CN109706489A - A kind of zinc-plated antistatic electroplate liquid - Google Patents
A kind of zinc-plated antistatic electroplate liquid Download PDFInfo
- Publication number
- CN109706489A CN109706489A CN201711013876.XA CN201711013876A CN109706489A CN 109706489 A CN109706489 A CN 109706489A CN 201711013876 A CN201711013876 A CN 201711013876A CN 109706489 A CN109706489 A CN 109706489A
- Authority
- CN
- China
- Prior art keywords
- parts
- zinc
- chloride
- electroplate liquid
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of zinc-plated antistatic electroplate liquid, in parts by weight, comprising: 30-50 parts of copper sulphate, 40-50 parts of aluminum sulfate, 30-60 parts of copper chloride, 15-20 parts of nickel hydroxide cobaltous sulfate, 10-20 parts of cobalt chloride, 15-30 parts of ferric sulfate, 10-20 parts of frerrous chloride, 10-15 parts of cuprous oxide, 15-20 parts of hydrochloric acid, 3-5 parts of acetic acid, 10-15 parts of dibastic sodium phosphate, 15-20 parts of sodium nitrite, 20-30 parts of zinc oxide, 20-50 parts of sodium stannate, 20-50 parts of potassium hydroxide, alkylamine 50-80 parts of ethoxylated fat race, 1000-3000 parts of deionized water.It joined ethoxylated fat race alkylamine in electroplate liquid of the present invention, can effectively realize antistatic effect.
Description
Technical field
The present invention relates to electroplate liquids, and in particular to one kind is zinc-plated to use electroplate liquid.
Background technique
In mechanical processing process, the anti-corrosive grease of component surface adherency, cutting fluid, machinery oil, lubricant grease, grinding
Liquid, release agent etc. are mixed and are sticked together with dust, polishing dust, form thicker dirt.If the above dirt is not removed before heat treatment
It goes, then degreasing and rust removal is difficult to clean up after its quenching sinters obstinate solid grease into, and bubble attachment makes to plate thereon when plating
Layer forms gas detention type pin hole.Heat treated part surface inevitably adheres to one layer of greasy dirt, when dust is fallen on the surface,
And mix and stick together with grease, it is difficult to clean up over time, so that workpiece surface be made to form unconspicuous tiny oil mark, applies
Bubble residence forms pin hole thereon when plating.When in addition using mesh band type resistor furnace quenching, the greasy dirt and dust etc. of workpiece surface are miscellaneous
Matter particle is mixed to stick together, and sinters obstinate solid grease into, and when salt made from earth containing a comparatively high percentage of sodium chloride is tempered, the above grease forms with nitro salt obstinate again
Thermopolymer, when plating, are difficult that the above dirt is thoroughly cleared, and bubble hydrogen is easily adhered to above dirt, it is difficult to is discharged, to make
Coating generates pin hole and point phenomenon, and as bubble is gradually grown up, coating can be burst automatically, decortication phenomenon is generated, to lead
Send a telegraph the disadvantage of plating solution difference of hardness, dispersion performance and covering power difference.
In view of the above shortcomings, the designer, is actively subject to research and innovation, it is a kind of new structural zinc-plated to found
With electroplate liquid, make it with more the utility value in industry.
Summary of the invention
In order to solve the above technical problems, the object of the present invention is to provide a kind of zinc-plated antistatic electroplate liquids.
Technical scheme is as follows:
A kind of zinc-plated antistatic electroplate liquid, which is characterized in that in parts by weight, comprising:
30-50 parts of copper sulphate, 40-50 parts of aluminum sulfate, 30-60 parts of copper chloride, 15-20 parts of nickel hydroxide cobaltous sulfate, chlorination
10-20 parts of cobalt, 15-30 parts of ferric sulfate, 10-20 parts of frerrous chloride, 10-15 parts of cuprous oxide, 15-20 parts of hydrochloric acid, acetic acid 3-5
Part, 10-15 parts of dibastic sodium phosphate, 15-20 parts of sodium nitrite, 20-30 parts of zinc oxide, 20-50 parts of sodium stannate, potassium hydroxide 20-50
Part, alkylamine 50-80 parts of ethoxylated fat race, 1000-3000 parts of deionized water.
Further, in parts by weight, comprising: 40 parts of copper sulphate, 44 parts of aluminum sulfate, 34 parts of copper chloride, hydroxide
18 parts of nickel cobaltous sulfate, 15 parts of cobalt chloride, 20 parts of ferric sulfate, 15 parts of frerrous chloride, 12 parts of cuprous oxide, 18 parts of hydrochloric acid, acetic acid 4
Part, 12 parts of dibastic sodium phosphate, 18 parts of sodium nitrite, 25 parts of zinc oxide, 30 parts of sodium stannate, 35 parts of potassium hydroxide, ethoxylated fat
60 parts of race's alkylamine, 2000 parts of deionized water.
A kind of preparation method of zinc-plated antistatic electroplate liquid, it is characterised in that: by copper sulphate, aluminum sulfate, copper chloride, hydrogen-oxygen
Change nickel cobaltous sulfate, cobalt chloride, ferric sulfate, frerrous chloride, cuprous oxide, hydrochloric acid, acetic acid, dibastic sodium phosphate, sodium nitrite, oxidation
It is added to after zinc, sodium stannate, potassium hydroxide, ethoxylated fat race alkylamine are mixed, then after being dispersed by dispersion machine
In ionized water, the electroplate liquid is obtained after stirring by high-speed mixer.
According to the above aspect of the present invention, the present invention has at least the following advantages:
It joined ethoxylated fat race alkylamine in electroplate liquid of the present invention, can effectively realize antistatic effect.
Specific embodiment
With reference to embodiment, the embodiment of the present invention is furthur described in detail.Following embodiment is used for
Illustrate the present invention, but is not intended to limit the scope of the invention.
A kind of preparation method of zinc-plated antistatic electroplate liquid, by copper sulphate, aluminum sulfate, copper chloride, nickel hydroxide cobaltous sulfate,
Cobalt chloride, ferric sulfate, frerrous chloride, cuprous oxide, hydrochloric acid, acetic acid, dibastic sodium phosphate, sodium nitrite, zinc oxide, sodium stannate, hydrogen
It is add to deionized water, passes through after potassium oxide, ethoxylated fat race alkylamine are mixed, then after being dispersed by dispersion machine
The electroplate liquid is obtained after high-speed mixer stirring.
Embodiment 1
A kind of zinc-plated antistatic electroplate liquid, in parts by weight, comprising:
30 parts of copper sulphate, 40 parts of aluminum sulfate, 30 parts of copper chloride, 15 parts of nickel hydroxide cobaltous sulfate, 10 parts of cobalt chloride, ferric sulfate
15 parts, 10 parts of frerrous chloride, 10 parts of cuprous oxide, 15 parts of hydrochloric acid, 3 parts of acetic acid, 10 parts of dibastic sodium phosphate, 15 parts of sodium nitrite, oxygen
Change 20 parts of zinc, 20 parts of sodium stannate, 20 parts of potassium hydroxide, 50 parts of ethoxylated fat race alkylamine, 1000 parts of deionized water.
Embodiment 2
A kind of zinc-plated antistatic electroplate liquid, in parts by weight, comprising:
40 parts of copper sulphate, 45 parts of aluminum sulfate, 45 parts of copper chloride, 18 parts of nickel hydroxide cobaltous sulfate, 15 parts of cobalt chloride, ferric sulfate
20 parts, 15 parts of frerrous chloride, 12 parts of cuprous oxide, 18 parts of hydrochloric acid, 4 parts of acetic acid, 12 parts of dibastic sodium phosphate, 18 parts of sodium nitrite, oxygen
Change 25 parts of zinc, 30 parts of sodium stannate, 30 parts of potassium hydroxide, 30 parts of ethoxylated fat race alkylamine, 2000 parts of deionized water.
Embodiment 3
A kind of zinc-plated antistatic electroplate liquid, in parts by weight, comprising:
50 parts of copper sulphate, 50 parts of aluminum sulfate, 60 parts of copper chloride, 20 parts of nickel hydroxide cobaltous sulfate, 20 parts of cobalt chloride, ferric sulfate
30 parts, 20 parts of frerrous chloride, 15 parts of cuprous oxide, 20 parts of hydrochloric acid, 5 parts of acetic acid, 15 parts of dibastic sodium phosphate, 20 parts of sodium nitrite, oxygen
Change 30 parts of zinc, 50 parts of sodium stannate, 50 parts of potassium hydroxide, 80 parts of ethoxylated fat race alkylamine, 3000 parts of deionized water.
It joined ethoxylated fat race alkylamine in electroplate liquid of the present invention, can effectively realize antistatic effect.
The above is only a preferred embodiment of the present invention, it is not intended to restrict the invention, it is noted that for this skill
For the those of ordinary skill in art field, without departing from the technical principles of the invention, can also make it is several improvement and
Modification, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (3)
1. a kind of zinc-plated antistatic electroplate liquid, which is characterized in that in parts by weight, comprising:
30-50 parts of copper sulphate, 40-50 parts of aluminum sulfate, 30-60 parts of copper chloride, 15-20 parts of nickel hydroxide cobaltous sulfate, cobalt chloride 10-
20 parts, 15-30 parts of ferric sulfate, 10-20 parts of frerrous chloride, 10-15 parts of cuprous oxide, 15-20 parts of hydrochloric acid, 3-5 parts of acetic acid, phosphoric acid
10-15 parts of hydrogen sodium, 15-20 parts of sodium nitrite, 20-30 parts of zinc oxide, 20-50 parts of sodium stannate, 20-50 parts of potassium hydroxide, ethoxy
50-80 parts of base aliphatic alkylamine, 1000-3000 parts of deionized water.
2. the zinc-plated antistatic electroplate liquid of one kind according to claim 1, which is characterized in that in parts by weight, comprising:
40 parts of copper sulphate, 44 parts of aluminum sulfate, 34 parts of copper chloride, 18 parts of nickel hydroxide cobaltous sulfate, 15 parts of cobalt chloride, 20 parts of ferric sulfate, chlorine
Change ferrous 15 parts, 12 parts of cuprous oxide, 18 parts of hydrochloric acid, 4 parts of acetic acid, 12 parts of dibastic sodium phosphate, 18 parts of sodium nitrite, zinc oxide 25
Part, 30 parts of sodium stannate, 35 parts of potassium hydroxide, 60 parts of ethoxylated fat race alkylamine, 2000 parts of deionized water.
3. the preparation method of the zinc-plated antistatic electroplate liquid of one kind according to claim 2, it is characterised in that: by copper sulphate,
Aluminum sulfate, copper chloride, nickel hydroxide cobaltous sulfate, cobalt chloride, ferric sulfate, frerrous chloride, cuprous oxide, hydrochloric acid, acetic acid, phosphoric acid hydrogen
After sodium, sodium nitrite, zinc oxide, sodium stannate, potassium hydroxide, ethoxylated fat race alkylamine are mixed, then pass through dispersion
It is add to deionized water after machine dispersion, the electroplate liquid is obtained after stirring by high-speed mixer.