, spare；
Step 2: modulation paint body；Mix water-based paint and metal powder, basis proportion in proportion according to the depth of required color
It is 5:1 for water-based paint and metal powder mixed proportion, the color needed is deep, increases the adding proportion of metal powder, conversely, subtracting
The adding proportion of few metal powder；
Step 3: the paint body modulated in second step is sprayed on building site plate matrix surface；It is then allowed to stand 24 hours, keeps it naturally dry
It is dry；
Step 4: doing curing process after painting body drying, finished product is formed.
2. a kind of technique using color powder preparation surface flash of light frosted Environmental protection floor according to claim 1, special
Sign is that frosted processing is done on the floor base body surface.
3. a kind of technique using color powder preparation surface flash of light frosted Environmental protection floor according to claim 1, special
Sign is that array distribution has multiple grooves on the floor base body surface, and the groove is for filling paint body.
4. a kind of technique using color powder preparation surface flash of light frosted Environmental protection floor according to claim 1, special
Sign is, in paint body roller coating before floor base body surface, first heats to floor base body, so that the floor base when painting body roller coating
Body is maintained at 70-80 DEG C.