CN109679178A - A kind of high-wearing feature rubber roller - Google Patents
A kind of high-wearing feature rubber roller Download PDFInfo
- Publication number
- CN109679178A CN109679178A CN201811609379.0A CN201811609379A CN109679178A CN 109679178 A CN109679178 A CN 109679178A CN 201811609379 A CN201811609379 A CN 201811609379A CN 109679178 A CN109679178 A CN 109679178A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- wearing feature
- roller
- rubber roller
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of high-wearing feature rubber roller, including roller core and the rubber being coated on roller core, the rubber is prepared from the following raw materials in parts by weight: 100 parts of carboxy nitrile rubber, 6~12 parts of titanium dioxide, 2~5 parts of antiaging agent, 15~30 parts of aluminium oxide, 3~8 parts of sulphur, 4~7 parts of zinc oxide, 1~4 part of promotor, 10~20 parts of white carbon black, 1~3 part of stearic acid.Aluminium oxide is added in a kind of rubber compounding of high-wearing feature rubber roller, not only effectively increase wear-resisting property, and have the characteristics that chemical property is stable, to effectively extend the service life of rubber roller, reduce maintenance times, Spinning process cost is virtually reduced, Spinning process efficiency is improved.
Description
Technical field
The present invention relates to textile machine equipment part field more particularly to a kind of high-wearing feature rubber rollers.
Background technique
Important component one of of the rubber roller as spinning, drawing region, the fine or not yarn quality concerning spinning of quality, life
Produce efficiency and recruitment cost.Spinning rubber-roller must have the characteristic that elasticity is good, wear-resisting, antistatic.However, the glue on existing market
Roller wear-resisting property is poor, and then causes its service life shorter, and frequent shutdown is needed to safeguard, virtually reduces Spinning process effect
Rate improves Spinning process cost.
Summary of the invention
It is an object of the invention in view of the above-mentioned problems, a kind of high-wearing feature rubber roller is provided, to solve existing textile machine
On the rubber roller wear-resisting property that uses it is poor, the short problem of service life.
The purpose of the present invention is be achieved through the following technical solutions:
A kind of high-wearing feature rubber roller, including roller core and the rubber being coated on roller core, the rubber is by following parts by weight
Raw material be made:
100 parts of carboxy nitrile rubber, 6~12 parts of titanium dioxide, 2~5 parts of antiaging agent, 15~30 parts of aluminium oxide, sulphur 3
~8 parts, 4~7 parts of zinc oxide, 1~4 part of promotor, 10~20 parts of white carbon black, 1~3 part of stearic acid.
As a preferred solution of the present invention, the rubber is prepared from the following raw materials in parts by weight:
100 parts of carboxy nitrile rubber, 8 parts of titanium dioxide, 4 parts of antiaging agent, 25 parts of aluminium oxide, 7 parts of sulphur, zinc oxide 6
Part, 3 parts of promotor, 20 parts of white carbon black, 3 parts of stearic acid.
As a preferred solution of the present invention, the mesh number of the aluminium oxide is 900 mesh~1100 mesh.
As a preferred solution of the present invention, the promotor is accelerant CZ, and its chemical name is N- cyclohexyl -2-
Benzothiazole sulfenamide.
As a preferred solution of the present invention, the antiaging agent is 2-mercaptobenzimidazole.
Beneficial effects of the present invention are, are added with aluminium oxide in a kind of rubber compounding of high-wearing feature rubber roller, not only
Wear-resisting property is effectively increased, and has the characteristics that chemical property is stable, to effectively extend the service life of rubber roller, is reduced
Maintenance times, virtually reduce Spinning process cost, improve Spinning process efficiency.
Specific embodiment
The technical scheme of the invention is further explained by means of specific implementation.It is understood that this place
The embodiment of description is used only for explaining the present invention rather than limiting the invention.
Embodiment one
In this present embodiment, a kind of high-wearing feature rubber roller, including roller core and the rubber being coated on roller core, the rubber by
The raw material of following parts by weight is made:
100 parts of carboxy nitrile rubber, 12 parts of titanium dioxide, 5 parts of antiaging agent, 30 parts of aluminium oxide, 8 parts of sulphur, zinc oxide 7
Part, 4 parts of promotor, 20 parts of white carbon black, 3 parts of stearic acid, wherein the mesh number of the aluminium oxide is 1100 mesh, and the promotor is
Accelerant CZ, the antiaging agent are 2-mercaptobenzimidazole.
Embodiment two
In this present embodiment, a kind of high-wearing feature rubber roller, including roller core and the rubber being coated on roller core, the rubber by
The raw material of following parts by weight is made:
100 parts of carboxy nitrile rubber, 6 parts of titanium dioxide, 2 parts of antiaging agent, 15 parts of aluminium oxide, 3 parts of sulphur, zinc oxide 4
Part, 1 part of promotor, 10 parts of white carbon black, 1 part of stearic acid, wherein the mesh number of the aluminium oxide is 900 mesh, and the promotor is to promote
Into agent CZ, the antiaging agent is 2-mercaptobenzimidazole.
Embodiment three
In this present embodiment, a kind of high-wearing feature rubber roller, including roller core and the rubber being coated on roller core, the rubber by
The raw material of following parts by weight is made:
100 parts of carboxy nitrile rubber, 7 parts of titanium dioxide, 4 parts of antiaging agent, 22 parts of aluminium oxide, 6 parts of sulphur, zinc oxide 5
Part, 2 parts of promotor, 18 parts of white carbon black, 2 parts of stearic acid, wherein the mesh number of the aluminium oxide is 950 mesh, and the promotor is to promote
Into agent CZ, the antiaging agent is 2-mercaptobenzimidazole.
Example IV
In this present embodiment, a kind of high-wearing feature rubber roller, including roller core and the rubber being coated on roller core, the rubber by
The raw material of following parts by weight is made:
100 parts of carboxy nitrile rubber, 8 parts of titanium dioxide, 4 parts of antiaging agent, 25 parts of aluminium oxide, 7 parts of sulphur, zinc oxide 6
Part, 3 parts of promotor, 20 parts of white carbon black, 3 parts of stearic acid, wherein the mesh number of the aluminium oxide is 1000 mesh, and the promotor is
Accelerant CZ, the antiaging agent are 2-mercaptobenzimidazole.
Rubber by using the formula production of the present embodiment has splendid wearability and elasticity, and can effectively extend it makes
With the service life, the present embodiment is preferred embodiment of the invention.
The above embodiments only describe the basic principles and characteristics of the invention, and the present invention is not limited by above-described embodiment,
Without departing from the spirit and scope of the present invention, the invention also has various changes and changes, and these changes and changes are all fallen
Enter in scope of the claimed invention.The claimed scope of the invention is defined by the following claims.
Claims (5)
1. a kind of high-wearing feature rubber roller, including roller core and the rubber being coated on roller core, it is characterised in that: the rubber is by following
The raw material of parts by weight is made:
100 parts of carboxy nitrile rubber, 6~12 parts of titanium dioxide, 2~5 parts of antiaging agent, 15~30 parts of aluminium oxide, sulphur 3~8
Part, 4~7 parts of zinc oxide, 1~4 part of promotor, 10~20 parts of white carbon black, 1~3 part of stearic acid.
2. a kind of high-wearing feature rubber roller according to claim 1, it is characterised in that: the rubber is by following parts by weight
Raw material is made:
100 parts of carboxy nitrile rubber, 8 parts of titanium dioxide, 4 parts of antiaging agent, 25 parts of aluminium oxide, 7 parts of sulphur, 6 parts of zinc oxide, promote
Into 3 parts of agent, 20 parts of white carbon black, 3 parts of stearic acid.
3. a kind of high-wearing feature rubber roller according to claim 2, it is characterised in that: the mesh number of the aluminium oxide is 900 mesh
~1100 mesh.
4. a kind of high-wearing feature rubber roller according to claim 3, it is characterised in that: the promotor is accelerant CZ.
5. a kind of high-wearing feature rubber roller according to claim 4, it is characterised in that: the antiaging agent is 2- sulfydryl benzo
Imidazoles.