CN109679784A - 一种水基型防雨玻璃清洁剂及其制备方法 - Google Patents

一种水基型防雨玻璃清洁剂及其制备方法 Download PDF

Info

Publication number
CN109679784A
CN109679784A CN201710979032.4A CN201710979032A CN109679784A CN 109679784 A CN109679784 A CN 109679784A CN 201710979032 A CN201710979032 A CN 201710979032A CN 109679784 A CN109679784 A CN 109679784A
Authority
CN
China
Prior art keywords
type rain
aqua type
proof glass
glass cleaner
organosilan
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201710979032.4A
Other languages
English (en)
Inventor
黄春龙
尹昌威
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DONGGUAN FANYA CHEMICAL PRODUCTS Co Ltd
Original Assignee
DONGGUAN FANYA CHEMICAL PRODUCTS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DONGGUAN FANYA CHEMICAL PRODUCTS Co Ltd filed Critical DONGGUAN FANYA CHEMICAL PRODUCTS Co Ltd
Priority to CN201710979032.4A priority Critical patent/CN109679784A/zh
Publication of CN109679784A publication Critical patent/CN109679784A/zh
Withdrawn legal-status Critical Current

Abstract

本发明涉及清洁剂技术领域，具体涉及一种水基型防雨玻璃清洁剂及其制备方法。该水基型防雨玻璃清洁剂，由以下重量份数的原料组成：有机硅烷微乳液、改性聚丙烯酸树脂、溶剂、碱剂、防腐剂、去离子水。本发明的清洁剂，以去离子水为载体，通过去离子水的极性作用，溶解有机硅烷微乳液和改性聚丙烯酸树脂，使其溶解性和稳定性更好；有机硅烷微乳液和聚丙烯酸树脂的亲油基能够与玻璃表面吸附，在玻璃表面形成薄薄的紧密性网络沉积层，起到疏水的作用，疏水角达到110°以上。本发明的制备方法，操作简单，成本低，效率高，通过严格控制各原料的用量、加入顺序使各原料协同反应，使整个反应体系有序、稳定进行。

Description

一种水基型防雨玻璃清洁剂及其制备方法
技术领域
本发明涉及清洁剂技术领域，具体涉及一种水基型防雨玻璃清洁剂及其制备方法。
背景技术
目前，市场上常见的水基型玻璃清洁剂并不具有疏水功能，其利用配方里含有的表面活性剂和溶剂只能到达清洁的作用；另外，市场上常见的玻璃疏水剂为醇基型玻璃疏水剂，其配方以低分子醇为载体，通过非极性键方式，让聚丙烯酸酯和有机硅烷分散和溶解，使用成本和操作性难度高，而且在使用时气味大，对人和物件伤害大，易腐蚀橡塑件，对环境也不友好；其作用于玻璃后会在玻璃表面形成一层较厚的油层，导致玻璃的透明性降低及产生散光模糊效应，严重影响视线，且稳定性不好，即易水解失效。
发明内容
为了克服现有技术中存在的缺点和不足，本发明的目的之一在于提供一种水基型防雨玻璃清洁剂，以水为载体，气味小、对人体和环境的伤害小，同时具有良好的疏水功效。
本发明的目的之二在于提供一种水基型防雨玻璃清洁剂的制备方法，该制备方法操作简单，成本低，效率高，通过严格控制各原料的用量、加入顺序使各原料协同反应，使整个反应体系有序、稳定进行。
本发明的目的通过下述技术方案实现：一种水基型防雨玻璃清洁剂，由以下重量份数的原料组成：
本发明选用去离子水为载体，通过去离子水的极性作用，溶解有机硅烷微乳液和改性聚丙烯酸树脂，使得溶液的溶解性和稳定性均更好，且以去离子水为载体相比传统的以溶剂为载体，使制得的水基型防雨玻璃清洁剂气味更小，对环境和人体的伤害更小，符合绿色环保，本发明中去离子水的添加量高达80％，进一步提高了清洁剂的溶解性和稳定性，价格低廉，操作方便。
本发明选用的有机硅烷微乳液为亲水性的微乳化有机硅烷微乳液，能够溶于水中，使用有机硅烷微乳液作为疏水剂，其亲油基能够与玻璃表面吸附，在玻璃表面形成薄薄的紧密型网络沉积层，即单分子疏水膜，其厚度范围为10-100nm，并起到疏水的作用，疏水角能够达到110°以上，在清洁玻璃的同时，能够在玻璃表面形成一层疏水膜。
本发明选用的改性聚丙烯酸树脂为水溶性改性聚丙烯酸树脂，能够溶于水中，改性聚丙烯酸树脂起到协助疏水的作用，其亲油基与有机硅烷微乳液的亲油基一起与玻璃表面吸附，在玻璃表面形成薄薄的紧密型网络沉积层，即单分子疏水膜，其厚度范围为10-100nm，并起到疏水的作用，疏水角能够达到110°以上，在清洁玻璃的同时，能够在玻璃表面形成一层疏水膜。
本发明选用的溶剂为水溶性溶剂，配合有机硅烷微乳液自身的乳化性质，进一步提高分解、剥离、溶解汽车外表面的污物的能力，从而提高本发明的水基型防雨玻璃清洁剂的整体清洗能力。
本发明选用的碱剂，用于调节清洁剂的pH，更加有效的溶解有机污物。
本发明选用的防腐剂，用于增强清洁剂的抗菌抑菌的功能，在清洁玻璃表面的同时，具有抗菌抑菌的作用。
优选的，由以下重量份数的原料组成：
优选的，由以下重量份数的原料组成：
优选的，所述的有机硅烷微乳液由以下重量份数的原料组成：
本发明的有机硅烷微乳液通过采用聚二甲基硅氧烷和八甲基环四硅氧烷使本发明有机硅烷微乳液能够在玻璃表面形成薄薄的紧密型网络沉积层，即单分子疏水膜，其厚度范围为10-100nm，并起到疏水的作用；通过采用阳离子表面活性剂十六烷基三甲基氯化铵和十六烷基二甲基胺，增强了本发明有机硅烷微乳液的自乳化性质；通过采用鲸蜡基聚乙二醇作为乳化剂，可以增强本发明有机硅烷微乳液的滑顺性和溶解作用；通过采用油酸作为油性乳化剂，可以增强本发明有机硅烷微乳液的乳化效果；通过采用二乙醇胺作为碱剂，起到调节本发明有机硅烷微乳液的pH的作用，使其保持中性，并能促进其乳化作用，更加有效的溶解有机污物；通过采用异噻唑啉酮作为防腐剂，用于增强本发明有机硅烷微乳液的抗菌抑菌的功能，在清洁玻璃表面的同时，具有抗菌抑菌的作用。
本发明采用的有机硅烷微乳液在溶于水后，起到疏水的作用，作用原理为：通过表面活性剂对聚二甲基硅氧烷和八甲基环四硅氧烷进行开环乳液聚合，表面活性剂的亲水基结合在硅氧烷的两端。由于聚二甲基硅氧烷和八甲基环四硅氧烷微乳化成细小胶粒及亲水基的作用，使得有机硅烷微乳液可以连续溶于水中，并处于稳定分散系，此体系在水过量时，即过量的OH-会抢夺表面活性剂的亲水基而促使硅氧烷聚合分子形成游离状态及分散在水中与H+结合，此结合力足于支撑小量硅氧烷离子而不会聚沉。当游离的硅氧烷离子与固体表面接触时，就会吸附在表面上，并自然水解而形成一种全闭合状态，即起到疏水作用。
优选的，所述的聚二甲基硅氧烷是道康宁生产的粘度为350CS、1000CS、12500CS、30000CS、60000CS中的一种或者几种。另一优选的，所述的聚二甲基硅氧烷是道康宁生产的粘度为350CS、1000CS按照质量比为1-2:1复配而成。
优选的，所述的改性聚丙烯酸树脂为水溶性聚丙烯酸甲酯、季铵基丙烯酸酯共聚物和水溶性聚丙烯酸乙酯中的一种或者几种。另一优选的，所述的改性聚丙烯酸树脂为水溶性聚丙烯酸甲酯、季铵基丙烯酸酯共聚物和水溶性聚丙烯酸乙酯按照质量比为3-4：2-1：1复配而成。本发明选用的改性聚丙烯酸树脂为水溶性改性聚丙烯酸树脂，能够溶于水中，改性聚丙烯酸树脂起到协助疏水的作用，其亲油基与有机硅烷微乳液的亲油基一起与玻璃表面吸附，在玻璃表面形成薄薄的紧密型网络沉积层，即单分子疏水膜，其厚度范围为10-100nm，并起到疏水的作用，疏水角能够达到110°以上，在清洁玻璃的同时，能够在玻璃表面形成一层疏水膜。
优选的，所述的溶剂为低分子醇溶剂或者醇醚溶剂，所述的低分子醇溶剂或者醇醚溶剂为甲醇、乙醇、异丙醇、二丙二醇甲醚、乙二醇丁醚、二乙二醇丁醚、丙二醇、乙二醇中的一种或者几种。另一优选的，所述的溶剂是醇溶剂与醇醚溶剂的混合物，所述醇溶剂与醇醚溶剂按照质量比为2-3：1复配而成；其中，所述的醇溶剂为甲醇、乙醇、异丙醇、丙二醇和乙二醇中的一种或几种，所述的醇醚溶剂为二丙二醇甲醚、乙二醇丁醚和二乙二醇丁醚中的一种或者几种。再一优选的，所述的溶剂为乙醇、丙二醇、乙二醇丁醚和二丙二醇甲醚按照质量比2-3：1-2：1-2：1复配而成。本发明选用的溶剂为水溶性低分子醇溶剂或醇醚溶剂，其能提高本发明清洁剂的乳化性能，可以分解、剥离、溶解汽车外表面的有机类污物，提高本发明的水基型防雨玻璃清洁剂的整体清洗能力。
优选的，所述的碱剂为氢氧化钠、氢氧化钾、碳酸钠、三乙醇胺、二乙醇胺和单乙醇胺中的一种或者几种。另一优选的，所述碱剂为氢氧化钠、碳酸钠和三乙醇胺按照质量比1-3:1:2-3复配而成。本发明选用的碱剂，用于调节清洁剂的pH，更加有效的溶解有机污物。
优选的，所述的防腐剂为己内酰胺、异噻唑啉酮和对羟基苯甲酸乙酯中的一种或者几种。另一优选的，所述防腐剂为异噻唑啉酮。本发明选用的防腐剂，用于增强清洁剂的抗菌抑菌的功能，在清洁玻璃表面的同时，具有抗菌抑菌的作用。
本发明的目的之二通过下述技术方案实现：一种上述的水基型防雨玻璃清洁剂的制备方法，包括以下步骤：
(1)取去离子水，加入有机硅烷微乳液和改性聚丙烯酸树脂，搅拌至溶解；
(2)向步骤(1)得到的溶液中加入溶剂，搅拌至溶解；
(3)向步骤(2)得到的溶液中加入碱剂，搅拌至溶解；
(4)向步骤(3)得到的溶液中加入防腐剂，搅拌至分散均匀，即得到所述水基型防雨玻璃清洁剂。
优选的，所述步骤(1)-(4)均在常温下进行；所述步骤(1)的搅拌转速为20-40r/min；所述步骤(2)的搅拌转速为25-50r/min；所述步骤(3)的搅拌转速为20-40r/min；所述步骤(4)的搅拌转速为20-40r/min。
本发明的有益效果在于：本发明的水基型防雨玻璃清洁剂，以去离子水为载体，通过去离子水的极性作用，溶解有机硅烷微乳液和改性聚丙烯酸树脂，使得本发明的水基型防雨玻璃清洁剂的溶解性和稳定性更好；本发明的水基型防雨玻璃清洁剂中的有机硅烷微乳液利用自身的乳化性质可以清除污垢；本发明的溶剂也能进一步提高本发明清洁剂分解、剥离、溶解汽车外表面的有机类污物，提高本发明的水基型防雨玻璃清洁剂的整体清洗能力；本发明的水基型防雨玻璃清洁剂中的有机硅烷微乳液和聚丙烯酸树脂的亲油基能够与玻璃表面吸附，在玻璃表面形成薄薄的紧密性网络沉积层，即单分子疏水膜，并起到疏水的作用，疏水角达到110°以上。
本发明的水基型防雨玻璃清洁剂，结合水基型和疏水功能制造出一种水基型又具有疏水功能的玻璃清洁剂，其以水为载体，含水量高达80％，再通过水的极性作用，溶入有机硅烷微乳液和改性聚丙烯酸树脂，使其具有疏水的功能，且可以达到较好的溶解性和稳定性，使用成本和操作性难度低；其使用时气味小，对人和物件伤害更小，不腐蚀橡塑件，即更符合绿色环保。本发明是在玻璃表面形成薄薄的紧密型网络沉积层，即单分子疏水膜，其厚度范围为10-100nm，不影响玻璃的透明性和散光性，还可以直接用于汽车雨刮壶喷洗玻璃，一喷一刮即可完成清洁和疏水功效，且降低对汽车物件的伤害。
本发明的水基型防雨玻璃清洁剂含去离子水量高达80％，可以替换传统醇基型疏水玻璃清洁剂，气味更小、对环境和人体的伤害更小，体现绿色环保性，使用时可以直接对着玻璃喷洗，不需特别防护，在不损伤汽车车漆及其周围的金属、橡胶、塑料和玻璃的前提下，可以高效地去除汽车玻璃表面上的有机污物。
本发明的水基型防雨玻璃清洁剂可以直接加入汽车雨刮壶做挡风玻璃清洁用，一喷一刮即可完成清洁和疏水功效，价格低廉，使用简单易行，让玻璃疏水和清洁更环保，且降低对汽车物件的伤害。
本发明的制备方法，操作简单，成本低，效率高，通过严格控制各原料的用量、加入顺序使各原料协同反应，使整个反应体系有序、稳定进行。
具体实施方式
为了便于本领域技术人员的理解，下面结合实施例对本发明作进一步的说明，实施方式提及的内容并非对本发明的限定。
实施例1
一种水基型防雨玻璃清洁剂，由以下重量份数的原料组成：有机硅烷微乳液0.05份、改性聚丙烯酸树脂0.05份、溶剂3份、碱剂0.01份、防腐剂0.05份、去离子水70份。
所述的有机硅烷微乳液由以下重量份数的原料组成：聚二甲基硅氧烷10份、八甲基环四硅氧烷1份、十六烷基三甲基氯化铵1份、鲸蜡基聚乙二醇1份、十六烷基二甲基胺1份、油酸1份、二乙醇胺0.1份、异噻唑啉酮0.1份、去离子水70份。
所述的聚二甲基硅氧烷是道康宁生产的粘度为350CS。
所述的改性聚丙烯酸树脂为水溶性聚丙烯酸甲酯。
所述的溶剂为甲醇。
所述的碱剂为氢氧化钠。
所述的防腐剂为己内酰胺。
一种上述的水基型防雨玻璃清洁剂的制备方法，包括以下步骤：
(1)取去离子水，加入有机硅烷微乳液和改性聚丙烯酸树脂，搅拌至溶解；
(2)向步骤(1)得到的溶液中加入溶剂，搅拌至溶解；
(3)向步骤(2)得到的溶液中加入碱剂，搅拌至溶解；
(4)向步骤(3)得到的溶液中加入防腐剂，搅拌至分散均匀，即得到所述水基型防雨玻璃清洁剂。
所述步骤(1)-(4)均在常温下进行；所述步骤(1)的搅拌转速为20r/min；所述步骤(2)的搅拌转速为25r/min；所述步骤(3)的搅拌转速为20r/min；所述步骤(4)的搅拌转速为20r/min。
实施例2
一种水基型防雨玻璃清洁剂，由以下重量份数的原料组成：有机硅烷微乳液0.1份、改性聚丙烯酸树脂0.1份、溶剂5份、碱剂0.01份、防腐剂0.1份、去离子水80份。
所述的有机硅烷微乳液由以下重量份数的原料组成：聚二甲基硅氧烷12份、八甲基环四硅氧烷4份、十六烷基三甲基氯化铵2份、鲸蜡基聚乙二醇2份、十六烷基二甲基胺2份、油酸2份、二乙醇胺0.2份、异噻唑啉酮0.2份、去离子水75份。
所述的聚二甲基硅氧烷是道康宁生产的粘度为1000CS。
所述的改性聚丙烯酸树脂为季铵基丙烯酸酯共聚物。
所述的溶剂为二丙二醇甲醚。
所述的碱剂为碳酸钠。
所述的防腐剂为异噻唑啉酮。
一种上述的水基型防雨玻璃清洁剂的制备方法，包括以下步骤：
(1)取去离子水，加入有机硅烷微乳液和改性聚丙烯酸树脂，搅拌至溶解；
(2)向步骤(1)得到的溶液中加入溶剂，搅拌至溶解；
(3)向步骤(2)得到的溶液中加入碱剂，搅拌至溶解；
(4)向步骤(3)得到的溶液中加入防腐剂，搅拌至分散均匀，即得到所述水基型防雨玻璃清洁剂。
所述步骤(1)-(4)均在常温下进行；所述步骤(1)的搅拌转速为25r/min；所述步骤(2)的搅拌转速为30r/min；所述步骤(3)的搅拌转速为25r/min；所述步骤(4)的搅拌转速为25r/min。
实施例3
一种水基型防雨玻璃清洁剂，由以下重量份数的原料组成：有机硅烷微乳液2份、改性聚丙烯酸树脂2份、溶剂20份、碱剂1份、防腐剂2份、去离子水90份。
所述的有机硅烷微乳液由以下重量份数的原料组成：聚二甲基硅氧烷15份、八甲基环四硅氧烷5份、十六烷基三甲基氯化铵3份、鲸蜡基聚乙二醇4份、十六烷基二甲基胺3份、油酸3份、二乙醇胺0.3份、异噻唑啉酮0.3份、去离子水80份。、所述的聚二甲基硅氧烷是道康宁生产的粘度为12500CS。
所述的改性聚丙烯酸树脂为水溶性聚丙烯酸乙酯中。
所述的溶剂为乙二醇丁醚。
所述的碱剂为三乙醇胺。
所述的防腐剂为对羟基苯甲酸乙酯中。
一种上述的水基型防雨玻璃清洁剂的制备方法，包括以下步骤：
(1)取去离子水，加入有机硅烷微乳液和改性聚丙烯酸树脂，搅拌至溶解；
(2)向步骤(1)得到的溶液中加入溶剂，搅拌至溶解；
(3)向步骤(2)得到的溶液中加入碱剂，搅拌至溶解；
(4)向步骤(3)得到的溶液中加入防腐剂，搅拌至分散均匀，即得到所述水基型防雨玻璃清洁剂。
所述步骤(1)-(4)均在常温下进行；所述步骤(1)的搅拌转速为30r/min；所述步骤(2)的搅拌转速为32r/min；所述步骤(3)的搅拌转速为30r/min；所述步骤(4)的搅拌转速为30r/min。
实施例4
一种水基型防雨玻璃清洁剂，由以下重量份数的原料组成：有机硅烷微乳液3份、改性聚丙烯酸树脂3份、溶剂25份、碱剂2份、防腐剂3份、去离子水100份。
所述的有机硅烷微乳液由以下重量份数的原料组成：聚二甲基硅氧烷20份、八甲基环四硅氧烷5份、十六烷基三甲基氯化铵4份、鲸蜡基聚乙二醇5份、十六烷基二甲基胺4份、油酸4份、二乙醇胺0.5份、异噻唑啉酮0.4份、去离子水85份。
所述的聚二甲基硅氧烷是道康宁生产的粘度为30000CS。
所述的改性聚丙烯酸树脂为季铵基丙烯酸酯共聚物。
所述的溶剂为二乙二醇丁醚。
所述的碱剂为二乙醇胺。
优选的，所述的防腐剂为己内酰胺。
一种上述的水基型防雨玻璃清洁剂的制备方法，包括以下步骤：
(1)取去离子水，加入有机硅烷微乳液和改性聚丙烯酸树脂，搅拌至溶解；
(2)向步骤(1)得到的溶液中加入溶剂，搅拌至溶解；
(3)向步骤(2)得到的溶液中加入碱剂，搅拌至溶解；
(4)向步骤(3)得到的溶液中加入防腐剂，搅拌至分散均匀，即得到所述水基型防雨玻璃清洁剂。
所述步骤(1)-(4)均在常温下进行；所述步骤(1)的搅拌转速为40r/min；所述步骤(2)的搅拌转速为50r/min；所述步骤(3)的搅拌转速为40r/min；所述步骤(4)的搅拌转速为40r/min。
实施例5
一种水基型防雨玻璃清洁剂，由以下重量份数的原料组成：有机硅烷微乳液1份、改性聚丙烯酸树脂1份、溶剂15份、碱剂0.5份、防腐剂1份、去离子水83份。
所述的有机硅烷微乳液由以下重量份数的原料组成：聚二甲基硅氧烷30份、八甲基环四硅氧烷10份、十六烷基三甲基氯化铵5份、鲸蜡基聚乙二醇10份、十六烷基二甲基胺5份、油酸5份、二乙醇胺1份、异噻唑啉酮0.5份、去离子水90份。
所述的聚二甲基硅氧烷是道康宁生产的粘度为350CS、1000CS按照质量比为1:1复配而成。
所述的改性聚丙烯酸树脂为水溶性甲基丙烯酸辛酯、水溶性聚丙烯酸乙酯和水溶性水溶性聚丙烯酸甲酯按照质量比为3：2：1复配而成。
所述的溶剂为乙醇、丙二醇、乙二醇丁醚和二丙二醇甲醚按照质量比2：1：1：1复配而成。
所述碱剂为氢氧化钠、碳酸钠和三乙醇胺按照质量比1:1:2复配而成。
所述的防腐剂为异噻唑啉酮。
一种上述的水基型防雨玻璃清洁剂的制备方法，包括以下步骤：
(1)取去离子水，加入有机硅烷微乳液和改性聚丙烯酸树脂，搅拌至溶解；
(2)向步骤(1)得到的溶液中加入溶剂，搅拌至溶解；
(3)向步骤(2)得到的溶液中加入碱剂，搅拌至溶解；
(4)向步骤(3)得到的溶液中加入防腐剂，搅拌至分散均匀，即得到所述水基型防雨玻璃清洁剂。
所述步骤(1)-(4)均在常温下进行；所述步骤(1)的搅拌转速为30r/min；所述步骤(2)的搅拌转速为50r/min；所述步骤(3)的搅拌转速为40r/min；所述步骤(4)的搅拌转速为40r/min。
实施例6
一种水基型防雨玻璃清洁剂，由以下重量份数的原料组成：有机硅烷微乳液0.5份、改性聚丙烯酸树脂0.8份、溶剂15份、碱剂0.02份、防腐剂0.15份、去离子水85份。
所述的有机硅烷微乳液由以下重量份数的原料组成：聚二甲基硅氧烷20份、八甲基环四硅氧烷8份、十六烷基三甲基氯化铵4份、鲸蜡基聚乙二醇8份、十六烷基二甲基胺3份、油酸3份、二乙醇胺0.2份、异噻唑啉酮0.2份、去离子水80份。
所述的聚二甲基硅氧烷是道康宁生产的粘度为350CS、1000CS按照质量比为2:1复配而成。
所述的改性聚丙烯酸树脂为水溶性甲基丙烯酸辛酯、水溶性聚丙烯酸乙酯和水溶性水溶性聚丙烯酸甲酯按照质量比为4：1：1复配而成。
所述的溶剂为乙醇、丙二醇、乙二醇丁醚和二丙二醇甲醚按照质量比3：2：2：1复配而成。
所述碱剂为氢氧化钠、碳酸钠和三乙醇胺按照质量比3:1:3复配而成。
所述的防腐剂为对羟基苯甲酸乙酯。
一种上述的水基型防雨玻璃清洁剂的制备方法，包括以下步骤：
(1)取去离子水，加入有机硅烷微乳液和改性聚丙烯酸树脂，搅拌至溶解；
(2)向步骤(1)得到的溶液中加入溶剂，搅拌至溶解；
(3)向步骤(2)得到的溶液中加入碱剂，搅拌至溶解；
(4)向步骤(3)得到的溶液中加入防腐剂，搅拌至分散均匀，即得到所述水基型防雨玻璃清洁剂。
所述步骤(1)-(4)均在常温下进行；所述步骤(1)的搅拌转速为40r/min；所述步骤(2)的搅拌转速为50r/min；所述步骤(3)的搅拌转速为35r/min；所述步骤(4)的搅拌转速为35r/min。
对比例
一种水基型防雨玻璃清洁剂，由以下重量份数的原料组成：有机硅烷微乳液0.05份、改性聚丙烯酸树脂0.05份、溶剂4份、碱剂0.002份、防腐剂0.2份、去离子水96份。
各实施例产品性能测试：
清洁效果 疏水效果 透明度
实施例1 69％ 80％ 90％
实施例2 75％ 75％ 90％
实施例3 78％ 82％ 90％
实施例4 73％ 78％ 90％
实施例5 80％ 88％ 90％
实施例6 85％ 93％ 90％
对比例 48％ 60％ 90％
上述实施例为本发明较佳的实现方案，除此之外，本发明还可以其它方式实现，在不脱离本发明构思的前提下任何显而易见的替换均在本发明的保护范围之内。

Claims (10)

1.一种水基型防雨玻璃清洁剂，其特征在于，由以下重量份数的原料组成：
2.根据权利要求1所述的一种水基型防雨玻璃清洁剂，其特征在于，由以下重量份数的原料组成：
3.根据权利要求1所述的一种水基型防雨玻璃清洁剂，其特征在于：所述的有机硅烷微乳液由以下重量份数的原料组成：
4.根据权利要求3所述的一种水基型防雨玻璃清洁剂，其特征在于：所述的聚二甲基硅氧烷是道康宁生产的粘度为350CS、1000CS、12500CS、30000CS、60000CS中的一种或者几种。
5.根据权利要求1所述的一种水基型防雨玻璃清洁剂，其特征在于：所述的改性聚丙烯酸树脂为水溶性聚丙烯酸甲酯、季铵基丙烯酸酯共聚物和水溶性聚丙烯酸乙酯中的一种或者几种。
6.根据权利要求1所述的一种水基型防雨玻璃清洁剂，其特征在于：所述的溶剂为甲醇、乙醇、异丙醇、二丙二醇甲醚、乙二醇丁醚、二乙二醇丁醚、丙二醇、乙二醇中的一种或者几种。
7.根据权利要求1所述的一种水基型防雨玻璃清洁剂，其特征在于：所述的碱剂为氢氧化钠、氢氧化钾、碳酸钠、三乙醇胺、二乙醇胺和单乙醇胺中的一种或者几种。
8.根据权利要求1所述的一种水基型防雨玻璃清洁剂，其特征在于：所述的防腐剂为己内酰胺、异噻唑啉酮和对羟基苯甲酸乙酯中的一种或者几种。
9.一种根据权利要求1-8任一项所述的水基型防雨玻璃清洁剂的制备方法，其特征在于，包括以下步骤：
(1)取去离子水，加入有机硅烷微乳液和改性聚丙烯酸树脂，搅拌至溶解；
(2)向步骤(1)得到的溶液中加入溶剂，搅拌至溶解；
(3)向步骤(2)得到的溶液中加入碱剂，搅拌至溶解；
(4)向步骤(3)得到的溶液中加入防腐剂，搅拌至分散均匀，即得到所述水基型防雨玻璃清洁剂。
10.根据权利要求9所述的一种水基型防雨玻璃清洁剂的制备方法，其特征在于：所述步骤(1)-(4)均在常温下进行；所述步骤(1)的搅拌转速为20-40r/min；所述步骤(2)的搅拌转速为25-50r/min；所述步骤(3)的搅拌转速为20-40r/min；所述步骤(4)的搅拌转速为20-40r/min。
CN201710979032.4A 2017-10-19 2017-10-19 一种水基型防雨玻璃清洁剂及其制备方法 Withdrawn CN109679784A (zh)