CN109666419A - A kind of preparation method and products thereof that can tear off anti-absorbent-type screen process film at a high speed - Google Patents
A kind of preparation method and products thereof that can tear off anti-absorbent-type screen process film at a high speed Download PDFInfo
- Publication number
- CN109666419A CN109666419A CN201811650812.5A CN201811650812A CN109666419A CN 109666419 A CN109666419 A CN 109666419A CN 201811650812 A CN201811650812 A CN 201811650812A CN 109666419 A CN109666419 A CN 109666419A
- Authority
- CN
- China
- Prior art keywords
- film
- conductive layer
- absorbent
- high speed
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses one kind can tear off anti-absorbent-type screen process film and its production method at a high speed, the screen is made of with process film substrate, high-effective conductive layer, pressure-sensitive adhesive layer, release film and anti-absorption conductive layer, substrate is coated with high-effective conductive layer on one side, then it is bonded with release film by pressure-sensitive adhesive layer, another side and release back of the membrane are coated with anti-absorption conductive layer.The anti-static ability of glue surface greatly improved in the technical process film of the invention patent, so that it is can satisfy up to 10cm/s to the dissipation speed of electrostatic and is torn off the screen of speed and takes piece process, dust will not be caused to suck because of a large amount of accumulation of static electricity or screen punctures, raising production efficiency and yield rate;Simultaneously because the presence of anti-absorption conductive layer, the case where Electrostatic Absorption will not be generated during taking piece, increases the stability of technical process.
Description
Technical field
The present invention relates to adhesive tape areas, are specifically related to a kind of preparation that can tear off anti-absorbent-type screen process film at a high speed
Method and products thereof.
Background technique
Electronic apparatus class product is highly prone to contact staining or production in its surface during carrying perhaps production and application
Raw polishing scratch scratches, and protective film need to be used to carry out covering to make it from getting dirty or being damaged to its surface.This electron-like or electric type
Protective film used in product must also have a characteristic, it may be assumed that it not can produce larger electrostatic when removing, in order to avoid to electronic apparatus class product
It causes to damage;With becoming larger for screen size, the raising of production efficiency is required to be promoted, to the static dissipation capability of protective film
It asks in the case where large scale and high speed are torn off, high electrical breakdown capacitor or sucking dust cannot be generated.And it is used for the protection of screen protection
For film other than requirements above, also requiring the protective film is optical grade, and clean surface is visually observed with screen as if one.
Current antistatic protection film can only generally guarantee the screen protection of low speed or small size, in large scale screen or height
In the case of speed is torn off, electrostatic dissipation speed is too slow, be easy to cause accumulation of static electricity, generates the high voltage of 2-5KV, in this case
Easily puncture capacitor, causes screen damage, reduce yield rate or production efficiency, be unable to satisfy large-scale industrial production.
And can largely be stacked after being cut due to protective film, it is easily made because of the reason of Electrostatic Absorption during taking piece
It is not readily separated together at several films of contact are glutinous, causes to take piece difficult, influence production efficiency and stability.
Summary of the invention
In view of the deficiencies of the prior art, present invention aims at: providing one kind, can to tear off anti-absorbent-type screen at a high speed used
The preparation method of journey film.
Another object of the present invention is: provide above method preparation can tear off at a high speed anti-absorbent-type screen process film
Product.
In order to achieve the above objectives, the object of the invention is achieved through the following technical solutions: one kind can tear off at a high speed anti-absorption
The production method of type screen process film, includes: substrate, high-effective conductive layer, pressure-sensitive adhesive layer, release film from bottom to top, including under
State preparation step:
(a) two sides of substrate and the back side of release film are subjected to sided corona treatment, until the substrate corona surface surface tension >=
It is spare to be placed a period of time by 48dyn for the good substrate of corona;
(b) the anti-absorption of backsize of the anti-absorption conductive layer one of the coated on one side for the substrate that step (a) obtains and release film is led
Electric layer two;
(c) the another side coating high-efficient conductive layer for the substrate for obtaining step (b), sheet resistance 102-107Ω/□;
(d) layer upper surface for the release film for coating pressure-sensitive adhesive layer on high-effective conductive layer and obtaining with step (b) is compound, is prepared into half
Finished product material film;
(e) the material film for completing production carries out maturation process, obtains target product;
Preferably, the substrate is PET, PE, PVC or COP class optical thin film, with a thickness of 10-100 μm, is coated after sided corona treatment
High-effective conductive layer.Other suitable materials and thickness can also be first selected according to screen feature, technique and the optical requirement of client.
On the basis of above scheme, the ingredient of the high-effective conductive layer is PEDOT/PSS, the conductive layer with a thickness of
50-500nm.When coating pressure sensitive adhesive, due to the presence of PEDOT/PSS solvent, the PEDOT macromolecular meeting of part high-effective conductive layer
It mixes or is dissolved into pressure-sensitive adhesive layer, greatly improve the conductive capability of pressure-sensitive adhesive layer, while pressure-sensitive adhesive layer and high-effective conductive layer shape
At resistor coupled in parallel structure, the resistance value of entire glue surface is further decreased.
Preferably, the pressure-sensitive adhesive layer is with a thickness of 3-30 μm, peeling force 0-50g/25mm, glue group composition be polyurethane,
Polyacrylic acid or silicon based polymers will not generate the pollution such as residue glue under long term high temperature high humidity to screen, the pressure-sensitive adhesive layer
Sheet resistance is 103-109Ω/, under the speed of 5cm-50cm/s, the instant surface voltage < 500V of screen, it is ensured that in height
Under fast operating process adverse effect will not be generated to screen.
On the basis of above scheme, organic metal salt conductive agent is added in the pressure-sensitive adhesive layer, additive amount is described pressure-sensitive
1-the 20% of glue-line quality.Due to the presence of PEDOT/PSS solvent, the PEDOT macromolecular of part high-effective conductive layer can mix or
It is dissolved into pressure-sensitive adhesive layer, acts synergistically with the conductive agent small molecule in pressure-sensitive adhesive layer, further increase the conduction of pressure-sensitive adhesive layer
Ability.
Preferably, the organic metal salt conductive agent can by aperture 0.1um or more filter core.Its additive amount is very few
It is bad to will lead to anti-static effect, and is difficult to ensure prolonged anti-static effect, additive amount can excessively be prevented because pasting for a long time
Electrostatic agent is gradually precipitated, to pollute affixed object, while increasing cost, and has an impact to performances such as peeling forces.
Preferably, the release film is the PET film with release performance, pressure-sensitive to reach protection with a thickness of 25-150um
The effect of glue-line.
Preferably, (ingredient is identical, is PEDOT/PSS or polysiloxane-based conduction material for the anti-absorption conductive layer one, two
Expect coating, coating with a thickness of 50-500nm, sheet resistance 104-1011Ω/ can be reduced between product of the present invention film and film
The generation of electrostatic prevents the absorption between diaphragm.
On the basis of above scheme, in step (a), the standing time be 3 days or more, place environment be room temperature or
40-60 DEG C of high temperature prevents from having an impact back segment so that the ozone that corona generates decomposes.
Preferably, in process step (e), the curing time be 3-10 days, place environment be room temperature or 40-60 DEG C of high temperature,
Stablize to peeling force, i.e. curing is completed.
The present invention also provides one kind can tear off anti-absorbent-type screen process film at a high speed, the side according to any of the above-described
What method was prepared.
The present invention is advantageous in that the present invention can tear off at a high speed screen process film, can be existed with effective solution process film
The problems such as dust absorption generated during tearing off and screen puncture, while will not be generated between film and film during taking piece
Electrostatic Absorption the case where, increase the safe and stable property of technical process.
Detailed description of the invention
By the description carried out with reference to the accompanying drawing to its exemplary embodiment, features described above and advantage of the present invention will become
It obtains more clear and is readily appreciated that.
Fig. 1 is a kind of structural schematic diagram that can tear off anti-absorbent-type screen process film at a high speed;
Fig. 2 is a kind of production process schematic diagram that can tear off anti-absorbent-type screen process film at a high speed;
Figure label explanation:
1 --- substrate;2 --- high-effective conductive layer;
3 --- pressure-sensitive adhesive layer;4 --- release film;
5,5 ' --- anti-absorption conductive layer one, two.
Specific embodiment
The present invention is described in further detail below in conjunction with the accompanying drawings.
If Fig. 1 is that a kind of can to tear off anti-absorbent-type screen at a high speed with the structural schematic diagram of process film and Fig. 2 be that one kind can be high
Speed is torn off shown in the production process schematic diagram of anti-absorbent-type screen process film, and it is used that one kind can tear off at a high speed anti-absorbent-type screen
The production method of journey film, such as Fig. 1, from bottom to top by: anti-absorption conductive layer 1, substrate 1, high-effective conductive layer 2, pressure-sensitive adhesive layer 3,
Release film 4 and anti-absorption conductive layer 25 ' constitute laminar product, and preparation step is as shown in Figure 2:
(a) two sides of substrate 1 and the back side of release film 4 are subjected to sided corona treatment respectively, until the electricity of the substrate 1 and release film 4
The good substrate of corona and release film 4 are stood no less than 3 days by dizzy face surface tension >=48dyn, and placing environment is room temperature or 40-
60 DEG C of high temperature, it is spare, wherein
Wherein, the substrate 1 is PET, PE, PVC or COP class optical thin film, with a thickness of 10-100 μm.
The release film 4 is the PET film with release performance, with a thickness of 25-150um.
(b) the anti-absorption conductive layer 1 of the coated on one side for the substrate 1 for obtaining step (a), in addition, the back side of release film 4 applies
Deployment absorption conductive layer 25 ';Wherein, the ingredient of anti-absorption conductive layer one, two (5,5 ') is identical, for PEDOT/PSS or poly-
Type siloxane conductive material coating, coating with a thickness of 50-500nm, sheet resistance 104-1011Ω/□。
(c) the another side coating high-efficient conductive layer 2 of the good substrate 1 of the corona for obtaining step (b), the high-effective conductive layer
2 ingredient be PEDOT/PSS, the conductive layer with a thickness of 50-500nm, sheet resistance 102-107Ω/□;
(d) pressure-sensitive adhesive layer 3 is coated on high-effective conductive layer 2, the pressure-sensitive adhesive layer 3 is with a thickness of 3-30 μm, peeling force 0-50g/
25mm, glue group composition are polyurethane, polyacrylic acid or silicon based polymers, add organic metal salt conductive agent, additive amount is described
1-the 20% of 3 mass of pressure-sensitive adhesive layer, the sheet resistance of pressure-sensitive adhesive layer 3 are 103-109Ω/, under the speed of 5cm-50cm/s,
The instant surface voltage < 500V of screen;
The layer upper surface of the pressure-sensitive adhesive layer 3 and the release film 4 that step (b) obtains is compound, is prepared into semi-finished product material film;
Wherein, the organic metal salt conductive agent can by aperture 0.1um or more filter core.
(e) the semi-finished product material film of production is carried out curing 3-10 days, placing environment is room temperature or 40-60 DEG C of high temperature, until stripping
Stablize from power, i.e. curing is completed, and anti-absorbent-type screen process film can be torn off at a high speed by obtaining one kind.
It is provided by the present invention to tear off anti-absorbent-type screen at a high speed and can guarantee that screen is torn off by protective film with process film
Situations such as screen breakdown and dust sucking will not be generated in the process, and still can guarantee screen when large scale or high speed are torn off
Scene plot face maximum voltage < 500V;Simultaneously because the presence of anti-absorption conductive layer, will not generate electrostatic suction during taking piece
Attached situation increases the stability of technical process.
Claims (10)
1. the preparation method that one kind can tear off at a high speed anti-absorbent-type screen process film, it is characterised in that: from bottom to top include: base
Material (1), high-effective conductive layer (2), pressure-sensitive adhesive layer (3), release film (4), including following preparation steps:
(a) two sides of substrate (1) and the back side of release film (4) are subjected to sided corona treatment, until the substrate (1) corona surface surface
It is spare to be placed a period of time by power >=48dyn for the good substrate of corona and release film (4);
(b) backsize of anti-absorption conductive layer one (5) and release film (4) of the coated on one side of the substrate (1) obtained step (a)
Anti- absorption conductive layer two (5 ');
(c) the another side coating high-efficient conductive layer (2) of the substrate (1) obtained step (b), sheet resistance 102-107Ω/□;
(d) layer upper surface for the release film (4) for coating pressure-sensitive adhesive layer (3) on high-effective conductive layer (2) and obtaining with step (b) is multiple
It closes, is prepared into semi-finished product material film;
(e) the semi-finished product material film of production is subjected to maturation process, obtains target product;
Wherein, the substrate (1) is PET, PE, PVC or COP class optical thin film, with a thickness of 10-100 μm, is coated after sided corona treatment
High-effective conductive layer (2).
2. the preparation method of anti-absorbent-type screen process film can be torn off at a high speed as described in claim 1, it is characterised in that: institute
State high-effective conductive layer (2) ingredient be PEDOT/PSS, the conductive layer with a thickness of 50-500nm.
3. the preparation method of anti-absorbent-type screen process film can be torn off at a high speed as described in claim 1, it is characterised in that: institute
Pressure-sensitive adhesive layer (3) is stated with a thickness of 3-30 μm, peeling force 0-50g/25mm, glue group composition is polyurethane, polyacrylic acid or silica gel
Polymer, sheet resistance 103-109Ω/, under the speed of 5cm-50cm/s, the instant surface voltage < 500V of screen.
4. the preparation method as claimed in claim 1 or 3 that can tear off anti-absorbent-type screen process film at a high speed, feature exist
In: organic metal salt conductive agent is added in the pressure-sensitive adhesive layer (3), additive amount is 1-the 20% of the pressure-sensitive adhesive layer (3) quality.
5. the preparation method of anti-absorbent-type screen process film can be torn off at a high speed as claimed in claim 4, it is characterised in that: institute
The organic metal salt conductive agent stated can by aperture 0.1um or more filter core.
6. the preparation method of anti-absorbent-type screen process film can be torn off at a high speed as described in claim 1, it is characterised in that: institute
Stating release film (4) is the PET film with release performance, with a thickness of 25-150um.
7. the preparation method of anti-absorbent-type screen process film can be torn off at a high speed as described in claim 1, it is characterised in that: institute
The ingredient for stating anti-absorption conductive layer one, two (5,5 ') is identical, is PEDOT/PSS or polysiloxane-based conductive material coating, coating
With a thickness of 50-500nm, sheet resistance 104-1011Ω/□。
8. the preparation method of anti-absorbent-type screen process film can be torn off at a high speed as described in claim 1, it is characterised in that:
In step (a), the standing time is 3 days or more, and placing environment is room temperature or 40-60 DEG C of high temperature.
9. the preparation method of anti-absorbent-type screen process film can be torn off at a high speed as described in claim 1, it is characterised in that:
In step (e), the curing time is 3-10 days, and placing environment is room temperature or 40-60 DEG C of high temperature, until peeling force is stablized, i.e., it is ripe
Change and completes.
10. one kind can tear off at a high speed anti-absorbent-type screen process film, according to claim 1 to any one of 9 preparation methods
It obtains.