CN108070202A - A kind of pyroceram steel composite material - Google Patents
A kind of pyroceram steel composite material Download PDFInfo
- Publication number
- CN108070202A CN108070202A CN201610990348.9A CN201610990348A CN108070202A CN 108070202 A CN108070202 A CN 108070202A CN 201610990348 A CN201610990348 A CN 201610990348A CN 108070202 A CN108070202 A CN 108070202A
- Authority
- CN
- China
- Prior art keywords
- parts
- steel composite
- composite material
- bisphenol
- pyroceram
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of pyroceram steel composite materials, are mixed by the raw material of following component：25 29 parts of phenolic resin, 20 25 parts of bisphenol-A epoxy vinylite, 60 70 parts of glass fibre, 79 parts of dibutyl phthalate, 67 parts of ethylenediamine, 14 parts of ethyl alcohol, 10 12 parts of calcium carbonate.Heat-resisting ability of the present invention is strong, can effectively prevent from solving because of temperature excessively high the drawbacks of intensity is caused to decline, and corrosion resistance and good, to ageing resistance is strong, anti-shearing effect is good.
Description
Technical field
The present invention relates to a kind of glass-reinforced plastic material more particularly to a kind of pyroceram steel composite materials.
Background technology
The concept of composite material refers to that a kind of material cannot meet requirement, it is necessary to material by two or more
It is combined with each other, composition another kind can meet the material of people's requirement, i.e. composite material.For example, single kind of glass fibre, although
Intensity is very high, but is loose between fiber, can only bear pulling force, it is impossible to bear to bend, shear and compression, be also less prone to make solid
Fixed geometry is soft body.If they are bonded together with synthetic resin, can make various with fixed shape
Hard product, tensile stress and bearing can be born and bend, compress and shear stress.Since its intensity is equivalent to steel, again
Contain glass ingredient, it may have the performances such as color and luster, body, corrosion-resistant, electrical isolation, heat-insulated as glass as glass, are gone through
This straightaway title " fiberglass " is formd in history.Existing fiberglass heat-resisting ability is poor, weak to ageing resistance.
The content of the invention
Above-mentioned to solve the problems, such as, the present invention provides a kind of strong heat-resisting ability, corrosion resistance and good, resists aging
The pyroceram steel composite material that ability is strong, anti-shearing effect is good.
The present invention solve the technical solution that uses of above-mentioned technical problem for：A kind of pyroceram steel composite material, by with
The raw material of lower component is mixed：
25-29 parts of phenolic resin, 20-25 parts of bisphenol-A epoxy vinylite, 60-70 parts of glass fibre, two fourth of phthalic acid
7-9 parts of ester, 6-7 parts of ethylenediamine, 1-4 parts of ethyl alcohol, 10-12 parts of calcium carbonate.
Preferably, above-mentioned pyroceram steel composite material, is mixed by the raw material of following component：
27 parts of phenolic resin, 23 parts of bisphenol-A epoxy vinylite, 65 parts of glass fibre, 8 parts of dibutyl phthalate, second
6.5 parts of diamines, 2 parts of ethyl alcohol, 11 parts of calcium carbonate.
Advantageous effect caused by present invention solution technical problem is：Heat-resisting ability of the present invention is strong, can effectively prevent
Only solve because of temperature excessively high the drawbacks of intensity is caused to decline, and corrosion resistance and good, to ageing resistance is strong, anti-shearing effect
It is good.
Specific embodiment
The present invention is described in further details with reference to specific embodiment.
Embodiment 1
A kind of pyroceram steel composite material, is mixed by the raw material of following component：
25 parts of phenolic resin, 20 parts of bisphenol-A epoxy vinylite, 60 parts of glass fibre, 7 parts of dibutyl phthalate, second
6 parts of diamines, 1 part of ethyl alcohol, 10 parts of calcium carbonate.
Embodiment 2
A kind of pyroceram steel composite material, is mixed by the raw material of following component：
27 parts of phenolic resin, 23 parts of bisphenol-A epoxy vinylite, 65 parts of glass fibre, 8 parts of dibutyl phthalate, second
6.5 parts of diamines, 2 parts of ethyl alcohol, 11 parts of calcium carbonate.
Embodiment 3
A kind of pyroceram steel composite material, is mixed by the raw material of following component：
29 parts of phenolic resin, 25 parts of bisphenol-A epoxy vinylite, 70 parts of glass fibre, 9 parts of dibutyl phthalate, second
7 parts of diamines, 4 parts of ethyl alcohol, 12 parts of calcium carbonate.
Although the above-mentioned specific embodiment to the present invention is described, not to the limit of the scope of the present invention
System, those skilled in the art should understand that, based on the technical solutions of the present invention, those skilled in the art need not pay
Go out various modifications or changes that creative work can be made still within protection scope of the present invention.
Claims (2)
1. a kind of pyroceram steel composite material, it is characterised in that：It is mixed by the raw material of following component：
25-29 parts of phenolic resin, 20-25 parts of bisphenol-A epoxy vinylite, 60-70 parts of glass fibre, two fourth of phthalic acid
7-9 parts of ester, 6-7 parts of ethylenediamine, 1-4 parts of ethyl alcohol, 10-12 parts of calcium carbonate.
2. pyroceram steel composite material according to claim 1, it is characterised in that：It is mixed by the raw material of following component
It is made：
27 parts of phenolic resin, 23 parts of bisphenol-A epoxy vinylite, 65 parts of glass fibre, 8 parts of dibutyl phthalate, second
6.5 parts of diamines, 2 parts of ethyl alcohol, 11 parts of calcium carbonate.