CN109705521A - A kind of pyroceram steel composite material - Google Patents
A kind of pyroceram steel composite material Download PDFInfo
- Publication number
- CN109705521A CN109705521A CN201711013403.XA CN201711013403A CN109705521A CN 109705521 A CN109705521 A CN 109705521A CN 201711013403 A CN201711013403 A CN 201711013403A CN 109705521 A CN109705521 A CN 109705521A
- Authority
- CN
- China
- Prior art keywords
- parts
- steel composite
- composite material
- bisphenol
- pyroceram
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of pyroceram steel composite materials, are mixed by the raw material of following component: 25-29 parts of phenolic resin, 20-25 parts of bisphenol-A epoxy vinylite, 60-70 parts of glass fibre, 7-9 parts of dibutyl phthalate, 6-7 parts of ethylenediamine, 1-4 parts of ethyl alcohol, 10-12 parts of calcium carbonate.Heat-resisting ability of the present invention is strong, can effectively prevent solving because of temperature excessively high the drawbacks of causing intensity to decline, and corrosion resistance and good, supports that ageing resistance is strong, anti-shearing effect is good.
Description
Technical field
The present invention relates to a kind of glass-reinforced plastic material more particularly to a kind of pyroceram steel composite materials.
Background technique
The concept of composite material refers to that a kind of material is not able to satisfy requirement, needs the material by two or more
It is combined with each other, composition another kind is able to satisfy the material of people's requirement, i.e. composite material.For example, single kind of glass fibre, although
Intensity is very high, but between fiber be it is loose, pulling force can only be born, bending, shearing and compression cannot be born, be also less prone to be made into solid
Fixed geometry is soft body.If they are bonded together with synthetic resin, can be made various with fixed shape
Hard product, can bear tensile stress and bear bending, compression and shear stress.Since its intensity is equivalent to steel, again
Contain glass ingredient, it may have the performances such as color as glass, body, corrosion-resistant, electrical isolation, heat-insulated are gone through as glass
This straightaway title " glass reinforced plastic " is formd in history.Existing glass reinforced plastic heat-resisting ability is poor, and it is weak to support ageing resistance.
Summary of the invention
Above-mentioned to solve the problems, such as, the present invention provides a kind of strong heat-resisting ability, corrosion resistance and good, resists aging
The pyroceram steel composite material that ability is strong, anti-shearing effect is good.
The present invention solve above-mentioned technical problem use technical solution are as follows: a kind of pyroceram steel composite material, by with
The raw material of lower component is mixed:
25-29 parts of phenolic resin, 20-25 parts of bisphenol-A epoxy vinylite, 60-70 parts of glass fibre, two fourth of phthalic acid
7-9 parts of ester, 6-7 parts of ethylenediamine, 1-4 parts of ethyl alcohol, 10-12 parts of calcium carbonate.
Preferably, above-mentioned pyroceram steel composite material, is mixed by the raw material of following component:
27 parts of phenolic resin, 23 parts of bisphenol-A epoxy vinylite, 65 parts of glass fibre, 8 parts of dibutyl phthalate, second
6.5 parts of diamines, 2 parts of ethyl alcohol, 11 parts of calcium carbonate.
The present invention solves beneficial effect brought by technical problem and is: heat-resisting ability of the present invention is strong, can effectively prevent
It only solves because of temperature excessively high the drawbacks of causing intensity to decline, and corrosion resistance and good, strong, the anti-shearing effect to ageing resistance
It is good.
Specific embodiment
The present invention is described in further details combined with specific embodiments below.
Embodiment 1
A kind of pyroceram steel composite material, is mixed by the raw material of following component:
25 parts of phenolic resin, 20 parts of bisphenol-A epoxy vinylite, 60 parts of glass fibre, 7 parts of dibutyl phthalate, second
6 parts of diamines, 1 part of ethyl alcohol, 10 parts of calcium carbonate.
Embodiment 2
A kind of pyroceram steel composite material, is mixed by the raw material of following component:
27 parts of phenolic resin, 23 parts of bisphenol-A epoxy vinylite, 65 parts of glass fibre, 8 parts of dibutyl phthalate, second
6.5 parts of diamines, 2 parts of ethyl alcohol, 11 parts of calcium carbonate.
Embodiment 3
A kind of pyroceram steel composite material, is mixed by the raw material of following component:
29 parts of phenolic resin, 25 parts of bisphenol-A epoxy vinylite, 70 parts of glass fibre, 9 parts of dibutyl phthalate, second
7 parts of diamines, 4 parts of ethyl alcohol, 12 parts of calcium carbonate.
Above-mentioned, although specific embodiments of the present invention have been described, not to the limit of the scope of the present invention
System, those skilled in the art should understand that, based on the technical solutions of the present invention, those skilled in the art do not need to pay
The various modifications or changes that creative work can be made out are still within protection scope of the present invention.
Claims (2)
1. a kind of pyroceram steel composite material, it is characterised in that: be mixed by the raw material of following component:
25-29 parts of phenolic resin, 20-25 parts of bisphenol-A epoxy vinylite, 60-70 parts of glass fibre, two fourth of phthalic acid
7-9 parts of ester, 6-7 parts of ethylenediamine, 1-4 parts of ethyl alcohol, 10-12 parts of calcium carbonate.
2. pyroceram steel composite material according to claim 1, it is characterised in that: mixed by the raw material of following component
It is made: 27 parts of phenolic resin, 23 parts of bisphenol-A epoxy vinylite, 65 parts of glass fibre, 8 parts of dibutyl phthalate, second
6.5 parts of diamines, 2 parts of ethyl alcohol, 11 parts of calcium carbonate.